CN1250667C - Dynamic structural adhesive for bridge - Google Patents
Dynamic structural adhesive for bridge Download PDFInfo
- Publication number
- CN1250667C CN1250667C CN 200310105299 CN200310105299A CN1250667C CN 1250667 C CN1250667 C CN 1250667C CN 200310105299 CN200310105299 CN 200310105299 CN 200310105299 A CN200310105299 A CN 200310105299A CN 1250667 C CN1250667 C CN 1250667C
- Authority
- CN
- China
- Prior art keywords
- component
- share
- weight proportion
- parts
- bridge
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention discloses dynamic structural adhesive for a bridge, which is composed of two sets of a first and a second materials by the following weight compounding ratio, wherein the first component comprises 80 to 120 share of epoxy resin, 1 to 2 share of rigid particle flexibilizer-gas phase white charcoal, 0.5 to 2 share of oxidation inhibitor, 0.5 to 1.5 share of ultraviolet absorbent-uv-9, 0.5 to 2 share of active flexibilizer-polysulfide rubber, 2 to 4 share of reactive diluent-501, and 0.5 to 2 share of silane coupling agent-KH-560; the second component comprises 18 to 36 share of end amino polyoxypropylene ether, and 2.4 to 4.0 share of diphenyl guanidine. The present invention is used for sticking a complex fiber cloth to strengthen a bridge in a state of no traffic interruption, and is the structural adhesive with low viscosity in a response type of two components of room temperature solidification agent. The present invention has the characteristics of good mechanical property, high adhesive property, good dynamic resistance and ageing resistance performance, good construction performance, no poison, no pollution, etc.
Description
Technical field
The present invention relates to the structure glue that a kind of building trade is used, relate in particular to a kind of bridge dynamic structure glue that the complex fabric cloth reinforcement bridge is used of under the uninterrupted traffic state, pasting.
Background technology
Existing structure glue is reinforced in the use in bridge structure, finds that weak point is as follows:
1, in use there is following problem in makeup of the imports glue:
1.. curing cross-linking reaction is slow, and the construction time is long, gel does not take place in 2~3 days under cryogenic situation, and cure period, generally more than 10 days, initial adhesion strength was lower, had so not only influenced sticking effect but also had influenced on-site construction operations;
2.. the dynamic physical mechanical property is relatively poor after solidifying, and fragility is big, only is adapted at using under the static conditions.
3.. weather-proof relatively poor with ageing-resistant performance, use the later stage that xanthochromic trend is arranged.
2, in use there is following problem in homemade structure glue:
1.. viscosity is higher, and is poor to the wetting property of complex fabric cloth, influences bonding effect, also is unfavorable for constructing operation simultaneously.
2.. can not adjust working life, and the construction time of most of structure glue is shorter, especially in summer, very short time inner structure glue gelatin phenomenon just takes place, amount of preparation can not be excessive, is unfavorable for large-area construction, when temperature is low the construction time long again, influence the construction period;
3.. it is big equally also to exist fragility, and poor toughness only is adapted at static the use.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of bridge dynamic structure glue at the problems referred to above, and the present invention can be used to paste the complex fabric cloth reinforcement bridge under the uninterrupted traffic state.
Be achieved in that and it is characterized in that it is to be made of by following weight proportion two groups of raw materials of first, second in order to solve the problems of the technologies described above the present invention: wherein in the first component: 80~120 parts of Resins, epoxy; 1~2 part of rigid particles toughner-thermal silica; 0.5~2 part of antioxidant; UV light absorber-uv-90.5~1.5 part; 0.5~2 part of endurable active toughener-thiorubber; Reactive thinner-501 is 2~4 parts; Silane coupling agent-KH-560 is 0.5~2 part; 18~36 parts in solidifying agent in the component B wherein; 2.4~4.0 parts of promotor.
Preparation technology of the present invention is as follows:
One. the preparation of first component:
A. get rigid particles toughner-thermal silica by described weight proportion, thermal silica is placed in the agitator allocates, make it in the pasty state with 4~8 parts acetone; Add the silane coupling agent-KH-560 meet above-mentioned weight proportion again and stir and make the activation of rigid toughening particle, make colloid A;
B. add the reactive thinner-501 that meets described weight proportion after getting oxidation inhibitor and UV light absorber-uv-9 mixing by described weight proportion, solid particulate fully dissolves the formation solution B, preparation complex protection system;
C. get liquid-state epoxy resin by described weight proportion and endurable active toughener-thiorubber is put into another agitator simultaneously, heat, make agitator and inner material temperature thereof remain on 50~60 ℃, stir, make liquid C;
D. the above-mentioned colloid A for preparing and solution B are poured among the liquid C and stirred, the quiet object of back restir in agitator of putting becomes till the translucent liquid of oyster white, promptly gets the first component;
Two. the preparation of component B:
Get by described weight proportion that quiet putting after 35~55 minutes stirs gently in the container that the mixing of solidifying agent and promotor is placed on 65-85 ℃, be cooled to room temperature again, continue to stir 20~40 minutes, promptly get component B;
Three. above-mentioned first component for preparing and component B are mixed, promptly get bridge dynamic structure glue of the present invention.
Advantage of the present invention and effect are:
Bridge dynamic structure glue of the present invention is the structure glue of double-component cold curing agent, low viscosity, response type, it have good mechanical property, bond properties height, anti-dynamically, ageing-resistant performance is excellent, characteristics such as workability is good, and is nontoxic, pollution-free, its advantage is:
1, viscosity is suitable, and is good to the wetting property of complex fabric cloth, increases contact area, improves bonding effect.The curing cross-linking reaction gentleness, heat release is few, and temperature is lower, and it is unrestricted to join the glue amount.Be fit to extensive constructing operation.
2, by active composite toughening to Resins, epoxy, bridge dynamic structure glue not only can under static state be used, and be adapted at using under the vibrational state, its bond properties and physical and mechanical properties all there is not influence, thereby can be under the uninterrupted traffic situation reinforcement bridge, shock-resistant and vibrations excellent performance.
3, by composite epoxy resin solidifying system; Can arbitrarily be adjusted working life according to envrionment temperature, shorten the presetting period, adjust condensate content just, curing reaction course gradient is carried out, the fragility of having improved epoxy resin glue is solidified course.
4, by adjusting curing system, make the dynamic application specific architecture glue of bridge adapt to low-temperature curing, and the operation in wet environment, even carry out the bridge strengthening construction under water and also can use the present invention.
5, shrinking percentage is low, and the shrinking percentage of this glue is 0.2%~0.5%, is 1/2~1/5 of its their like product, and therefore conjugated fibre layer of cloth and the shear-stress between bridge member after the dynamic application specific architecture adhesive curing of bridge is little, not easy to crack; Good stability.
6, weathering resistance is good, has good uvioresistant and weather-proof and aging resistance, acidproof, alkaline-resisting and anti-various media (as oil, kerosene, alcohol, water etc.) excellent performance.Work-ing life is more than 50 years.
7, bridge dynamic structure glue makes the toxicological harmless, pollution-free in construction and use of this bridge dynamic structure glue with its free of contamination protection system.
Embodiment
The present invention is to be a kind of bridge application specific architecture glue of base-material according to Resins, epoxy, it comprises first component and component B, wherein the raw material and the deal of first component and component B are carried out rational allotment, under the uninterrupted traffic situation, pasted the use of complex fabric cloth reinforcement bridge to adapt to bridge under different temperature environments, the wet environment; According to specific embodiment the present invention is further elaborated below:
Embodiment one
The prescription and the weight proportion of bridge dynamic structure glue:
The first component: liquid-state epoxy resin E-44 is 80 parts; Rigid particles toughner-thermal silica is 1 part; Antioxidant-2,6 ditertbutylparacresol is 0.5 part; UV light absorber-uv-9 is 0.5 part; Endurable active toughener-thiorubber is 0.5 part; Reactive thinner-501 is 2 parts; Silane coupling agent-KH-560 is 0.5 part; Component B: holding amino polyoxytrimethylene ether is 18 parts; Vulkacit D is 2.4 parts.
Its preparation method comprises the steps:
One. the preparation of first component:
A. get rigid particles toughner-thermal silica by described weight proportion, thermal silica is placed in the agitator allocates, make it in the pasty state with 4 parts of acetone; Add again and meet described silane coupling agent-KH-560 by weight ratio and stir and make the activation of rigid toughening particle, make colloid A;
B. add the reactive thinner-501 that meets described weight proportion after getting oxidation inhibitor-2,6 ditertbutylparacresol and UV light absorber-uv-9 mixing by described weight proportion, solid particulate fully dissolves the formation solution B, preparation complex protection system;
C. get liquid-state epoxy resin E-44 by described weight proportion and endurable active toughener-thiorubber is put into another agitator simultaneously, heat, keep agitator and inner material temperature thereof to remain on 60 ℃, stir, make liquid C;
D. the above-mentioned colloid A for preparing and solution B are poured among the liquid C and stirred 20 minutes, the quiet object of back restir in agitator of putting becomes till the translucent liquid of oyster white, promptly gets the first component;
Two. the preparation of component B:
Get end amino polyoxytrimethylene ether and vulkacit D by described weight proportion and mix that quiet putting stirs after 35 minutes gently in the container that is placed on 65 ℃, be cooled to room temperature again, continue to stir 40 minutes, promptly get component B;
Three. above-mentioned first component for preparing and component B are mixed, promptly get bridge dynamic structure glue of the present invention.
Embodiment two
The prescription of bridge dynamic structure glue and weight part proportioning:
The first component: liquid-state epoxy resin E-51 is 120 parts; Rigid particles toughner-thermal silica is 2 parts; 2 parts of antioxidants-natural Rosmarinus officinalis; UV light absorber-uv-9 is 1.5 parts; Endurable active toughener-thiorubber is 2 parts; Reactive thinner-501 is 4 parts; Silane coupling agent-KH-560 is 2 parts; Component B: the amino polyoxytrimethylene ether of solidifying agent-end is 36 parts; Promotor-vulkacit D is 4 parts.
Its preparation method comprises the steps:
One. the preparation of first component:
A. get rigid particles toughner-thermal silica by described weight proportion, thermal silica is placed in the agitator allocates, make it in the pasty state with 6 parts acetone; Add the silane coupling agent-KH-5 60 meet described weight proportion again and stir and make the activation of rigid toughening particle, make colloid A;
B. add the reactive thinner-501 that meets described weight proportion after getting oxidation inhibitor-natural Rosmarinus officinalis and UV light absorber-uv-9 mixing by described weight proportion, solid particulate fully dissolves the formation solution B, preparation complex protection system;
C. get liquid-state epoxy resin E-51 by described weight proportion and endurable active toughener-thiorubber is put into another agitator simultaneously, heat, keep agitator and inner material temperature thereof to remain on 55 ℃, stir, make liquid C;
D. the above-mentioned colloid A for preparing and solution B are poured among the liquid C and stirred 30 minutes, the quiet object of back restir in agitator of putting becomes till the translucent liquid of oyster white, promptly gets the first component;
Two. the preparation of component B:
Amino polyoxytrimethylene ether of the end that will take by weighing in described ratio and vulkacit D mix that quiet putting after 40 minutes stirs gently in the container that is placed on 85 ℃, are cooled to room temperature again, continue to stir 30 minutes, promptly get component B;
Three. above-mentioned first component for preparing and component B are mixed, promptly get bridge dynamic structure glue of the present invention.
Embodiment three
The prescription and the weight proportion of bridge dynamic structure glue:
The first component: liquid-state epoxy resin E-51 is 100 parts; 1.5 parts of rigid particles toughner-thermal silicas; 1.5 parts of antioxidant-2,6 ditertbutylparacresols; UV light absorber-uv-9 is 1 part; Endurable active toughener-thiorubber is 1 part; Reactive thinner-501 is 3 parts; Silane coupling agent-KH-560 is 1.5 parts; Component B: the amino polyoxytrimethylene ether of solidifying agent-end is 20 parts; Promotor-vulkacit D is 2 parts.
Its preparation method comprises the steps:
One. the preparation of first component:
A. get rigid particles toughner-thermal silica by described weight proportion, thermal silica is placed in the agitator allocates, make it in the pasty state with 8 parts acetone; Add the silane coupling agent-KH-5 60 meet described weight proportion again and stir and make the activation of rigid toughening particle, make colloid A;
B. add the reactive thinner-501 that meets described weight proportion after getting oxidation inhibitor-2,6 ditertbutylparacresol and UV light absorber-uv-9 mixing by described weight proportion, solid particulate fully dissolves the formation solution B, preparation complex protection system;
C. get liquid-state epoxy resin E-51 by described weight proportion and endurable active toughener-thiorubber is put into another agitator simultaneously, heat, keep agitator and inner material temperature thereof to remain on 5 ℃, stir, make liquid C;
D. the above-mentioned colloid A for preparing and solution B are poured among the liquid C and stirred 15 minutes, the quiet object of back restir in agitator of putting becomes till the translucent liquid of oyster white, promptly gets the first component;
Two. the preparation of component B:
Amino polyoxytrimethylene ether of the end that will take by weighing in described ratio and vulkacit D mix that quiet putting after 40 minutes stirs gently in the container that is placed on 85 ℃, are cooled to room temperature again, continue to stir 30 minutes, promptly get component B;
Three. above-mentioned first component for preparing and component B are mixed, promptly get bridge dynamic structure glue of the present invention.
Embodiment four
The prescription and the weight proportion of bridge dynamic structure glue:
The first component: liquid-state epoxy resin E-44 is 90 parts; Rigid particles toughner-thermal silica is 1.8 parts; Antioxidant-2,6 butyl p-cresol is 1 part; UV light absorber-uv-9 is 1 part; Endurable active toughener-thiorubber is 1 part; Reactive thinner-501 is 2.5 parts; Silane coupling agent-KH-560 is 1 part; Component B: holding amino polyoxytrimethylene ether is 24 parts; Vulkacit D is 2.6 parts.
Its preparation method is with embodiment three.
Embodiment five
The prescription and the weight proportion of bridge dynamic structure glue:
The first component: liquid-state epoxy resin E-44 is 110 parts; Rigid particles toughner-thermal silica is 1.2 parts; Antioxidant-2,6 butyl p-cresol is 1.3 parts; UV light absorber-uv-9 is 1.3 parts; Endurable active toughener-thiorubber is 1.3 parts; Reactive thinner-501 is 3.2 parts; Silane coupling agent-KH-560 is 1.2 parts; Component B: holding amino polyoxytrimethylene ether is 25 parts; Vulkacit D is 2.7 parts.
Its preparation method is with embodiment three.
Embodiment six
The prescription and the weight proportion of bridge dynamic structure glue:
The first component: liquid-state epoxy resin E-51 is 100 parts; Rigid particles toughner-thermal silica is 1.2 parts; 1.3 parts of antioxidants-natural Rosmarinus officinalis; UV light absorber-uv-9 is 1.3 parts; Endurable active toughener-thiorubber is 1.3 parts; Reactive thinner-501 is 3.2 parts; Silane coupling agent-KH-560 is 1.2 parts; Component B: modification Ammonia solidifying agent 5784 is that 30 parts of DMP30 are 3 parts.
Its preparation method is with embodiment two.
Embodiment seven
The prescription and the weight proportion of bridge dynamic structure glue:
The first component: liquid-state epoxy resin E-51 is 100 parts; Rigid particles toughner-thermal silica is 1.6 parts; 0.8 part of antioxidant-natural Rosmarinus officinalis; UV light absorber-uv-9 is 0.8 part; Endurable active toughener-thiorubber is 1.6 parts; Reactive thinner-501 is 3.2 parts; Silane coupling agent-KH-560 is 1.6 parts; Component B: holding amino polyoxytrimethylene ether is 36 parts; Vulkacit D is 3.5 parts.
Its preparation method is with embodiment two.
Embodiment eight
The prescription and the weight proportion of bridge dynamic structure glue:
The first component: liquid-state epoxy resin E-51 is 100 parts; Rigid particles toughner-thermal silica is 1.2 parts; 1.3 parts of antioxidants-natural Rosmarinus officinalis; UV light absorber-uv-9 is 1.3 parts; Endurable active toughener-thiorubber is 1.3 parts; Reactive thinner-501 is 3.2 parts; Silane coupling agent-KH-560 is 1.2 parts; Component B: holding amino polyoxytrimethylene ether is 36 parts; Vulkacit D is 3.6 parts.
Its preparation method is with embodiment two.
The mixed initial viscosity of first, component B is 0.8 ± 0.05Pa.s, the tensile strength of cured glue is greater than 45MPa, ultimate compression strength is greater than 80MPa, bending strength is greater than 50MPa, tensile shear strength is greater than 10MPa, just drawing cohesive strength greater than 2.5Mpa, and be not less than and be reinforced the concrete tensile strength standard value.
Table one: embodiment one, two, three, four and performance test data domestic, external like product
Experimental project | Experiment condition | External product | Home products | Embodiment one | Embodiment two | Embodiment three | Embodiment four |
Tensile strength (Mpa) | Normal temperature 7 days | 42.0 | 39.2 | 59.2 | 52.3 | 53.5 | 52.9 |
Tensile modulus (Mpa) | Normal temperature 7 days | 3.01×10 3 | 2.94×10 3 | 3.46×10 3 | 3.24×10 3 | 3.21×10 3 | 3.19×10 3 |
Elongation at break | Normal temperature 7 days | 1.3 | 1.6 | 2.2 | 2.1 | 1.9 | 1.9 |
Compressive strength (Mpa) | Normal temperature 7 days | 105.0 | 95.0 | 102.0 | 102.0 | 101.0 | 99.0 |
Flexural strength (Mpa) | Normal temperature 7 days | 76.0 | 68.0 | 92.1 | 91.6 | 92.3 | 91.0 |
Tensile shear strength | Normal temperature 7 days | 10.2 | 10.5 | 10.6 | 11.2 | 11.1 | 1.02 |
Cloth and concrete cohesive strength | Normal temperature 3 days | The C4 concrete destroys | The C4 concrete destroys | The C4 concrete destroys | The C4 concrete destroys | The C4 concrete destroys | The C4 concrete destroys |
The artificial tensile strength (Mpa) of quickening | GB/T16422-1999 artificial accelerated aging 500 hours | 38.3 | 36.1 | 59.6 | 52.3 | 54.1 | 54.0 |
The artificial accelerated aging cohesive strength | GB/F16422-1999 artificial accelerated aging 500 hours | The C4 concrete destroys | 2.6Mpa cloth and the fracture of concrete contact surface | The C4 concrete destroys | The C4 concrete destroys | The C4 concrete destroys | The C4 concrete destroys |
Claims (4)
1. bridge dynamic structure glue is characterized in that it is to be made of by following weight proportion two groups of raw materials of first, second:
The first component:
Bisphenol-A diglycidyl ether type epoxy resin 80-120 part
Rigid particles toughner-thermal silica 1-2 part;
Antioxidant 0.5-2 part;
2-hydroxyl-4-methoxy benzophenone 0.5-1.5 part;
Endurable active toughener-thiorubber 0.5-2 part;
Epoxy propane butyl ether 2-4 part;
γ-Racemic glycidol oxidation propyl trimethoxy silicane 0.5-2 part;
Component B:
Hold amino polyoxytrimethylene ether 18-36 part;
Vulkacit D or 2,4,6-three (dimethylamino methyl) phenol 2.4-4.0 part;
Above-mentioned raw materials uses proportioning to be: first component: component B=2.5-4.5: 1.
2. bridge dynamic structure glue according to claim 1 is characterized in that described dihydroxyphenyl propane Racemic glycidol ether type epoxy is E-44 liquid-state epoxy resin or E-51 liquid-state epoxy resin.
3. bridge dynamic structure glue according to claim 1 is characterized in that described antioxidant can be 2,6-di-t-butyl-4-cresols or natural Rosmarinus officinalis.
4. the preparation method of a bridge dynamic structure glue is characterized in that it is to be made of by following weight proportion two groups of raw materials of first, second:
The first component:
Bisphenol-A diglycidyl ether type epoxy resin 100-120 part
Rigid particles toughner-thermal silica 1-2 part;
Antioxidant 0.5-2 part;
2-hydroxyl-4-methoxy benzophenone 0.5-1.5 part;
Endurable active toughener-thiorubber 0.5-2 part;
Epoxy propane butyl ether 2-4 part;
γ-glycidyl ether propyl trimethoxy silicane 0.5-2 part;
Component B:
Hold amino polyoxytrimethylene ether 18-36 part;
Vulkacit D or 2,4,6-three (dimethylamino methyl) phenol 2.4-4.0 part;
Above-mentioned raw materials uses proportioning to be: first component: component B=2.5-4.5: 1;
Its preparation method comprises the following steps:
One. the preparation of first component:
A. get rigid particles toughner-thermal silica by described weight proportion, thermal silica is placed in the agitator allocates, make it in the pasty state with the acetone of 4-8 part; Add the γ-glycidyl ether propyl trimethoxy silicane meet described weight proportion again and stir and make the activation of rigid toughening particle, make colloid A;
B. add the epoxy propane butyl ether that meets described weight proportion after getting antioxidant and 2-hydroxyl-4-methoxy benzophenone mixing by described weight proportion, solid particulate fully dissolves the formation solution B, preparation complex protection system;
C. get liquid bisphenol A diglycidyl ether-type epoxy resin by described weight proportion and endurable active toughener-thiorubber is put into another agitator simultaneously, heat, make agitator and inner material temperature thereof remain on 50~60 ℃, stir, make liquid C;
D. the above-mentioned colloid A for preparing and solution B are poured among the liquid C and stirred, the quiet object of back restir in agitator of putting becomes till the translucent liquid of oyster white, promptly gets the first component;
Two. the preparation of component B:
Get the amino polyoxytrimethylene ether of solidifying agent end and promotor vulkacit D or 2 by described weight proportion, 4,6-three (dimethylamino methyl) phenol mixes in the container be placed on 65-85 ℃ and stirs gently after the quiet 35-55 of putting minute, is cooled to room temperature again, continue to stir 20-40 minute, promptly get component B;
Three. above-mentioned first component for preparing and component B are mixed, promptly get bridge dynamic structure glue of the present invention.