CN1306118A - 导电涤纶纤维的制造方法 - Google Patents

导电涤纶纤维的制造方法 Download PDF

Info

Publication number
CN1306118A
CN1306118A CN 01106925 CN01106925A CN1306118A CN 1306118 A CN1306118 A CN 1306118A CN 01106925 CN01106925 CN 01106925 CN 01106925 A CN01106925 A CN 01106925A CN 1306118 A CN1306118 A CN 1306118A
Authority
CN
China
Prior art keywords
fiber
minute
acid
alligatoring
clean
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 01106925
Other languages
English (en)
Inventor
谭松庭
王霞瑜
周计
周建萍
赵斌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xiangtan University
Original Assignee
Xiangtan University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Xiangtan University filed Critical Xiangtan University
Priority to CN 01106925 priority Critical patent/CN1306118A/zh
Publication of CN1306118A publication Critical patent/CN1306118A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种导电涤纶纤维的制造方法,是以涤纶纤维为原料,采用化学镀和电镀技术在涤纶纤维表面镀上一层金属铜和镍,制成具有导电性能的导电涤纶纤维,该导电涤纶纤维具有导电性好(体积电阻率为9.6×10－5Ω·cm),比重小(<1.5g/cm3)、成本低(低于金属纤维和碳纤维)等优点。经过测试,这种表面金属化的纤维在室温－220℃范围内擦洗不易脱落。

Description

导电涤纶纤维的制造方法
本发明属高分子材料领域，涉及一种导电涤纶纤维的制造方法。
目前，导电纤维是一种需求量越来越大的新型材料，如为了制造带电作业的屏蔽服，需用导电纤维织布；为了制备电磁屏蔽材料，需要用导电纤维掺入树脂中制成导电塑料。但常用的化学纤维是不导电的，为了满足上述需要，目前采用金属纤维或碳纤维作导电纤维，用拉拨法生产的金属纤维作上述用途时，导电性能可以达到要求，但这种金属纤维价格很高(目前国产价高于400元/公斤)，且这种金属纤维比重大，生产的产品很重，不受用户欢迎。如用碳纤维虽然比重较小，但除价格较高外，导电性能也不能满足要求。
本发明的目的在于提供一种导电性能好，比重小，价格低的导电纤维的制造方法。
本发明的目的是通过如下途径实现的：一种导电涤纶纤维制造方法，其具体工艺流程如下：(1)除油：将涤纶纤维放入除油液中浸泡洗涤；(2)粗化：将除油后的纤维放在粗化液中粗化15-30分钟；(3)敏化：将粗化后的纤维洗净，放入含氯化亚锡、盐酸和锡粒的敏化液中敏化5-8分钟；(4)活化：将敏化后的纤维用热水洗净，放入含有硝酸银、氨水的活化液中活化5-8分钟；(5)化学镀：将活化后的纤维用水漂洗干净，放入含硫酸铜、甲醛、酒石酸钾钠、氢氧化钠配成的化学镀铜液中反应5-8分钟；(6)电镀：将化学镀铜后的纤维漂洗干净，放入含硫酸镍、氯化钠、硼酸、十二烷基磺酸钠组成的电镀液中电镀30-45分钟，洗净烘干即得到导电涤纶纤维。除油液由氢氧化钠、洗洁净配成的混合液。粗化液为重络酸钾、浓硫酸配成的混合液。
本发明是以涤纶纤维为原料，采用化学镀和电镀技术将纤维表面金属化，制造的导电涤纶纤维具有导电性好(体积电阻率为9.6×10-5Ω·cm)，比重小(＜1.5g/cm3)、成本低(低于金属纤维和碳纤维)等优点。经过测试，这种表面金属化的纤维在室温-220℃范围内擦洗不易脱落。
下面结合实施例对本发明作进一步详细说明：
取100克涤纶纤维，在70℃的除油液中浸泡30分钟；取出洗净后，放入80℃的粗化液中粗化30分钟。纤维取出后，洗净放入常温的敏化液中敏化5分钟；取出用热水洗涤10分钟；洗净后放入活化液中在室温下活化10分钟；将活化后的纤维漂洗干净，放入化学镀铜液中在室温下反应5-8分钟，待纤维表面变为古铜色后取出漂洗干净，在室温下进行电镀，电镀时电流密度为0.01安/分米2，时间约30分钟，当纤维变为银灰色，镀层达一定厚度(约0.1μm)后，取出纤维，清洗干净后烘干可得导电纤维112克。
制剂配方：a．除油液：氢氧化钠15克/升，洗洁净5克/升，其余部分为蒸溜水(下同)b．粗化液：重铬酸钾120克/升，硫酸500克/升。c．敏化液：氯化亚锡10克/升，盐酸50毫升/升，锡粒若干。d．活化液：硝酸银15克/升，氨水7毫升/升。e．化学镀铜液：酒石酸钾钠43克/升，氢氧化钠10克/升，硫酸铜10克/升，甲醛(40％)100毫升/升(化学镀前临时加入)，醋酸铅5毫克/克。f．电镀镍溶液：硫酸镍200克/升，氯化钠9克/升，硼酸35克/升，十二烷基磺酸钠0.1克/升。

Claims (3)

1．一种导电涤纶纤维的制造方法，其特征在于：其具体工艺流程如下：(1)除油：将涤纶纤维放入除油液中浸泡洗涤；(2)粗化：将除油后的纤维放在粗化液中粗化15-30分钟；(3)敏化：将粗化后的纤维洗净，放入含氯化亚锡、盐酸和锡粒的敏化液中敏化5-8分钟；(4)活化：将敏化后的纤维用热水洗净，放入含有硝酸银、氨水的活化液中活化5-8分钟；(5)化学镀：将活化后的纤维用水漂洗干净，放入含硫酸铜、甲醛、酒石酸钾钠、氢氧化钠配成的化学镀铜液中反应5-8分钟；(6)电镀：将化学镀铜后的纤维漂洗干净，放入含硫酸镍、氯化钠、硼酸、十二烷基磺酸钠组成的电镀液中电镀30-45分钟，洗净烘干即得到导电涤纶纤维。
2．如权利要求1所述导电涤纶纤维的制造方法，其特征在于：除油液由氢氧化钠、洗洁净配成的混合液。
3．如权利要求1所述导电涤纶纤维的制造方法，其特征在于：粗化液为重络酸钾、浓硫酸配成的混合液。
CN 01106925 2001-02-27 2001-02-27 导电涤纶纤维的制造方法 Pending CN1306118A (zh)