CN1363695A - 一种钢制工件深冷处理工艺 - Google Patents

一种钢制工件深冷处理工艺 Download PDF

Info

Publication number
CN1363695A
CN1363695A CN 01131772 CN01131772A CN1363695A CN 1363695 A CN1363695 A CN 1363695A CN 01131772 CN01131772 CN 01131772 CN 01131772 A CN01131772 A CN 01131772A CN 1363695 A CN1363695 A CN 1363695A
Authority
CN
China
Prior art keywords
workpiece
steel
tempering
deep
sub
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 01131772
Other languages
English (en)
Other versions
CN1159461C (zh
Inventor
李士燕
刘秀芝
刘天佐
袁子洲
安丽丽
陈秀娟
林焰
梁志民
陈长风
徐树深
段春争
李雄
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GANSU POLYTECHNIC UNIV
Original Assignee
GANSU POLYTECHNIC UNIV
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GANSU POLYTECHNIC UNIV filed Critical GANSU POLYTECHNIC UNIV
Priority to CNB011317728A priority Critical patent/CN1159461C/zh
Publication of CN1363695A publication Critical patent/CN1363695A/zh
Application granted granted Critical
Publication of CN1159461C publication Critical patent/CN1159461C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明的工艺,工件在深冷前进行淬火,在液氮中进行深冷处理,在淬火后进行回火,回火后进行深冷处理,液氮温度为－170～－196℃,碳钢和低合金钢制工件在液氮中的等温时间为其工件的有效厚度或有效直径乘以(2～3min/mm),高合金钢的等温时间为其工件的有效厚度或有效直径乘以(5～8min/mm)。高合金钢淬火后进行两次回火。形状复杂或大型的工件进行2～3次深冷处理。钢制工件在深冷后放置在100～200℃的油液中加热。

Description

一种钢制工件深冷处理工艺
技术领域
本发明是一种钢制工件的热处理工艺，特别适用于高合金钢制工件的强韧化。
技术背景
在现有技术中，用于深冷处理的工件是钢制半成品，根据不同钢种的相变临界点，先进行淬火处理，然后加热至100℃，在-170℃的液氮中进行深冷处理，最后进行回火处理。高合金钢制工件在深冷后进行三次回火处理。上述深冷处理使钢中碳化物析出不充分，残余奥氏体由大块向膜状的转变也不充分，从而不能更大限度地提高半成品工件的强度和韧性。高合金钢工件在深冷后进行三次回火，能耗较高。
发明内容
本发明是一种钢制工件深冷处理工艺，工件在深冷前进行淬火，在液氮中进行深冷处理，液氮温度为-170∽-196℃，工件在淬火后进行回火，回火后进行深冷处理，在液氮中的等温时间为：碳钢和低合金钢制工件的等温时间为其工件的有效厚度或有效直径乘以(2∽3min/mm)，高合金钢的等温时间为其工件的有效厚度或有效直径乘以(5∽8min/mm)。高合金钢淬火后在600℃进行三次回火，每次进行1小时。钢制工件在深冷后放置在100∽200℃的油液中加次进行1小时。钢制工件在深冷后放置在100∽200℃的油液中加热。形状复杂或大型的工件进行2-3次深冷处理。高合金钢淬火后进行两次回火，比现有技术少一次回火，节约了能源。
经本发明的深冷工艺处理的钢制工件，其碳化物得到充分析出，并且有纳米尺度的碳化物析出，残余奥氏体由块状充分转变为膜状，与未深冷的工件相比，工件的多冲韧性增加1.5倍，韧性也有所提高，耐磨性提高了2-3倍。
具体实现方式
对于碳钢和低合金钢制工件，如9SiCr、GCr15钢制工件，根据其钢种特定的相变临界点进行淬火处理，然后进行一次回火，回火后在-170∽-190℃的液氮中进行深冷处理，深冷处理的等温时间为工件的有效厚度或有效直径乘以(2∽3min/mm)，对于形状复杂或大型的工件，要进行2∽3次深冷处理，最后在100∽200℃的油液中加热，加热后取出工件，放置至室温。
对于高合金钢制工件，如Cr12MoV钢、W18Cr4V钢和W6Mo5Cr4V2钢，根据其钢种特定的相变临界点进行淬火处理，然后进行两次回火，回火后在-170∽-190℃的液氮中进行深冷处理，深冷处理的等温时间为工件的有效厚度或有效直径乘以(2∽3min/mm)，对于形状复杂或大型的工件，要进行2∽3次深冷处理，最后在100∽200℃的油液中加热，加热后取出工件，放置至室温。
深冷处理设备为一开口式100立升真空绝热设备，其技术参数为：贮存介质：液态氮，公称容积：100ml，容器日蒸发率≤3.5％/天，容器封口真空度≤6.67×10-3pa，容器夹层静态漏放气率≤1.33×10-5pa·L/s，绝热方式：高真空+多层多屏绝热，最大承重≤50Kg。

Claims (4)

1、一种钢制工件深冷处理工艺，工件在深冷前进行淬火，在液氮中进行深冷处理，其特征是：工件在淬火后进行回火，回火后进行深冷处理，液氮温度为-170∽-196℃，在液氮中的等温时间为：碳钢和低合金钢制工件的等温时间为其工件的有效厚度或有效直径乘以(2∽3min/mm)，高合金钢的等温时间为其工件的有效厚度或有效直径乘以(5∽8min/mm)。
2、根据权利要求1所述的金属深冷处理工艺，其特征是高合金钢淬火后在600℃进行三次回火，每次进行1小时。
3、根据权利要求1所述的金属深冷处理工艺，其特征是形状复杂或大型的工件进行2∽3次深冷处理。
4、根据权利要求1所述的金属深冷处理工艺，其特征是钢制工件在深冷后放置在100∽200℃的油液中加热。
CNB011317728A 2001-10-16 2001-10-16 一种钢制工件深冷处理工艺 Expired - Fee Related CN1159461C (zh)