CN1304185C - Production method of plastic floor brick - Google Patents

Production method of plastic floor brick Download PDF

Info

Publication number
CN1304185C
CN1304185C CNB021041547A CN02104154A CN1304185C CN 1304185 C CN1304185 C CN 1304185C CN B021041547 A CNB021041547 A CN B021041547A CN 02104154 A CN02104154 A CN 02104154A CN 1304185 C CN1304185 C CN 1304185C
Authority
CN
China
Prior art keywords
floor tile
thickness
hot pressing
plastic cement
finished product
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB021041547A
Other languages
Chinese (zh)
Other versions
CN1367073A (en
Inventor
张小平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
MEIZHE INTERNATIONAL ENTERPRISE CO Ltd
Original Assignee
MEIZHE INTERNATIONAL ENTERPRISE CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by MEIZHE INTERNATIONAL ENTERPRISE CO Ltd filed Critical MEIZHE INTERNATIONAL ENTERPRISE CO Ltd
Priority to CNB021041547A priority Critical patent/CN1304185C/en
Publication of CN1367073A publication Critical patent/CN1367073A/en
Application granted granted Critical
Publication of CN1304185C publication Critical patent/CN1304185C/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

The present invention discloses a method for making plastic floor tiles, which comprises the following working procedures: the making of plastic particles, the plastic particles are produced and are wrapped with additives to obtain plastic particles needed by the floor tiles; sticking, through heating, pressing and sticking the plastic particles, a stuck semifinished product is obtained; the thickness of the heated, pressed and stuck semifinished product obtained in a sticking working procedure is more than 2 times of the thickness of a finished product, a slitting apparatus is used for cutting the semifinished product into a plurality of finished products of needed thickness through a slitting working procedure, and post treatment is carried out to obtain a final product. After the floor tiles are heated, pressed and stuck by the plastic particles and by adopting the method of the present invention, the floor tiles are processed into multi-layer products by a cutting machine. Thereby, the purposes of improving production efficiency and reducing apparatus cost and production cost can be achieved.

Description

A kind of manufacture method of plastic floor tile
Technical field
The present invention relates to a kind of manufacture method of plastic floor tile.
Technical background
At building decorating industry, PVC (polyvinyl chloride) plastic floor tile is convenient to construction because its light weight, pattern can be ever-changing and cost and price lower, so rather popular in American-European building materials market, also there is the production PVC of the man production firm of number plastic floor tile existing China's Mainland.Traditional PVC plastic cement stamp floor tile generally needs the mixing through PVC powder, plasticizer, filler and processing aid, opens operations such as refining and lamination coating, and the homogeneous floor tile then can obtain finished product as waxing directly through mill slice and necessary post processing after mixing.
Demand for the various performances of catering to the consumer, as need have the luminous noctilucence floor tile of energy at night in hotels and other places, with when having a power failure or unusual condition such as breaking out of fire guide the usefulness of direction when not having electric lighting, the dance hall then needs the radium-shine floor tile that can reflect laser light, to cooperate the irradiation of laser light, produce special lighting effects.The manufacture process of above-mentioned floor tile is identical with the manufacture process of aforementioned homogeneous floor tile, and adds the additive with specific function in mixed processes, as luminescent powder and fluorescent material etc.But because these additives are because price is very high, so on additional proportion, be difficult to grasp control: because of it is scattered in the PVC floor tile, most ofly hidden, cross as additional proportion and hang down that then effect is bad by PVC and filler, but as too much, then can cause irrational rising of cost.
In addition, for cooperating the needs of informatization epoch for the elimination and the prevention of static, the PVC producer also releases antistatic or the conduction floor tile.Recently the plastic cement conduction floor tile that occurs on the domestic and international market ties up to the conduction black smoke or the graphite of sneaking into larger proportion in the plastic cement component mostly and leads the purpose of releasing static as conductive agent to reach.But because such conductive agent color and luster is single, the conduction floor tile of gained also is difficult to change on impression, is difficult to satisfy the demand of existing interior decoration variation.
United States Patent (USP) 4,101 discloses a kind of conduction floor tile and manufacture method thereof No. 689, and so that above-mentioned shortcoming is improved, this product is led by insulating barrier and conductive layer and the static that runs through insulating barrier and released post and constitute.It is to produce insulating barrier earlier, on this insulating barrier, go out several and run through hole up and down, this hole is up-small and down-big, the paste resin that will contain conductive agent again has the conductive layer that becomes certain thickness than a side coated of big frustum diameter from the sheet semi-finished product, and the opposite side that makes pastel penetrate into taper hole forms static and leads and release post, make it plasticizing at a certain temperature, thereby utilizing the static penetrate insulating barrier to lead to release post reaches the floor tile bottom with surface charge, and utilizes the conductive layer of bottom that static is led to disengage.This kind manufacture method is more loaded down with trivial details and its resulting product outward appearance is more single, also can not effectively solve the diversified problem of impression.
Existing producer releases a kind of new-type conduction floor tile, and this conduction floor tile is to wrap up in attached conductive agent around the plastic cement particle, again with the particle compacting in flakes, thereby utilizes conductive agent to form conductive network, reaches and leads the purpose of releasing static.This kind product is because pattern is many and outward appearance is beautiful, and can be according to the actual requirements, changing its static leads and releases performance, so it is very popular on the market, as the conductive column (STATIC CONDUCTIVE) of Britain Mary company (MARLEY), the VIP of LG Corp of South Korea conduction floor tile series (LG VIP CONDUCTIVE TILE) etc.But the manufacturing process of these floor tiles is wrap up in attached conductive agent around the plastic cement particle after, accurate running roller calendering by special heater and automation control is handled, obtain finished product through operations such as the surface finish and the bottom mill ends again, the equipment precision of these processing procedure needs is very high, investment cost is very high, and control technology requires also very high.The floor tile dealer, especially medium and small dealer is difficult to even can't reaches.
Among the existing plastic floor tile dealer, the hot pressing Heat sealing machine is similar to vulcanizing press, is very general equipment, and its investment cost is not high, operates also simpler.For utilizing existing equipment and avoiding huge equipment investment, the dealer studies one after another and uses the hot pressing make-up machine to produce required function floor tile, as the method for noctilucence floor tile, conduction floor tile etc.The existing practice is wrapped up in attached additive by specific function for producing particles, utilizes the hot pressing Heat sealing machine to carry out the single slice hot pressing fusion, the semi-finished product of hot pressing fusion back gained is polished again and polishes, and obtains required floor tile.This kind production method also has significant disadvantages: at first, this kind producer genealogy of law monolithic production method is difficult to even stone, lacks material so very easily cause when producing, thus the finished product fraction defective of production and heavily the burning rate is high.In addition, when the plastic cement particle fused into the sheet semi-finished product, volume can be reduced into about original half, thus need matched molds can, this can cause stone inconvenience, and fusion effectiveness is extremely low.
Summary of the invention
The invention reside in the manufacture method that a kind of plastic floor tile is provided, utilize this method can reach the input cost of saving equipment, the purpose of enhancing productivity.
The manufacture method of plastic floor tile of the present invention comprises following operation: plastic cement particle production process, and promptly produce the plastic cement particle and wrap up in attached additive to obtain the required plastic cement particle of floor tile; Fusion process is by fusing the hot pressing of plastic cement particle to obtain fusing half product; It is characterized in that: to fuse half-finished thickness be more than 2 times of finished product thickness in resulting hot pressing in the fusion process, and hack operation through one, with the equipment that hacks these semi-finished product are cut into the finished product of some desired thicknesses, carry out post processing again, with end article.
Adopt method of the present invention, this floor tile is processed into multi-layer product through cutting equipment after plastic cement particle hot pressing fusion, enhance productivity thereby can reach, and reduces the purpose of equipment cost and production cost.
The specific embodiment
Embodiment 1:
With weight fraction is DBP (mutual-phenenyl two acid bromide two alcohol ester), heat stabilizer (second base lead sulfate) 1-4 part, powdered filler 20-200 part of 100 parts of PVC, 20-55 part and pigment is some stirs in machine, in banbury, carry out its mixture further mixing, and it is rolled into the sheet material of thick 1.0-5.0mm respectively, the particle that is crushed to suitable size in pulverizer is standby.
According to the electric conductivity demand, above-mentioned particle by existing technology and an amount of conductive agent, as conduction black smoke, conductive carbon fibre, is stirred, make its wrap up in equably invest the plastic cement particle around, promptly obtain conducting electricity the required conductive particle of floor tile.
Hot pressing fuses the Thickness Design of half-finished mould and can carry out according to the size of target product.This mould can be designed to the form of general matched molds, and matched molds has the suitable thickness and the degree of depth, and formpiston can move down filling up the space that the plastic cement particle forms because of compression when producing, thereby makes it press more closely knitly.Utilize this mould that the hot pressing fusion semi-finished product that the hot pressing of conductive plastic particle goes out can be left 2 flake products at least with the suitable equipment that hacks.Consider production efficiency and the machinable maximum ga(u)ge of slicer, this hot pressing fuses half-finished thickness should produce the greater as much as possible to raise the efficiency and to prevent to lack the generation of material situation.Have big thickness person and can prevent effectively that hot pressing from fusing the scarce material problem in the semi-finished product, and when the filling conductive particle, its operation is more convenient, efficient is higher.But the blocked up person of thickness, then can cause hot pressing fusion irrational prolongation of time, even the false phenomenon of pasting of hot pressing fusion semi-finished product can appear, i.e. the surface combination preferably of hot pressing fusion semi-finished product, but these semi-finished product are at the conductive particle in the rough centre position of thickness direction fusion plastification not as yet, fail between the particle to be combined as a whole, thereby, cause the failure of hot pressing fusion, for anti-plant here bad, need to burn again to press fusion, cause irrational rising of production cost.In addition, press semi-finished product thickness too thick as burning, its heat transfer efficiency is extremely low, causes manufacturing cost to rise.In the present embodiment, it is 0.5-8.0cm that hot pressing fuses half-finished thickness, is preferably 1.0CM-5.0cm.
The hot pressing fusion semi-finished product that the conductive plastic particle obtains after the hot pressing fusion can use to hack according to desired thickness and hack processing and necessary post processing, as polishing, stamping-out moulding etc., afterwards, promptly obtain required conduction floor tile.
The employed slicer of present embodiment can directly be purchased in market and sell and get, the splitter that existing leather manufacturing industry is used, and the water cutter that uses as processing industry etc. all can.Hot pressing being fused the finished product that semi-finished product cut out predetermined thickness, and the surplus portion after the cutting carries out cutting operation more again, during less than finished product thickness, stops cutting, the clout recycling up to surplus integral thickness.
The finished product that will hack gained carries out post processings such as surface finish, stamping-out moulding and promptly obtains needed product.
Embodiment 2
With weight fraction is 100 parts of polyvinyl chloride resins, the DOP of 30-60 part (DOTP), the heat stabilizer of 3-10 part and powdered filler 20-200 part and suitable processing aid stir in extruder, and granulation in extruder, obtain the plastic cement particle that shape and size are fit to, and particle is carried out the processing identical as embodiment 1.
Embodiment 3
Resulting plastic cement particle among embodiment 1 or the embodiment 2 is mixed with an amount of luminescent powder, luminescent powder is wrapped up in invest the plastic cement particle around, implement the processing identical again as embodiment 1, promptly obtain having the noctilucence floor tile of luminous effect.
Embodiment 4
Resulting plastic cement particle among embodiment 1 or the embodiment 2 is mixed with an amount of pearl essence, pearl essence is wrapped up in equably invest the plastic cement particle around, implement the processing identical again, even obtain having the pearly-lustre floor tile of pearl effect as embodiment 1.
In sum, the above person only is the present invention's preferred embodiment, and all those skilled in the art all can be imitated according to core of the present invention and be modified or variation, all should be covered by in the claimed scope of the application.

Claims (4)

1, a kind of manufacture method of plastic floor tile comprises following operation: plastic cement particle production process, and promptly produce the plastic cement particle and wrap up in attached additive to obtain the required plastic cement particle of floor tile; Fusion process, by with plastic cement particle hot pressing fusion with obtain plastic floor tile fusion half product; It is characterized in that: to fuse half-finished thickness be more than 2 times of finished product thickness in resulting hot pressing in the fusion process, and hack operation through one, with hacking equipment these semi-finished product are cut into the finished product of some desired thicknesses, and carry out post processing, end article.
2, by the manufacture method of the described plastic floor tile of claim 1, it is characterized in that: the additive that adds in the described plastic cement particle production process is conductive agent, pearl essence or luminescent powder.
3, by the manufacture method of claim 1 or 2 described plastic floor tiles, it is characterized in that: it is 0.5-8.0cm that hot pressing fuses half-finished thickness.
4, by the manufacture method of the described plastic floor tile of claim 3, it is characterized in that: it is 1.0-5.0cm that hot pressing fuses half-finished thickness.
CNB021041547A 2002-03-12 2002-03-12 Production method of plastic floor brick Expired - Fee Related CN1304185C (en)