CN1382656A - Process for preparing strengthend antiearthquake glass with colour pattern - Google Patents
Process for preparing strengthend antiearthquake glass with colour pattern Download PDFInfo
- Publication number
- CN1382656A CN1382656A CN 02117976 CN02117976A CN1382656A CN 1382656 A CN1382656 A CN 1382656A CN 02117976 CN02117976 CN 02117976 CN 02117976 A CN02117976 A CN 02117976A CN 1382656 A CN1382656 A CN 1382656A
- Authority
- CN
- China
- Prior art keywords
- glass
- printing
- antiearthquake
- tempering
- manufacture method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A process for preparing strengthened antiearthquake glass with colour pattern includes cutting by needed sizes, grinding, off-set printing with low-temp baking between printing steps, strengthening, quick cooling, and solhering antiearthquake rubber. Its advantages are lifelike pattern, and high antiearthquake and anti-impact power.
Description
Invention field
The present invention relates to a kind of manufacture method of strengthend antiearthquake glass with colour pattern.
Background technology
The traditional glass painting methods has methods such as colored drawing, spraying, transfer printing and screen painting.When present toughened glass colouring mode is spray pattern.For example, Chinese patent 89105933-6 discloses the manufacture method that colored gradual change look glass-making processes and Chinese patent application number 0010045.4 discloses toughened color glass.All adopt the spraying chemical agent, staining method through the tempering processing, the result of its colouring is solid color or progressive coloured or intermediate color, its shortcoming is that color has only the depth of single colour system to change, and do comprehensive coating, can't handle at part colouring or several colourings more than color, more can't find expression on glass for given pattern or scenery.
According to the technology of glass colouring at present, have only the screen painting mode can be revealed in real pattern on glass.Chinese patent notification number 1062238 discloses the method at reduction pigment figure on glass, be the screen painting mode and manifest figure, but after its plate-making mode need have physical item to take a picture, by making separation negative through the color separation printing, make the color separation half tone more again by the egative film after taking a picture.Its prerequisite ratio need have actual object to take, and shooting process can be because of the generation distortion phenomenon of amblent air temperature, light.
Summary of the invention
The invention reside in and change comprehensive coating that traditional toughened glass can only be made single colour system, do the breakthrough of an invention of great significance, make toughened glass not only as outside present building figure curtain and the windshield, polychrome printing through half tone, various appointed pattern or scenery are truly found expression on glass, make the scope of toughened glass utilization more extensive.
Operating system is to obtain scenery from the CD laser disc before the seal of the present invention, utilize the figure of computer video composing system with the desire printing, no matter be actual object or virtual scene even computer video synthetic figure, directly connect egative film output machine, make the printing egative film, do not need by finding a view, take, carry out color separation with taking the egative film of finishing again, make the color separation half tone, avoiding the phenomenon of distortion, and be not subject to obtaining of physical item.
Method of the present invention may further comprise the steps:
A, cut the glass of desired size, after grinding, print after making half tone by lithographic plate color printing chromatography principle (off-set printing), need after every look printing to repeat print and drying operation, finish until last look chromatography through the oven drying at low temperature processing;
B, the glass that is completed for printing is carried out tempering handle, utilize quick cooling behind the high temperature of tempering, destroy glass interior molecules structural arrangement, glass hard (HRC65 is increased;
C, the glass that tempering is finished and Shockproof rubber are fitted, and reach shockproof effect.Promptly finished the manufacturing of strengthend antiearthquake glass with colour pattern.
Though the mode of printing that the present invention relates to is all the screen painting mode with Chinese patent 1062838 in the manufacture method of reducing matter colour and figure on glass, but the former is required to be actual object for finding a view be shortcoming one, and shooting process can be influenced by externalities and distortion is a shortcoming two, and the egative film of shooting carries out color-dividing system and becomes that color separation half tone process is very complicated to be shortcoming three.Operating system is utilized computer video composing system before the seal of the present invention, find a view to handle the back with video and directly be connected egative film output machine and make the color separation half tone, process simply and video more true.
And the present invention and the former bigger not being all: the glass after the former is completed for printing needs through high bake, power consumption, consume man-hour, yield poorly, and the glass finished of baking only with clagging in glass surface, not making tempering handles and shockproof processing, so its glass only can be made the purposes of vision, and the glass of the present invention after being completed for printing is handled and shockproof processing through tempering, and shatter-proof and impact-resistant function is arranged, its practicality and functionally more can extensively use, and the production capacity that tempering is handled is 10 times of high bake, more can reduce production costs, improve output, improve the quality of products.
Description of drawings
Fig. 1 is a process flow sheet of the present invention.
Embodiment
Original sheet glass is removed to the CNC cutting machine, desired the size that cuts, utilize the diamond glass-cutting in computer input.
The glass that cutting is finished places on the automatic diamond edge grinding machine, utilizes the rotation of diamond wheel edging, with contacting of glass edge, reaches the grinding on four limits.
Utilize computer video composing system, the CD laser disc of desire printing is made separation negative via egative film output machine, again separation negative are shone the system color separation half tone and the ratio of blending ink.
Printing ink after the blending is poured on the half tone that completes, and carried out chromaticity printing with the method for lithographic plate color printing chromatography principle (off-set printing).
Glass after the printing is inserted in the process furnace, and in the low temperature mode, temperature is 200-250 ℃, with printing ink oven dry on glass.
Aforesaid printing and drying operation are carried out repeatedly, and extremely last look chromatography finishes, and promptly finishes printing and oven dry.
Send the glass that is completed for printing to annealing furnace, utilize the type of heating of annealing furnace, temperature is 580-620 ℃, heating back quick cooling principle, the molecular arrangement mode of destruction glass inside, the hardness of increase glass.
The glass that tempering is finished is done shockproof processing, glass and Shockproof rubber are fitted, promptly finish strengthend antiearthquake glass with colour pattern with manual mode.
It should be understood that above only is of the present invention one preferable embodiment, and it is used for illustrating the present invention, and does not limit its scope.
Claims (4)
1, a kind of manufacture method of strengthend antiearthquake glass with colour pattern, this method may further comprise the steps:
A, cut the glass of desired size, after grinding, print after making half tone by lithographic plate color printing chromatography principle (off-set printing), need after every look printing to repeat print and drying operation, finish until last look chromatography through the oven drying at low temperature processing;
B, the glass that is completed for printing is carried out tempering handle, utilize quick cooling behind the high temperature of tempering, destroy glass interior molecules structural arrangement, glass hard (HRC65 is increased;
C, the glass that tempering is finished and Shockproof rubber are fitted, and reach shockproof effect.
2, according to the manufacture method of claim 1, the temperature of wherein said oven drying at low temperature is between 200-250 ℃.
3, according to the manufacture method of claim 1, the high temperature of wherein said tempering is between 580-620 ℃.
4, the strengthend antiearthquake glass with colour pattern that obtains according to the manufacture method of claim 1.