CN1382584A - Adhered composite film cloth and its making method - Google Patents
Adhered composite film cloth and its making method Download PDFInfo
- Publication number
- CN1382584A CN1382584A CN 01110790 CN01110790A CN1382584A CN 1382584 A CN1382584 A CN 1382584A CN 01110790 CN01110790 CN 01110790 CN 01110790 A CN01110790 A CN 01110790A CN 1382584 A CN1382584 A CN 1382584A
- Authority
- CN
- China
- Prior art keywords
- cloth
- composite film
- top layer
- cloth body
- adhered composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A composite cloth with film layer is composed of a cloth layer as main body and several surface layers including a resin layer or adhesive layer close to the cloth layer and different film layers with different characteristics. As soon as the film layer is formed, it is adhered onto the cloth layer. Its advantages are high softness, and no environmental pollution. The method for mfg. the same is also disclosed.
Description
The present invention is about a kind of adhered composite film cloth and manufacture method thereof, refers to a kind ofly with easier, the manufacture method of environmental protection more especially, produces the multiple field thin-film adhesive cloth of providing diversified function.
Variation has been moved towards in the design of cloth body at present, multi-functional direction, so that the cloth body is original warming except possessing, outside the basic function such as attractive in appearance, still other properties of tool, as: the cloth body in its warp, all form the gap between weft yarn, except aspect intensity, be able to the yarn material select for use and burst the footpath design and changing, itself do not have the function of waterproof, and in recent years because of the application of some cloth body, must make it have the function of waterproof concurrently, how to make the cloth body have the function of waterproof concurrently? promptly in the industry cycle by extensive discussions, when only the cloth body possesses the waterproof effect, whether the design requirement that must consider cloth body itself simultaneously is destroyed, change, as the pliability of cloth body itself, the intensity of cloth body, even the waterproof cloth system is when making, whether causing problems such as environmental pollution on the contrary, also is that the dealer must consider.
And being seen the earliest waterproof cloth body, be that the plasticity waterproof solution is formed watertight composition in the mode that is coated with in the cloth surface, only not only processing procedure speed is slow, consuming time for this kind method, and easier external factor because of other, and the situation that causes crawling to be spared, so that can't make the cloth body possess the function of comprehensive waterproof, therefore present waterproof cloth body except the part poor quality is seen in industry is less still making in this way.
Near and replacement be the manufacture method of laminated method, it is by the bonding mode, watertight composition is attached on the cloth body, and being seen laminated method has two kinds of patterns at present, promptly be respectively Fig. 7 and manufacturing process shown in Figure 8, please refer to shown in Figure 7, it is that material feeding district 81 is set on the conveyer belt of cloth body 80 in regular turn, applying area 82 and bonding zone 83, wherein material feeding district 81 can annotate an amount of glutinous agent and spill in cloth body 80 surfaces, and glutinous agent is by after the applying area 82, promptly make its even distribution, make the 80 uniform glutinous agent in surface of cloth body, during to bonding zone 83 by scraper 821, make the watertight composition 84 that is volume again, contact with cloth body 80 in regular turn, the applying one makes cloth body one side have watertight composition by the pressing wheel 831 of bonding zone 83 again.
Manufacture shown in Figure 8 in addition, be that coating area 91 and bonding zone 92 are set on the conveyer belt of cloth body 90, wherein gluing 91 has and can contain the rubber tire 912 that is dipped in the glue groove 911, rubber tire 912 upper ends are provided with presses wheel 913, when cloth body 90 passes through rubber tire 912, be about to glue application in cloth body 90 1 sides, when making it to bonding zone 92, simultaneously can with watertight composition 93 applying one.
Only above-mentionedly watertight composition and cloth are shown consideration for manufacture of unify and the waterproof cloth body of making, all have shortcoming, come opinion with manufacture earlier, i.e. shortcoming below the existence in the bonding mode:
1. above-mentioned two kinds of manufacture methods, in single manufacturing process, only can form watertight composition in cloth body one side, after if one-sided fabrication schedule must possess watertight composition the time, must be finished in cloth body both sides, the mode that is inverted with the cloth body again, form watertight composition again in other side, therefore the mode of making is restricted, and the waterproof cloth body of single face waterproof can't be provided on demand and fast, or the waterproof cloth body of two-sided equal waterproof.
2. the watertight composition of above-mentioned two kinds of manufacture methods be utilize other make-up machine to make to furl in advance be tubular after, the conveyer belt place that moves to the cloth body again carries out the applying program, so this applying program, two road procedures promptly must be arranged, one is the moulding watertight composition, and two are the applying watertight composition, and make procedure for producing too numerous and diverse, and cause manufacturing cost higher, the manufacturing cost of waterproof cloth body is reduced.
3. above-mentioned waterproof cloth body must be with viscose as adhesive, so this type of viscose mostly is PU, acryl, CR glue or other organic solids greatly, wherein contain organic solvent materials such as dimethylbenzene, toluene, and because of above-mentioned waterproof cloth body in the applying process, the palpus heat treated, so pine in adding, above-mentioned substance promptly can volatilize in air, causes environmental pollution.
Come opinion with above-mentioned example with the waterproof patch that laminating type forms again, also have following shortcoming:
1. above-mentioned watertight composition is because of being to show consideration for cloth after the in advance moulding to close again, so present dealer adopts the manufacturing of PVC material to be the kenel of diaphragm mostly, so because of its must furl earlier be tubular after, show consideration for cloth again and close, so its thickness is limited in more than 0.06, so after watertight composition and cloth body fit again, promptly because of the excessive cause of thickness, cause to present the original soft texture of cloth body,, more make the purposes of cloth body limited so not only destroy the original meaning of cloth body design.
2. above-mentioned watertight composition is to make with the PVC material, therefore easily causes the problem of environmental protection.
So from the above, the not only own product of waterproof cloth body that forms with laminating type can't satisfy the demands of consumers at present, and its manufacture is not more had an economic worth of utilizing on the industry, environmental pollution problems is more arranged, therefore, for providing one to have more the applying cloth of practicality and a manufacture method that has more economic benefit is provided, this creator designs the present invention's " adhered composite film cloth and manufacture method thereof ", uncommonly reaches following purpose by design of the present invention:
The main purpose of the present invention's design, provide a kind of adhered composite film cloth, this applying cloth mainly has a cloth body, one-sided or the bilateral of Yu Buti is provided with plural top layer respectively in regular turn, wherein the top layer that contacts with the cloth body can be the pouring film resin of the high now characteristic of tool or tool property own and contains the top layer of attached outstanding effect, remaining top layer can be the thin layer of tool different qualities, each top layer is after the moulding of T type shaping mould, promptly show consideration for cloth simultaneously and close, therefore its thickness that is able to as thin as a wafer combines with the cloth body, make the still splendid pliability of tool of cloth body, and by solvent-free processing procedure, therefore do not have the misgivings of environmental protection and make the cloth body possess multiple strengthening function, and an adhered composite film cloth that has more practicality is provided.
Another main purpose of the present invention's design, provide a kind of manufacture method of adhered composite film cloth, this manufacture method is that the several shaping moulds by shaping area form each top layer simultaneously, combine with each top layer with the cloth body that is about to input afterwards, then applying cloth is pressed be one by being close to wheels, promptly form adhered composite film cloth, reason method of the present invention, the applying cloth that even the cloth body is one-sided or bilateral all has property, all can finish with same easy program, and each top layer combines with the cloth body after moulding immediately, therefore manufacturing cost is reduced more.
A kind of adhered composite film cloth of the present invention is characterized in that, this applying cloth has the cloth body, and the cloth body side surface is fitted plural number to drench film formed film shape top layer.
Wherein the one-sided applying plural number of cloth body is to drench film formed film shape top layer.
Wherein cloth body bilateral is fitted plural number to drench film formed film shape top layer.
Wherein the top layer that contacts with the cloth body can be the hot castable resin material of compound high now characteristic.
Wherein Wai Ce top layer can be the PE material.
Wherein Wai Ce top layer can be the PP material.
Wherein Wai Ce top layer can be the EVA material.
The manufacture method of a kind of adhered composite film cloth of the present invention, it is characterized in that, this manufacture method is that the several shaping moulds by shaping area form plural top layer simultaneously, combine with each top layer with the cloth body that is about to input afterwards, then applying cloth is pressed be one, promptly form adhered composite film cloth by being close to wheels.
For making the auditor can further understand the feature of processing procedure of the present invention and adhered composite film cloth, special conjunction with figs. is illustrated, wherein:
Fig. 1 is a manufacturing flow chart of the present invention.
Fig. 2 is the manufacturing sketch of first kind of adhered composite film cloth of the present invention.
Fig. 3 is the stereo appearance figure of first kind of adhered composite film cloth of the present invention.
Fig. 4 is the manufacturing sketch of second kind of adhered composite film cloth of the present invention.
Fig. 5 is the stereo appearance figure of second kind of adhered composite film cloth of the present invention.
Fig. 6 is the manufacturing sketch of the third adhered composite film cloth of the present invention.
Fig. 7 is the manufacturing sketch of existing first kind of applying cloth.
Fig. 8 is the manufacturing sketch of existing second kind of applying cloth.
The manufacture method of adhered composite film cloth of the present invention is the flow chart manufacturing that is presented with Fig. 1, and cooperates above-mentioned flow chart, being able to different enforcement processing procedures finishes, as Fig. 2, Fig. 4 and shown in Figure 6, be different enforcement processing procedures, and cooperate the manufacturing process of Fig. 1 to be described as follows with Fig. 2 earlier:
This manufacture method is to form plural top layer simultaneously with forming technique earlier, as being depicted as the design of extexine 10 and endosexine 20 on the figure, this forming technique is each the T type shaping mould 11 that utilizes shaping area, 21 form extexine 10 and endosexine 20 respectively, wherein extexine 10 can be PE, PP, EVA or the like thermoplasticity material, or the admixture of its different resins forms to drench membrane technology, so it can be thickness thin layer as thin as a wafer, endosexine 20 then is that the hot castable resin material of compound high now characteristic forms to drench membrane technology, be similarly thickness thin layer as thin as a wafer, in addition cloth body 30 delivers into pressing before the wheels 40 behind the shaping area by conveyer belt, contact with endosexine 20 earlier, and fit with extexine 10 by endosexine 20, because of extexine 10 and endosexine 20 still have suitable temperature after the shaping mould moulding, so under the situation of appropriate hot melt, form the comprehensive closely applying of the utmost point, and make adhered composite film cloth as shown in Figure 3; And above-mentioned endosexine 20 also can tool adherence energy own and has property simultaneously concurrently, as the thin layer of functions such as waterproof, reinforcement.
Manufacture method shown in Figure 4 in addition, be to have the both sides that two shaping areas 50,51 are divided into cloth body 52 conveyer belts, and wherein a shaping area 50 forms extexine 503 and endosexine 504 with shaping mould 501,502 respectively, another shaping area 51 then forms extexine 513 and endosexine 514 with shaping mould 511,512, carry out heat posted with cloth body 52 afterwards and close program, make cloth body 52 both sides respectively have the function of waterproof or other characteristics, and adhered composite film cloth as shown in Figure 5.
Manufacture method shown in Figure 6 in addition, be to be provided with three shaping moulds 60,61,62 in shaping area, wherein two shaping moulds 60,61 form the top layer film of different qualities respectively, and shaping mould 62 forms the film of the attached outstanding characteristic of tool, make cloth body 63 single side surface form the top layer of plural layer, and get the top layer that forms plural layer in the same way in cloth body 63 bilaterals.
And the manufacture method of manufacture method of the present invention and existing bonding formula is compared, design of the present invention can be shown consideration for cloth immediately after film forms and close, and be with solvent-free resin bed as plastering agent, therefore, manufacture method of the present invention promptly possesses following effect:
1. no matter manufacture method desire of the present invention forms the applying cloth of one-sided tool fire resistance characteristic or other characteristics, or the applying cloth of the equal tool fire resistance characteristic of bilateral or other characteristics, all can form by single processing procedure, so the method that can provide a processing procedure to simplify more.
2. manufacture method of the present invention, show consideration for cloth immediately after film forms and close, therefore single procedure promptly forms adhered composite film cloth, so need not make under the situation of watertight composition in advance, manufacturing cost is obviously reduced, a processing procedure that meets economic benefit is provided.
3. in the processing procedure of the present invention by the top layer of the attached outstanding characteristic of tool, be a solvent-free resin bed, therefore itself no environmental protection problem not only, and in manufacture process, the generation of non-volatility gas, and the puzzlement of non-environmental-pollution.
The adhered composite film cloth of manufacturing of the present invention then possesses following special efficacy in addition:
1. because of being in the processing procedure of the present invention behind each top layer formation film, show consideration for cloth immediately and close, therefore need not take the problem that furls into account, its thickness can be to state as thin as a wafer, after event was closed with the cloth consideration, the integral thickness of cloth body can't be excessive, and the unlikely texture that influences cloth body itself.
2. each top layer because of adhered composite film cloth of the present invention all is to make with solvent-free plastic material, therefore is difficult for causing the problem of environmental protection.
So from the above, adhered composite film cloth of the present invention and manufacture method thereof can provide one to have more the manufacture method of economic benefit and have more the applying cloth of practicality really, should meet the regulation of Patent Law, are to file an application in accordance with the law.
Claims (8)
1. adhered composite film cloth and manufacture method thereof is characterized in that this applying cloth has the cloth body, and the cloth body side surface is fitted plural number to drench film formed film shape top layer.
2. adhered composite film cloth according to claim 1 and manufacture method thereof is characterized in that, wherein the one-sided applying plural number of cloth body is to drench film formed film shape top layer.
3. adhered composite film cloth according to claim 1 and manufacture method thereof is characterized in that, wherein cloth body bilateral is fitted plural number to drench film formed film shape top layer.
4. according to claim 1,2 or 3 described adhered composite film cloth and manufacture methods thereof, it is characterized in that wherein the top layer that contacts with the cloth body can be the hot castable resin material of compound high now characteristic.
5. according to claim 1,2 or 3 described adhered composite film cloth and manufacture methods thereof, it is characterized in that wherein Wai Ce top layer can be the PE material.
6. according to claim 1,2 or 3 described adhered composite film cloth and manufacture methods thereof, it is characterized in that wherein Wai Ce top layer can be the PP material.
7. according to claim 1,2 or 3 described adhered composite film cloth and manufacture methods thereof, it is characterized in that wherein Wai Ce top layer can be the EVA material.
8. adhered composite film cloth and manufacture method thereof, it is characterized in that, this manufacture method is that the several shaping moulds by shaping area form plural top layer simultaneously, combine with each top layer with the cloth body that is about to input afterwards, then applying cloth is pressed be one, promptly form adhered composite film cloth by being close to wheels.