CN1300860A - Method for removing coating from coated spheres - Google Patents
Method for removing coating from coated spheres Download PDFInfo
- Publication number
- CN1300860A CN1300860A CN 00130344 CN00130344A CN1300860A CN 1300860 A CN1300860 A CN 1300860A CN 00130344 CN00130344 CN 00130344 CN 00130344 A CN00130344 A CN 00130344A CN 1300860 A CN1300860 A CN 1300860A
- Authority
- CN
- China
- Prior art keywords
- roasting
- ball
- shrend
- roasting ball
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A method for removing coating from coated spheres includes calcining at 250-500 deg.C and quenching in water at ordinary temp. Its advantages include simple process, full removal of coating and low loss of metal. It is suitable for different S or As ore or concentrate.
Description
The present invention relates to a kind of pretreatment process that is used for sulphur arsenic metallic ore or concentrate, specifically, relate to a kind of method that is used for the removing coating from coated spheres of pelletizing covering roasting oxidation method acquisition.
Chinese patent CN1237640A discloses a kind of pelletizing covering roasting oxidation method that is used for sulphur arsenic metallic ore or concentrate, and its principal feature is that ore or concentrate and caking agent are mixed and made into pelletizing; With sulphur arsenic fixing agent white lime at pelletizing external parcel one deck successive, certain thickness tectum (being referred to as dressing) is arranged; The roasting of dressing ball; Roasting ball (the dressing ball after the roasting is referred to as the roasting ball) removes clothing, the coatings waste material is separated with calcining etc.
Be suitable for above-mentioned roasting ball to go the clothing method to have a variety of, can adopt gravitational segregation, also can adopt magnetic force sorting etc.These methods need more mechanical means, long technical process, and also every kind of method has its specific scope of application.
The object of the present invention is to provide a kind of technology simple, flow process is short, the method for removing the slap-up removing coating from coated spheres of clothing.
Purpose of the present invention can reach by following measure: a kind of method that is used for removing coating from coated spheres comprises the cooling of roasting ball, the shrend of roasting ball, compound dehydration and screening and the sorting of screen underflow magnetic force; During the shrend of roasting ball, water temperature is a room temperature, and the roasting ball is cooled to skin temperature greater than 250 ℃, shrend during less than 500 ℃.
The screen underflow of screening is the coatings waste material, delivers to scrap yard and store up after the magnetic force sorting, and screen overflow is a calcining, delivers to subsequent handling and extracts metal.
Dressing ball roasting: raw material sulphur arsenic metallic ore or concentrate are carried out roasting, make the sulfoarsenide oxygenolysis in ore or the concentrate, sulfoarsenide is converted into metal oxide.Maturing temperature is generally 450 ℃～750 ℃.Operable roasting apparatus has shaft furnace, rotary kiln and belt type roasting machine etc.Dressing ball through roasting is referred to as the roasting ball.
Roasting ball cooling: cooling purpose be make the roasting ball the thermal adaptation subsequent handling requirement and utilize waste heat, save energy.By regulating the cooling section length of roasting apparatus, can effectively change the tapping temperature of roasting ball.
The shrend of roasting ball: shrend is a key of the present invention, and the concrete practice is that the roasting ball that will be cooled to certain temperature directly drops in the water that water temperature is room temperature (normal temperature), the consumption the when consumption of water is not less than complete submergence roasting ball.During the roasting ball shrend of certain temperature, from inside to outside form temperature head from high to low.The top layer cooling of roasting ball is fast, and shrinkage is big, and the internal layer cooling is slow, and shrinkage is little, thereby generates thermal stress between ectonexine.When this thermal stress during greater than the tensile strength of roasting ball, break and come off in roasting ball top layer, forms broken laminar.When roasting ball skin temperature was lower than 250 ℃, the shrend effect was bad, and removing coating from coated spheres is not thorough; When roasting ball skin temperature is higher than 500 ℃, waste energy.
Dehydration of shrend compound and screening: slough moisture when the compound after the shrend is pulled out naturally from water, then screening.Screen overflow is like the globular calcining, sends into subsequent handling and extracts metal.
The sorting of screen underflow magnetic force: the screen underflow of screening is the coatings waste material, is being mingled with a small amount of calcining in the waste material, and after this part calcining was reclaimed in sorting through magnetic force, final waste material was delivered to scrap yard and stored up.
The present invention has following advantage: technology is uncomplicated, and roasting ball skin temperature is low during shrend, saves the energy, and easy handling goes clothing completely, and is applied widely, can be used for various types of sulphur arsenic metallic ores or concentrate.
The drawing of accompanying drawing is described as follows:
Fig. 1: remove the clothing process flow sheet
The invention will be further described below in conjunction with embodiment:
Embodiment: the gold ore of sulfur-bearing arsenic, Au 70 * 10
-6S 22.2%, As 7.17%, concentrate is prepared burden, is mixed in 100: 10 ratio with caking agent, make diameter and be 10～12 millimeters like spherical pelletizing, pelletizing sulphur arsenic fixing agent white lime dressing, 15～16 millimeters of dressing spherical diameter, the dressing ball warp is crossed roasting (temperature is 600 ℃) back and is obtained the roasting ball.When the roasting ball cools off 1 to 500 ℃, 450 ℃, 400 ℃, 300 ℃, 250 ℃, respectively the roasting ball is dropped into shrend 2 in the water that water temperature is room temperature (normal temperature).When temperature was 250 ℃ roasting ball shrend, the roasting ball went clothing not thorough, has only a small amount of coatings to come off.Temperature is greater than 250 ℃, and during less than the roasting ball shrend of 500 ℃ of temperature, the roasting ball goes clothing completely, and pelletizing is kept perfectly.After the shrend compound dehydration, be 8 millimeters sieve screening 3 with the aperture, screen overflow is a calcining, and screen underflow is the coatings waste material, and coatings waste material employing magneticstrength is the drum magnetic separator sorting 4 of 800KA/m.The final clearance of coatings waste material is greater than 80%, and waste material contains gold less than 0.2 * 10
-6, golden rate of loss is less than 0.46%.Identical roasting ball directly adopts magneticstrength without shrend and screening be that clothing is removed in the strong magnetic force magnetic separator magnetic force sorting of 1200KA/m, and the result is: feed particle size is during less than 20 orders, and coatings waste material clearance 51.8%, waste material contain gold 1.0 * 10
-6, golden rate of loss 0.8 * 10
-6Feed particle size is during less than 40 orders, and coatings waste material clearance 40.7%, waste material contain gold 0.9 * 10
-6, golden rate of loss 1.1%; Feed particle size is during less than 60 orders, and coatings waste material clearance 24.7%, waste material contain gold 2.4 * 10
-6, golden rate of loss 2.5%.
Claims (3)
1, a kind of method that is used for removing coating from coated spheres comprises roasting ball cooling (1), compound dehydration and screening (3) and screen underflow magnetic force sorting (4), it is characterized in that: directly carry out roasting ball shrend (2) when the roasting ball is cooled to certain temperature.
2, removing coating from coated spheres method according to claim 1 is characterized in that: during the shrend of roasting ball, water temperature is a room temperature.
3, removing coating from coated spheres method according to claim 1 is characterized in that: the roasting ball is cooled to skin temperature greater than 250 ℃, shrend during less than 500 ℃.