CN1281697C - Anti-pollution paint and its making method - Google Patents
Anti-pollution paint and its making method Download PDFInfo
- Publication number
- CN1281697C CN1281697C CN 200310111719 CN200310111719A CN1281697C CN 1281697 C CN1281697 C CN 1281697C CN 200310111719 CN200310111719 CN 200310111719 CN 200310111719 A CN200310111719 A CN 200310111719A CN 1281697 C CN1281697 C CN 1281697C
- Authority
- CN
- China
- Prior art keywords
- dispersed
- minutes
- synthetic fluid
- stirring
- resistant coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to anti-pollution dope and a preparing method thereof. The product respectively comprises the components and the corresponding compounding ratio: 15 to 23% of organosilyl modified resin, 65 to 76% of low-aromatic solution, 5.8 to 6.1% methylhydro-dichloro silicone oil, 0.05 to 0.08% of UV-531 (ultraviolet light polymerization agent) and 3% to 5% of 120# solvent. The preparing method comprises the following steps: the organosilyl modified resin is added in the low-aromatic solution to be stirred and dispersed for 10 to 20 minutes, and synthesized liquid e is obtained; the 120# solvent is added in the methylhydro-dichloro silicone oil to be stirred and dispersed for 10 minutes, and synthesized liquid f is obtained; the UV-531 (ultraviolet light polymerization agent) is added in the synthesized liquid f to be stirred and dispersed for 10 minutes, and synthesized liquid g is obtained; the synthesized liquid e and the synthesized liquid g are completely mixed and are filtered into a finished product after stirred and dispersed for 20 minutes; in the process of the steps, temperature is controlled from 35 to 70 DEG C, and pressure is controlled from 1300 to 1600 Pas. The present invention has the advantages of low viscosity, high solid components and good anti-pollution performance, and can effectively prevent the technical effects of 'urban psoriasis'.
Description
Technical field the present invention relates to chemical coating, particularly relates to a kind of stain resistant coating and compound method thereof.
Background technology is current, and various circles of society more and more pay attention to environmental issue, and the public image appearance in city also more and more is subjected to government and civic and pays close attention to.The problem of " city psoriasis " (disorderly put up to scrawl and write) still remains incessant after repeated prohibition, and becomes worse but meanwhile; The anti-stick subsides and the contamination resistance of existing building coating are all not so good, and wear resisting property is also limited.
The summary of the invention the technical problem to be solved in the present invention is to avoid above-mentioned the deficiencies in the prior art part and proposes a kind of stain resistant coating and compound method thereof, use this stain resistant coating anti-stick subsides contamination resistance of reinforce surface greatly, improve the wear resisting property of body surface.
The present invention solve the technical problem can be by realizing by the following technical solutions:
Dispose a kind of stain resistant coating, its moiety and corresponding weight proportion are respectively: organic-silicon-modified resin 15-23%, low aromatic solvent 65-76%, methyl hydrogen dichloro silicone oil 5.8-6.1%, UV-531 (ultraviolet curable agent) 0.05-0.08% and 120
#Solvent (gasoline exceeds standard) 3-5%.
The present invention solve the technical problem also will be by realizing by the following technical solutions:
Propose a kind of compound method of stain resistant coating, comprise the steps:
1. the organic-silicon-modified resin of 15-23% is joined the low aromatic solvent the inside of 65-76%, dispersed with stirring 10 to 20 minutes;
2. with step 1. the gained synthetic fluid mix fully with the methyl hydrogen dichloro silicone oil of 5.8-6.1%, dispersed with stirring 20 minutes refilters into product and packs;
Implementing described step 2. the time, also comprise the steps:
A. with 120 of 3-5%
#Solvent joins the methyl hydrogen dichloro silicone oil the inside of 5.8-6.1%, and dispersed with stirring 10 minutes gets synthetic fluid c;
B. the UV-531 (ultraviolet curable agent) with 0.05--0.08% joins among the synthetic fluid c of steps A gained, and dispersed with stirring 10 minutes gets synthetic fluid d;
1. after the synthetic fluid of gained mixed fully with described step with synthetic fluid d at last, just dispersed with stirring was 20 minutes, is filtered into product and packs.
And in above-mentioned all step process, temperature is controlled at 35 ℃-70 ℃, and pressure-controlling is within the 1300--1600 handkerchief.
Compare with prior art, the technique effect of stain resistant coating of the present invention is:
1. viscosity is low, solid part is high, and antifouling property is good, can effectively prevent " city psoriasis ";
2. waterproof, acid-proof, alkali prevention performance are good, can improve the wear resisting property of body surface;
Strong adhesion, the life-span is long, glossiness good, of many uses, except that being applicable to the anti-stick subsides of surperficial antipollution such as marble, ceramic tile, cement products, rock, metal, timber and common buildings coating, can also be used for the maintaining on surfaces such as general technology product, historical relic.
Embodiment is described in further detail below in conjunction with the most preferred embodiment shown in the accompanying drawing.
Stain resistant coating of the present invention, its moiety and corresponding mixture ratio are respectively: organic-silicon-modified resin 15--23%, low aromatic solvent 65--76%, methyl hydrogen dichloro silicone oil 5.8--6.1%.For coating of the present invention can be solidified in rapid drying, add the UV--531 (ultraviolet curable agent) of 0.05--0.08%.Simultaneously, also add 120 of 3-5%
#Solvent is to increase ADHESION OF PAINTS power of the present invention.
The compound method of described stain resistant coating comprises the steps:
1. the organic-silicon-modified resin of 5-23% is joined the low aromatic solvent the inside of 65-76%, dispersed with stirring 10 to 20 minutes gets synthetic fluid e;
2. with 120 of 3-5%
#Solvent joins in the methyl hydrogen dichloro silicone oil of 5.8-6.1%, and dispersed with stirring 10 minutes gets synthetic fluid f;
3. the UV-531 (ultraviolet curable agent) of 0.05-0.08% is joined step 2. among the synthetic fluid f of gained, dispersed with stirring 10 minutes, synthetic fluid g;
4. described synthetic fluid e mixes with the complete g of described synthetic fluid, and dispersed with stirring 20 minutes is filtered into product then and packs;
In the above-mentioned steps process, temperature is controlled at 35-70 ℃, and pressure-controlling is within the 1300--1600 handkerchief.
The best proportioning of the moiety of product of the present invention is: organic-silicon-modified resin 20%, low aromatic solvent 70%, methyl hydrogen dichloro silicone oil 5.93%, UV-531 (ultraviolet curable agent) 0.07%, 120
#Solvent 4%.
Product of the present invention is to be in harmonious proportion with organic silicic acid, oxidation inhibitor and organic agent to form, and is a kind of resin based on silicon of ardent hope property, is colourless transparent liquid.Its organosilicon feature is obvious, belongs to the high-grade material with Modern Decorative color and luster.Be mainly used in the lifting of the public image appearance in city, effectively solve all kinds of old stone material face renovations and problems such as " city psoriasis ".This product has great social effect, economic worth and dissemination.
During use, at first with body surface with clean cloth or cotton yarn wiped clean, make body surface free from dust, greasy dirt, wax stain and loosening material; Again stain resistant coating of the present invention evenly is brushed to body surface with row brush, in order to form the successive protective layer, brushing 2 effects can be better; After having brushed, got final product completely solidified in 24 hours.After the curing, non-setting adhesive or other glue are difficult to attach to this body surface, and the word that inks this body surface also can be wiped easily, really can play the anti-pasting effect of antipollution.
Claims (10)
1. stain resistant coating, it is characterized in that: its moiety and corresponding weight proportion are respectively: organic-silicon-modified resin 15-23%, low aromatic solvent 65-76%, methyl hydrogen dichloro silicone oil 5.8-6.1%.
2. stain resistant coating as claimed in claim 1 is characterized in that: its moiety comprises that also the UV-531 proportion is 0.05-0.08%.
3. stain resistant coating as claimed in claim 1 is characterized in that: its moiety also comprises 120
#The solvent proportion is 3-5%.
4. stain resistant coating as claimed in claim 1 is characterized in that: its moiety also comprises 120 of the UV-531 of 0.05-0.08% and 3-5%
#Solvent.
5. stain resistant coating as claimed in claim 4 is characterized in that: each moiety and corresponding mixture ratio are respectively: organic-silicon-modified resin 20%, low aromatic solvent 70%, methyl hydrogen dichloro silicone oil 5.93%, UV-531 0.07%, 120
#Solvent 4%.
6. the compound method of a stain resistant coating is characterized in that: comprise the steps:
1. the organic-silicon-modified resin of 15-23% is joined the low aromatic solvent the inside of 65-76%, dispersed with stirring 10 to 20 minutes;
2. with step 1. the gained synthetic fluid mix fully with the methyl hydrogen dichloro silicone oil of 5.8-6.1%, dispersed with stirring 20 minutes refilters into product and packs;
And in the above-mentioned steps process, temperature is controlled at 35-70 ℃, and pressure-controlling is within the 1300-1600 handkerchief.
7. the compound method of stain resistant coating as claimed in claim 6 is characterized in that: implemented step 1. after, continue following step: with 120 of 3-5%
#Solvent joins the methyl hydrogen dichloro silicone oil the inside of 5.8-6.1%, and dispersed with stirring 10 minutes gets synthetic fluid a; This synthetic fluid a again with described step 1. institute's synthetic liquid mix fully, dispersed with stirring 20 minutes is filtered into product at last and packs.
8. the compound method of stain resistant coating as claimed in claim 6, it is characterized in that: implemented step 1. after, continue following step: the UV-531 of 0.05-0.08% is joined the methyl hydrogen dichloro silicone oil the inside of 5.8-6.1%, dispersed with stirring 10 minutes, synthetic fluid b; This synthetic fluid b again with described step 1. the gained synthetic fluid mix fully, dispersed with stirring 20 minutes is filtered into product at last and packs.
9. the compound method of stain resistant coating as claimed in claim 6 is characterized in that: implemented step 1. after, continue following step:
A. with 120 of 3-5%
#Solvent joins the methyl hydrogen dichloro silicone oil the inside of 5.8-6.1%, and dispersed with stirring 10 minutes gets synthetic fluid c;
B. the UV-531 with 0.05-0.08% joins among the synthetic fluid c of steps A gained, and dispersed with stirring 10 minutes gets synthetic fluid d;
At last with synthetic fluid d and described step 1. the synthetic fluid of gained mix fully, just dispersed with stirring was filtered into product and packs after 20 minutes.
10. the compound method of a stain resistant coating is characterized in that: comprises the steps,
1. 20% organic-silicon-modified resin is joined in 70% the low aromatic solvent, dispersed with stirring 10 to 20 minutes, synthetic fluid e;
2. with 4% 120
#Solvent joins in 5.93% the methyl hydrogen dichloro silicone oil, dispersed with stirring 10 minutes, synthetic fluid f;
3. 0.07% UV-531 is joined step 2. among the synthetic fluid f of gained, dispersed with stirring 10 minutes, synthetic fluid g;
4. described synthetic fluid e is mixed with the complete g of described synthetic fluid, dispersed with stirring 20 minutes is filtered into product then and packs;
In the above-mentioned steps process, temperature is controlled at 35 ℃-70 ℃, and pressure-controlling is within the 1300-1600 handkerchief.