CN1380168A - Storage method of green masson pine squaresawn lumber and plates - Google Patents
Storage method of green masson pine squaresawn lumber and plates Download PDFInfo
- Publication number
- CN1380168A CN1380168A CN 01107985 CN01107985A CN1380168A CN 1380168 A CN1380168 A CN 1380168A CN 01107985 CN01107985 CN 01107985 CN 01107985 A CN01107985 A CN 01107985A CN 1380168 A CN1380168 A CN 1380168A
- Authority
- CN
- China
- Prior art keywords
- plates
- lumber
- storage method
- squaresawn
- masson pine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The storage method of undried masson-pine plate squared timber is characterized by that for red core plates said method can make them do not produce color change and rot, it adopts molten paraffin wax, and applies it to two ends of the sawn timber and its plain-sawed plate surface of reduce diffusion of water content and can resist deformation and crack. For red-white plates, whole-white plates and squared timber is adopts non-toxic, harmless and odourless mixture solution made up by mixing boric acid and borax according to mixing ratio of 7:3 to coat and brush and above-mentioned timbers for resisting rot and preventing colour change and adopts nitrolacquer to brush them to resist crack. After having been treated by adopting said invented method the above-mentioned plates and squared timber have to mildew stain or colour change within 20-30 days.
Description
The present invention relates to a kind of anticorrosion mildew-resistant anticracking treatment technology of masson pine sheet material.
Masson pine timber is rich in carbohydrate, protein and trace element, under the situation that temperature, damp condition are fit to, be easy to mouldy and variable color, in China south, if several days time serious mouldy and variable color will take place, and the timber after the variable color, no matter carry out later which type of processing, handle, all be difficult to remove these colors.In order to guarantee that timber products has graceful decorative pattern and natural colour, masson pine as can not in time carrying out drying, just should carry out mildew-resistant, anti-variable color processing after being sawn into sheet material.In addition, sapwood and material difference in spring and autumn are obviously deposited easy cracking in the air because horse hair is got relaxed, and also must carry out anticracking and handle.
Traditional masson pine mildew-resistant, anti-variable color processing are that masson pine is immersed in the water, and this method demand place is big, has to fish for time-consuming and the big shortcoming of drying load.The method that has bibliographical information to handle with chemical reagent such as penta sodium pentachlorophenates though this method has the advantage that pair place demand is little and the processing time is short, because these reagent toxicities are strong, is unfavorable for that environmental protection and workman are healthy recently.Anticracking for undried masson pine timber also mainly is to take water-extraction method, and additive method yet there are no bibliographical information.
The objective of the invention is to utilize nontoxic reagent that masson pine sheet material is carried out anticorrosion, anti-variable color and handle, reach the purpose of long-time storage masson pine plate.
Storage method of the present invention is as follows to the processing of various masson pine sheet materials: because red heart sheet material can not produce variable color, rotten, adopt two ends and the plain-sawed lumber face of paraffin brushing at sawn timber, slow down distributing of moisture, stop distortion and cracking.For red blank material, full blank material, square bar with the boric acid and the borax solution brushing mildew-resistant of nontoxic odorless, prevent variable color, concentration is 5-25%, consumption is 80-140 kilogram/cube timber.With nitrate paint brushing anticracking, coating layer thickness is 80-120um, preferably 90-100um.
After adopting above mildew-resistant, anti-variable color and anticracking to handle, no mould and look change within 20-30 days, and with low cost.
The invention will be further described below in conjunction with embodiment:
The embodiment of the invention is specific as follows to the processing of various masson pine sheet materials: because red heart sheet material can not produce variable color, rotten, we adopt melted paraffin wax, and brushing slows down distributing of moisture at the two ends and the plain-sawed lumber face of sawn timber, stop distortion and cracking.For red blank material, full blank material, square bar with 7: 3 the boric acid and the borax solution brushing mildew-resistant of nontoxic odorless, prevent variable color, concentration is 10-12%, consumption is 100-120 kilogram/cube timber.With nitrate paint brushing anticracking, coating layer thickness is 90-100um.
Claims (5)
1. the storage method of a green masson pine squaresawn lumber and plates is characterized in that: adopt boric acid and borax solution brushing mildew-resistant, prevent variable color, with nitrate paint brushing anticracking for red blank material, full blank material, square bar; Red heart sheet material adopts melted paraffin wax, and brushing is at the two ends and the plain-sawed lumber face of sawn timber.
2. by the storage method of the described green masson pine squaresawn lumber and plates of claim 1, it is characterized in that boric acid and the borax solution brushing with 7: 3 comes mildew-resistant, anti-variable color, concentration is 5-25%, and consumption is 80-140 kilogram/cube timber.
3. by the storage method of the described green masson pine squaresawn lumber and plates of claim 1, it is characterized in that with 7: 3 boric acid and borax solution brushing come mildew-resistant, the colour saturation of preapring for an unfavorable turn of events is 10-12%, consumption is 100-120 kilogram/cube timber.
4. by the storage method of the described green masson pine squaresawn lumber and plates of claim 1, it is characterized in that: with nitrate paint brushing anticracking, coating layer thickness is 80-120um.
5. by the storage method of the described green masson pine squaresawn lumber and plates of claim 1, it is characterized in that: with nitrate paint brushing anticracking, coating layer thickness is 90-100um.