CN1341763A - 高铝铅锌基合金及其生产工艺 - Google Patents

高铝铅锌基合金及其生产工艺 Download PDF

Info

Publication number
CN1341763A
CN1341763A CN 01112885 CN01112885A CN1341763A CN 1341763 A CN1341763 A CN 1341763A CN 01112885 CN01112885 CN 01112885 CN 01112885 A CN01112885 A CN 01112885A CN 1341763 A CN1341763 A CN 1341763A
Authority
CN
China
Prior art keywords
zinc
aluminium
lead
base alloy
pig
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 01112885
Other languages
English (en)
Other versions
CN1164781C (zh
Inventor
蒋光华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANGHAI LIXI METAL PRODUCT CO Ltd
Original Assignee
SHANGHAI LIXI METAL PRODUCT CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI LIXI METAL PRODUCT CO Ltd filed Critical SHANGHAI LIXI METAL PRODUCT CO Ltd
Priority to CNB011128852A priority Critical patent/CN1164781C/zh
Publication of CN1341763A publication Critical patent/CN1341763A/zh
Application granted granted Critical
Publication of CN1164781C publication Critical patent/CN1164781C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明涉及冶金工业薄板用冶金材料制造技术领域的高铝铅锌基合金及其生产工艺。高铝铅锌基合金组分的重量配比是(以100份计):Zn:99.2－99.34份,Al:0.48－0.6份,Pb:0.16－0.20份。生产工艺包括以下步骤:准备铅锭、锌锭、铝锭,将铅锭熔化制成铅颗粒,将铝锭熔化,配加锌锭浇注成10%的条状锌铝合金,按配比将各组分加入熔化炉中,采用机械搅拌使各组分均匀分布,采用红外测温控制炉子的温度在590－650℃,然后浇注成型,冷却后脱模。解决了锌和铅的互熔性及“锌爆”现象,大大提高了镀锌薄板的耐蚀性和质量。

Description

高铝铅锌基合金及其生产工艺
本发明涉及的是冶金材料制造技术领域，特别涉及冶金工业薄板用冶金材料制造技术领域的高铝铅锌基合金及其生产工艺。
为了提高薄钢板抗腐蚀性，一般采用对薄钢板进行镀层保护，即在薄钢板的两个表面形成一层致密的镀层，镀锌是解决钢铁表面耐蚀的主要方法之一，一是氧化皮膜的生成可以阻止腐蚀介质的入侵，二是锌的牺牲阳极的作用可以代替基材腐蚀，但在潮湿、高盐份地区，锌镀层的耐蚀性能较差，在镀层中铝的加入可以消除镀层中脆性的γ相铁-锌合金层，使镀件更具加工性。研究表明，高铝铅锌基合金可以减少热镀锌脆性层，提高了锌层的附着力。目前低铝铅锌基合金的生产已为大家掌握，其主要技术指标是：合金成分：Al0.14-0.16％，Pb0.2-0.25％，Zn大于99.5％，但高铝锌基合金的生产仍未解决。中国专利ZL99100887介绍了“钢铁热浸镀5％铝-锌合金的方法”，该方法采用的是二元镀，存在镀层氧化膜较松散的缺点，而且该方法没有涉及到二元合金的生产方法。
本发明的目的在于：提供一种可以防止锌爆的产生，镀层致密，能使冶金企业生产的薄板提高抗腐蚀性能，成倍地延长薄钢板的使用寿命的高铝铅锌基合金及其生产工艺。
本发明的目的是这样实现的：一种高铝铅锌基合金，其组分的重量配比是(以100份计)：Zn：99.2-99.34份Al：0.48-0.6份Pb：0.16-0.20份杂质的控制：Fe：0-0.006份，Cd：0-0.001份。
高铝铅锌基合金的生产工艺包括以下步骤：准备铅锭、锌锭、铝锭，将铅锭熔化制成4-6mm的颗粒，将铝锭熔化，配加锌锭浇注成10％的条状锌铝合金，按配比将各组分加入熔化炉中，采用机械搅拌使各组分均匀分布，采用红外测温控制炉子的温度在590-650℃，然后浇注成型，采用高速风冷与水冷相结合的冷却工艺，冷却后脱模。
本发明高铝铅锌基合金及其生产工艺的有益效果在于：高铝铅锌基合金中铝和铅的成份允许波动范围万分之4～5之间达到均匀；介决了锌和铅的互熔性，尤其是铝含量增至0.45～0.6％后，保证了铝、铅、锌三种比重悬殊的金属充分混合，且使块与炉批的成份波动范围得到控制；添加铅，可使镀层表面产生铅花，提高了产品的附加值。采用了高速风冷与水冷相结合的冷却工艺，介决了锌的热胀冷缩，尤其是冷凝时要产生较大且深的缩孔问题，同时在使用本产品热镀时不产生“锌爆”现象，极大地提高了锌层附着力创造了条件，能使冶金企业生产的热镀锌薄板提高了抗腐蚀性能，成倍地延长薄钢板的使用寿命，提高了薄钢板的使用价值。
附图说明
附图为本发明主要工艺流程图
下面结合附图对本发明作进一步详细说明
实施例：如图中所示，准备经检验的铅锭、锌锭、铝锭，将铅锭熔化制成4-6mm的颗粒(需进行成份分析)。将铝锭熔化，配加锌锭浇注成10％的条状锌铝合金(需进行成份分析)，按配比将各组分加入熔化炉中，以1000公斤总量计，Zn：993公斤，Al：5.2公斤，Pb：1.8公斤，即加入铅粒1.8公斤，10％的条状锌铝合金5.78公斤，锌锭992.42公斤。在反射炉炉盖开孔并设置一可移动密封盖，当合金熔化后，从孔中置入搅拌装置，采用机械搅拌使各组分均匀分布，并取样进行炉前分析。采用红外测温控制炉子的温度在590-650℃，然后浇注成型，采用高速风冷与水冷相结合的冷却工艺，冷却后脱模。对成品进行外观检验和取样分析，合格品入库，不合格品返回重熔。

Claims (4)

1、一种高铝铅锌基合金，包括Zn、Al、Pb三种合金元素，其特征在于各组分的重量配比是(以100份计)：Zn：99.2-99.34份Al：0.48-0.6份Pb：0.16-0.20份杂质的控制：Fe：0-0.006份，Cd：0-0.001份。
2、一种高铝铅锌基合金的生产工艺，将铅锭、锌锭、铝锭熔化后浇铸成型，其特征在于生产工艺包括以下步骤：准备铅锭、锌锭、铝锭，将铅锭熔化制成铅颗粒，将铝锭熔化，配加锌锭浇注成10％的条状锌铝合金，按配比将各组分加入熔化炉中，采用机械搅拌使各组分均匀分布，采用红外测温控制炉子的温度在590-650℃，然后浇注成型，冷却后脱模。
3、根据权利要求2所述的一种高铝铅锌基合金的生产工艺，其特征在于采用高速风冷与水冷相结合的冷却工艺。
4、根据权利要求2所述的一种高铝铅锌基合金的生产工艺，其特征在于铅颗粒的直径为4-6mm。
CNB011128852A 2001-05-15 2001-05-15 高铝铅锌基合金及其生产工艺 Expired - Fee Related CN1164781C (zh)