CN1253082A - Method for making simulative woodcut - Google Patents
Method for making simulative woodcut Download PDFInfo
- Publication number
- CN1253082A CN1253082A CN 98124407 CN98124407A CN1253082A CN 1253082 A CN1253082 A CN 1253082A CN 98124407 CN98124407 CN 98124407 CN 98124407 A CN98124407 A CN 98124407A CN 1253082 A CN1253082 A CN 1253082A
- Authority
- CN
- China
- Prior art keywords
- making
- woodcut
- simulative
- resin
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A simulative woodcut picture is made up through such technological steps as making mould, making surface layer with resin, chalk, solidifying agent and promoter, making the reinforcing material with resin, hollow glass microbeads, saw dust, and chalk, pasting netty glass cloth or glass fibres to form reinforcing layer, compounding filling layer with polymer and isocyanate, sticking back surface, demoulding, grinding smooth, spraying paint, colouring and writing. Its advantages are high productivity, low cost, light weight, no deformation, fire retarding and high acid and alkali resistance.
Description
The present invention relates to a kind of technology of copying art ware.
The making of traditional woodcut etching is that the author with certain woodcut etching art designing technical ability forms with engravings such as redwood or lindens, its complex process, cost height, long in time limit and woodcut etching weight is big, yielding, inflammable, acid and alkali-resistance, moisture-sensitive cracking, service life is short.Because of it is that single-piece is made by hand,, can't realize large-scale production again so production efficiency is low.
The objective of the invention is to overcome above-mentioned shortcoming, provide a kind of production efficiency height, cost product weight low, that produced light, indeformable, do not ftracture, the method for making simulative woodcut of nonflammable, acid and alkali-resistance, long service life.
Method for making simulative woodcut of the present invention comprises following process steps:
(1) according to the product model of made, makes production mould;
(2) make surface layer: with resin, chalk powder, curing agent, promoter preparation surface material, its volume ratio is: the portions of resin chalk powder is 100: (50～100); The portions of resin curing agent: promoter is 100: (2-4): (4-8), wherein curing agent is 1: 2 with the ratio of promoter, it is stirred into pasty state and is coated on the described mould make surface layer, and make its spontaneous curing;
(3) make at least two layers of enhancement layer: with resin, hollow glass bead, sawdust, chalk powder preparation enhancement layer material, its volume ratio is 100: (40～60): (40～60): (20～60), it is stirred into pasty state is painted on the described surface layer and pastes ground floor glass web or glass fibre, the reinforcing material paste that brushing one deck is prepared on it again, paste second layer glass web or glass fibre again, and spontaneous curing;
(4) paste the back side with bonding agent;
(5) fine finishining such as calligraphy and painting are polished, spray paint, paint, retouch in the demoulding to surface layer.
Method for making simulative woodcut of the present invention is made packed layer after being preferably in processing step 3, uses the poly-close and carbimide preparation packed layer material of combination, and its volume ratio is 100: 100, is stirred into slurries and brushes and spontaneous curing on described enhancement layer.
Another alternative technology scheme of method for making simulative woodcut of the present invention is that the material available volume ratio of the described packed layer of making is 100: the resin of (100～300) and perlite replace.
It is 100: 60 that method for making simulative woodcut of the present invention preferably makes the material resin of described making surface layer, the volume ratio of chalk powder, and the volume ratio of the material resin of described making enhancement layer, hollow glass bead, sawdust, chalk powder is 100: 40: 40: 40.
The another alternative technology scheme of method for making simulative woodcut of the present invention is that the described back side is three-ply board or woodgrained paper or cloth.
A method for making simulative woodcut of the present invention alternative technology scheme again is that the thickness of described surface layer is that 1～3 millimeter, the thickness of enhancement layer are that 2～5 millimeters, the thickness of packed layer are 10～20 millimeters.
A method for making simulative woodcut of the present invention also alternative technology scheme is to add an amount of pigment in the described surface material of preparation.
Method for making simulative woodcut of the present invention adopts the mould manufacturing, replace high-quality timber such as expensive redwood, linden with industrial chemicals such as resin making surface layer, enhancement layer, packed layer, can produce by batch, its production efficiency height, cost is low, and the single products duration makes than traditional-handwork and saves time about 80%, and cost reduces about 70%, that the product of being produced has is in light weight, humidity, indeformable, do not ftracture, advantage such as nonflammable, acid and alkali-resistance, and its artistic effect is identical with the woodcut etching.
Other details of method for making simulative woodcut of the present invention and characteristics can be cheer and bright by reading the embodiment hereinafter encyclopaedize in conjunction with the accompanying drawings, wherein:
Fig. 1 is the product design sketch of producing with method for making simulative woodcut of the present invention;
Fig. 2 is the product section structure schematic diagram of producing with method for making simulative woodcut of the present invention.
Embodiment: with method for making simulative woodcut manufacturing of the present invention imitative redwood woodcut etching as shown in Figure 1, its processing step is as follows:
(1) with producing wood imitative redwood woodcut etching model shown in Figure 1, and by modelling nonmetal mould 1.Also can make metal die in this step.
(2) make surface layer 2: with unsaturated polyester resin 191, chalk powder, curing agent, promoter, fluorescent transparent red pigment preparation surface material, wherein resin 191 is 100: 60 with the volume ratio of chalk powder; Resin 191 is 100: 2: 4 with the volume ratio of curing agent, promoter.Wherein curing agent is initator again, available No. 1 initator or No. 2 initators, and promoter can be selected benzoyl peroxide-tertiary amine promoter or the ketone peroxide-aphthenic acids titanium promoter that is complementary with initator for use.Resin in the step 2 also can be selected resins such as 196 unsaturated polyester resins or epoxy resin for use, and the volume ratio of resin and chalk powder all could between 100: 50 or 100: 100.The effect selection of the color of pigment, the deep or light simulative woodcut that can make as required, allotment; The volume ratio of resin, curing agent, promoter can be 100: (2-4): select (4-8), wherein curing agent should be 1: 2 with the ratio of promoter, and room temperature should be selected 100: 2: 4 in the time of 20 ℃～35 ℃; Room temperature should be selected 100: 4: 8 in the time of 10 ℃～20 ℃.
Above-mentioned raw materials mix stirred mix well into starchiness and be coated on the above-mentioned mould 1, surface layer 2 thickness are 1 millimeter, and thickness all can between 1～3 millimeter.
(3) make enhancement layer 3,4: with unsaturated polyester resin 191, hollow glass bead, sawdust, chalk powder preparation enhancement layer material, its volume ratio is 100: 40: 40: 40, it mix is stirred mix well into starchiness and be applied on the surface layer 2 and paste the ground floor glass web, and then be coated with the paste that one deck is prepared, paste second layer glass web again, at least should make two layers of enhancement layer 3,4, spontaneous curing then.Normal temperature is promptly curable about next hour.When making enhancement layer, resin can be selected other resins equally, and as unsaturated polyester resin 196 etc., wherein the ratio of resin, hollow glass bead, sawdust, chalk powder volume can be 100: (40～60): (40～60): select between (20～60).Enhancement layer also can be suitably more does which floor, gross thickness between 2～5 millimeters all can, surface layer and enhancement layer can use talcum powder, dry powder to replace chalk powder, available straw replaces sawdust the last reign of a dynasty.
(4) make packed layer 5: use the poly-close and carbimide preparation packed layer material of combination, its volume ratio is 100: 100, is stirred into slurries and brushes on enhancement layer 4, and its thickness is 10 millimeters, and makes it spontaneous curing.The THICKNESS CONTROL of packed layer 5 is comparatively suitable between 10～20 millimeters during production.Packed layer 5 is usable resins and perlite making also, and its volume ratio is 100: (100～300) all can.If the size of simulative woodcut is less, also can not make packed layer 5, directly enhancement layer 4 is sticked on the plank.
(5) make the back side 6: on packed layer 5, paste three-ply board or woodgrained paper or cloth with bonding agents such as white glue with vinyl or resins.
(6) demoulding, surface layer is polished, sprays imitative redwood coat with lacquer, paint, retouch fine finishining such as calligraphy and painting.
In step 6, make woodcut etchings such as imitative linden as need, then available paint add required pigment transfer to woody form and aspect with color after spray paint.
The etching effect of producing with method for making simulative woodcut of the present invention is true to nature, cheap.
Claims (7)
1, a kind of method for making simulative woodcut comprises following process steps:
(1) according to the product model of made, makes production mould;
(2) with resin, chalk powder, curing agent, promoter preparation surface material, its volume ratio is: the portions of resin chalk powder is 100: (50～100); The portions of resin curing agent: promoter is 100: (2-4): (4-8), wherein curing agent is 1: 2 with the ratio of promoter, it is stirred into pasty state and is coated on the described mould make surface layer, and make its spontaneous curing;
(3) make at least two layers of enhancement layer: with resin, hollow glass bead, sawdust, chalk powder preparation enhancement layer material, its volume ratio is 100: (40～60): (40～60): (20～60), it is stirred into pasty state is painted on the described surface layer and pastes ground floor glass web or glass fibre, the reinforcing material paste that brushing one deck is prepared on it again, paste second layer glass web or glass fibre again, and spontaneous curing;
(4) paste the back side with bonding agent;
(5) demoulding, surface layer polished, sprays paint, paints, retouches fine finishining such as calligraphy and painting.
2, according to the described method for making simulative woodcut of claim 1, it is characterized in that between processing step 3 and 4, making packed layer, the poly-close and carbimide preparation packed layer material with combination, its volume ratio is 100: 100, is stirred into slurries and brushes and spontaneous curing on described enhancement layer.
3, according to the described method for making simulative woodcut of claim 2, it is characterized in that the material available volume ratio of described packed layer is 100: the resin of (100～300) and perlite replace.
4, according to claim 1 or 2 or 3 described method for making simulative woodcut, it is characterized in that the material resin of described making surface layer, the volume ratio of chalk powder are 100: 60, the volume ratio of the material resin of described making enhancement layer, hollow glass bead, sawdust, chalk powder is 100: 40: 40: 40.
5,, it is characterized in that the described back side is three-ply board or woodgrained paper or cloth according to the described method for making simulative woodcut of claim 4.
6, according to the described method for making simulative woodcut of claim 5, the thickness that it is characterized in that described surface layer is that 1～3 millimeter, the thickness of enhancement layer are that 2～5 millimeters, the thickness of packed layer are 10～20 millimeters.
7,, it is characterized in that in the described surface material of preparation, adding an amount of pigment according to the described method for making simulative woodcut of claim 6.