CN1259379C - Waterproof, thermal insulating fire resisting coating - Google Patents
Waterproof, thermal insulating fire resisting coating Download PDFInfo
- Publication number
- CN1259379C CN1259379C CN 200410012788 CN200410012788A CN1259379C CN 1259379 C CN1259379 C CN 1259379C CN 200410012788 CN200410012788 CN 200410012788 CN 200410012788 A CN200410012788 A CN 200410012788A CN 1259379 C CN1259379 C CN 1259379C
- Authority
- CN
- China
- Prior art keywords
- parts
- portions
- weight
- waterproof
- mica
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to waterproof, thermal insulating and fire resistant paint which is prepared from an auxiliary material and a base material. The paint is characterized in that a main material is prepared from 5 to 16 portions by weight of pentaerythritol, 0.2 to 6 portions by weight of antimony trioxide, 0.2 to 6 portions by weight of chloroparaffin, 2 to 20 portions by weight of mica, 2 to 20 portions by weight of sepiolite, 1 to 11 portions by weight of melamine, 0.3 to 7 portions by weight of silicon powder, 1 to 18 portions by weight of ammonium phosphate and 5 to 40 portions by weight of perlite. The present invention has the advantages of nontoxicity, odorlessness, safety, environmental protection, stable performance and favorable waterproof, thermal insulating and fire resistant effects; the paint can be widely used for walls, roofs, floors, basements, pipelines, wood plates and metal.
Description
Technical field
The present invention relates to the coating composition field, particularly waterproof, heat insulation, anti-flaming dope.
Background technology
Coating is as a kind of New Building Materials, be widely used on the decoration, finishing of the buildings such as external and internal wall, floor aspect, bottom of the building roofing, pipeline of buildings, technical progress to aspects such as coating combination ingredient, manufacturing process in the prior art emerges in an endless stream, as application number: 98113501, denomination of invention is " heat insulated waterproof flame-retardant paint and preparation method thereof, a using method ", mainly by composition (A): silicon sol, Sodium hexametaphosphate 99, emulsifying agent, defoamer etc.; Composition (B), clorafin, dibutyl phthalate, defoamer, anti-aging agent etc.; Compounded mix is: wollastonite powder, lime carbonate etc.; Group of solvents (second): dibutyl phthalate, solvent etc.This coating has good heat insulated waterproof flame-retardant effect, and construction is simple, and is easy to use, but because of the selection of its oil-based solvent and the combination of two components, makes that its toxicity is difficult to avoid, the consumption of constructing is difficult to control, standard is difficult to hold.Application number and for example: 00120958, denomination of invention is " expanding super-thin steel structure fire-proof corrosive-resistant paint and preparation method ", its preparation method is: join epoxide modified chlorinated high polymers in the solvent at normal temperatures, after dissolving, add ammonium polyphosphate, tetramethylolmethane, trimeric cyanamide, melamine phosphate, antimonous oxide, pure aluminium silicate, clorafin, components such as titanium white after the dispersion, are ground to evenly promptly.More than two kinds of coating all can get waterproof, heat insulation, fire-retardant effect.However, for waterproof, heat insulation, fire-retardant still to no effect good especially coating, coating effect of the prior art still can not be satisfactory.
Summary of the invention
Therefore, still there is demand in people for waterproof, heat insulation, the better coating of flame retardant effect.Up to the present, still find no the data of any destruction novelty of the present invention, present inventor people is through studying intensively for many years, thereby finished the present invention.
The object of the present invention is to provide waterproof, heat insulation, fire-retardant coating.
The present invention realizes like this, it comprises auxiliary material: dispersion agent, defoamer, frostproofer, emulsifying agent, thickening material, base-material: emulsion, solvent, each composition of described major ingredient is: tetramethylolmethane, antimonous oxide, clorafin, mica, sepiolite, weight part ratio is between each composition: 5～16 parts of tetramethylolmethanes, 0.2～6 part of antimonous oxide, 0.2～6 part of clorafin, 2～20 parts on mica, 2～20 parts of sepiolites.
Each composition consumption of described major ingredient is: 10 parts of tetramethylolmethanes, 2 parts of antimonous oxides, 2 parts of clorafins, 12 parts on mica, 12 parts of sepiolites.
Described major ingredient also has 1～11 part of trimeric cyanamide, 0.3～7 part of silica flour.
Each composition consumption of described major ingredient is: 10 parts of tetramethylolmethanes, 5 parts of trimeric cyanamides, 2 parts of antimonous oxides, 2 parts of clorafins, 3 parts of silica flours, 12 parts on mica, 12 parts of sepiolites.
Described major ingredient also has 1～18 part of phosphamide, 5～40 parts of perlites.
Each composition consumption of described major ingredient is: 10 parts of tetramethylolmethanes, 5 parts of trimeric cyanamides, 2 parts of antimonous oxides, 2 parts of clorafins, 8 parts of phosphamides, 3 parts of silica flours, 12 parts on mica, 12 parts of sepiolites, 20 parts of perlites.
Manufacturing process is: stir evenly tetramethylolmethane, trimeric cyanamide, antimonous oxide, clorafin, phosphamide mixing stand-by; Adding silica flour, mica, sepiolite, perlite, dispersion agent, Mierocrystalline cellulose, solvent then stirs evenly stand-by; Stir evenly frostproofer, defoamer, emulsifier mix stand-by; Again three's high-speed stirring 30 minutes, can after carry out ball milling; Adding emulsion again stirs and gets final product.
The present invention is owing to adopt materials such as tetramethylolmethane, trimeric cyanamide, clorafin fire-retardant, adopt material waterproof such as ethene-vinyl acetate emulsion, adopt silica flour, mica, sepiolite, perlite heat insulation, therefore the present invention is nonpoisonous and tasteless, safety and environmental protection, stable performance is difficult for aging, the elasticity height is suitable for solving cracking, the modification of buildings, pipeline, and the water proof fire retardant effect is remarkable.The present invention smears, whitewashes and can paste ceramic tile, powder cement mortar after the drying in the above and do not flake, and can be widely used in the waterproof, heat insulation, fire-retardant, effective of body of wall, roofing, bottom of the building face, vault, pipeline, plank, metal.
Embodiment
Auxiliary material: dispersion agent is six flat sodium phosphates, and defoamer is a tbp, and frostproofer is an ethylene glycol, and emulsifying agent is OP-10, and thickening material is a Mierocrystalline cellulose.
Base-material: emulsion is the ethene-vinyl acetate emulsion, and solvent is a water solvent.
Embodiment 1: adopt each composition consumption of described major ingredient to be: 10 parts of tetramethylolmethanes, 2 parts of antimonous oxides, 2 parts of clorafins, 12 parts on mica, 12 parts of sepiolites.
Embodiment 2: adopt each composition consumption of described major ingredient to be: 10 parts of tetramethylolmethanes, 5 parts of trimeric cyanamides, 2 parts of antimonous oxides, 2 parts of clorafins, 3 parts of silica flours, 12 parts on mica, 12 parts of sepiolites.
Embodiment 3: adopt each composition consumption of described major ingredient to be: 10 parts of tetramethylolmethanes, 5 parts of trimeric cyanamides, 2 parts of antimonous oxides, 2 parts of clorafins, 8 parts of phosphamides, 3 parts of silica flours, 12 parts on mica, 12 parts of sepiolites, 20 parts of perlites.
Adopt each composition consumption of auxiliary material to be among embodiment 1, embodiment 2, the embodiment 3: dispersion agent: 0.8 part of six flat sodium phosphate, defoamer: 0.05 part of tbp, frostproofer: 6 parts of ethylene glycol, emulsifying agent: OP-100.05 part, thickening material: 2 parts of Mierocrystalline celluloses; Each composition consumption of base-material is: emulsion: 100 parts of ethene-vinyl acetate emulsions, solvent: 26 parts of water solvents.Manufacturing process is: stir evenly tetramethylolmethane, trimeric cyanamide, antimonous oxide, clorafin, phosphamide mixing stand-by; Add then silica flour, mica, sepiolite, perlite, six flat sodium phosphates, Mierocrystalline cellulose, water solvent mix stir evenly stand-by; Stir evenly ethylene glycol, tbp, OP-10 mixing stand-by; Again three's high-speed stirring 30 minutes, can after carry out ball milling; Adding the ethene-vinyl acetate emulsion again stirs and gets final product.
Claims (6)
1, waterproof, heat insulation, anti-flaming dope, it comprises auxiliary material, base-material and major ingredient, auxiliary material: dispersion agent, defoamer, frostproofer, emulsifying agent and thickening material, base-material: emulsion and solvent, it is characterized in that each composition of described major ingredient is: tetramethylolmethane, antimonous oxide, clorafin, mica and sepiolite, weight part is between each composition: 2～20 parts of 5～16 parts of tetramethylolmethanes, 0.2～6 part of antimonous oxide, 0.2～6 part of clorafin, 2～20 parts on mica and sepiolites.
2, according to the described waterproof of claim 1, heat insulation, anti-flaming dope, it is characterized in that: each composition consumption of described major ingredient is: 12 parts of 10 parts of tetramethylolmethanes, 2 parts of antimonous oxides, 2 parts of clorafins, 12 parts on mica and sepiolites.
3, according to the described waterproof of claim 1, heat insulation, anti-flaming dope, it is characterized in that: described major ingredient also has 0.3～7 part of 1～11 part of trimeric cyanamide and silica flour.
4, according to the described waterproof of claim 3, heat insulation, anti-flaming dope, it is characterized in that: each composition consumption of described major ingredient is: 12 parts of 10 parts of tetramethylolmethanes, 5 parts of trimeric cyanamides, 2 parts of antimonous oxides, 2 parts of clorafins, 3 parts of silica flours, 12 parts on mica and sepiolites.
5, according to the described waterproof of claim 3, heat insulation, anti-flaming dope, it is characterized in that: described major ingredient also has 5～40 parts of 1～18 part of phosphamide and perlites.
6, according to the described waterproof of claim 5, heat insulation, anti-flaming dope, it is characterized in that: each composition consumption of described major ingredient is: 20 parts of 10 parts of tetramethylolmethanes, 5 parts of trimeric cyanamides, 2 parts of antimonous oxides, 2 parts of clorafins, 8 parts of phosphamides, 3 parts of silica flours, 12 parts on mica, 12 parts of sepiolites and perlites.