CN1239130A - Flame-retarding oily binder - Google Patents
Flame-retarding oily binder Download PDFInfo
- Publication number
- CN1239130A CN1239130A CN 98102077 CN98102077A CN1239130A CN 1239130 A CN1239130 A CN 1239130A CN 98102077 CN98102077 CN 98102077 CN 98102077 A CN98102077 A CN 98102077A CN 1239130 A CN1239130 A CN 1239130A
- Authority
- CN
- China
- Prior art keywords
- flame
- retarding
- binding agent
- rock wool
- tankage
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A flame-retarding oily binder is prepared from waste polystyrene resin (20-40 portions), toluene (30-50), leftover generated during production of stearic acid (3-45), beta-triester phosphate (3-15) and rock wool (10-20), and features high adhesion, no pollution and flame-retarding nature. It can be used as the binder of decorative materials or for anti-leakage purpose of roof.b
Description
The present invention relates to a kind of flame-retarding oily binder, be applicable to the bonding of house decorative material, the roof waterproof leak stopping.
At present, many technology that prepare binding agent with waste polystyrene foam are arranged, its majority is made solvent with toluene, dimethyl phthalate is made softening agent, the not anti-extraction of this binding agent has just formed a kind of light face bonding after the solvent of binding agent and solvent-type plasticizer are extracted out, promptly form very crisp tack coat, therefore it is insecure to bond, not anti-aging yet, when construction, require adhesive surface very strict simultaneously, during as kitchen or lavatory bonding ceramic tile, originally be coated with paint as metope and just be difficult for construction, and must shovel with solvent or diluent flush away paint or with baked wheaten cake or with scoop, perhaps scutching point on metope, therefore require great effort very much, bother again, this kind binding agent viscosity is big during construction, and operability is bad, free-running property is poor, again contaminate environment.
Purpose of the present invention provides a kind of flame-retarding oily binder for the shortcoming that overcomes above-mentioned prior art just with deficiency, thereby improves operability and adhesive property.
The objective of the invention is to realize by following technical proposal:
A kind of flame-retarding oily binder is characterized in that it is to be made by the following weight proportion raw material:
Deposed polystyrene resin 20-40 branch
Toluene 30-50 part
Produce tankage 3-45 part of lipid acid
Phosphoric acid β three ester 3-15 parts
Rock wool powder 10-20 part
Wherein the deposed polystyrene resin is waste polystyrene foam, deposed polystyrene plate, waste organic glass tankage, and the rock wool powder directly is below the 0.1mm.
The deposed polystyrene resin that the present invention adopts, it is a kind of waste material, can reduce white pollution after the utilization, and the tankage of production lipid acid, it is a kind of a kind of waste material that contains siccative oil, promptly be that oil chemistry factory produces oleic acid and stearic tankage, be commonly referred to as oil foot, it is the flowability that a kind of softening agent can improve binding agent, top layer paint to adhesive surface has good solvency action simultaneously, makes binding agent firm, does not therefore need to remove adhesive surface paint, phosphoric acid β three esters are a kind of fire retardants, effluent Nankai envelope chemical plant, great river produces, and it can make binding agent prevent to catch fire, and the rock wool powder also has the mineral wool of title powder, it has the heat-insulation and heat-preservation effect, makes the interior decoration environment better.
The preparation method of binding agent of the present invention:
The deposed polystyrene resin pack into retort with adding the tankage of producing lipid acid after the toluene dissolving again, phosphoric acid β three esters, the rock wool powder gets final product after stirring.
Compared with the prior art binding agent of the present invention has following advantage and effect:
A) binding agent of the present invention adopts multiple waste material, can turn waste into wealth, and reduces the pollution of refuse to environment simultaneously again;
B) preparation method is simple, and raw material sources are extensive, and cost is low, and set time is short;
C) can directly bond, not need metope is carried out special processing, when especially there is paint on the top layer, also do not handle and to bond, and cohesiveness is good;
D) consumption is few, easy to use, good operability, and only needing to coat a very thin layer binder with scraper at two adhesive surfaces can bond.
Embodiment 1
30kg toluene is added in the retort, add again after the 20kg waste polystyrene foam dissolves, add the tankage that 3kg produces lipid acid again, 5kg phosphoric acid β three esters and 20kg particle diameter 0.1mm rock wool powder, stirring promptly can be finished product.
Embodiment 2
45kg toluene is added in the retort, add again after 30kg waste organic glass tankage dissolve, add 25kg again and produce the lipid acid tankage, 8kg phosphoric acid β three esters and 15kg particle diameter 0.1mm rock wool powder, stirring promptly can be finished product.
Embodiment 3
50kg toluene is added in the retort, add again after 40kg deposed polystyrene sheet material dissolves, add the tankage that 45kg produces lipid acid again, 10kg phosphoric acid β three esters and 10kg particle diameter 0.1mm rock wool powder, stirring is finished product.
Claims (3)
1. flame-retarding oily binder is characterized in that it is to be made by the following weight proportion raw material:
Deposed polystyrene resin 20-40 branch
Toluene 30-50 part
Produce tankage 3-45 part of lipid acid
Phosphoric acid β three ester 3-15 parts
Rock wool powder 10-20 part
2. binding agent according to claim 1 is characterized in that described deposed polystyrene resin is waste polystyrene foam, deposed polystyrene plate, waste organic glass tankage.
3. binding agent according to claim 1 is characterized in that described rock wool powder is directly for below the 0.1mm.