银锡氧化物电工触头材料及其制备方法 Download PDFInfo
- Publication number
- CN1299307C CN1299307C CNB200410079614XA CN200410079614A CN1299307C CN 1299307 C CN1299307 C CN 1299307C CN B200410079614X A CNB200410079614X A CN B200410079614XA CN 200410079614 A CN200410079614 A CN 200410079614A CN 1299307 C CN1299307 C CN 1299307C
- Authority
- CN
- China
- Prior art keywords
- silver
- electrical contact
- tin oxide
- contact material
- alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了银锡氧化物电工触头材料及其制备方法,能够克服银氧化锡合金加工性能差、质量不稳定等难题。其化学成份(重量比)SnO2为:3%~10%,混合稀土氧化物(Sm2O3、Gd2O3、Y2O3)为:O.1%~2.0%,余量为Ag。制备方法为:将Ag、Sn、混合稀土元素按合金设计成分比例配好,在真空熔炼炉内合金化,通过快速凝固,制备成AgSnRE合金。该合金首先经过挤压、轧制、拉拔、热处理等加工工艺,制备成丝材、板材、异型材或铆钉等制品,再通过制品内氧化方法制备为AgSnO2混合稀土氧化物电工触头材料。可用于交、直流接触器、继电器、控制器、断路器、开关等。
Description
技术领域
本发明涉及一种银基合金及其制备方法,特别是涉及一种银锡氧化物电工触头材料及其制备方法。
背景技术
银氧化物系列电工触头材料主要有AgCdO、AgSnO2、AgZnO等。AgCdO电工触头材料(含CdO:8%~15%)由于其优良的抗电弧侵蚀性、抗熔焊性和较低的接触电阻,长期以来被称为“最好的电接触材料”。但是由于镉元素及其化合物的存在,在AgCdO材料的生产、使用、回收等过程中都面临着“镉毒”的污染问题。这是由于(1)CdO会聚集在生物体内,如在肾赃、骨骼及血液中,使其毒性增强;(2)对于人类来说,镉及其化合物为第二类毒性化学物质,特别是容易导致肝癌、肺癌等。(3)镉及其化合物在环境中的迁移率很高,很容易传播和扩散,对人体和自然环境具有较大的破坏和污染作用,吸收含镉的烟雾或尘埃超过临界含量时均对人体有害,会引起骨痛病、呼吸道疾病、肾衰竭等,重者危及人体生命。
鉴于AgCdO材料存在的污染环境、危害人体健康等问题,国内外有关行业进行了大量的研究和开发工作。国际上,如德国(Degussa、Doduco、Siemens公司)、英国(JMM公司)、日本(东芝、田中、中外电器、佳友会社)、美国(西屋公司、Fensteel联合公司、Mallory公司)等;国内,如昆明贵金属研究所、桂林电科所、上海电科所、佛山精密电工合金有限公司、苏州电工合金厂、济南电工合金厂等单位,进行了大量卓有成效的工作。
在银氧化物系列电接触材料中,银氧化锡材料是众多代镉材料中较理想的一种,但是AgSn合金内氧化时表面生成致密的SnO2,会阻止合金继续氧化,加入In可以加速合金内氧化,但是In的价格昂贵,资源储备较少,成本较高。而且银氧化锡合金的温升比银氧化镉高,严重地影响了合金的接触电阻和抗熔焊性能。同时,AgSnO2材料加工困难的难题,一直均未得到很好解决。
发明内容
本发明能够解决银氧化锡合金的温升比银氧化镉高,严重地影响了合金的接触电阻和抗熔焊性能问题以及AgSnO2材料加工困难的难题。为此,本发明的银锡氧化物电触头材料的化学成份(重量比)SnO2为:3%~10%,混合稀土氧化物(Sm2O3、Gd2O3、Y2O3)为:0.1%~2.0%,余量为Ag。其中SnO2(重量比)为5%~8%,混合稀土氧化物(Sm2O3、Gd2O3、Y2O3)重量比为:0.08%~1.0%则效果更好。
本发明的银锡氧化物电触头材料的制备方法为:将Ag、Sn、混合稀土元素按合金设计成分比例配好,在真空熔炼炉内合金化,通过快速凝固,制备成AgSnRE合金,其中RE表示稀土元素。该合金首先经过挤压、轧制、拉拔、热处理等加工工艺,制备成丝材、板材、异型材或铆钉等制品,再通过制品内氧化方法制备为AgSnO2混合稀土氧化物电工触头材料。
详细具体制备工艺步骤如下:
(1)将纯度为99.99%的Ag、Sn、混合稀土元素按合金设计成分比例配好,在真空中频熔炼炉内合金化,并且快速凝固浇注。
(2)再将AgSnRE合金锭挤压为板材、丝材,挤压比>30∶1,挤压温度为500℃~800℃。
(3)挤压材料再经过轧制、拉拔、热处理等工序加工,制备成丝材、板材、异型材或铆钉等制品;轧制、拉拔变形量为30%~70%,热处理温度为500℃~800℃。
(4)根据使用要求,再进行丝材、板材、异型材或铆钉等材料的内氧化,内氧化温度为400℃~800℃,最终制备得AgSnO2混合稀土氧化物电工触头材料。
本发明的银基电工触头材料的物理、力学性能如表1所示。
表1.AgSnO2RE2O3合金技术性能指标
序号 | 材料名称 | 性能 | ||
密度(g/cm3) | 硬度(HV) | 电阻率(μm.cm) | ||
1 | AgSnO25RE2O30.5 | 10.27 | 78 | 2.1 |
2 | AgSnO26RE2O31.0 | 10.1 | 95 | 2.3 |
3 | AgSnO28RE2O31.5 | 9.93 | 120 | <2.7 |
4 | AgSnO210RE2O32.0 | 9.85 | 135 | <2.9 |
(2)本发明的银基电工触头材料在ASTM综合电性能试验机上进行电寿命试验,具体结果如表2所示。
表2.AgSnO2RE2O3合金电性能指标
序号 | 材料名称 | 试验条件 | 工作寿命(>) |
1 | AgSnO25RE2O30.5 | AC:220V,10A | 5万次 |
2 | AgSnO26RE2O31.1 | DC:24V,10A | 8万次 |
3 | AgSnO28RE2O31.5 | AC:220V,20A | 10万次 |
4 | AgSnO210RE2O32.0 | AC:380,30A | 6万次 |
本发明选择混合稀土(Sm、Gd、Y)作为添加剂,有效地促进了AgSn合金的内氧化过程,明显地降低了AgSnRE合金的内氧化温度。同时,形成细微的等轴晶粒,稀土元素或稀土氧化物均匀分布于合金晶体的晶内和晶界上,改善了材料的组织结构,提高了材料的抗熔焊性、耐电弧烧损性等,同时对合金材料的塑性和电阻率影响较小。
该工艺技术简单、效率高、成本低,合金晶粒细小、组织均匀、氧化物质点弥散分布,克服了银氧化锡合金加工性能差、质量不稳定等难题,新型电工合金可用于交、直流接触器、继电器、控制器、断路器、开关等。并提供了利用添加混合稀土元素,制品内氧化等先进技术的优化集成,为新型银基电触头材料的制备开辟了新途径。
具体实施方式
实施例1~4为表3中序号1至4号样合金材料配方比例,按照下列步骤方法制得。
(1)将纯度为99.99%的Ag、Sn、混合稀土元素按合金设计成分比例配好,在真空中频熔炼炉内合金化,并且快速凝固浇注。
(2)再将AgSnRE合金锭挤压为板材、丝材,挤压比>30∶1,挤压温度为500℃~800℃。
(3)挤压材料再经过轧制、拉拔、热处理等工序加工,制备成丝材、板材、异型材或铆钉等制品;轧制、拉拔变形量为30%~70%,热处理温度为500℃~800℃。
(4)根据使用要求,再进行丝材、板材、异型材或铆钉等材料的内氧化,内氧化温度为400℃~800℃,最终制备得AgSnO2混合稀土氧化物电工触头材料。
表3实施例1~4合金材料配方比例
序号 | 材料名称 | SnO2 | 混合稀土(Sm2O3、Gd2O3、Y2O3) | Ag |
1 | AgSnO25RE2O30.5 | 5 | 0.5 | 余量 |
2 | AgSnO26RE2O31.0 | 6 | 1.0 | 余量 |
3 | AgSnO28RE2O31.5 | 8 | 1.5 | 余量 |
4 | AgSnO210RE2O32.0 | 10 | 2.0 | 余量 |
Claims (5)
1、一种银锡氧化物电触头材料,其特征在于这种材料的化学成份重量比,SnO2为:3%~10%,混合稀土氧化物为:0.1%~2.0%,余量为Ag。
2、根据权利要求1所述的银锡氧化物电触头材料,其特征在于所述的混合稀土氧化物为Sm2O3、Gd2O3、Y2O3的混合物。
3、根据权利要求1所述的银锡氧化物电触头材料,其特征在于所述的SnO2重量比为5%~8%。
4、根据权利要求1所述的银锡氧化物电触头材料,其特征在于所述的混合稀土氧化物的重量比为:0.1%~1.0%。
5、根据权利要求1所述的银锡氧化物电触头材料的制备方法,其特征在于这种方法的具体步骤为:
(1)将纯度为99.99%的Ag、Sn、混合稀土元素按合金设计成分比例配好,在真空中频熔炼炉内合金化,并且快速凝固浇注;
(2)再将AgSn稀土合金锭挤压为板材、丝材,挤压比>30∶1,挤压温度为500℃~800℃;
(3)挤压材料再经过轧制、拉拔、热处理加工,制备成丝材、板材、异型材或铆钉制品;轧制、拉拔变形量为30%~70%,热处理温度为500℃~800℃;
(4)根据使用要求,再进行丝材、板材、异型材或铆钉材料的内氧化,内氧化温度为400℃~800℃,最终制备得AgSnO2混合稀土氧化物电工触头材料。