CN1227093C - Ball-driving face plate bonding method of golf wood club head - Google Patents
Ball-driving face plate bonding method of golf wood club head Download PDFInfo
- Publication number
- CN1227093C CN1227093C CNB001072498A CN00107249A CN1227093C CN 1227093 C CN1227093 C CN 1227093C CN B001072498 A CNB001072498 A CN B001072498A CN 00107249 A CN00107249 A CN 00107249A CN 1227093 C CN1227093 C CN 1227093C
- Authority
- CN
- China
- Prior art keywords
- bar head
- batting panel
- capsule body
- panel
- club head
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a method for bonding a batting panel of a wood golf club head. A batting panel covers the opening position of a casing of a club head, and the shape of the club head of a wood club is combined by pressing location or point welding location. A circle of welding materials are arranged along the connecting edge of the panel and the casing on the surface of the club head. The melting point of the welding materials is lower than the melting points of the casing and the panel, and then, the club head is arranged and heated in a high temperature furnace, so that the welding materials are melted and infiltrated between the panel and the casing by capillarity. An annular welding layer is formed on an interface of the panel and the casing after the welding materials are coagulated, and an annular welding strip for welding the panel and the casing is formed on the edge of the opening at the inner part of the club head. A circle of welding materials can be welded along the connecting edge on the surface of the club head after the club head is taken out from the inside of the furnace, and finally, the surface is smooth by grinding beautification.
Description
Technical field
The present invention is relevant with the method for making of golf driver head, particularly about a kind of batting panel bonding method of golf club head.
Background technology
Golf club head now mostly is the metallic article of hollow greatly, the normal a kind of method for making that adopts of industry is as follows at present: make one earlier and slightly be bar head shapes and positive housing with opening, and a shape is to batting panel that should opening, again this panel cover is bonded to this opening part on the housing, then along the circle that freezes of the seam between panel and housing, make the two weldering form a hollow stem head, remake Surface Machining at last and form finished product.Before take off in the processing procedure, batting panel is that mat generally freezes and is engaged to bar head capsule body, yet the fusion of welding rod is difficult for stable control when freezing, make that the weldering knot layer on the girth joint often is not a well-balanced annular, the part, composition surface may still have the space, the part then may because of fused solution too much drip form the outer weight of expection and influence bar head precision to back side of panel and condense into agglomerate.
Summary of the invention
Purport of the present invention is in solving aforementioned scarce fraud, and promptly its main purpose is providing a kind of batting panel bonding method of golf club head, has splendid joint quality, and can keep the precision of bar head.
Take off purpose for before reaching, the batting panel bonding method of golf club head provided by the invention is to prepare a bar head capsule body and a batting panel earlier, wherein this housing generally is the shape of club head, hollow, be formed with an opening in the positive position of corresponding bar head, the shape of this panel is corresponding and is slightly larger than this opening; Then this panel is covered on the opening part of this housing and gives the location temporarily, make the shape of the two synthetic golf club head; Then the edge that connects at bar head surface upper edge panel and housing installs a circle wlding, and the fusing point of this wlding is the material fusing point that is lower than this housing and this panel; Afterwards the bar head is inserted and be heated to predetermined temperature in the high temperature furnace, make wlding fusion and mat capillarity infiltrate joint gap, the bar head is taken out in appropriateness cooling back, and the circle that can freeze in its surface along seam again makes joint smooth smooth with Surface Machining at last.
Wherein in abovementioned steps a, make this bar head capsule body forward in the some positioning strips that protrude out of this opening edge integral shape; In abovementioned steps b, this batting panel is being covered to the opening part of this bar head capsule body, to the pressurization of these positioning strips, this positioning strip tail end is colluded toward inner bending be pressed on this batting panel periphery, make this batting panel temporarily be positioned on this bar head capsule body; In abovementioned steps e, grind and remove these positioning strips.
Wherein in abovementioned steps b, this batting panel is being covered to the opening part of this bar head capsule body, at this batting panel periphery number place that freezes at interval, this batting panel temporarily is being positioned on this bar head capsule body in the mode of spot welding.
Wherein between abovementioned steps d and step e, on the half-finished surface of bar head, connect the edge circle that freezes along this batting panel and this bar head capsule body.
Wherein in abovementioned steps a, make this bar head capsule body, make this batting panel with titanium alloy with stainless steel; In abovementioned steps c, this wlding is selected gluey money base wlding for use; In abovementioned steps d, heating-up temperature is about 1050 ℃, is about 60 minutes heat time heating time.
Wherein in abovementioned steps a, make this batting panel with titanium alloy; Between abovementioned steps d and step e, bar head semi-finished product are inserted in the welding chamber that is filled with argon gas, connect the edge circle that freezes in its surface along this batting panel and this bar head capsule body.
Description of drawings
Now after lifting graphic being described in more detail in of preferred embodiment cooperation, wherein:
Fig. 1 is the prepared bar head capsule body of the present invention's one preferred embodiments and the stereogram of batting panel;
Fig. 2 shows to cover the batting panel among Fig. 1 to bar head capsule body and mat is pressed aspect after work gives the location temporarily;
Fig. 3 is the cutaway view along 3-3 hatching line among Fig. 2;
Fig. 4 is the aspect after the bar head semi-finished product upper edge batting panel periphery that is shown in Fig. 2 installs a circle wlding;
Fig. 5 is the cutaway view along 5-5 hatching line among Fig. 4;
Fig. 6 corresponding diagram 5 only is the aspect after signal wlding melting after heating is permeated and solidified;
Fig. 7 is the finished product stereogram that shows by the golf club head of state after Surface Machining of Fig. 6; And
Fig. 8 is the cutaway view along 8-8 hatching line among Fig. 7.
The specific embodiment
The batting panel bonding method of the golf club head that a preferred embodiment of the present invention provides includes the following step:
Step a: see also Fig. 1, prepare a bar head capsule body 10 and a batting panel 20 earlier, wherein this housing 10 forms with the stainless steel casting, profile generally is the golf club head shape, inner hollow, be formed with an opening 12 at the positive position of corresponding bar head, housing 10 has several positioning strips that protrude out 14 forward at these opening 12 edge integral shapes; This batting panel 20 is made (can also maraging steel (maraging steel) or other metal material make) with titanium alloy, and shape is corresponding and be slightly larger than opening 12 shapes on this housing 10;
Step b: the batting panel 20 of preparation is covered opening 12 places to bar head capsule body 10, enclose by these positioning strips 14 and be stuck in batting panel 20 peripheries, panel 20 can the accurately involutory unlikely skew in the precalculated position; Then, its tail end is colluded toward inner bending be pressed on batting panel 20 peripheries, use that panel 20 temporarily is positioned to make on the housing 10 the unlikely displacement that comes off, as shown in Figures 2 and 3 these positioning strip 14 pressurizations on the housing 10;
Step c: on the half-finished surface of bar head of previous step gained,, install a circle hard solder wlding 30 in right amount, as Fig. 4 and shown in Figure 5 along on the girth joint of 10 of this batting panel 20 and bar head capsule bodies; This wlding 30 be with the metal of housing 10 and panel 20 unlike materials (as silver, copper, nickel, aluminium ... Deng) powder modulation forms, the money base wlding of commonly using is adopted in this enforcements, is gluey, and it is standby to can be made into strip, can be stained with and show on panel 20 and housing 10;
Steps d: the bar head semi-finished product that will be coated with wlding 30 are inserted vacuum-pumping or are had in the high temperature furnace of inert gas shielding, be heated to predetermined temperature, this heating-up temperature is the fusing point that is higher than this wlding 30, and be lower than the material fusing point of bar head capsule body 10 and batting panel 20, particularly, the fusing point of present embodiment middle shell 10 (stainless steel) and panel 20 (titanium alloy) is about 1600 and 1500 ℃ respectively, and the fusing point of money base wlding is 800-1050 ℃, present embodiment is to be heated to 1050 ℃, and heat time heating time is about 60 minutes; When wlding 30 melted by heating, the slit that membership capillarity infiltration panel 20 and housing are 10, moisten full composition surface equably, and and then to infiltrate housing 10 inner and agglutinate in this opening 12 rims, see also Fig. 6, after the cooled and solidified, wlding 30 can connect in the ring-type of panel 20 and housing 10 and form ring-type weldering knot layer 32 on the face, and can form section ring-type weldering knot bar 34 general triangular in shape at these opening 12 rims, the hypotenuse of these weldering knot bar 34 sections is the arc concavity, and other dual side-edge moistens the work weldering respectively to be tied on housing 10 and panel 20; Through after suitable cool time, the bar head semi-finished product of finishing hard solder are taken out in stove;
Step e: grind the wlding residue of removing batting panel 20 peripheries on the bar head surface, and previous positioning strip 14 in order to temporary transient positioning panel 20, make panel 20 and housing 10 joints smooth smooth, remake polishing and application etc. afterwards and modify processing, finish the golf club head finished product, as shown in Figures 7 and 8.
That takes off before comparing to commonly uses bonding method (at the bar head surface along the batting panel periphery circle that freezes), panel bonding method provided by the invention has preferable bond strength significantly, because of can evenly infiltrating 10 of panel 20 and housings after these wlding 30 fusions among the present invention, solidify the back and form a complete uniform circular weldering knot layer 32, be better than commonly using the desultory weldering knot layer of welding gained; And this wlding 30 can also more can significantly be strengthened bond strength at the inner ring-type weldering knot bar 34 that forms a weldering crust body 10 and panel 20 of bar head.Moreover, the Hollow wooden rod bar head that mat the present invention makes, inside is also very white and pure well-balanced, please consult Fig. 8 once more, this weldering knot bar 34 of bar head inside is that the wlding fused solution agglutinates to become in the corner naturally, the uniform ring bar that is corresponding batting panel 20 profiles can not make the counterweight of panel 20 or bar head unbalance, can guarantee the precision of golf driver head.
Before take off among the embodiment, integrated these positioning strips 14 on the bar head capsule body 10 are in order to temporarily panel 20 being positioned on the housing 10 as previously mentioned, guarantee the two panel 20, housing 10 at the accurate involutory hard solder joint of accepting down, to be joined finish give again worn; Only the means of temporary transient place hitting panel are not limited to the method for taking off among the present invention, bar head capsule body these positioning strips that also can be shaped for example, when batting panel covers to this housing, at this faceplate perimeter number place that freezes at interval, make the several weldering nodes of batting panel mat temporarily be positioned on the housing in the mode of spot welding; Can use welding rod during spot welding, the weldering of mat welding rod fusion after coagulation is tied the two, also can not use welding rod, directly makes panel or housing partial melting and welding each other; Behind the temporary transient location of batting panel, smear a circle wlding along faceplate perimeter equally, to send into again and carry out hard solder in the high temperature furnace, the cooling back is taken out and is done surface processing, finishes bar head finished product.
For asking higher bond strength, the present invention also can be after finishing hard solder (after the abovementioned steps d), on the half-finished surface of bar head, connect the edge circle that freezes along panel and housing, make the surface go up the two joint partial melting and welding, so can increase by one connected structure again, make panel more firm with combining of housing.If take off embodiment before complying with, batting panel is made with titanium, reacts and goes bad because titanium at high temperature easily produces with oxygen element etc., carries out the aforementioned operation of freezing so be preferably in vacuum or have (for example to be filled with in the welding chamber of argon gas) under the inert gas shielding.
Claims (5)
1. the batting panel bonding method of a golf club head is characterized in that, includes the following step:
A. prepare a bar head capsule body and a batting panel, wherein this bar head capsule body is a metal material, generally is the shape of golf club head, hollow, be formed with an opening in the positive position of corresponding bar head, this batting panel also be a metal material, and the shape correspondence also is slightly larger than the opening of this housing;
B. this batting panel among the step a is covered on the opening part of this bar head capsule body and gives the location temporarily, the shape of synthetic golf club head;
C. on the half-finished surface of bar head that step b draws, install a circle wlding along the edge that connects of this batting panel and this bar head capsule body, the fusing point of this wlding is lower than the fusing point of the material of this bar head capsule body and this batting panel;
The bar head semi-finished product that d draws step c are inserted in the high temperature furnace and are heated, and heating-up temperature is higher than the fusing point of this wlding, and are lower than the fusing point of the material of this bar head capsule body and this batting panel; Through after suitable heat time heating time and cool time, the soldering tip semi-finished product are taken out in stove;
E. bar head semi-finished product are done surface processing, make on the bar head surface this batting panel and this bar head capsule body joint smooth smooth;
Wherein in abovementioned steps a, make this bar head capsule body forward in the some positioning strips that protrude out of this opening edge integral shape; In abovementioned steps b, this batting panel is being covered to the opening part of this bar head capsule body, to the pressurization of these positioning strips, this positioning strip tail end is colluded toward inner bending be pressed on this batting panel periphery, make this batting panel temporarily be positioned on this bar head capsule body; In abovementioned steps e, grind and remove these positioning strips.
2. the batting panel bonding method of golf club head according to claim 1, it is characterized in that, wherein in abovementioned steps b, this batting panel is being covered to the opening part of this bar head capsule body, at this batting panel periphery number place that freezes at interval, this batting panel temporarily is positioned on this bar head capsule body in the mode of spot welding.
3. the batting panel bonding method of Gao Er days according to claim 1 and 2 club heads is characterized in that, wherein between abovementioned steps d and step e, on the half-finished surface of bar head, connects the edge circle that freezes along this batting panel and this bar head capsule body.
4. the batting panel bonding method of golf club head according to claim 1 is characterized in that, wherein in abovementioned steps a, makes this bar head capsule body with stainless steel, makes this batting panel with titanium alloy; In abovementioned steps c, this wlding is selected gluey money base wlding for use; In abovementioned steps d, heating-up temperature is about 1050 ℃, is about 60 minutes heat time heating time.
5. the batting panel bonding method of golf club head according to claim 1 is characterized in that, wherein in abovementioned steps a, makes this batting panel with titanium alloy; Between abovementioned steps d and step e, bar head semi-finished product are inserted in the welding chamber that is filled with argon gas, connect the edge circle that freezes in its surface along this batting panel and this bar head capsule body.