CN1320378A - High-temp inorganic antibacterial agent - Google Patents
High-temp inorganic antibacterial agent Download PDFInfo
- Publication number
- CN1320378A CN1320378A CN 00108801 CN00108801A CN1320378A CN 1320378 A CN1320378 A CN 1320378A CN 00108801 CN00108801 CN 00108801 CN 00108801 A CN00108801 A CN 00108801A CN 1320378 A CN1320378 A CN 1320378A
- Authority
- CN
- China
- Prior art keywords
- antibacterial agent
- kinds
- temp
- carrier
- inorganic antibacterial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A high-temp inorganic antibacterial agent is prepared from antibacterial metal ions released from AgNO3, CuO, or ZnO, primary carrier (CaSO4, Al6Si2O13, or ZrO2, and secondary carrier (SiO2 or Al2O3) through solid reaction and sintering. Its advantages are low cost, high antibacterial effect and excellent high temp. resistance.
Description
The present invention relates to a kind of high-temp inorganic antibacterial agent, belong to field of new.
Existing inorganic antiseptic combines by high efficiency and the broad spectrum activity with inorganic material inherent stability and antibiotic composition, has successfully overcome safety in utilization, persistence, the broad-spectrum antibacterial property of organic anti-bacterial material, the shortcoming of warm tolerance equal difference.But still exist when temperature during above 1200 ℃ of left and right sides, its antibacterial effect extreme difference that just becomes almost loses the shortcoming of antibacterial effect.
The objective of the invention is to overcome the deficiency of prior art, and provide a kind of with low cost, antibiotic rate is high, heat-resisting quantity good, the high-temp inorganic antibacterial agent that the scope of application is wide.
The present invention is achieved in that this high-temp inorganic antibacterial agent is made up of antibacterial metal ions and carrier.Wherein, antibacterial metal ions is by AgNO
3, among CuO, the ZnO any one, two kinds or three kinds select acquisition simultaneously for use, its monodrome or and value shared percentage by weight in always filling a prescription be not less than 4%.Span is respectively: AgNO
3Get that 0～10wt%, CuO get 0～10wt%, ZnO gets 0～20wt%.Carrier is made up of main carrier and attached carrier, and main carrier is CaSO
4, Al
6Si
2O
13, ZrO
2In any one, two kinds or three kinds select for use simultaneously, its span is 0～95wt%; Attached carrier is SiO
2, AlO
3In any one or two kinds select for use simultaneously, its monodrome or and value shared percentage by weight can not be less than 1% in total prescription, its span is 0～15wt%.Antibacterial agent is made with solid state reaction sintering.
Embodiments of the invention are as follows:
Select for use down the each component in the page table to determine prescription, technology weighing routinely, mixings of preparing, mill, afterwards again through solid state reaction sintering (temperature is got 750 ℃～1300 ℃, and the time is more than one hour) are milled carefully, operation such as packing and obtain high-temp inorganic antibacterial agent.This high-temp inorganic antibacterial agent after testing, its antibiotic circle is more than 1mm, the minimum growth stops concentration MIC all less than 300ppm.This antibacterial agent mixes the domestic ceramics glaze and imposes on the idiosome surface, and its antibiotic rate reaches 99.99%.Antibacterial agent is made with solid state reaction sintering.
The present invention compared with prior art has advantages such as with low cost, that antibiotic rate is high, heat-resisting quantity is good.Can be widely used in construction material, domestic ceramics, plastics, coating, paint, paper, textile and the timber etc.
High-temp inorganic antibacterial agent each component list of values
| Sequence number | Antibacterial metal (wt%) | Carrier (wt%) | ||||||
| AgNO 3 | ?CuO | ???ZnO | ?CaSO 4 | ?Al 6Si 2O 13 | ?ZrO 2 | ?Al 2O 3 | ?SiO 2 | |
| ?1 | ????3 | ????18 | ????66 | ????13 | ||||
| ?2 | ????10 | ????18 | ????59 | ????13 | ||||
| ?3 | ????5 | ????90 | ????5 | |||||
| ?4 | ????8 | ????91 | ????1 | |||||
| ?5 | ????2 | ????5 | ????90 | ????3 | ||||
| ?6 | ????2 | ????4 | ????93 | ????1 | ||||
| ?7 | ????2 | ????10 | ????73 | ????15 | ||||
| ?8 | ????5 | ????93 | ????2 | |||||
| ?9 | ????3 | ????4 | ????3 | ????80 | ????10 | |||
| ?10 | ????10 | ????8 | ????65 | ????4 | ????13 | |||
| ?11 | ????4 | ????95 | ????1 | |||||
| ?12 | ????3 | ????3 | ????10 | ????20 | ????40 | ????20 | ????4 | |
Claims (1)
1, a kind of high-temp inorganic antibacterial agent is characterized in that this high-temp inorganic antibacterial agent is made up of antibacterial metal ions and carrier; Wherein:
1,1 antibacterial metal ions is by AgNO
3, among CuO, the ZnO any one, two kinds or three kinds select acquisition simultaneously for use, its monodrome or and value shared percentage by weight can not be less than 4% in total prescription, its span is respectively: AgNO
2Get that 0～10wt%, CuO get 0～10wt%, ZnO gets 0～20wt%;
1,2 carriers are made up of main carrier and attached carrier, and main carrier is CaSO
4, Al
6Si
2O
13, ZrO
2In any one, two kinds or three kinds select for use simultaneously, its span is 0～95wt%; Attached carrier is SiO
2, Al
2O
3In any one or two kinds or select for use simultaneously, its monodrome or and value shared percentage by weight can not be less than 1% in total prescription, its span is 0～15wt%;
1,3 antibacterial agents are made with solid state reaction sintering.