CN1215072A - Tempered porcelain-imitation paint - Google Patents
Tempered porcelain-imitation paint Download PDFInfo
- Publication number
- CN1215072A CN1215072A CN 97106666 CN97106666A CN1215072A CN 1215072 A CN1215072 A CN 1215072A CN 97106666 CN97106666 CN 97106666 CN 97106666 A CN97106666 A CN 97106666A CN 1215072 A CN1215072 A CN 1215072A
- Authority
- CN
- China
- Prior art keywords
- water
- coating
- polyvinyl alcohol
- aluminium silicate
- phenylcarbimide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a wall coating formed from polyvinyl alcohol, calcium carbonate, formamide and aluminium silicate, etc.. Said wall coating features high hardness, high degree of finish, water-proofing, fire-resisting, resistance to weathering and low cost.
Description
The present invention relates to a kind of building wall coating, particularly a kind of steel ceramics-like coating.
The coating of Xiao Shouing is general in the market adopts water miscible organic high molecular polymer as adhesive substance, easy and metope disengaging behind the chance water, and organic high molecular polymer easily stays cut as its difference of hardness of adhesive substance.As wallcovering, its result of use is not good.
The purpose of this invention is to provide a kind of hardness height, smooth, water-fast, high temperature resistant, corrosion-resistant, wallcovering that cost is low.
The object of the present invention is achieved like this:
Under normal pressure and hot conditions, in reactor, add polyvinyl alcohol, lime carbonate, three magnesium oxide, four silicon oxide crystalline hydrates, methane amide, pure aluminium silicate, 4.4 ＇-diaminobenzene ethene disulfonic acid phenylcarbimide, n-nonanoic acid, formaldehyde, ammoniacal liquor and water successively, stirred 30～40 minutes, rotating speed is 70 ± 5 rev/mins, promptly gets product of the present invention.
In composition of the present invention, polyvinylalcohol microsphere is water-soluble, and this composition has improved the water tolerance that is coated with product in the coating preparation.Lime carbonate is as a kind of filler, super quality and competitive price.Three magnesium oxide, four silicon oxide crystalline hydrate light weights, exquisiteness are used to improve the levelling property of filming, and make film coated surface smooth.Methane amide has fabulous corrosion-resistant, high thermal resistance, is used for coating and makes it become a kind of refractory materials.Pure aluminium silicate is a kind of inexpensive coloured material, and it is heat-resisting, fast light, weathering resistance is all good, can make the coating conversion go out various colors.4,4 ＇-diaminobenzil disulfonic acid phenylcarbimide absorbs the ultraviolet ray in daylight or other light source in coating, send bluish voilet or cyanic colours fluorescence.
Compare with existing coating, steel ceramics-like coating of the present invention has the hardness height, film coated surface is highly polished, waterproof, fire prevention, weather resistance and the low advantage of cost.
Embodiment (one)
Under 1 normal atmosphere and 25 ℃ of conditions, in reactor, add following material by weight percentage successively, stirred 32 minutes, rotating speed is 72 rev/mins, promptly gets product of the present invention, wherein each substances in percentage by weight is as follows:
Polyvinyl alcohol: 0.15%, lime carbonate: 17%,
Three magnesium oxide, four silicon oxide crystalline hydrates: 60%, methane amide: 0.02%,
Pure aluminium silicate: 0.08%,
4,4 ＇-diaminobenzil disulfonic acid phenylcarbimide: 0.05%
N-nonanoic acid: 0.2%, formaldehyde: 0.3%, ammoniacal liquor: 0.2%, surplus is a water.
Embodiment (two)
Other conditions are identical with embodiment (), and wherein each substances in percentage by weight is as follows:
Polyvinyl alcohol: 0.2%, lime carbonate: 20%,
Three magnesium oxide, four silicon oxide crystalline hydrates: 40%, methane amide: 0.04%,
Pure aluminium silicate: 0.06%,
4,4 ＇-diaminobenzil disulfonic acid phenylcarbimide: 0.08%
N-nonanoic acid: 0.3%, formaldehyde: 0.4%, ammoniacal liquor: 0.4%, surplus is a water.
Claims (1)
1. steel ceramics-like coating, be made up of polyvinyl alcohol, lime carbonate, three magnesium oxide, four silicon oxide crystalline hydrates, methane amide, pure aluminium silicate, 4.4 ＇-diaminobenzil disulfonic acid phenylcarbimide, n-nonanoic acid, formaldehyde, ammoniacal liquor and water, it is characterized in that: wherein each substance weight per-cent is:
Polyvinyl alcohol: 0.1～0.5%,
Lime carbonate: 10～30%,
Three magnesium oxide, four silicon oxide crystalline hydrates: 30～60%,
Methane amide: 0.01～0.05%,
Pure aluminium silicate: 0.01～0.1%,
4,4 ＇-diaminobenzil disulfonic acid phenylcarbimide: 0.01～0.1%
N-nonanoic acid: 0.1～0.5%,
Formaldehyde: 0.1～0.5%,
Ammoniacal liquor: 0.1～0.5%,
Surplus is a water.