CN1287960A - Bottom plate of container made of dahurian larch and mfg. method therefor - Google Patents
Bottom plate of container made of dahurian larch and mfg. method therefor Download PDFInfo
- Publication number
- CN1287960A CN1287960A CN 00130601 CN00130601A CN1287960A CN 1287960 A CN1287960 A CN 1287960A CN 00130601 CN00130601 CN 00130601 CN 00130601 A CN00130601 A CN 00130601A CN 1287960 A CN1287960 A CN 1287960A
- Authority
- CN
- China
- Prior art keywords
- tamarack
- container bottom
- bottom board
- veneer
- modulus
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to larch container baseboard and its manufacturing technology. It is characterized by that the larch is treated through softening degreasing, revolving cutting into single plate, drying, dressing forming bland and hot pressing into container baseboard with following physical properties; static bending strength (longitudinal) equal to or greater than 75 MPa; static bending strength (horizontal) equal to or greater than 30 MPa; modulus of elasticity (longitudinal) equal to or larger than 10000 MPa; modulus of elasticity (norizontal) equal to or larger than 3000 MPa; density 0.65-0.85 g /cu.cm; and compression ratio equal to or larger than 20%.
Description
Tamarack container bottom board and manufacturing process belong to a kind of container bottom board and manufacturing process.
The freight container timber apron is different from normal plywood, and physical properties requirements such as MOR, modulus of elasticity, bonding strength, presentation quality, working accuracy are very high in length and breadth for it.Therefore, nearly all to rely on the high-density hard timber of growing in the hylaea be raw material to world's container bottom board in decades.Because this seeds growth cycle is long, the cutting large resource is day by day poor.The scholar of part businessman has developed with the medium timber of density and has produced substrate, and the face basal surface glues together the composite bed of chemical industry fiber or high density Wooden veneer again, because this technical matters complexity, productive costs is higher, is not generally adopted by manufacturing enterprise.Used veneer of manufacturing enterprise of domestic a few family and juggle all rely on import, consume a large amount of foreign exchanges every year.To the continuous increase of freight container demand, protect limited hard wood resource along with in the world, the medium timber of developing density, what widen container bottom board is a far reaching problem with the material source.
The present invention its objective is development and use China density of wood medium seeds, particularly tamarack, aboundresources, moderate cost, beautiful texture is through the processing of science, rational assembly structure, make its increase in the density of density assortment reach a kind of novel wooden base plate of trans-container industrial standard.
Major technique solution of the present invention is, 1, softening degreasing, the warm water that the tamarack juggle is put into 25 ℃-30 ℃ soaked 6-8 hour, be warming up to 50 ℃-55 ℃ then, be incubated 6-8 hour, be warming up to 75 ℃-95 ℃ again, be incubated 18-20 hour, be cooled to 55 ℃-60 ℃ again, make juggle soften degreasing; 2, be peeled into veneer, 3, drying, 4, trimming, 5, gluing, use the phenolic resin glue of solids content, and add insect-proof agent at 48-50%, guarantee when hot pressing, to permeate uniformly in plate, reach the order ground of long-term insect protected.6 assemblies are mated formation veneer by crisscross, and face layer at the face base plate and respectively spread layer 2-3, and vertically long core veneer is hot pressed into the thick finished product of 28mm, guarantees to meet international standards requirement.
Most preferred embodiment:
Embodiment 1: is raw material with the tamarack, softens degreasing, be peeled into the veneer of thickness 1.85mm, and drying, trimming, the even level veneer is coated with phenolic resin glue 280-300 gram/m
2, by 19 layers of assembly, the face base plate respectively increases by 2 layers of vertical long core veneer, at 140 ℃+5 ℃ of temperature, pressure 18-22kg/cm
2Condition under divide a stage to boost, the three phases release was hot pressed into the thick container bottom board that just can obtain following physical property of 28mm in 40-50 minute.
MOR (vertically) 〉=95mpa
MOR (laterally) 〉=41mpa
Modulus of elasticity (vertically) 〉=11000mpa
Modulus of elasticity (laterally) 〉=3300mpa
Density 0.75-0.81kg/cm
3
Compression ratio 〉=20%
Embodiment 2: is raw material with the tamarack, softens degreasing, be peeled into the veneer of thickness 1.7mm, and drying, trimming, the even level veneer is coated with phenolic resin glue 270-290 gram/m
2, adopting 21 layers of assembly, the face base plate respectively increases by 2 layers of vertical long core veneer, at 140 ℃+5 ℃ of temperature, pressure 18-22kg/cm
2Condition under divide a stage pressure reduction, the three phases release was hot pressed into the 28 thick container bottom boards that just can obtain following physical property in 40-50 minute.
MOR (vertically) 〉=98mpa
MOR (laterally) 〉=43mpa
Modulus of elasticity (vertically) 〉=12000mpa
Modulus of elasticity (laterally) 〉=3400mpa tastes
Density 0.75-0.85kg/cm
3
Compression ratio 〉=20%
Embodiment 3: with the tamarack is raw material, is peeled into the veneer that thickness is 1.55mm, and the even level veneer is coated with phenolic resin glue 280-300 gram/m
2(layer 5 and the 18th layer of horizontal veneer single spreading) respectively increases by three layers of vertical long core veneer at the bottom of adopting 23 layers of assemble pattern face, at 140 ℃+5 ℃ of temperature, pressure 18-22kg/cm
2Condition under divide a stage to boost, the thick container bottom board that just can obtain down physical property of 28mm is made in three phases release, hot pressing in 40-50 minute.
MOR (vertically) 〉=98.2mpa
MOR (laterally) 〉=43.1mpa
Modulus of elasticity (vertically) 〉=12100mpa
Modulus of elasticity (laterally) 〉=3400mpa
Density 0.75-0.86kg/cm
3
Compression ratio 〉=20%
The tamarack container bottom board that adopts this fabrication process through Chinese ship inspection group know, French international ship tests association (B.V) and detects, the container bottom board of three kinds of assembly structures, met or exceeded the standard of international freight container fully, obtained the international product certificates of recognition with wood floors.
The properties of product synopsis
| Test item | Unit | Standard value | Detected value |
| MOR (vertically) | mpa | ＞75 | ≥95 |
| MOR (laterally) | mpa | ＞30 | ≥11000 |
| Modulus of elasticity (vertically) | mpa | ＞10000 | ≥41 |
| Modulus of elasticity (laterally) | mpa | ＞3000 | ≥3300 |
| Density | g/cm 3 | 0.65-0.85 | ≥0.75 |
| Water ratio | ％ | 6-14 | ≤8.7 |
Adopt the medium timber container bottom board of the present technique pressure-formed density of institute, its performance figure from table contrasting data as can be seen all indexs all met or exceeded international container bottom board required standard and planted, the present invention can substitute traditional tropical hard wood veneer sheet base plate fully.Actv. has reached the source that enlarges the container bottom board raw material, and it is domesticized fully, reduces dependence on import and expends the foreign exchange target.
Claims (3)
1, a kind of tamarack container bottom board and production technology is characterized in that tamarack softens degreasing, are peeled into veneer, drying, and trimming, assembly, hot pressing obtains the container bottom board of following physical property:
MOR (vertically) 〉=75mpa
MOR (laterally) 〉=30mpa
Modulus of elasticity (vertically) 〉=10000mpa
Modulus of elasticity (laterally) 〉=3000mpa
Density 0.65-0.85kg/cm
3
Compression ratio 〉=20%
2, a kind of according to claim 1 tamarack container bottom board and production technology, it is characterized in that the softening degreasing of tamarack is the tamarack juggle to be put into 25 ℃-30 ℃ warm water soaked 6-8 hour, be warming up to 50 ℃-55 ℃ then, be incubated 6-8 hour, be warming up to 75 ℃-95 ℃ again, be incubated 18-20 hour, be cooled to 55 ℃-60 ℃ again, make juggle soften degreasing.
3, a kind of according to claim 1 tamarack container bottom board and production technology is characterized in that assembly is that veneer is mated formation by crisscross, and face layer at the face base plate and respectively spread layer 2-3, vertically long core veneer