CN1374381A - Gear oil composition for reduction box of oil pumping unit and its prepn - Google Patents
Gear oil composition for reduction box of oil pumping unit and its prepn Download PDFInfo
- Publication number
- CN1374381A CN1374381A CN 02110133 CN02110133A CN1374381A CN 1374381 A CN1374381 A CN 1374381A CN 02110133 CN02110133 CN 02110133 CN 02110133 A CN02110133 A CN 02110133A CN 1374381 A CN1374381 A CN 1374381A
- Authority
- CN
- China
- Prior art keywords
- oil
- reduction box
- pumping unit
- base oil
- oil composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention belongs to the field of petrochemical technology. The present invention is mainly using special densifier to densify medium-viscosity refined oil, adding additives for resisting oxidation, resisting water, antirust, antifriction, extreme pressure lubricating and othre purposes separately and adding solid bead so as to compose semi-fluid gear oil composite for reduction box of oil pumping unit. The lubricating oil for gear box has good extreme pressure lubricating performance, good temperature stability and other advantages.
Description
(1) technical field
The present invention relates to antitheft gear oil composition of a kind of oil-field oil pumper reduction box and preparation method thereof, belong to petrochemical industry.
(2) background technology
The oil-field oil pumper reduction box is a kind of general transmission apparatus.At present, the oil field generally adopts machinery oil or gear oil to do lubricant to lubricate, and in the use, the ubiquity following point: 1. oil consumption is big, wastes energy at the scene.Because of good fluidity, stolen by the lawless person easily.Drain period short, increased the working strength of maintaining, as on request, the oil-field oil pumper reduction box must change twice oil every year, spring, once winter was once.3. machinery oil can not meet the demands fully, and mechanical wear is very fast, and some oil field is stolen in order to prevent lubricating oil, welds dead wheel casing, and lubricating oil can not in time be changed, and because of mechanical oil deterioration, has quickened the wearing and tearing of wheel casing gear, makes shortened equipment life.4. comprehensive cost height.
(3) summary of the invention
The present invention is directed to the shortcoming of prior art, a kind of novel oil-field oil pumper speed reduction gear box oil is provided, make it to have and caution against stealing, anti-leak, extreme boundary lubrication is good, characteristics such as heatproof good stability and life cycle are long, stolen easily, the lubricity difference that solves that plain oil exists and work-ing life short problem.
To the effect that of the present invention: with extraordinary viscosifying agent multiviscosisty high viscosity treated oil, and adding antioxygen, waterproof, antirust, anti-friction and extreme pressure profit additives such as sliding, and solid microballon lubricant, the antitheft gear oil composition of oil-field oil pumper reduction box that synthesizes the semi-fluid shape, its component is as follows, is weight part: the refining base oil B 5-35 part extreme boundary lubrication membrane-forming agent 1-8 part water-resisting agent 3-10 part of the refining base oil A 50-90 part medium viscosity of extraordinary viscosifying agent 5-30 part oxidation inhibitor 0.4-10 part solid microballon lubricant 0.2-12 part rust inhibitor 0.6-9 part medium viscosity
Described extraordinary viscosifying agent is ten dihydroxystearic acids or hydrogenated castor oil.
Described oxidation inhibitor is sulphur phosphorus fourth octyl group zinc salt or 2,6 ditertiary butyl p cresol.
Described solid microballon lubricant is high temperature resistance wear resistant resin microballon or molybdenumdisulphide.
Described rust inhibitor is phenylpropyl alcohol triazole or dinonyl bitter edible plant barium sulfonate.
Described extreme boundary lubrication membrane-forming agent is a dialkyl dithio ammonium cesium formate.
Described water-resisting agent is 124 Triazole fatty acid amine sodium salt or 124 Triazole fatty acid amine sylvite.
The refining base oil A of described medium viscosity is refinery medium viscosity base oil or CA-40 bavin machine oil.
The refining base oil B of described medium viscosity is refining 4 line oil of refinery or QA-40 steam turbine oil.
Gear oil composition for reduction box of oil pumping unit preparation method of the present invention is as follows:
1. refining base oil A 50-90 part of medium viscosity and viscosifying agent are added in the reactor, under 80-120 ℃ of temperature, carry out the multiviscosisty reaction, reaction times 4-6 hour;
2. after the multiviscosisty reaction finishes, be warmed up to 140-220 ℃, add other additives such as oxidation inhibitor, rust inhibitor, extreme boundary lubrication membrane-forming agent, water-resisting agent then, and add base oil B 5-30 part, carry out secondary reaction;
3. after secondary reaction finishes, cool to 120-170 ℃, add solid microballon lubricant then;
4. cleavage reaction 1-2 hour, by adding base oil B1-5 part cone governor in-degree 400-600 (10
-1Mm)/25 ℃, go out the still packing when cooling to 70-900 ℃ then.
Main innovate point of the present invention is:
1. used solid microballon lubricant, improved lubricity, high voltage performance is good, and the drain period that makes lubricating oil is by being increased to 1-2 half a year.
2. lubricating oil has special performances, and lubricating oil can only be used in the oil pumper wheel casing, can burn charing in case be used for some component of diesel engine or tractor-luboil, thereby machine is burnt, and prevents that thoroughly lubricating oil is stolen.
3. in lubricating oil, added extraordinary viscosifying agent, made whole system become a kind of unlikely automatic mobile stiff ointment state.When mechanical position remained static, lubricating oil had the ability that keeps self shape, prevented to leak and the boring stealing; When gear was kept in motion, shear-stress increased, and lubricating oil can flow deformation can take place as viscous fluid, by the extreme boundary lubrication that the adsorbed lubricating film that forms on moving parts has improved lubricating oil, can prevent the spatter loss of lubricating oil simultaneously.Therefore, the lubricant of the present invention's research has good lubrication and seal and theftproof performance.
4. in lubricating oil, add water-resisting agent, improved the water resisting property of lubricating oil, guaranteed the lubricated reliability of mechanical part.
(4) embodiment
Embodiment 1: 65 parts of refining 10 parts of preparation methods of 4 line oil (base oil B), 22 parts of extreme boundary lubrication membrane-forming agent dialkyl dithios ammonium cesium formate, 8 parts of water-resisting agent 124 Triazoles fatty acid amine sodium salt are as follows for 30 parts of oxidation inhibitor sulphur of extraordinary viscosifying agent hydrogenated castor oil phosphorus fourth octyl group zinc salt 10 parts of solid microballons lubricant molybdenumdisulphide 12 parts of rust inhibitor phenylpropyl alcohols triazole 9 parts of refinery medium viscosities base oil (base oil A): 1. refining base oil A of high viscosity and viscosifying agent are added in the reactor, under 100 ℃ of temperature, carry out the multiviscosisty reaction, 5 hours reaction times; 2. after the multiviscosisty reaction finishes, be warmed up to 180 ℃, add other additives such as oxidation inhibitor, rust inhibitor, extreme boundary lubrication membrane-forming agent, water-resisting agent then, and add 20 parts of base oil B, carry out secondary reaction; 3. after secondary reaction finishes, cool to 150 ℃ rapidly, add solid microballon lubricant then; 4. cleavage reaction is 1.5 hours, by 2 parts of cone governor in-degrees of increase and decrease base oil B 500 (10
-1Mm)/25 ℃, go out the still packing when cooling to 80 ℃ then.Embodiment 2: 5 parts of oxidation inhibitor 2 of extraordinary viscosifying agent ten dihydroxystearic acids, 50 parts of refining 35 parts of preparation methods of 4 line oil (base oil B) are as follows for 0.4 part of solid microballon of 6-ditertbutylparacresol lubricant high temperature resistance wear resistant resin microballon 0.3 part of rust inhibitor dinonyl bitter edible plant barium sulfonate, 0.8 part of extreme boundary lubrication membrane-forming agent dialkyl dithio ammonium cesium formate 2 parts of water-resisting agent 124 Triazoles fatty acid amine sylvite, 4 parts of CA-40 bavins machine oil (base oil A): 1. refining base oil A of high viscosity and viscosifying agent are added in the reactor, under 110 ℃ of temperature, carry out the multiviscosisty reaction, 4.5 hours reaction times; 2. after the multiviscosisty reaction finishes, be warmed up to 200 ℃, add other additives such as oxidation inhibitor, rust inhibitor, extreme boundary lubrication membrane-forming agent, water-resisting agent then, and add 30 parts of base oil B, carry out secondary reaction; 3. after secondary reaction finishes, cool to 160 ℃ rapidly, add solid microballon lubricant then; 4. cleavage reaction is 1.5 hours, by adding 5 parts of cone governor in-degrees of base oil B 550 (10
-1Mm)/25 ℃, go out the still packing when cooling to 85 ℃ then.
Embodiment 3: 30 parts of preparation methods are as follows for 55 parts of QA-40 steam turbine oils of 18 parts of oxidation inhibitor sulphur of extraordinary viscosifying agent hydrogenated castor oil phosphorus fourth octyl group zinc salt 2 parts of solid microballons lubricant molybdenumdisulphide 4 parts of rust inhibitor phenylpropyl alcohols triazole 5 parts of extreme boundary lubrication membrane-forming agents dialkyl dithio ammonium cesium formate 3 parts of water-resisting agent 124 Triazoles fatty acid amine sodium salt, 6 parts of refinery medium viscosities base oil (base oil A) (base oil B): 1. refining base oil A of high viscosity and viscosifying agent are added in the reactor, under 110 ℃ of temperature, carry out the multiviscosisty reaction, 4.5 hours reaction times; 2. after the multiviscosisty reaction finishes, be warmed up to 200 ℃, add other additives such as oxidation inhibitor, rust inhibitor, extreme boundary lubrication membrane-forming agent, water-resisting agent then, and add 28 parts of base oil B, carry out secondary reaction; 3. after secondary reaction finishes, cool to 160 ℃ rapidly, add solid microballon lubricant then; 4. cleavage reaction is 1.5 hours, by adding 2 parts of cone governor in-degrees of base oil B 480 (10
-1Mm)/25 ℃, go out the still packing when cooling to 85 ℃ then.
Claims (10)
1. gear oil composition for reduction box of oil pumping unit, it is characterized in that, comprise following component, be weight part: the refining base oil B 5-35 part extreme boundary lubrication membrane-forming agent 1-8 part water-resisting agent 3-10 part of the refining base oil A 50-90 part medium viscosity of the refining base oil 50-90 part medium viscosity of extraordinary viscosifying agent 5-30 part oxidation inhibitor 0.4-10 part solid microballon lubricant 0.2-12 part rust inhibitor 0.6-9 part high viscosity.
2. according to claims 1 described gear oil composition for reduction box of oil pumping unit, it is characterized in that described extraordinary viscosifying agent is ten dihydroxystearic acids or hydrogenated castor oil.
3. according to claims 1 described gear oil composition for reduction box of oil pumping unit, it is characterized in that described oxidation inhibitor is sulphur phosphorus fourth octyl group zinc salt or 2,6 ditertiary butyl p cresol.
4. according to claims 1 described gear oil composition for reduction box of oil pumping unit, it is characterized in that described solid microballon lubricant is high temperature resistance resin microballon or molybdenumdisulphide.
5. according to claims 1 described gear oil composition for reduction box of oil pumping unit, it is characterized in that described extraordinary rust inhibitor is phenylpropyl alcohol triazole or dinonyl bitter edible plant barium sulfonate.
6. according to claims 1 described gear oil composition for reduction box of oil pumping unit, it is characterized in that described water-resisting agent is 124 Triazole fatty acid amine sodium salt or 124 Triazole fatty acid amine sylvite.
7. according to claims 1 described gear oil composition for reduction box of oil pumping unit, it is characterized in that described extreme boundary lubrication membrane-forming agent is a dialkyl dithio ammonium cesium formate.
8. according to claims 1 described gear oil composition for reduction box of oil pumping unit, it is characterized in that the refining base oil A of described medium viscosity is refinery medium viscosity base oil or CA-40 bavin machine oil.
9. according to claims 1 described gear oil composition for reduction box of oil pumping unit, it is characterized in that the refining base oil B of described medium viscosity is refining 4 line oil of refinery or QA-40 steam turbine oil.
10. preparation method as claims 1 described gear oil composition for reduction box of oil pumping unit, comprise the steps: that (1) adds refining base oil A of high viscosity and viscosifying agent in the reactor, under 80-120 ℃ of temperature, carry out multiviscosisty reaction, reaction times 4-6 hour by special technology; (2) after the multiviscosisty reaction finishes, be warmed up to 140-220 ℃, add other additives then, and add base oil B 5-30 part, carry out secondary reaction; (3) after secondary reaction finishes, cool to 120-170 ℃, add solid microballon lubricant then; (4) cleavage reaction is 1~2 hour, by adding base oil B 1-5 part cone governor in-degree 400-600 (10
-1Mm)/25 ℃, go out the still packing when cooling to 70-90 ℃ then.