CN1377927A - Polyphenylethylene paint - Google Patents
Polyphenylethylene paint Download PDFInfo
- Publication number
- CN1377927A CN1377927A CN 02117416 CN02117416A CN1377927A CN 1377927 A CN1377927 A CN 1377927A CN 02117416 CN02117416 CN 02117416 CN 02117416 A CN02117416 A CN 02117416A CN 1377927 A CN1377927 A CN 1377927A
- Authority
- CN
- China
- Prior art keywords
- polystyrene
- gasoline
- height
- varnish
- product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to the production process of polystyrene paint produced with polystyrene as main material. During its production, cyclohexanone in 0.8-12%, ehtyl salicylate in 12-24 %, butyl salicylate in 8-20 % and high-grade gasoline in 31-55% are mixed inside one container; foamed polystyrene plastic in 16-25% is then added through stirring; and the mixture is ground and filtered into the product. The product has excellent quality, wide application range, less environmental pollution, low cost and service life longer than other paints.
Description
Technical field
The present invention relates to a kind of lacquer and preparation method, particularly a kind of polystyrene varnish and preparation method.
Background technology
In China's coating technology develop rapidly, the kind of lacquer is a lot of at present, but lacks the characteristics that a kind of lacquer possesses various lacquers, is widely applied to the lacquer product that goes in the industries such as industrial or agricultural and building.Current polystyrene foamed plastics has played bigger white pollution to environment, and radical cure and improvement also are problems that is difficult to solution.
Summary of the invention
According to our experiment and research, having invented a kind of finally is raw material with polystyrene foamed plastics, produces the polystyrene varnish and the production method of the characteristics that possess various lacquers.
Material component of the present invention and weight percent are as follows:
Pimelinketone 0.8-12%, salicylic ether 12-24%, butyl salicylate 8-20%, height gasoline 31-55%, polystyrene foamed plastics 16-25%.
Preferably: pimelinketone 2-8%, salicylic ether 12-20%, butyl salicylate 10-17%, height gasoline 40-50%, polystyrene foamed plastics 19-23%.
The used height gasoline of the present invention is 93-120 number.
Production technique is as follows:
With pimelinketone 0.8-12%, salicylic ether 12-24%, butyl salicylate 8-20%, height gasoline 31-55%, put in the container stir after, add polystyrene foamed plastics 16-25%, through stirring, grind again, filter, make finished product.
According to actual needs, can add stopping composition.
Big as needs concentration, during the big lacquer of opacity, can add 5-15% zinc sulfide white by the weight of making lacquer; If be used to set fire lacquer, add mica powder of 40% or the like by the weight of making lacquer.
Simultaneously, identical with the production method of other lacquers, can add shades of colour as required.
The performance of this product is as follows:
1. water resistance is extremely strong, and acid-proof, alkali are anti-aging simultaneously, adapt in the medium-term and long-term immersion of seawater, and anti-clam,
The sticking power extra-heavy, quick solidifying.With 15 minutes epidermal stems behind the painting brush, parched in 50 minutes, suitable iron,
Wooden boat only reaches oil platform and uses.
As: water 500 grams, put salt 50 grams, alkali 50 grams, sulfuric acid 50 grams, the iron that brush is good,
Wood-block immerses in the liquid for preparing and soaked 21 days, takes out back and the good iron of brush that does not have to soak,
Wood-block compare without any variation.
Simultaneously can also make phosphorescent coating, fluorescent material, granulated glass sphere is made fluorescent paint.
2. product Applicable temperature test: (1) puts into taking-up in 60 minutes in 60 containers of spending of heating, can be normal
Use, quality is without any infringement.(2) put after product is sealed in the ice cube and to take out energy in 60 minutes
The normal use, quality is without any infringement.Can produce fluorescent behind the light-illuminating, be applicable to the highway branch
Diatom, electric power facility sign, road and bridge and obstruction marking.
That polystyrene varnish has is best in quality, practicality is wide, and product is to reduce environmental pollution, profit
Useless is main product, and facility investment is few, and cost is lower, and is higher than other lacquers work-ing life, behaviour
Do simply, nontoxic, no waste belongs to environmental protection product.
Concrete true mode
Embodiment 1:
Pimelinketone 3%, salicylic ether 20%, 10%, No. 100 gasoline 45% of butyl salicylate is made into solvent, put in the container stir after, add polystyrene foamed plastics 22%, through stirring, grind again, filter, make finished product.
Embodiment 2:
Pimelinketone 6%, salicylic ether 12%, 15%, No. 120 gasoline 42% of butyl salicylate is made into solvent.Put in the container stir after, add polystyrene foamed plastics 25%, add 8% zinc sulfide white stopping composition of above-mentioned raw materials total amount, through stirring, grind again, filter, make finished product.Pour in accordance with regulations in the container that iron sheet makes and seal.
Claims (5)
1. polystyrene varnish, material component and weight percent are as follows: pimelinketone 0.8-12%, salicylic ether 12-24%, butyl salicylate 8-20%, height gasoline 31-55%, polystyrene foamed plastics 16-25%.
2. polystyrene varnish as claimed in claim 1, material component and weight percent are: pimelinketone 2-8%, salicylic ether 12-20%, butyl salicylate 10-17%, height gasoline 40-50%, polystyrene foamed plastics 19-23%.
3. polystyrene varnish as claimed in claim 1 or 2 is characterized by by the weight adding 5-15% zinc sulfide white of making lacquer.
4. polystyrene varnish as claimed in claim 1 or 2, it is characterized by height gasoline is 90-120 gasoline.
5. the production method of a sharp polystyrene varnish: it is characterized by with pimelinketone 0.8-12% salicylic ether 12-24%, butyl salicylate 8-20%, height gasoline 31-55%, put in the container stir after, add polystyrene foamed plastics 16-25%, through stirring, grind and make finished product again.