CN106009981A - Bactericidal plastic-wood material composition, bactericidal plastic-wood product and production method of bactericidal plastic-wood product - Google Patents
Bactericidal plastic-wood material composition, bactericidal plastic-wood product and production method of bactericidal plastic-wood product Download PDFInfo
- Publication number
- CN106009981A CN106009981A CN201610570561.4A CN201610570561A CN106009981A CN 106009981 A CN106009981 A CN 106009981A CN 201610570561 A CN201610570561 A CN 201610570561A CN 106009981 A CN106009981 A CN 106009981A
- Authority
- CN
- China
- Prior art keywords
- weight portion
- wood
- consumption
- content
- acetate emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a bactericidal plastic-wood material composition, a bactericidal plastic-wood product and a production method of the bactericidal plastic-wood product. The composition comprises a plastic-wood matrix and bactericidal coating applied to the outer surface of the plastic-wood matrix. The bactericidal coating comprises water, polyvinyl acetate emulsion, poly(vinyl alcohol), ethylene glycol, nanosilicon dioxide, CMIT and sodium benzoate. Specifically, to 100 parts of water by weight, there are 30-70 parts of polyvinyl acetate emulsion, 10-30 parts of poly(vinyl alcohol), 20-50 parts of ethylene glycol, 5-15 parts of nanosilicon dioxide, 0.1-2 part of CMIT and 0.1-1 part of sodium benzoate. According to the design, the composition is bactericidal; and invasion of bacteria to the composition is weak even in an environment full of bacteria.
Description
Technical field
The present invention relates to mould the production preparation field of wood, in particular it relates to from sterilization plastic-wood material compositions
Wood and preparation method thereof is moulded with from sterilization.
Background technology
Along with global resources are the most exhausted, social environment consciousness is the most surging, to timber in producing and living
Have higher requirement with petroleum chemicals application.Plastic-wood material as a kind of emerging environment-friendly materials, its
Main with plant fiber material as major ingredient, add plastics synthesis, form a kind of suitability and be combined widely
Material.Because it has the advantage of Plant fiber and plastics concurrently, so that range in actual use
Extremely wide.
But it is mixed with by plastics and wood powder often because moulding wood, thus it has the characteristic of wood powder,
Easily make its long bacterium because of problems such as environment time actually used, thus largely effect on this serviceability moulding wood
And service life, cause scrappage to be greatly increased.
Therefore it provides one can be from sterilization, even if also being able to ensure antibacterial in the environment of antibacterial is more
Less from sterilization plastic-wood material compositions with to mould wood and preparation method thereof from sterilization be this to its infringement
The bright problem needing solution badly.
Summary of the invention
For above-mentioned prior art, it is an object of the invention to overcome in prior art because of mould wood often by
Plastics and wood powder are mixed with, thus it has the characteristic of wood powder, easily because of environment etc. when actually used
Problem makes its long bacterium, thus largely effects on this serviceability moulding wood and service life, causes scrappage
The problem being greatly increased, thus provide one certainly to sterilize, even if also can in the environment of antibacterial is more
Enough ensure that it is encroached on less sterilization plastic-wood material compositions certainly and moulds wood and preparation thereof from sterilization by antibacterial
Method.
To achieve these goals, the invention provides a kind of from sterilization plastic-wood material compositions, wherein,
Described compositions includes moulding wood matrix and moulds the fungicidal paint on wood outer surface of matrix described in being applied in, its
In, described fungicidal paint includes water, polyvinyl acetate emulsion, polyvinyl alcohol, ethylene glycol, nano-silica
SiClx, methylchloroisothiazandnone and sodium benzoate；Wherein,
Relative to the described water of 100 weight portions, the content of described polyvinyl acetate emulsion is 30-70 weight
Part, the content of described polyvinyl alcohol is 10-30 weight portion, and the content of described ethylene glycol is 20-50 weight
Part, the content of described nano silicon is 5-15 weight portion, containing of described methylchloroisothiazandnone
Amount is 0.1-2 weight portion, and the content of described sodium benzoate is 0.1-1 weight portion.
Present invention also offers a kind of preparation method moulding wood from sterilization, wherein, described preparation method includes:
1) by water, polyvinyl acetate emulsion, polyvinyl alcohol, ethylene glycol, nano silicon, methyl
Chloroisothiazole quinoline ketone and sodium benzoate mixing, prepare fungicidal paint M1；
2) by step 1) in prepare fungicidal paint M1 be applied in mould wood outer surface of matrix on, prepare from
Wood is moulded in sterilization；Wherein,
Relative to the described water of 100 weight portions, the consumption of described polyvinyl acetate emulsion is 30-70 weight
Part, the consumption of described polyvinyl alcohol is 10-30 weight portion, and the consumption of described ethylene glycol is 20-50 weight
Part, the consumption of described nano silicon is 5-15 weight portion, the use of described methylchloroisothiazandnone
Amount is 0.1-2 weight portion, and the consumption of described sodium benzoate is 0.1-1 weight portion.
Present invention also offers a kind of sterilization certainly prepared according to preparation method described above and mould wood.
By technique scheme, the present invention by water, polyvinyl acetate emulsion, polyvinyl alcohol, ethylene glycol,
Nano silicon, methylchloroisothiazandnone and sodium benzoate are mixed to prepare sterilization according to a certain percentage
Coating, is then applied in above-mentioned prepared fungicidal paint and moulds on wood outer surface of matrix, so that pass through
What said method prepared mould wood has good from bactericidal property when actually used, significantly widens it and uses
Environment, increases the service life, and reduces scrappage.
Other features and advantages of the present invention will be described in detail in detailed description of the invention part subsequently.
Detailed description of the invention
Hereinafter the detailed description of the invention of the present invention is described in detail.It should be appreciated that this place is retouched
The detailed description of the invention stated is merely to illustrate and explains the present invention, is not limited to the present invention.
The invention provides a kind of from sterilization plastic-wood material compositions, wherein, described compositions includes moulding wood
Matrix moulds the fungicidal paint on wood outer surface of matrix described in being applied in, and wherein, described fungicidal paint includes
Water, polyvinyl acetate emulsion, polyvinyl alcohol, ethylene glycol, nano silicon, methyl chloride isothiazoline
Ketone and sodium benzoate；Wherein,
Relative to the described water of 100 weight portions, the content of described polyvinyl acetate emulsion is 30-70 weight
Part, the content of described polyvinyl alcohol is 10-30 weight portion, and the content of described ethylene glycol is 20-50 weight
Part, the content of described nano silicon is 5-15 weight portion, containing of described methylchloroisothiazandnone
Amount is 0.1-2 weight portion, and the content of described sodium benzoate is 0.1-1 weight portion.
Above-mentioned design is by by water, polyvinyl acetate emulsion, polyvinyl alcohol, ethylene glycol, nanometer titanium dioxide
Silicon, methylchloroisothiazandnone and sodium benzoate are mixed to prepare fungicidal paint according to a certain percentage, then
Above-mentioned prepared fungicidal paint is applied in and moulds on wood outer surface of matrix, so that by said method system
Wood of moulding have good from bactericidal property when actually used, significantly widen it and use environment, extend
In service life, reduce scrappage.
The present invention one preferred embodiment in, in order to improve the prepared suicide moulding wood further
Bacterium performance, relative to the described water of 100 weight portions, the content of described polyvinyl acetate emulsion is 40-60
Weight portion, the content of described polyvinyl alcohol is 15-25 weight portion, and the content of described ethylene glycol is 30-40
Weight portion, the content of described nano silicon is 8-12 weight portion, described methylchloroisothiazandnone
Content be 1-2 weight portion, the content of described sodium benzoate is 0.5-1 weight portion.
Certainly, in a kind of embodiment being more highly preferred to, prepared mould making of wood to improve further
By performance, described fungicidal paint can also include processing aid.
Here processing aid can be processing aid type commonly used in the art, such as, in one
In preferred embodiment, described processing aid can be selected from anti ultraviolet agent and/or antistatic additive.
Described polyvinyl acetate emulsion can be type commonly used in the art, such as, in one more
In preferred embodiment, described polyvinyl acetate emulsion can be further selected as viscosity and be
4500-7000mPa·s。
Similarly, in a kind of embodiment being more highly preferred to, the viscosity of described polyvinyl alcohol is not less than
30mPa·s。
Present invention also offers a kind of preparation method moulding wood from sterilization, wherein, described preparation method includes:
1) by water, polyvinyl acetate emulsion, polyvinyl alcohol, ethylene glycol, nano silicon, methyl
Chloroisothiazole quinoline ketone and sodium benzoate mixing, prepare fungicidal paint M1；
2) by step 1) in prepare fungicidal paint M1 be applied in mould wood outer surface of matrix on, prepare from
Wood is moulded in sterilization；Wherein,
Relative to the described water of 100 weight portions, the consumption of described polyvinyl acetate emulsion is 30-70 weight
Part, the consumption of described polyvinyl alcohol is 10-30 weight portion, and the consumption of described ethylene glycol is 20-50 weight
Part, the consumption of described nano silicon is 5-15 weight portion, the use of described methylchloroisothiazandnone
Amount is 0.1-2 weight portion, and the consumption of described sodium benzoate is 0.1-1 weight portion.
In a preferred embodiment, in order to improve further prepared mould wood from bactericidal property,
Relative to the described water of 100 weight portions, the consumption of described polyvinyl acetate emulsion is 40-60 weight portion,
The consumption of described polyvinyl alcohol is 15-25 weight portion, and the consumption of described ethylene glycol is 30-40 weight portion,
The consumption of described nano silicon is 8-12 weight portion, and the consumption of described methylchloroisothiazandnone is
1-2 weight portion, the consumption of described sodium benzoate is 0.5-1 weight portion.
Similarly, in order to make the serviceability moulding wood prepared more preferable, the one in the present invention is more highly preferred to
Embodiment in, step 1) in can also include add processing aid mix.
Described processing aid, described polyvinyl acetate emulsion and described polyvinyl alcohol are as previously mentioned.
Step 1) in mixed process can operate according to this area usual manner, such as, Yi Zhongyou
Choosing embodiment in, step 1) in mixed process be to be placed in the bar that stir speed (S.S.) is 300-600r/min
Stirring mixing under part.
Present invention also offers a kind of sterilization certainly prepared according to preparation method described above and mould wood.
In order to ensure that on the premise of cost-effective it from bactericidal property, is more highly preferred to a kind of as far as possible
In embodiment, step 2) in be applied in the thickness of the fungicidal paint M1 moulded on wood outer surface of matrix and be
0.1-1mm。
Hereinafter will be described the present invention by embodiment.In following example, described poly-acetic acid
Vac emulsion is the commercially available polyvinyl acetate emulsion of Ningbo Hai Shuyiduo chemical products company limited supply, institute
State the city that the commercially available trade mark is 100-40H that polyvinyl alcohol is the supply of Longjiang, Shenyang Jian Hui trade Co., Ltd
Sell product, described ethylene glycol, described nano silicon, described methylchloroisothiazandnone and described rest in peace
Fragrant acid sodium is conventional commercial product.
Embodiment 1
1) by 100g water, 40g polyvinyl acetate emulsion, 15g polyvinyl alcohol, 30g ethylene glycol, 8g
Nano silicon, 1g methylchloroisothiazandnone and 0.5g sodium benzoate are placed in stir speed (S.S.)
Stirring mixing under conditions of 300r/min, prepares fungicidal paint M1；
2) by step 1) in prepare fungicidal paint M1 be applied in mould wood outer surface of matrix up to thickness be
0.1mm, prepares and moulds wood A1 from sterilization.
Embodiment 2
1) by 100g water, 60g polyvinyl acetate emulsion, 25g polyvinyl alcohol, 40g ethylene glycol, 12g
Nano silicon, 2g methylchloroisothiazandnone and 1g sodium benzoate are placed in stir speed (S.S.)
Stirring mixing under conditions of 600r/min, prepares fungicidal paint M1；
2) by step 1) in prepare fungicidal paint M1 be applied in mould wood outer surface of matrix up to thickness be
1mm, prepares and moulds wood A2 from sterilization.
Embodiment 3
1) by 100g water, 50g polyvinyl acetate emulsion, 20g polyvinyl alcohol, 35g ethylene glycol, 10g
Nano silicon, 2g methylchloroisothiazandnone and 1g sodium benzoate are placed in stir speed (S.S.)
Stirring mixing under conditions of 500r/min, prepares fungicidal paint M1；
2) by step 1) in prepare fungicidal paint M1 be applied in mould wood outer surface of matrix up to thickness be
0.5mm, prepares and moulds wood A3 from sterilization.
Embodiment 4
It is prepared according to the preparation method of embodiment 1, except for the difference that, described polyvinyl acetate emulsion
Consumption is 30g, and the consumption of described polyvinyl alcohol is 10g, and the consumption of described ethylene glycol is 20g, described in receive
The consumption of rice silicon dioxide is 5g, and the consumption of described methylchloroisothiazandnone is 0.1g, described Benzoinum
The consumption of acid sodium is 0.1g, prepares and moulds wood A4 from sterilization.
Embodiment 5
It is prepared according to the preparation method of embodiment 2, except for the difference that, described polyvinyl acetate emulsion
Consumption is 70g, and the consumption of described polyvinyl alcohol is 30g, and the consumption of described ethylene glycol is 50g, described in receive
The consumption of rice silicon dioxide is 15g, and the consumption of described methylchloroisothiazandnone is 2g, described Benzoinum
The consumption of acid sodium is 1g, prepares and moulds wood A5 from sterilization.
Comparative example 1
It is prepared according to the preparation method of embodiment 3, except for the difference that, described polyvinyl acetate emulsion
Consumption is 10g, and the consumption of described polyvinyl alcohol is 5g, and the consumption of described ethylene glycol is 10g, described in receive
The consumption of rice silicon dioxide is 2g, prepares and moulds wood D1.
Comparative example 2
It is prepared according to the preparation method of embodiment 3, except for the difference that, described polyvinyl acetate emulsion
Consumption is 100g, and the consumption of described polyvinyl alcohol is 50g, and the consumption of described ethylene glycol is 80g, described
The consumption of nano silicon is 30g, and the consumption of described methylchloroisothiazandnone is 5g, described in rest in peace
The consumption of fragrant acid sodium is 2g, prepares and moulds wood D2.
Comparative example 3
Mould wood matrix D3.
Test case
Above-mentioned A1-A5 and D1-D3 is respectively placed in bacterial content more in the environment of place 7 days, point
Jie Qu not be placed in 100g water immersion by the above-mentioned wood of moulding of 1g, bacterial content in detection water, the result obtained is such as
Shown in table 1.
Table 1
| Numbering | Total plate count (cfu) |
| A1 | 12 |
| A2 | 8 |
| A3 | 10 |
| A4 | 26 |
| A5 | 35 |
| D1 | ＞ 100 |
| D2 | ＞ 100 |
| D3 | ＞ 100 |
The preferred embodiment of the present invention described in detail above, but, the present invention is not limited to above-mentioned reality
Execute the detail in mode, in the technology concept of the present invention, can be to the technical side of the present invention
Case carries out multiple simple variant, and these simple variant belong to protection scope of the present invention.
It is further to note that each the concrete technology described in above-mentioned detailed description of the invention is special
Levy, in the case of reconcilable, can be combined by any suitable means, in order to avoid need not
The repetition wanted, various possible compound modes are illustrated by the present invention the most separately.
Additionally, combination in any can also be carried out between the various different embodiment of the present invention, as long as its
Without prejudice to the thought of the present invention, it should be considered as content disclosed in this invention equally.
Claims (10)
1. the plastic-wood material compositions that certainly sterilizes, it is characterised in that described compositions includes moulding wood base
Body and the fungicidal paint moulded described in being applied on wood outer surface of matrix, wherein, described fungicidal paint include water,
Polyvinyl acetate emulsion, polyvinyl alcohol, ethylene glycol, nano silicon, methylchloroisothiazandnone and
Sodium benzoate；Wherein,
Relative to the described water of 100 weight portions, the content of described polyvinyl acetate emulsion is 30-70 weight
Part, the content of described polyvinyl alcohol is 10-30 weight portion, and the content of described ethylene glycol is 20-50 weight
Part, the content of described nano silicon is 5-15 weight portion, containing of described methylchloroisothiazandnone
Amount is 0.1-2 weight portion, and the content of described sodium benzoate is 0.1-1 weight portion.
Compositions the most according to claim 1, wherein, relative to the described water of 100 weight portions,
The content of described polyvinyl acetate emulsion is 40-60 weight portion, and the content of described polyvinyl alcohol is 15-25
Weight portion, the content of described ethylene glycol is 30-40 weight portion, and the content of described nano silicon is 8-12
Weight portion, the content of described methylchloroisothiazandnone is 1-2 weight portion, containing of described sodium benzoate
Amount is 0.5-1 weight portion.
Compositions the most according to claim 1 and 2, wherein, described fungicidal paint also includes adding
Work auxiliary agent；
Preferably, described processing aid is selected from anti ultraviolet agent and/or antistatic additive.
Compositions the most according to claim 1 and 2, wherein, described polyvinyl acetate emulsion
Viscosity is 4500-7000mPa s；
The viscosity of described polyvinyl alcohol is not less than 30mPa s.
5. the preparation method moulding wood from sterilization, it is characterised in that described preparation method includes:
1) by water, polyvinyl acetate emulsion, polyvinyl alcohol, ethylene glycol, nano silicon, methyl
Chloroisothiazole quinoline ketone and sodium benzoate mixing, prepare fungicidal paint M1；
2) by step 1) in prepare fungicidal paint M1 be applied in mould wood outer surface of matrix on, prepare from
Wood is moulded in sterilization；Wherein,
Relative to the described water of 100 weight portions, the consumption of described polyvinyl acetate emulsion is 30-70 weight
Part, the consumption of described polyvinyl alcohol is 10-30 weight portion, and the consumption of described ethylene glycol is 20-50 weight
Part, the consumption of described nano silicon is 5-15 weight portion, the use of described methylchloroisothiazandnone
Amount is 0.1-2 weight portion, and the consumption of described sodium benzoate is 0.1-1 weight portion.
Preparation method the most according to claim 5, wherein, described in 100 weight portions
Water, the consumption of described polyvinyl acetate emulsion is 40-60 weight portion, and the consumption of described polyvinyl alcohol is
15-25 weight portion, the consumption of described ethylene glycol is 30-40 weight portion, the use of described nano silicon
Amount is 8-12 weight portion, and the consumption of described methylchloroisothiazandnone is 1-2 weight portion, described Benzoinum
The consumption of acid sodium is 0.5-1 weight portion.
7. according to the preparation method described in claim 5 or 6, wherein, step 1) in also include add
Processing aid mixes；
Preferably, described processing aid is selected from anti ultraviolet agent and/or antistatic additive.
8. according to the preparation method described in claim 5 or 6, wherein, described polyvinyl acetate emulsion
Viscosity be 4500-7000mPa s；
The viscosity of described polyvinyl alcohol is not less than 30mPa s.
9. according to the preparation method described in claim 5 or 6, wherein, step 1) in mixed process be
Being placed in stir speed (S.S.) is stirring mixing under conditions of 300-600r/min.
10. mould from sterilization according to what the preparation method described in any one in claim 5-9 prepared for one kind
Wood；
Preferably, step 2) in be applied in the thickness of fungicidal paint M1 moulded on wood outer surface of matrix and be
0.1-1mm。