CN1388178A - Prepn of low-temperature resistant intermingled polycarbonate material - Google Patents
Prepn of low-temperature resistant intermingled polycarbonate material Download PDFInfo
- Publication number
- CN1388178A CN1388178A CN 02111911 CN02111911A CN1388178A CN 1388178 A CN1388178 A CN 1388178A CN 02111911 CN02111911 CN 02111911 CN 02111911 A CN02111911 A CN 02111911A CN 1388178 A CN1388178 A CN 1388178A
- Authority
- CN
- China
- Prior art keywords
- polycarbonate
- polyolefin elastomer
- low
- intermingled
- temperature resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention is the preparation of low-temperature resistant intermingled polycarbonate material. It is prepared with polycarbonate and polyolefin elastomer as basic material and through adding polyolefin elastomer grafted copolymer and ionic polymer compatibilizer and fusion in a double-screw extruder. The low-temperature resistant intermingled polycarbonate material has excellent low temperature impact property, improved polycarbonate notch sensitivity, high chemical corrosion resistance, high boiling water resistance and excellent mechanical property and thus has wide industrial application foreground.
Description
Technical field: the preparation method who the present invention relates to a kind of low-temperature resistant intermingled polycarbonate material.
Background technology: polycarbonate (PC) is as a kind of functional, and also there are some defectives in broad-spectrum engineering plastics, and are relatively poor as processing characteristics, easy stress cracking, and notch shock and low-temperature flexibility difference etc., and also price is higher.Can reach by blending and modifying and to improve performance, the purpose that reduces cost PC.PC blend patent and bibliographical information are more at present, and have multiple alloy to succeed in developing and realize suitability for industrialized production.For example U.S. Pat P6166133, USP5384353, USP5223573 have reported the blend of PC and acrylonitrile-butadiene-styrene copolymer, patent report such as USP6197873, USP6043322 PC and polyester blend, also have polycarbonate/polymethylmethacrylate (PC/PMMA), polycarbonate/thermoplastic polyurethane PC blends such as (PC/TPU) in addition.PC and polyethylene (PE) (the Japanese Patent spy opens clear 40-13663) and polypropylene (PP) (USP4568723) blend also have document and patent report.U.S. Pat P5021504 has reported the application of polyolefin elastomer in the PC alloy, and polyolefinic maleic anhydride graft copolymer is used for improving the consistency of PC and other polymkeric substance, can not give full play to the modifying function of polyolefin elastomer to PC.
Summary of the invention: the objective of the invention is to PC and polyolefin elastomer is that base mateiral prepares a kind of good low-temperature performance that has, the intermingling material that other over-all properties is good.
Low-temperature resistant intermingled polycarbonate material preparation method of the present invention is when selecting polyolefin graft copolymer as expanding material, at first prepare the polyolefin elastomer graft copolymer, polyolefin elastomer and graft copolymer thereof are concerned by a certain percentage with PC carry out blend then; When selecting ionic polymer as compatilizer, at first ionic polymer and polyolefin elastomer are carried out blend by a certain percentage, then with the gained mixture again with the PC blend.
The present invention utilizes polyolefin elastomer and PC blend, can obtain good modified effect.Behind polyolefin elastomer grafted maleic anhydride, vinylformic acid or the acrylic ester monomer, increased the polarity of polyolefin elastomer molecule, when carrying out blend with PC, the two-phase interface in the blend improves, and ionic polymer can improve the consistency between polyolefin elastomer and the PC equally.The polyolefin elastomer graft copolymer has extremely low second-order transition temperature, therefore under lower temperature, polyolefin elastomer graft copolymer in the blend still keeps good deformation and motor capacity, still can cause a large amount of crazing and shear zone to the PC matrix, thereby improve the low-temperature flexibility of blend.
The polycarbonate that the present invention uses comprises aliphatic polycarbonate, fat-aromatic copolycarbonate and aromatic copolycarbonate.Wherein based on bisphenol A polycarbonate, molecular weight is 26000～42000, and the consumption in intermingling material is 80%～98% (weight percent).
The polyolefin elastomer that the present invention uses is ethene and high alpha-olefin multipolymer, high alpha-olefin is that carbonatoms is 4～10 alpha-olefin, with ethylene copolymer in content be 5%～50%, the consumption in intermingling material is 2%～20% (weight percent).
The polyolefin elastomer graft copolymer that the present invention uses is the multipolymer of polyolefin elastomer and maleic anhydride, vinylformic acid and acrylics grafted monomer, the percentage of grafting of grafted monomer such as maleic anhydride, vinylformic acid and acrylics is 0.1%～3% in the polyolefin elastomer graft copolymer, best percentage of grafting is 0.3%～0.8%, and the consumption in intermingling material is 0%～10% (weight percent).
The ionic polymer that the present invention uses is to introduce metal ion (comprising Na, Zn, K, Mg ion) in ethene and the acrylic or methacrylic acid copolymer to carry out crosslinked product, and usage quantity is 0%～3% (weight percent) in intermingling material.
The production unit of the low temperature resistant intermingling material of the present invention is a twin screw extruder, and the processing temperature scope is 230 ℃～270 ℃, and screw speed is 160～240r/min.
The intermingling material of the present invention's preparation has good low temperature impact properties, and has improved PC notch sensitivity, chemical-resistant resistance and resistant to boiling water performance etc.Resulting other mechanical propertys of PC intermingling material of the present invention are good, and production technique is simple, has wide application and industrial prospect.
Embodiment: the following examples are to further specify of the present invention, do not limit the scope of the invention.
Embodiment 1-5 PC/ polyolefin elastomer binary intermingling material
PC was descended dry 10 hours at 120 ℃, melt extrude in twin screw extruder with the proportionlity of polyolefin elastomer then by routine 1-5, cooling, pelletizing, the processing temperature scope is 230 ℃～270 ℃, screw speed is 160～240r/min.Particle with blend descended the injection molding test bars dry 10 hours at 100 ℃ then.The injection top temperature is 260 ℃.The Impact Test batten is of a size of 63mm * 6.4mm * 12.66mm, and the injection batten was at room temperature parked 24 hours.Then at a side mechanical workout v-notch that impacts batten, notch depth 2.66mm, breach bottom radius 0.25mm.Test mode is carried out according to ASTM256: selecting temperature is 23 ℃ and-30 ℃, socle girder notch shock mode, impact velocity 3.5m/s.The measurement of tensile strength is tested according to ASTM D638.Test result is as shown in the table.
| Example | The PC/ polyolefin elastomer | The socle girder notched Izod impact strength, J/m | Tensile strength MPa | Elongation at break % | |
| ????23℃ | ????-30℃ | ||||
| ????1 | ????100/0 | ????145.6 | ????136.5 | ????58.12 | ????102 |
| ????2 | ????98/2 | ????542.1 | ????160.5 | ????50.36 | ????68 |
| ????3 | ????95/5 | ????828.4 | ????286.5 | ????53.74 | ????83 |
| ????4 | ????90/10 | ????765.3 | ????464.0 | ????43.30 | ????57 |
| ????5 | ????80/20 | ????581.3 | ????388.7 | ????38.24 | ????25 |
Embodiment 6-10 PC/ polyolefin elastomer/ionic polymer tertiary blending material
Ionic polymer is concerned by a certain percentage, at first in twin screw extruder, melt extrude granulation with polyolefin elastomer.Extruder temperature is set to 140 ℃～180 ℃.Elastomerics and ionic polymer blend grain after 5 hours, according to extruding and the injection technique condition of routine 1-5, are prepared test bars 70 ℃ of dryings.The weight ratio of polycarbonate and polyolefin elastomer is 80/20.Test tensile property, impact property and bending property according to ASTMD638, ASTMD256, ASTMD790 respectively.Test result is as shown in the table.
| Example | Ionic polymer consumption % | Tensile strength MPa | Elongation at break % | Socle girder notched Izod impact strength J/m | Modulus in flexure MPa |
| ????6 | ????0 | ????38.24 | ????25.4 | ????581.3 | ????1460 |
| ????7 | ????0.5 | ????40.52 | ????83.5 | ????624.4 | ????1658 |
| ????8 | ????1 | ????39.65 | ????105.4 | ????572.2 | ????1721 |
| ????9 | ????2 | ????39.44 | ????102.4 | ????504.7 | ????1632 |
| ????10 | ????3 | ????36.41 | ????26.7 | ????265.5 | ????1547 |
Claims (6)
1. the preparation method of low-temperature resistant intermingled polycarbonate material, it is characterized in that when selecting polyolefin graft copolymer as expanding material, at first prepare the polyolefin elastomer graft copolymer, polyolefin elastomer and graft copolymer thereof are concerned by a certain percentage with PC carry out blend then; When selecting ionic polymer as compatilizer, at first ionic polymer and polyolefin elastomer are carried out blend by a certain percentage, then with the gained mixture again with the PC blend.
2. the preparation method of low-temperature resistant intermingled polycarbonate material according to claim 1 is characterized in that polycarbonate comprises aliphatic polycarbonate, fat-aromatic copolycarbonate and aromatic copolycarbonate.Wherein based on bisphenol A polycarbonate, molecular weight is 26000～42000, and the consumption in intermingling material is 80%～98% (weight percent).
3. the preparation method of low-temperature resistant intermingled polycarbonate material according to claim 1, it is characterized in that polyolefin elastomer is ethene and high alpha-olefin multipolymer, high alpha-olefin is that carbonatoms is 4～10 alpha-olefin, with ethylene copolymer in content be 5%～50%, the consumption in intermingling material is 2%～20% (weight percent).
4. the preparation method of low-temperature resistant intermingled polycarbonate material according to claim 1, it is characterized in that the polyolefin elastomer graft copolymer is the multipolymer of polyolefin elastomer and maleic anhydride, vinylformic acid and acrylics grafted monomer, the percentage of grafting of grafted monomer such as maleic anhydride, vinylformic acid and acrylics is 0.1%～3% in the polyolefin elastomer graft copolymer, best percentage of grafting is 0.3%～0.8%, and the consumption in intermingling material is 0%～10% (weight percent).
5. the preparation method of low-temperature resistant intermingled polycarbonate material according to claim 1, it is characterized in that ionic polymer is to introduce metal ion (comprising Na, Zn, K, Mg ion) in ethene and the acrylic or methacrylic acid copolymer to carry out crosslinked product, usage quantity is 0%～3% (weight percent) in intermingling material.
6. the preparation method of low-temperature resistant intermingled polycarbonate material according to claim 1 is characterized in that production unit is a twin screw extruder, and the processing temperature scope is 230 ℃～270 ℃, and screw speed is 160～240r/min.