CN1342505A - Solidification process for treating waste water-base drilling liquid and its solidifying agent - Google Patents
Solidification process for treating waste water-base drilling liquid and its solidifying agent Download PDFInfo
- Publication number
- CN1342505A CN1342505A CN 00124329 CN00124329A CN1342505A CN 1342505 A CN1342505 A CN 1342505A CN 00124329 CN00124329 CN 00124329 CN 00124329 A CN00124329 A CN 00124329A CN 1342505 A CN1342505 A CN 1342505A
- Authority
- CN
- China
- Prior art keywords
- drilling liquid
- waste water
- base drilling
- agent
- curing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A process for solidifying the waste water-base drilling liquid with solidifying agent is disclosed. The solidifying agent is prepared from inorganic Fe-Salt coagulant (1-6%), clay adsorbent (0.1-0.6%), bitter earth magnesium oxide (1-6%) and cementing agent (1-10%). After treated for 3-6 days, the said waste drilling liquid becomes a solid with a certain water-proofing performance and strength. The educed water has pH value less than 7.5, Cr-content less than 1.5 mg/L, COD less than 200 mg/L and petroleum content less than 10 mg/L. Its advantages are simple process, and short solidifying time.
Description
The discarded object that the present invention relates to a kind of oilfield drilling and geological prospecting drilling well solidifies the solidification processing method and the curing agent thereof of the waste water-base drilling liquid of the environmental protection technical field of handling.
Oil exploitation and geological exploration all be unable to do without drillng operation, and drillng operation is mainly derived from the leakage of rejected well drilling liquid to the pollution of environment.In general, water-base drilling fluid is made up of solid phases such as clay, liquid phase water and chemical treatments three parts, and wherein chemical treatments is of a great variety, amounts to 16 big class hundreds of kind products.Some inorganic salts in the rejected well drilling liquid, heavy metal components, oil product and big weight organic compounds all have bigger harm to environment, can make the chemical oxygen demand COD of rejected well drilling liquid as organic polymer
CrIncrease, some inorganic salts makes its pH value increase and some heavy metal ion such as Cr are carcinogen.A large amount of rejected well drilling liquids are not handled; be deposited in the well site or bury or flow into farmland, river, seabed; infiltrate the stratum; the capital pollutes environment; influence drinking-water water source; influence soil and animal and plant growth, directly jeopardize human health and life security, therefore the processing of rejected well drilling liquid has been become an important research content of environmental protection.Chinese patent " drilling completion mud veclamation treating apparatus " (88218926.3) is introduced with heat drying and cure system and is handled waste mud, and this device exists energy consumption to reach the slow shortcoming of processing speed greatly, is not suitable for being used for the mass disposal rejected well drilling liquid.Patent " solidification technology for well waste mud " (88102388.4) proposes to add cement, waterglass and aluminum sulfate in waste mud, be main cementing material wherein with cement, handling the resulting firming body of rejected well drilling liquid with the method can not live harmful substance complete closed such as heavy metal and organic matter, chance water soaks the rear section harmful substance for a long time and can leach again, exists potential secondary pollution.Patent " processing method of waste drilling fluid and storage configuration " (92108103.0) proposes to add organic flocculants such as inorganic flocculating agent such as aluminum sulfate and hydrolyzed polyacrylamide in waste drilling fluid, extract supernatant liquor behind the flocculating setting out, on concentrated flocculate precipitate, add the lid layer fibre object, cover with the sealing of concrete such as cement again, the flocculate poor stability of handling rejected well drilling liquid in this way and being produced, the long-time immersion just returned glue automatically and formed mud in the water.Though flocculate end face concrete enclosing, return clay slurry can be around heatable adobe sleeping platform and bottom spread seepage in the soil towards periphery, continuation pollutes to environment.Patent " firming agent for drilling waste mud and production method thereof " (93110918.3) selects for use sodium metasilicate, cement, aluminum sulfate, alum, charcoal and sodium carbonate to solidify drilling waste mud, though reached solidification effect, but the dosage of curing agent is bigger, maximum dosage is 35%, and the combined producing tech complexity of curing agent.
The objective of the invention is to study a kind of solidification processing method and curing agent thereof of new waste water-base drilling liquid, the employing inorganic molysite is that flocculating agent, clay absorbent and magnesia, cement are curing materials, not only fixed rejected well drilling liquid, and the harmful substance in the rejected well drilling liquid (as heavy metal, high polymer, oils etc.) sealing is wrapped in wherein, reduce its diafiltration and migration, reach antipollution purpose.
The present invention is achieved in that
Constitute by waste water-base drilling liquid and hardener formula, in the waste water-base drilling liquid of petroleum geology drilling well, add the composite curing agent of forming by flocculating agent, adsorbent, cementing agent and cement, waste water-base drilling liquid will stir after adding composite curing agent, subsequently composite curing agent is divided and put in the rejected well drilling liquid for 4～5 times, cast a collection of after each curing agent that drops into stirs again, pour heatable adobe sleeping platform subsequently again into or be deposited in ground, just can form firming body through 3～6 days curing.
The present invention also adopts following scheme:
Flocculating agent is inorganic molysite compound such as ferric sulfate, ferric trichloride etc., and dosage is 1～6% of a waste water-base drilling liquid weight; Adsorbent is clay such as bentonite, and dosage is 0.1～0.6% of a waste water-base drilling liquid weight; Cementing agent is magnesia (MgO), and dosage is 1～6% of a waste water-base drilling liquid weight; Cement is common building 425
#Cement, dosage is 1～10% of a waste water-base drilling liquid weight, above-mentioned substance joins in the waste water-base drilling liquid with the form of homogeneous mixture, its maximum total dosage is 15% of a waste water-base drilling liquid weight, wherein the ratio of flocculating agent, adsorbent and cementing agent is 1: 0.1: 1, and it is cement that residue adds quantity of material.
The solidification processing method of waste water-base drilling liquid and the design of curing agent thereof, be to be flocculating agent with inorganic molysite compound such as ferric sulfate, ferric trichloride etc., by the physicochemical change of a series of complexity such as polymerization, nucleation and precipitation of ferric hydrolysate in rejected well drilling liquid, with the harmful substance in the rejected well drilling liquid (as heavy metal, high polymer, oils etc.) cohesion sealing; With clay such as bentonite is adsorbent, the organic compound in the absorption rejected well drilling liquid; Again with solid phase and coagulative precipitation thing in magnesia that itself just has certain cohesion and the fixed rejected well drilling liquid of cement, solidify waste water-base drilling liquid and harmful substance is wrapped in wherein effect to reach.
The invention has the advantages that: can solidify the processing waste water-base drilling liquid well, after solidifying, waste drilling fluid has good anti-water logging bubble ability and certain intensity, because it is nontoxic, the solid material that forms comprehensive utilization such as can pave the way, also can bury the back and recover landforms, the soil that takies very soon can farmland to field, has thoroughly eliminated the pollution of rejected well drilling liquid to environment.Firming body leaches pH≤7.5 of water, total Cr≤1.5mg/L, COD
Cr≤ 200mg/L, petroleum-type≤10mg/L.This solidification processing method treatment process is simple, and the processing time is short, and curing agent is bought easily, is fit to harmless treatment rejected well drilling liquid in enormous quantities.
Enforcement of the present invention is to solidify the equipment of handling as rejected well drilling liquid with the existing slurry tank of situ of drilling well, slurry agitator, slush pump etc.Its technological process is, at first (press the percetage by weight calculating of water base rejected well drilling liquid according to the proportioning of various materials in the composite curing agent, inorganic molysite flocculating agent 1～6%, clay absorbent 0.1～0.6%, magnesia 1～6% and cementing agent 1～10%) it is mixed, and determine total input amount that composite curing agent is required according to the quantity that rejected well drilling liquid is housed in the slurry tank.Subsequently composite curing agent is divided and put in the rejected well drilling liquid for 4～5 times, cast a collection of after each curing agent that drops into stirs again, so promptly can avoid curing agent to improve too big to the viscosity of rejected well drilling liquid, simultaneously guarantee that again curing agent is uniformly dispersed in the rejected well drilling liquid of thickness, give full play to the solidification effect of curing agent, after treating that whole curing agent add and stir, be pumped in the heatable adobe sleeping platform it or near ground with slush pump, the open-air placement down can form firming body in 3～6 days.
Embodiment 1: rejected well drilling liquid proportion 1.49g/cm
3, added additives such as PAC, CMC, SMP, FCLS, sulfonated gilsonite and machine oil, outward appearance brownish black during the preparation drilling fluid.Adopt the solidification processing method and the curing agent thereof of waste water-base drilling liquid of the present invention that it is cured processing, ferric trichloride 6%, bentonite 0.6%, magnesia 6% and 425# cement 1% in the hardener formula (percetage by weight by water base rejected well drilling liquid is calculated), the gained firming body is soaked 24 hours (25 ℃) of vibration again, firming body is complete, flawless, leaching water is limpid, and the character that leaches water sees Table 1.
Table 1
Firming body leachate before the character of water is solidified
Ph value 9.8 7.4
COD
Cr mg/L 3.55×10
4 185
Oils mg/L can't survey 10.0
Total Cr mg/L 243 0.102
Embodiment 2: rejected well drilling liquid proportion 1.21g/cm
3, added FA-367, XY-27, PAC-142, SMP, FC-427 and former wet goods chemical addition agent, outward appearance brownish black during the preparation drilling fluid.After the hardener formula of forming with ferric trichloride 6%, bentonite 0.1%, magnesia 1% and 425# cement 7% (calculating by the percetage by weight of water base rejected well drilling liquid) is cured processing to this well rejected well drilling liquid, firming body has better intensity, firming body is soaked vibration more not to be split indeformable in 24 hours after (25 ℃), leaching water is limpid, and the character that leaches water sees Table 2.
Table 2
Firming body leachate before the character of water is solidified
PH value 8.0 7.0
COD
Cr?mg/L 3.2×10
4 150
Oils mg/L 14.0 0.15
Total Cr mg/L 1.56 0.007
Embodiment 3: rejected well drilling liquid proportion 1.14g/cm
3, added additives such as HPAM, HPAN, CMC, XY-27, outward appearance khaki during the preparation drilling fluid.Adopt hardener formula ferric trichloride 1% of the present invention, bentonite 0.6%, magnesia 2% and 425# cement 10% (percetage by weight by water base rejected well drilling liquid is calculated), it is cured processing back gained firming body soaks 24 hours (25 ℃) of vibration again, firming body is complete, flawless, leaching water is limpid, and the character that leaches water sees Table 3.
Table 3
Firming body leachate before the character of water is solidified
PH value 9.0 7.1
COD
Cr?mg/L 1×104 190
Oils mg/L 2,870 7.2
Total Cr mg/L 0.046 0.020
Embodiment 4: rejected well drilling liquid proportion 1.15g/cm
3, added additives such as HPAM, HPAN, CMC, NaOH, outward appearance khaki during the preparation drilling fluid.Adopt hardener formula ferric sulfate 1% of the present invention, bentonite 0.6%, magnesia 5% and 425# cement 5% (percetage by weight by water base rejected well drilling liquid is calculated), it is cured processing back gained firming body soaks 24 hours (25 ℃) of vibration again, firming body is complete, flawless, leaching water is limpid, and the character that leaches water sees Table 5.
Table 4
Firming body leachate before the character of water is solidified
PH value 8.5 7.5
COD
Cr?mg/L 8000 180
Oils mg/L 1,640 5.9
Total Cr mg/L 0.272 0.031
Claims (4)
1. the solidification processing method of a waste water-base drilling liquid, it is characterized in that: in the waste water-base drilling liquid of petroleum geology drilling well, add the composite curing agent of forming by flocculating agent, adsorbent, cementing agent and cement, the composite curing agent that adds stirs, subsequently composite curing agent is divided and put in the rejected well drilling liquid for 4～5 times, cast a collection of after each curing agent that drops into stirs again, pour heatable adobe sleeping platform again into or be deposited in ground, just can form firming body through 3～6 days curing.
2. the curing agent of waste water-base drilling liquid, it is characterized in that: flocculating agent is the inorganic molysite compound, dosage is 1～6% of a waste water-base drilling liquid weight; Adsorbent is a clay, and dosage is 0.1～0.6% of a waste water-base drilling liquid weight; Cementing agent is magnesia (MgO), and dosage is 1～6% of a waste water-base drilling liquid weight; Cement is common building 425
#Cement, dosage is 1～10% of a waste water-base drilling liquid weight, above-mentioned substance joins in the waste water-base drilling liquid with the form of homogeneous mixture, its maximum total dosage is 15% of a waste water-base drilling liquid weight, wherein the ratio of flocculating agent, adsorbent and cementing agent is 1: 0.1: 1, and it is cement that residue adds quantity of material.
3. the curing agent of waste water-base drilling liquid according to claim 2, it is characterized in that: said flocculating agent is the inorganic molysite compound, can be ferric sulfate, ferric trichloride.
4. the curing agent of waste water-base drilling liquid according to claim 2, it is characterized in that: said adsorbent is a clay, can be bentonite.