CN1362537A - Metal foil and metal sheet with coated ceramic film or antioxidant metal film - Google Patents
Metal foil and metal sheet with coated ceramic film or antioxidant metal film Download PDFInfo
- Publication number
- CN1362537A CN1362537A CN 01106414 CN01106414A CN1362537A CN 1362537 A CN1362537 A CN 1362537A CN 01106414 CN01106414 CN 01106414 CN 01106414 A CN01106414 A CN 01106414A CN 1362537 A CN1362537 A CN 1362537A
- Authority
- CN
- China
- Prior art keywords
- metal
- thin material
- metal thin
- tinsel
- plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Firstly, it adopts general plasma spray-coating process, vacuum plasma coating and ion beam injection method to plate a layer of oxidation-resisting metal or alloy on the metal foil or metal thin material, then plating a layer of ceramic film. The metal foil and metal thin material produced has no environment pollution, its plated layer is good in firmness, and can resist oxidation and can resist wear, can be stored for a long period, and is applicable to technological decoration and building decoration.
Description
The invention discloses novel metal paper tinsel and the metal thin material of making a kind of Handicraft decorative and architectural decoration.It belongs to industrial art and decorates and the building and ornament materials class.Also belong to class of metal materials.
The tinsel and the metal thin material that are used for Handicraft decorative and building decoration now on the market all are material or plating materials such as gold and silver, platinum, titanium, copper, aluminium, zinc, stainless steel.Generally do not have protective membrane, what have has added plastic protective film for plastics or the protection that varnishes with lacquer, and has only used ceramic protective membrane on enamel is decorated.Enamel is decorated and generally all is limited to solid shape, can not be crooked, can not be applicable to the requirement of Handicraft decorative and building decoration to tinsel and metallic substance flexible.On tinsel and metal thin material, add plastic protective film for plastics or varnish with lacquer, because low, the easy to wear requirement that does not also meet Handicraft decorative and building decoration prolonged preservation to tinsel and metal thin material of hardness.
The objective of the invention is: utilize on ceramic wear-resisting is wiped, characteristic such as corrosion-resistant, high temperature resistant is given various Handicraft decoratives and building decoration is used tinsel and the metal thin material and plate ceramic coating; protect its not oxidized corrosion; be difficult for being damaged, can stand to expose to the sun and rain, prolonged preservation by friction.
The present invention realizes that the technical measures of being taked are: use methods such as common plasma spraying, vacuum plasma plated film and ionic fluid injection on tinsel and metal thin material surface: 1, plate the difficult oxidized metal of one deck gold and silver, platinum, titanium etc. or alloy earlier, protection tinsel and metal thin material are difficult for oxidized destruction.To body is that difficult oxidized metals such as gold and silver, platinum, titanium then need not this one deck plated film.2, plate a layer thickness in 1 nanometer (10
-9Rice) to 300 nano ceramics.
Plasma spraying, vacuum plasma plated film and ionic fluid inject existing standard equipment both at home and abroad, advantage be pollution-free, the coating stability is good.But cost of use is very high, is confined to some electronic components, the use of high rigidity cutter manufacturing process at present.Make tinsel and the metal thin material that utilizes plasma spraying, vacuum plasma plated film and ionic fluid injection to be applicable to production usefulness ceramic coating and difficult oxidized metal plated film by adjustment equipment structure, the product advantage of Sheng Chaning is an environmentally safe in this way, the coating stability is good, corrosion-resistant, wear-resistant Handicraft decorative and the building decoration that is used for preciousness.
Claims (4)
1, methods such as the common plasma spraying of a kind of use, vacuum plasma plated film and ionic fluid injection are on tinsel and metal thin material surface: plate the difficult oxidized metal of one deck gold and silver, platinum, titanium etc. or alloy earlier, protection tinsel and metal thin material are difficult for oxidized destruction; Plate one deck pottery, utilize on ceramic wear-resisting is wiped, characteristic such as corrosion-resistant, high temperature resistant is given various Handicraft decoratives and building decoration is used tinsel and the metal thin material and plate ceramic coating.
2, according to claim 1: tinsel and metal thin material (referring to 0.001 millimeter to 50 mm thick sheet metals) at Handicraft decorative and architectural decoration upward use common plasma spraying, vacuum plasma plated film and ion beam implantation to finish following plated film.
3, on used tinsel of Handicraft decorative and building decoration and metal thin material, plate the difficult oxidized metal of one deck gold and silver, platinum, titanium etc. or alloy according to the described method of claim 1 earlier.
4, according to claim 1: as to it is characterized in that plating a layer thickness in 1 nanometer (10 at the tinsel and the metal thin material of Handicraft decorative and architectural decoration
-9Rice) to 300 nano ceramics plated films.