CN1306050A - Organosilicon modified acrylic paint for external wall and its preparing process - Google Patents
Organosilicon modified acrylic paint for external wall and its preparing process Download PDFInfo
- Publication number
- CN1306050A CN1306050A CN 99112498 CN99112498A CN1306050A CN 1306050 A CN1306050 A CN 1306050A CN 99112498 CN99112498 CN 99112498 CN 99112498 A CN99112498 A CN 99112498A CN 1306050 A CN1306050 A CN 1306050A
- Authority
- CN
- China
- Prior art keywords
- defoamer
- organosilicon
- modified acrylic
- water
- external wall
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
An organosilicon modified acrylic paint for external surface of wall is prepared through solution polymerization reaction of organosilicon monomer, acrylate monomer, acrylic acid, emulsifier, trigger and distilled water, and mixing the resultant high-molecular polymer with water, defoaming agent, anticorrosion agent, disperser, filler and thickening agent. Its advantages are high weatherability, hardness, adhesion and surface hydrophobicity, gay lustre, long service life and no environmental pollution.
Description
The present invention relates to this technical field of coating, particularly a kind of organosilicon modified acrylic paint for external wall and preparation method.
At present, the most frequently used building coating of China can be divided into oil paint and water-borne coatings two big series.Oil paint contains objectionable constituent such as formaldehyde, organic solvent, benzene series thing and heavy metal, and organic solvent is inflammable, not only bring inconvenience, and evaporate in the air and can cause environmental pollution and waste of material, thereby also easily efflorescence, variable color of product, coming off influences decorative effect to construction.Though water-borne coatings can be protected environment, save energy, at present the coating quality of throwing on the domestic market is poor, of low grade, mainly shows: gloss is low, poor adhesive force, not water-fastly wash, self-cleaning is poor, fugitive color.
It is that 97105779.6 patent relates to silicon Acrylote paint and preparation method thereof that an application number is arranged.This coating is made up of ACRYLIC EMULSION, silicone resin, filler, film coalescence aid, thickening material, water-resisting agent, dispersion agent, defoamer, sanitas and water.The main drawback of this coating is that weathering resistance is still strong inadequately.
The objective of the invention is at above-mentioned the deficiencies in the prior art part, provide a kind of produce and use in do not have environment-friendly type coating of high-weatherability that " three wastes " discharge, high adhesive force, high hydrophobicity, long service life and preparation method thereof.
The present invention is achieved through the following technical solutions: this coating is to be main film forming matter with organosilicon crylic acid latex, adds filler, dispersion agent, defoamer, sanitas, thickening material, water and makes.Proportioning between each composition is: organosilicon crylic acid latex 30-38, filler 30-35, dispersion agent 0.5-1, defoamer 0.1-0.2, sanitas 0.1-0.3, thickening material 1-2, water 30-35.The composition of organosilicon crylic acid latex (weight %) is the high molecular polymer that is made by solution polymerization by organosilane monomer 5-8, acrylate monomer 8.6-10, adding vinylformic acid 1-6, initiator 0.6-1.6, emulsifying agent 3-5, distilled water 70-80.
The compound method of this coating is: prepare burden by the said components proportioning, in reactor, add distilled water and be heated to the 85-90 degree, splash into organosilane monomer, acrylate monomer, vinylformic acid and initiator, emulsifying agent, dropwised in 2-3 hour, be incubated 1 hour again, cool to the 30-40 degree, regulate pH value to 6-9 discharging and promptly make organosilicon crylic acid latex.In joining the lacquer cylinder, add entry, add defoamer, sanitas, dispersion agent while stirring, mix the back and add filler, continue to be stirred to evenly, regulate pH value to 7.5-8.5, with shredder grind to fineness less than after 40 microns, under stirring at low speed, add organosilicon crylic acid latex, defoamer, adjust to proper viscosity with thickening material at last and get final product.
The present invention compared with prior art has following advantage: the main film forming matter organosilicon crylic acid latex of this coating is the high molecular polymer that is made by solution polymerization by organosilane monomer, acrylate monomer, adding vinylformic acid, initiator, emulsifying agent, distilled water.This coating has high-weatherability, and is all splendid on gloss, hardness, adhesion strength, surface hydrophobicity, long service life, and do not have " three wastes " discharging in the production use.
Embodiments of the invention are described in detail in detail below: a kind of organosilicon modified acrylic paint for external wall, its component (weight %) contains: organosilicon crylic acid latex 30-38, filler 30-35, dispersion agent 0.5-1, defoamer 0.1-0.2, sanitas 0,1-0,3, thickening material 1-2, water 30-35.The composition of organosilicon crylic acid latex (weight %) is the high molecular polymer that is made by solution polymerization by organosilane monomer 5-8, acrylate monomer 8.6-10, adding vinylformic acid 1-6, initiator 0.6-1.6, emulsifying agent 3-5, distilled water 70-80.Filler is made up of titanium dioxide, mica powder and water-ground limestone or kaolin, and the proportioning between them (weight %) is titanium dioxide 40-50, mica powder 10-15, water-ground limestone or kaolin 35-45.The method for preparing organosilicon modified acrylic paint for external wall, be in reactor, to add distilled water to be heated to the 85-90 degree, splash into organosilane monomer, acrylate monomer, vinylformic acid and initiator, emulsifying agent, dropwised in 2-3 hour, be incubated 1 hour again, cool to the 30-40 degree, regulate pH value to 6-9 discharging and promptly make organosilicon crylic acid latex.Add entry in the cylinder, add defoamer, sanitas, dispersion agent while stirring joining lacquer, mix the back and add filler, continue to be stirred to evenly, regulate pH value to 7.5-8.5, with shredder grind to fineness less than after 40 microns, under stirring at low speed, add organosilicon crylic acid latex, defoamer, adjust to proper viscosity with thickening material at last and get final product.Use for the first time the amount of defoamer as using 60-70%, the second time of defoamer total amount the 30-40% of the amount of defoamer as total amount.For the first time using the effect of defoamer is to make this coating non-foaming in process of production, and using defoamer for the second time is to make this coating in use non-foaming.Organosilicon crylic acid latex is the main film forming matter of this coating, organosilicon has higher thermotolerance, hydrophobic nature, lower temperature resistance, vinylformic acid is through after organic-silicon-modified, and the copolymer emulsion of generation has characteristics such as high-weatherability, high gloss, high rigidity, high-adhesion, surface hydrophobicity be fabulous.Colors such as this coating is the multiple color of furnishing as required, can select Rutile type Titanium Dioxide for use as white, and is red, yellow, green are selected red iron oxide, iron oxide green, iron oxide yellow etc. for use.
This coating is through the detection of national agent authorized, and every performance index have have all met or exceeded the standard-required of GB/T9755-1995 acceptable end product.See Table:
Project name | Index request | Assay |
Color and outward appearance | Appearance of film is normal | Appearance of film meets the aberration scope |
Solids content | More than or equal to 45% | More than or equal to 50% |
Opacifying power | Be less than or equal to 250 the gram/square metre | Be less than or equal to gram/square metre |
Water tolerance (96h) | It is no abnormal to film | It is no abnormal to film |
At condition in container | Mix the no lump in back and be uniform state | No lump is uniform state |
Contrast ratio (white and light color) | More than or equal to 0.90 | More than or equal to 0.93 |
Alkali resistance (48h) | It is no abnormal to film | No abnormal |
Brushing resistance (1000 times) | It is no abnormal to film | No abnormal |
Artificial ageing resistance (250h) | Efflorescence I level variable color II level | Efflorescence I level variable color I level |
Claims (4)
1, a kind of organosilicon-modified acrylic rustproof lacquer is characterized in that its component (weight %) contains: organosilicon crylic acid latex 30-38, filler 30-35, dispersion agent 0.5-1, defoamer 0.1-0.2, sanitas 0,1-0,3, thickening material 1-2, water 30-35.The composition of organosilicon crylic acid latex (weight %) is the high molecular polymer that is made by solution polymerization by organosilane monomer 5-8, acrylate monomer 8.6-10, adding vinylformic acid 1-6, emulsifying agent 3-5, initiator 0.6-1.6, distilled water 70-80.
2, organosilicon modified acrylic paint for external wall according to claim 1, it is characterized in that filler is made up of titanium dioxide, mica powder and water-ground limestone or kaolin, the proportioning between them (weight %) is titanium dioxide 40-50, mica powder 10-15, water-ground limestone or kaolin 35-45.
3, a kind of preparation method who prepares the described organosilicon modified acrylic paint for external wall of claim 1, it is characterized in that in reactor, adding distilled water and be heated to the 85-90 degree, splash into organosilane monomer, acrylate monomer, vinylformic acid and initiator, emulsifying agent, dropwised in 2-3 hour, be incubated 1 hour again, cool to the 30-40 degree, regulate pH value to 6-9 discharging and promptly make organosilicon crylic acid latex.In joining the lacquer cylinder, add entry, add defoamer, sanitas, dispersion agent while stirring, mix the back and add filler, continue to be stirred to evenly, regulate pH value to 7.5-8.5, with shredder grind to fineness less than after 40 microns, under stirring at low speed, add organosilicon crylic acid latex, defoamer, adjust to proper viscosity with thickening material at last and get final product.
4, the preparation method of organosilicon modified acrylic paint for external wall according to claim 3 is characterized in that using for the first time the amount of defoamer as using 60-70%, the second time of defoamer total amount the 30-40% of the amount of defoamer as total amount.