CN1280028C - Chitin fiber static flocking face fabric and its manufacturing method - Google Patents
Chitin fiber static flocking face fabric and its manufacturing method Download PDFInfo
- Publication number
- CN1280028C CN1280028C CN 200410017969 CN200410017969A CN1280028C CN 1280028 C CN1280028 C CN 1280028C CN 200410017969 CN200410017969 CN 200410017969 CN 200410017969 A CN200410017969 A CN 200410017969A CN 1280028 C CN1280028 C CN 1280028C
- Authority
- CN
- China
- Prior art keywords
- chitin fiber
- fabric
- static flocking
- base fabric
- adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention discloses chitin fiber static flocking fabric which comprises a villus layer, an adhesive layer and a base fabric layer. The present invention is characterized in that the villus layer is made of chitin fibers. The present invention also discloses a manufacture method of the chitin fiber static flocking fabric, which is characterized in that the manufacture method comprises the following procedures: the chitin fibers are cut to make chitin fiber villi of which the length is 0.25mm to 0.6mm; firstly, static flocking base fabric is ironed and trimmed, and then an adhesive of which the thickness is 0.15mm to 0.3mm is coated; in a static flocking chamber, the villi are tidily implant on the surface of the base fabric which is coated with the adhesive in a high voltage static field under the function of electric field force. The manufactured flannelette is prebaked and baked, so that the villi and the base fabric are firmly compounded to form static flocking cloth. The chitin fiber static flocking fabric has an antibacterial function, is produced into health-care static flocking products, is widely applies to the static flocking products of the static flocking fabric, static flocking toys, static flocking artwork, etc., and has broad exploitation prospects and good economic benefit.
Description
Technical field
The present invention relates to a kind of electrostatic flocking fabric and make ten thousand methods, particularly relate to a kind of chitin fiber electrostatic flocking fabric and manufacture method thereof.
Background technology
Electrostatic spinning be by fiber through cutting or pulverize dyed again and after electrical property handles, become fine hair, fine hair is the primary raw material of electrostatic spinning product.Electrostatic flocking technology be base fabric behind surface sizing, input electrostatic spinning chamber, the interaction of fine hair and high-voltage electrostatic field in flocking room, fine hair are implanted under the effect of electrostatic force in the glue-line on base fabric surface, and the electrostatic spinning product is made in drying curing and the arrangement of various backs again.Used flocked fiber mostly is fibers material greatly at present, and the usefulness natural fiber is less as flocked material.
Summary of the invention
Technical problem to be solved by this invention provides a kind of chitin fiber electrostatic flocking fabric and manufacture method thereof.
In order to solve the problems of the technologies described above, the technical solution used in the present invention is: a kind of chitin fiber electrostatic flocking fabric, comprise tapetum, adhesive phase and bottom cloth layer, and it is characterized in that: described tapetum is a chitin fiber.
A kind of manufacture method of kowtowing shell cellulose fiber electrostatic spinning and expecting as claimed in claim 1 is characterized in that comprising the steps:
A. with the cutting of chitin fiber process, making length is the chitin fiber fine hair of 0.25～0.6mm.
B. earlier with the flocking base fabric through the arrangement of plating, coating adhesive again, adhesive thickness is 0.15～0.3mm.
C. indoor at electrostatic spinning, in the high-voltage electrostatic field, make fine hair under the effect of electric field force and the neat base fabric surface that scribbles adhesive of implanting.
D. the flannelette that step C is made passes through preliminary drying 2～3 minutes, baked 2～3 minutes, makes fine hair and base fabric firmly compound, becomes electrostatic spinning cloth.
Wherein, the fine hair moisture content is controlled at 12%～22% among the step a, is controlled at 10 than resistance
6～10
8Ω cm, ascending to heaven property of fine hair was controlled at 18～20 seconds.Electrostatic high-pressure on the step c mesohigh electrode network is controlled to be 30～45KV, and the distance that scribbles on high voltage electrode net and the base fabric between the one side of adhesive is 12～18cm.The preliminary drying temperature is 80～120 ℃ in the steps d, and baking temperature is 150～165 ℃.
The invention has the beneficial effects as follows: because the chitin fiber price is higher, utilizing electrostatic flocking technology to make the chitin electrostatic flocking fabric is distributed in chitin fiber on the fabric significant surface, not only give full play to the quality heterosis of chitin fiber and compare, can reduce the chitin raw material cost about half with the chitin fabric of same grammes per square metre.Chitin flocking lining is compared with existing general electrostatic flocking fabric, and the difference of matter is arranged again, because of the chitin fiber electrostatic flocking fabric has the various antibacterial functions of chitin, becomes health electrostatic spinning product.Can also be widely used in electrostatic spinning products such as flocking lining, flocking toy, flocking technique product, DEVELOPMENT PROSPECT is wide, and economic benefit and social benefit are good.
The specific embodiment
The present invention is described in detail below in conjunction with embodiment.
Embodiment 1
Through being cut into fine hair, the fine hair moisture content is controlled at 12%, is controlled at 3 * 10 than resistance with pure chitin fiber
6Ω cm, ascending to heaven property of fine hair was controlled at 18 seconds, and making length is the chitin fiber fine hair of 0.3mm.The flocking base fabric adopts polyester fabric, earlier with the flocking base fabric through the arrangement of plating, coating adhesive again, adhesive thickness is 0.15mm.Indoor at electrostatic spinning, the control electrostatic high-pressure is 30KV in the high-voltage electrostatic field, and the distance that scribbles on high voltage electrode net and the base fabric between the earthing pole of adhesive is 12cm, makes fine hair under the effect of electric field force and neat implantation scribbles the base fabric surface of adhesive.Preliminary drying 2 minutes under 80 ℃ of temperature baked 2 minutes under 150 ℃ of temperature again, made fine hair and base fabric firmly compound, became pure chitin fiber electrostatic spinning cloth.
Embodiment 2
Chitin fiber, cotton fiber are made fine hair through cutting or pulverizing, and the fine hair moisture content is controlled at 18%, is controlled at 3 * 10 than resistance
7Ω cm, ascending to heaven property of fine hair was controlled at 19 seconds, and making length is the chitin fiber fine hair of 0.4mm.The flocking base fabric adopts polyester fabric, earlier with the flocking base fabric through the arrangement of plating, coating adhesive again, adhesive thickness is 0.2mm.Indoor at electrostatic spinning, the control electrostatic high-pressure is 40KV in the high-voltage electrostatic field, and the distance that scribbles on high voltage electrode net and the base fabric between the earthing pole of adhesive is 15cm, makes fine hair under the effect of electric field force and neat implantation scribbles the base fabric surface of adhesive.Preliminary drying 2 minutes under 100 ℃ of temperature baked 2 minutes under 160 ℃ of temperature again, made fine hair and base fabric firmly compound, made the electrostatic spinning cloth of chitin fiber and cotton fiber blending.
Embodiment 3
Chitin fiber, viscose rayon are made fine hair through cutting or pulverizing, and the fine hair moisture content is controlled at 22%, is controlled at 3 * 10 than resistance
8Ω cm, ascending to heaven property of fine hair was controlled at 20 seconds, and making length is the chitin fiber fine hair of 0.6mm.The flocking base fabric adopts polyester fabric, earlier with the flocking base fabric through the arrangement of plating, coating adhesive again, adhesive thickness is 0.3mm.Indoor at electrostatic spinning, the control electrostatic high-pressure is 45KV in the high-voltage electrostatic field, and the distance that scribbles on high voltage electrode net and the base fabric between the earthing pole of adhesive is 18cm, makes fine hair under the effect of electric field force and neat implantation scribbles the base fabric surface of adhesive.Preliminary drying 3 minutes under 120 ℃ of temperature baked 3 minutes under 165 ℃ of temperature again, made fine hair and base fabric firmly compound, made the electrostatic spinning cloth of chitin fiber and viscose fiber blending.
The present invention is not limited to above-mentioned embodiment; every by pure chitin fiber or blending chitin fiber; as chitin and viscose glue, chitin and cotton, chitin and chemical fibre or the like, the electrostatic spinning product that makes all falls within protection scope of the present invention as long as at the fine hair electricity that aspects such as processing, dyeing pigment selection, adhesive allotment, electric-field intensity control are adjusted accordingly.
Claims (5)
1. a chitin fiber electrostatic flocking fabric comprises tapetum, adhesive phase and bottom cloth layer, it is characterized in that: described tapetum is a chitin fiber.
2. the manufacture method of a chitin fiber electrostatic flocking fabric as claimed in claim 1 is characterized in that comprising the steps:
A. with the cutting of chitin fiber process, making length is the chitin fiber fine hair of 0.25～0.6mm;
B. earlier with the flocking base fabric through the arrangement of plating, coating adhesive again, adhesive thickness is 0.15～0.3mm;
C. indoor at electrostatic spinning, in the high-voltage electrostatic field, make fine hair under the effect of electric field force and the neat base fabric surface that scribbles adhesive of implanting;
D. the flannelette that step C is made passes through preliminary drying, bakes, and makes fine hair and base fabric firmly compound, becomes electrostatic spinning cloth.
3. the manufacture method of chitin fiber electrostatic flocking fabric according to claim 2 is characterized in that: the fine hair moisture content is controlled at 12%～22% among the step a, is controlled at 3 * 10 than resistance
6～3 * 10
8Ω cm, ascending to heaven property of fine hair was controlled at 18～20 seconds.
4. the manufacture method of chitin fiber electrostatic flocking fabric according to claim 2, it is characterized in that: the electrostatic high-pressure on the step c mesohigh electrode network is controlled to be 30～45KV, and the distance that scribbles on high voltage electrode net and the base fabric between the one side of adhesive is 12～18cm.
5. the manufacture method of chitin fiber electrostatic flocking fabric according to claim 2 is characterized in that: the preliminary drying temperature is 80～120 ℃ in the steps d, and 2～3 minutes preliminary drying time, baking temperature is 150～165 ℃, bakes 2～3 minutes.