CN1276042C - Polyphenyl thioether modified paint and its preparing method and use - Google Patents
Polyphenyl thioether modified paint and its preparing method and use Download PDFInfo
- Publication number
- CN1276042C CN1276042C CN 200410040940 CN200410040940A CN1276042C CN 1276042 C CN1276042 C CN 1276042C CN 200410040940 CN200410040940 CN 200410040940 CN 200410040940 A CN200410040940 A CN 200410040940A CN 1276042 C CN1276042 C CN 1276042C
- Authority
- CN
- China
- Prior art keywords
- polyphenylene sulfide
- modified paint
- paint
- pipes
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention discloses polyphenyl thioether modified paint, a preparation method thereof and the application thereof. The paint is composed of polyphenyl thioether, polytetrafluoroethylene, chromium oxide, molybdenum sulphide, titanium dioxide, ethanol and water; the paint is used to produce a composite layer on the wall of a metal product. A metal composite product produced by using the paint and the method of the present invention has the advantages of good physical and chemical property, corrosion resistance, high temperature resistance, high insulation property, high intensity and impact resistance; especially, the STF composite pipe produced by the present invention is a significant breakthrough in the history of composite pipes. The STF composite pipe solves the problems existing in various medium conveying pipes of China, and satisfies various requirements of pipes with large using amounts, such as water supply pipes, gas supply pipes, petroleum supply pipes and conveying pipes for high corrosion mediums (except strong oxacid); compared with unprotected pipes, the service life of the product is raised for more than 100 times.
Description
Technical field
The present invention relates to a kind of coating, relate in particular to a kind of polyphenylene sulfide (PPS) modified paint and its production and use, be used on the wall of metal products, making composite bed with corrosion-resistant, high temperature resistant, high insulation, high strength, impact resistance.
Background technology
For improving the performance of metal products, expand Application Areas, setting up compound (protection) layer on the surface of metal products is the popular way, extensively utilization in a lot of fields, for example: 1. pipeline: corrosion-resistant, high temperature resistant, high insulation, high flame retardant, withstand voltage, impact-resistant natural gas line, petroleum pipeline, all kinds of chemical industry pipe, water-supply pipe, all kinds of liquid heating pipes; 2. flat-type: various corrosion-resistant, high insulating pressures vessels for the chemical industry, reactor, various wire netting; 3. special-shaped product: the synthetic protection in the surface of various corrosion-resistant, high temperature resistant, high insulating engineering goods.
But, the metal composite goods that adopt existing matrix material and complex method to make, its physicochemical property is more single, all can not possess acidproof, alkaline-resisting, salt tolerant, high temperature resistant simultaneously, shock-resistant, high strength, high insulating characteristic still exist many shortcomings, and for example: a. is zinc-plated, chromium, nickel dam: not corrosion-resistant, the severe contamination medium is forbidden in waterworks; B. ceramic thin film: end table separates, frangible, can't connect the cost height; C. aluminum-plastic laminated tube: end table separates, and intensity difference is not shock-resistant, not fire-retardant; D. steel-plastics composite pipe (promptly doing inner lining of steel pipe with plastics tubing): end table separates non-refractory, connects difficulty, and is yielding; E. steel band hole pattern multiple-unit tube (at wire netting surface recombination plastics): non-refractory, intensity difference, cost height.
Though, at Chinese patent a kind of " polyphenyl sulfoether resin anti-corrosive paint " disclosed (CN1133331A), only as the undercoat of certain utensil, performance is single, can't be as the surface protection of general pipe, plate, mechanical component." a kind of anticorrosion composite nano paint and preparation method thereof that is used for " also disclosed at Chinese patent (CN1346860A), but the preparation method is very complicated, and coating structure belongs to silica-based, and over-all properties is relatively poor, dispersion agent is higher with the Virahol cost, reclaims easily contaminate environment of difficulty.
Summary of the invention
The technical problem to be solved in the present invention provides a kind of polyphenylene sulfide modified paint (also claiming the STF matrix material), and this coating is used for making the composite bed with corrosion-resistant, high temperature resistant, high insulation, high strength, impact resistance on the wall of metal products; And provide the preparation method of this coating and the method for on the wall of metal products, making composite bed of this coating.
Technical scheme of the present invention is as follows:
A kind of polyphenylene sulfide (PPS) modified paint, form (by weight percentage) by following component:
Polyphenylene sulfide (PPS) 10--25%, polytetrafluoroethylene (PTFE) 5--30%, chromium sesquioxide (Cr
2O
3) 5--18%, cobalt sesquioxide (Co
2O
3) 4--14%, moly-sulfide (MoS
2) 6--12%, titanium dioxide (TiO
2) 9--14%, ethanol (CH
3CH
2OH) 7--30%, water (H
2O) 4--18%.
Preferably, form (by weight percentage) by following component:
Polyphenylene sulfide 10-20%, tetrafluoroethylene 5--30%, chromium sesquioxide 8-18%, cobalt sesquioxide 4--14%, moly-sulfide 8--10%, titanium dioxide 9--10%, ethanol 10--12%, water 14--18%.
Better, form (by weight percentage) by following component:
Polyphenylene sulfide 15--20%, tetrafluoroethylene 10--28%, chromium sesquioxide 5--8%, cobalt sesquioxide 4--10%, moly-sulfide 8--10%, titanium dioxide 12--14%, ethanol 16--30%, water 4--6%.
Preferably, form (by weight percentage) by following component:
Polyphenylene sulfide 20--25%, tetrafluoroethylene 10--25%, chromium sesquioxide 10--12%, cobalt sesquioxide 7--8%, moly-sulfide 6--12%, titanium dioxide 10%, ethanol 5--7%, water 7--16%
The preparation method of above-mentioned polyphenylene sulfide (PPS) modified paint comprises the steps:
1) gets polyphenylene sulfide, tetrafluoroethylene, chromium sesquioxide, cobalt sesquioxide, moly-sulfide, titanium dioxide by described weight ratio, in mixing tank, mix;
2) material that mixes is ground in milling apparatus, make 300-500 purpose micro mist;
3) micro mist after will grinding places mixing tank, adds dispersion agent second alcohol and water by described weight ratio, mixes, and becomes suspension.
Above-mentioned polyphenylene sulfide (PPS) modified paint is used for making the composite bed with corrosion-resistant, high temperature resistant, high insulation, high strength, impact resistance on the wall of metal products.Metal products can be metal tube or plate or various shaped piece.
Method with above-mentioned polyphenylene sulfide (PPS) modified paint is made composite bed on the wall of metal products comprises the steps:
1) surface derusting, the degreasing of metal products is also dry;
2) the polyphenylene sulfide modified paint evenly is sprayed on the metal products surface, coat-thickness 50-500 μ m;
3) metal products that will spray coating places the process furnace sintering, and temperature 300-420 ℃, time 20-60 minute;
4) composite product behind the sintering is placed the normal-temperature water naturally cooling, then oven dry.
Beneficial effect of the present invention:
The present invention (CN1133331A) compares with " polyphenyl sulfoether resin anti-corrosive paint ", and the composite bed that this coating is made on wall of metallic product has multiple performance, and Application Areas is wide, can be as the surface protection of general pipe, plate, mechanical component.
The present invention (CN1346860A) compares with " a kind of anticorrosion composite nano paint and preparation method thereof that is used for ", and preparation method for coating is simple, good combination property, and dispersion agent is low with second alcohol and water cost, reclaims free from environmental pollution easily.
Coating of the present invention is with the matrix material (also claim STF matrix material) of PPS material through modification; make the method sintering of composite bed on the metallic surface with the present invention; or on the metal products surfaces externally and internally, thereby on metal products, form the metal surface protection layer of corrosion-resistant, high temperature resistant, high insulation, high strength, impact resistance.
The experiment proved that the STF multiple-unit tube that adopts technical scheme of the present invention to produce has following over-all properties:
1. the liquid resistance is minimum: can reduce to carry when carrying the low viscosity medium and press, save energy can not deposit obstruction when the transfer of highly viscous medium.Especially more apparent its superiority when transfer oil.
2. wear resistance is good: when carrying solid-liquid mixture, strengthened wear resistance, especially the husky friction with the pipe end of pipe bed mud is very serious when transfer oil, Sweet natural gas, uses compound pipe not have friction substantially.
3. corrosion-resistant: this compound pipe does not still have to dissolve the chemical reagent of its inwall at normal temperatures, so any corrosive medium does not possess corrodibility to tube wall, promptly compound pipe can be used for any medium of permanent conveying.
4. nontoxic, harmless, pollution-free: this compound pipe inwall is the engineering materials that one deck is sintered also and metal pipe line combines together, and being used for fluming water is a kind of material that cleans most.
5. high temperature resistant: this pipeline can be carried the various fluids under 260 ℃.
6. shock-resistant: this pipeline inwall all can not chap under the effect of various surging forces, delamination, and has self-sealing function, is convenient to pipeline and connects sealing.
7. high strength: this pipeline does not change former pipeline self rigidity through compound.Its comprehensive mechanical performance still keeps the performance of steel pipe self.
Embodiment
Embodiment 1-10
In the following table the 10 assembly sides (component concentration is weight percentage) of polyphenylene sulfide of the present invention (PPS) modified paint
Embodiment 11
The preparation method of a kind of polyphenylene sulfide (PPS) modified paint:
1) gets polyphenylene sulfide resin cosmetics 23kg, tetrafluoroethylene 15kg, chromium sesquioxide 5kg, cobalt sesquioxide 8kg, moly-sulfide 6kg, titanium dioxide 10kg, in mixing tank, mix; 2) material that mixes is ground in milling apparatus, make about 400 purpose micro mists; 3) micro mist after will grinding places mixing tank, adds dispersion agent ethanol 20kg, water 13kg, mixes, and becomes suspension.
The polyphenylene sulfide of various proportionings (PPS) modified paint all prepares by the method for embodiment 11.
Embodiment 12
On the wall of metal tube, make composite bed with polyphenylene sulfide (PPS) modified paint, carry out according to the following steps:
1) surface derusting, the degreasing of metal tube is also dry; 2) polyphenylene sulfide (PPS) modified paint evenly is sprayed on metal tube or the plate surfaces externally and internally, sprays three times, total coating thickness 100 μ m; 3) metal tube that will spray coating places process furnace, and 400 ℃ of left and right sides sintering temperatures 3 times, about 40 minutes sintering total times, the composite bed free of pinholes gets final product after testing; 4), then multiple-unit tube is put hot case (about 80 ℃ of temperature) oven dry with the naturally cooling in normal-temperature water of the multiple-unit tube behind the sintering.
The metal products of different shape is all made composite bed by the method for embodiment 12.
Composite metal product with technical solution of the present invention is produced has good physics, chemical property, corrosion-resistant, high temperature resistant, high insulation, high strength, shock-resistant.
Be that example illustrates its technology, economical effectiveness now with the STF multiple-unit tube:
The STF multiple-unit tube of producing with technical solution of the present invention is an important breakthrough on the Chinese compound pipe history, solved the problem that all kinds of media of China (except that containing oxygen strong acid) line of pipes exists fully, the various requirement of water supply, air feed, confession oil and the high corroded pipeline of China's consumption maximum all is met, compare with common steel tube, improved product work-ing life more than 100 times, comprehensive cost is low, and every meter of Φ 630STF multiple-unit tube is below 1000 yuan.
The STF multiple-unit tube that adopts technical scheme of the present invention to produce reaches test rating as following table one, table two, table three through check:
The mechanical property of table one STF multiple-unit tube
| Project | Testing method | Test result |
| Outward appearance | Range estimation | Color and luster is even, smooth smooth |
| The attached power of work | Draw the circle method | One-level |
| Hardness | The pencil method | 4H |
| Impelling strength | GB 1732-79 | 50KGCM |
| Snappiness | Bent spindle | By the 1MM axle |
| Contact angle | Water, degree | 82° |
| Heat decomposition temperature | Analyser | 400℃ |
| Density | Specific weight determine | 1.36～1.6 |
| Sinuousness | D-796 | 60---95.8 |
| Coefficient of friction | 0.13 | |
| Wear intensity | The MM-200 trier, 100N, 200R/MIN, 1h, 50m/min | 0.1*10-5mm3/N.M |
| Shrinking percentage | ＜0.003 | |
| Water-absorbent | ＜0.002 | |
| Combustion safety | UL-94 | V-0/5v (highest level) |
| Tensile strength | D638 | 155 |
| Brinell hardness | The A-200 type carries 360.25N | 50MPa |
The chemical property of table two STF multiple-unit tube (having following various function simultaneously)
| Project | Testing method | Test result |
| Thermotolerance | Use temperature | 220℃-260℃ |
| Heat decomposition temperature | Thermal analyzer | 425℃ |
| Weathering resistance | Working temperature | -100℃----260℃ |
| Toxicity | Processing is used nontoxic | Produce micro-SO, COS, COCS more than 425 |
1. acid resistance: phosphoric acid, hydrofluoric acid, acetic acid, Glacial acetic acid, lactic acid, oxalic acid, Phenylsulfonic acid, the long period of soaking of the various concentration of 25% hydrochloric acid, 10% carbonic acid do not have corrosion.
2. alkali resistance: ammonium hydroxide, calcium hydroxide, potassium hydroxide, sodium hydroxide arbitrarily, long period of soaking does not have corrosion.
3. salt tolerance: acid, alkalescence, neutral salt, potassium permanganate, potassium cyanide, sodium cyanide, iron hydrogenation.
The electrical property of table Three S's TF multiple-unit tube
| Project | Testing method | Test result |
| Volume specific resistance | D-257Ω.cm | 7.51*1015 |
| Surface resistivity | D-257Ω | 7.66*1014 |
| Specific inductivity | D-150(LMHz) | 3.13 |
| Voltage breakdown | D-149kV/mm | 19.4 |
| Insulativity | 1000 volt-amperes of meggers | 7500MG |
Claims (7)
1. polyphenylene sulfide modified paint is characterized in that the each component weight percent of described coating is:
Polyphenylene sulfide 10--25%, tetrafluoroethylene 5--30%, chromium sesquioxide 5--18%, cobalt sesquioxide 4--14%, moly-sulfide 6--12%, titanium dioxide 9--14%, ethanol 7--30%, water 4--18%.
2. polyphenylene sulfide modified paint according to claim 1 is characterized in that the each component weight percent of described coating is:
Polyphenylene sulfide 10--20%, tetrafluoroethylene 5--30%, chromium sesquioxide 8--18%, cobalt sesquioxide 4--14%, moly-sulfide 8--10%, titanium dioxide 9--10%, ethanol 10--12%, water 4--18%.
3. polyphenylene sulfide modified paint according to claim 1 is characterized in that the each component weight percent of described coating is:
Polyphenylene sulfide 15--20%, tetrafluoroethylene 10--28%, chromium sesquioxide 5--8%, cobalt sesquioxide 4--10%, moly-sulfide 8--10%, titanium dioxide 12--14%, ethanol 16--30%, water 4--6%.
4. claim 1 to 3 preparation method of each described polyphenylene sulfide modified paint wherein comprises the steps:
1) gets polyphenylene sulfide, tetrafluoroethylene, chromium sesquioxide, cobalt sesquioxide, moly-sulfide, titanium dioxide by weight, in mixing tank, mix;
2) material that mixes is ground in milling apparatus, make 300--500 purpose micro mist;
3) micro mist after will grinding places mixing tank, adds dispersion agent second alcohol and water by weight, mixes, and becomes suspension.
5. claim 1 to 3 purposes of each described polyphenylene sulfide modified paint wherein is used for making the composite bed with corrosion-resistant, high temperature resistant, high insulation, high strength, impact resistance on the wall of metal products.
6. as the purposes of polyphenylene sulfide modified paint as described in the claim 5, it is characterized in that described metal products is metal tube or plate or shaped piece.
7. the making method of the polyphenylene sulfide modified paint composite bed described in the claim 5 comprises the steps:
1) surface derusting, the degreasing of metal products is also dry;
2) each polyphenylene sulfide modified paint among the claim 1-3 evenly is sprayed on the metal products surface, coat-thickness 50-500 μ m;
3) metal products that will spray coating places the process furnace sintering, and temperature 300-420 ℃, time 20-60 minute;
4) composite product behind the sintering is placed the water naturally cooling, then oven dry.