CN1291601A - Super-energy bioceramics and its synthesis - Google Patents
Super-energy bioceramics and its synthesis Download PDFInfo
- Publication number
- CN1291601A CN1291601A CN 99118484 CN99118484A CN1291601A CN 1291601 A CN1291601 A CN 1291601A CN 99118484 CN99118484 CN 99118484 CN 99118484 A CN99118484 A CN 99118484A CN 1291601 A CN1291601 A CN 1291601A
- Authority
- CN
- China
- Prior art keywords
- powder
- energy
- super
- bioceramics
- synthetic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A super-energy biochemical ceramic is prepared from about 100 natural minerals including granite, magnetite, coal, charcoal, malachite, zeolite, gypsum etc and features that it can split, desintegrate and generate isotopic activated rate-mitochondrions, bend lines of magnetic field and electric field, split cell membrane and then quickly repare it, and generate super energy. It has wide applications in agriculture, industry and medicine and possesses the functions of improving activating, enhancing liquid quality and increasing the immunity of human body.
Description
The present invention relates to a kind of super-energy bioceramics and synthetic.More specifically say so a kind of can with the life cells body common point that is in the inertia criticality when the moving magnetic field, can be accepted and produce the multiple resonance motion rapidly by its object, and causing occurring the X phenomenon of bursting apart, molecule that X bursts apart produces the phenomenon of active more life energy when repairing rapidly super-energy bioceramics synthetic appears after being activated thereby occur making.
Tradition science and technology is utilized the natural mineral as grouan, zeolite and Meng Moli pumice and so on, the characteristic of the exchange negative and positive particle that is had and utilize infrared rays to produce the characteristic of non-thermal effect; Also utilize as having the characteristic of the ability of sterilization, sterilization in the metalloid pit woods such as silver, copper; And far infrared rays and negative ion that coal and charcoal (as gac, long charcoal and bamboo charcoal etc.) are produced have deodorizing, make the characteristic of the function etc. of physiologically active, and make it to mix with other former stone to reach and make the purpose of the characteristic of the object of wanting to change quality being given full play to the most effective function.But all owing to effect single (as the upgrading material of being put down in writing in Japanese Patent 7-204664,7-330422 number) and do not draw ideal results.
The present invention is intended to overcome fully and has now at the same quasi-mineral that also exists aspect the development and use nature mineral substance separately respectively after the individual curing, also the independent effect of Cun Zaiing in time past and the slow defective of generation.And these natural mineral are because after very easily answering dissolved the separating out of impurity and foreign matter in application, and are directly absorbed by human body, jeopardize deficiencies such as human health.
The object of the present invention is achieved like this.Utilize electromagnetism sympathetic response resolver (Magnetic Resonance Analyzer) to visit to separate and analyze as the quality of various mineral materials such as pottery, natural stone and characteristic separately, from the assessment of the resolved data that go out, found to change the mineral material of the character of its object.(resolving the ability of mineral material as record MRA in the US5317265 patent announcement) adopts as grouan and magnetite powder powder material, and grouan and magnetite powder as can with other natural mineral, metal, can bring into play the necessary base mateiral of their wherein various separately materials characteristic property separately after the mixing such as coal to greatest extent, then selectively from coal, charcoal, malachite, zeolite, the Meng Moli pumice, Wingdale, gypsum, talcum powder, select a kind of in the similar material such as silver or some kinds of materials, and they are clayed into power separately, after the mixed with certainweight, under certain high temperature, fire and just can obtain the said super-energy bioceramics of the present invention.
The composition principle of super-energy bioceramics of the present invention is obtained from the enlightenment of native metal element at the new element of polonium (PO) bismuth (BI) that becomes, produces again after landslide that ground cleave etc. and the Nature happen occasionally and the division disintegration year in year out naturally.This new element division disintegration time institute set out the isotopic element of generation present rare activation of wire particle flux to, and this activation of wire particle flux can tortuous electric field and the ultrasonic energy of the flow direction in magnetic field and cause the X phenomenon of bursting apart to having.Resolve to find that through phenomenon that this is burst apart what play a decisive role is the simple vibrating numerical of helium (HE) charge particle that indicated in negative ion and positron, the negatron in X bursts apart.We are referred to as the supercycle energy acceleration effect of the ZG9000KM that ether energy Electromagnetic Wave produced to it under positron, negatron effect.
Super-energy bioceramics of the present invention mainly is by mineral material synthetic such as grouan, magnetite, coal, charcoal, malachite, zeolite, Meng Moli pumice, Wingdale, gypsum, talcum powder, silver.The maximum specific compound vibration that can produce separately according to the distinctive crystalline structure of above various materials, and this specific compound vibration simultaneously again can with its specific tuner-type resonance performance that object produced that will change.Grouan and magnetite clayed into power respectively and add water mix, again screening good coal, charcoal, malachite, zeolite, Meng Moli pumice, Wingdale, gypsum, talcum powder, the silver shape of claying into power, send to then as 228 special-purpose sealed stirrers in the accompanying drawing two with add water-lute after the grouan that mixes, magnetic iron ore base material raw material mix, and after mixing even matter in the specified time between 60 minutes-190 minutes, at high temperature be fired into desired shape again and get final product.
Various mineral materials required when super-energy bioceramics of the present invention is synthetic when claying into power, require various material powder diameters at 5 μ m-10 μ m for well.Before the super-energy bioceramics raw material that will mix carries out sintering, must the object product in the industrial circle that will be applied to be determined according to this shape.Through super-energy bioceramics synthesis material application experiment being proved when the super-energy bioceramics raw material is made the ball shape, it will be applied to this industrial circle of optimization to the tap water quality for several times.Kinds of experiments has according to this also proved and the super-energy bioceramics synthesis material has been made into different shapes such as anistree shape, awns starriness, triangular shape, regular hexagon shape, long hexagonal configuration, when its different shape all has their special shapes separately to bring into play beta maximum energy, its can be corresponding the industrial circle of object product, this phenomenon is referred to as biological chemistry (BIOCHEMIC).Super-energy bioceramics synthesis material of the present invention after making different shape during sintering temperature be advisable at 1000 ℃-1300 ℃.
Super-energy bioceramics of the present invention considers that it is applied to the requirement of different objects when synthetic, the weight mixing match scheme of each material has following four:
1, the grouan powder 70%; Magnetite powder 15%; Carbon powder 10-15%; Zeolite powder 0-5%; Silver powder 0-3%.
2, the grouan powder 70%; Magnetite powder 15%; Carbon powder 5-10%; Malachite powder 0-10%.
3, the grouan powder 70%; Magnetite powder 15%; Carbon powder 5-10%; Zeolite powder 5-10%; Silver powder 2-5%.
4, the grouan powder 70%; Magnetite powder 15%; Carbon powder 6-15%; Zeolite powder 0-5%; Silver powder 0-3%.
Super-energy bioceramics synthesis material of the present invention constitutes element and sees table.
Super-energy bioceramics of the present invention combines respectively with aforementioned four kinds of schemes, just can ideal reach and in liquid, place behind one (individual) or several piece (individual) super-energy bioceramics through 2 minutes-a few hours (as permanent placement), all can make in the liquid molecule promptly, received energy constantly, and the movement effects of " compound vibration " appears, the quality of any liquid is benefited and the user because of optimizing greatly.For example be applied in engine vapour (bavin) oil, just can make vapour (bavin) oil removing carbon and save energy greatly in running.Place and just can increase substantially the quality of water in the tap water and reach and make people this treated to eliminate constipation etc. after can water gaging uncomfortable and keep physical function stably to be in the metabolic balance state and improve health conditions having drunk, thereby significantly reduce ill chance.As wearing a super-energy bioceramics piece of the present invention on one's body, then can relieving fatigue, improve sleep, play the effect of diseases prevention.
Process flow sheet when accompanying drawing one synthesizes for super-energy bioceramics of the present invention.
The sealed stirrer that accompanying drawing two uses during for super-energy bioceramics raw material mixed preparing of the present invention.
Goal of the invention of the present invention in detail described below with embodiment in order further to prove.
Embodiment: (with aforementioned the 4th prescription case preparation)
Get grouan 50kg, magnetite 20kg, charcoal 20kg, zeolite 5kg, silver 3kg, put into respectively and be ground into its particle dia in the separately special-purpose pulverizer between 5 μ m-10 μ m the time, the taking-up of grouan powder is accounted for total amount 70% left and right sides deal, put into and stir even matter mixing in 228 sealed stirrers (1), then magnetite powder is taken out and account for total proportional quantity about 15% and put in 228 sealed stirrers (1) and stir, pour the suitable quantity of water sealing then into and mixed a specified time between about 60 minutes～190 minutes.Again the powdered carbon foam is taken out the 6-15% that accounts for total proportional quantity, the taking-up of zeolite powder is accounted for total proportional quantity 0-5%, get the silver powder foam and account for total proportional quantity 0-3%, pour into again after even matter mixes in 228 sealed stirrers (2) to mix in 228 sealed stirrers (1) and stir after the back takes out, after being made into the various shapes that are applicable to object such as octagon piece, sphere, trilateral, regular hexagon, long sexangle, awns star, send in the stove behind a specified time that carries out under 1000 ℃-1300 ℃ the high temperature between the sintering 60 minutes-190 minutes and take out, cooling gets final product naturally.
The color of super-energy bioceramics product gray of the present invention, purple.
The present invention has multiple advantage and disadvantage.
1, has and to be received rapidly by the object that it acted on, and produce with it simultaneously multiple Amount to the change molecular structure that shakes, make long strand diminish, shorten after, be difficult for again anti-Also, make the characteristics of the object critical kinetic energy effect that obviously constant performance is bigger;
2, have when producing multiple resonance with object, rapid repair cell body goes out again simultaneously The burst apart characteristics of isotopic element of existing X;
3, has the advantage that can obviously improve the quality of object own;
4, have the human body of directly acting on, and simultaneously improvement and balance body metabolism function is excellent The point;
5, have after being applied to object, can keep its fresh and tender degree and remove its extexine The characteristics of virus and bacteria impurities;
6, has in the function effect that improves object EXPANDING DISPLAY AREA thing function effect The characteristics of approach;
7, the advantage that has obvious raising object output;
But 8 mass industrial production.
Claims (7)
1, a kind of super-energy bioceramics and synthetic.It is characterized in that with grouan, magnetite be base material, it is synthetic to be equipped with charcoal, zeolite, malachite, silver, coal, Meng Moli pumice, Wingdale, gypsum, the talcum powder mixed sintering of claying into power.
2, the super-energy bioceramics described in claim 1 and synthetic.It is powdered to it is characterized in that wherein grouan, magnetite, charcoal, zeolite, malachite, silver, coal, Meng Moli pumice, Wingdale, gypsum need grind, and the powder particle diameter is the maximum 10 μ m of minimum 5 μ m-.
3, the super-energy bioceramics described in claim 1,2 and synthetic.It is characterized in that each the mineral material weight mixing match scheme that wherein adopts has four groups:
A, grouan powder 70%, magnetite powder 15%, carbon powder 10-15%, zeolite powder 0-5%, silver powder 0-3%;
B, grouan powder 70%, magnetite powder 15%, carbon powder 5-10%, malachite powder 0-10%;
C, grouan powder 70-80%, magnetite powder 0-15%, carbon powder 5-15%, zeolite powder 5-10%, silver powder 2-5%;
D, grouan powder 70%, magnetite powder 15%, carbon powder 6-15%, zeolite powder 0-5%, silver powder 0-3%.
4, the super-energy bioceramics described in claim 1,2,3 and synthetic.It is characterized in that the wherein raw material of super-energy bioceramics, must under the air-proof condition in 228 sealed stirrers (1), (2), mix that the time needs the specified time between 60 minutes-190 minutes.
5, as claim 1,3 described super-energy bioceramics and synthetic.The super-energy bioceramics raw material that it is characterized in that four groups of combination synthetic schemess in the claim 3 must be made into circle, ellipse, trilateral, regular hexagon, long sexangle, awns star, octagon, turriform, rhombus and different shape with the industrial circle that will be applied to according to it, its color gray and purple.
6, as claim 1,4 described super-energy bioceramics and synthetic.It is characterized in that the various super gauge block (body) that super-energy bioceramics wherein is made into, need under 1000 ℃-1300 ℃ high temperature, carry out sintering.
7, as claim 1,2,3,4,5 described super-energy bioceramics and synthetic.It is characterized in that super-energy bioceramics and synthetic unit that raw material constitutes thereof have: