CN1212280A - Gasfied ground coke inorganics activaled binding formed coke and its processing method - Google Patents
Gasfied ground coke inorganics activaled binding formed coke and its processing method Download PDFInfo
- Publication number
- CN1212280A CN1212280A CN 97116458 CN97116458A CN1212280A CN 1212280 A CN1212280 A CN 1212280A CN 97116458 CN97116458 CN 97116458 CN 97116458 A CN97116458 A CN 97116458A CN 1212280 A CN1212280 A CN 1212280A
- Authority
- CN
- China
- Prior art keywords
- coke
- inorganics
- lime
- formed coke
- coke breeze
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a moulding process of powdered coke, and is characterized by that it uses the gasified powdered coke and industrial lime and gypsum as inorganic activating agent, through the processes of pulverizing, digestion, adding water, mixing and kneading and pressure moulding, to obtain the invented inorganics-activated bonded moulded coke with low cost and extensive source as well as high strength, good water resistance, thermal stability and reaction property. At the same time it only has need of curing under the condition of room temp., has no need of drying or other curing equipment, so that it can save a lot of energy source and funds, and said product is a high-quality industrial raw material and civil fuel.
Description
The present invention relates to a kind of moulding process and technology of coke powder, particularly a kind of inorganics of the coke breeze that gasifies activates bonding formed coke and technology thereof.
In recent years, the fine coal gas producing technology more and more is subject to people's attention, and simultaneously, fluidized-bed coke carried heat coal gasifying process is also just obtaining corresponding development and application at present.Therefore, from the comprehensive utilization angle of coal, a large amount of coke breezes that the gasification back produces have also just become problem demanding prompt solution.Experiment shows that the gasification coke breeze is different with general coke powder, and it is good that it has reactivity worth, the microvoid structure prosperity, and performance is better than hard coal.Its purposes is widened in a large amount of coke breeze moulding after the gasification, is all to have great importance from the economy of young coal utilization or on the degree of depth of comprehensive utilization.Studying and use for the moulding of coke powder is existing in the prior art at present, mainly is to adopt the method for coke powder adding additives with its moulding, and promptly organic matter binding agent and inorganics binding agent are two kinds.Organic matter binding agent is mainly by industrial waste and other organic compound such as coal tar, pitch, sucrose and paper wastes.The production method that for example Chinese invention patent application (application number 94106771.8) discloses a kind of caking coke of coke powder adopts pitch as binding agent exactly.The defective that this class binding agent exists is mostly to contain objectionable impurities, and smog emission is arranged during burning, contaminate environment not only, and also the formed coke intensity of being produced can not meet the demands.The inorganics binding agent mainly adopts clay (or high-al clay), adds a small amount of lime or water glass etc.Chinese patent application (application number: 88104062.2) then belong to this type of for example.Because the formed coke poor water resistance that this class binding agent is produced, it also consumes a large amount of high-quality clay resources in addition, also is subjected to certain restriction so apply.
Purpose of the present invention and task are from the economy of coal utilization and the degree of depth of comprehensive utilization, utilize gasification coke powder and a kind of cheap, the inorganics activator that is easy to obtain, it is higher to produce a kind of intensity, water-tolerant, thermostability and reactive behavior be formed coke preferably all.
The present invention is achieved by the following technical solutions: the inorganics of this gasification coke breeze activates the bonding formed coke, is mainly formed by the gasification coke breeze with as the industrial gypsum and the commercial lime of inorganics activator, and its weight percent is: gasification coke breeze 60-90%
Industrial gypsum 3-20%
Commercial lime 3-20%
When the intensity of formed coke was had particular requirement, the silicate cement that also can add 0-10% (weight percent) was as binding agent.
The moulding process of above-mentioned formed coke is as follows:
To gasify its maximum particle size behind coke breeze and the industrial gypsum mix grinding less than 0.4 millimeter by said ratio; With the complete slaking of a certain proportion of commercial lime; The material after pulverizing and the lime of slaking are put to kneading machine, and the material after maybe will pulverizing and the lime of slaking and a certain amount of silicate cement are put to kneading machine, add that water 8-20% is mixed to be pinched 10-30 minute; Use the shaper extrusion forming, forming pressure is 80-200Mpa; Under room temperature and wet condition, carry out maintenance.
In the above-mentioned raw materials, the gasification coke powder is a combustibleconstituents, and its reactive behavior is better, is the coke breeze (semicoke) that is generated by coal gasifying process, generally contains the ash of 20-50%, and these ash are mainly unformed AI
2O
3And SiO
2, their agent that can be activated activate; Industrial gypsum and commercial lime are the inorganics activator, make the ash in the coke breeze have hydraulicity viscosifying power; Cement is binding agent, mainly is the intensity that further strengthens formed coke, and these materials mix the pressure forming of kneading and produce the formed coke blank by pulverizing, digest, add water, and maintenance becomes to have water tolerance, high-intensity formed coke finished product under room temperature and wet condition.
The present invention compared with prior art, have the following advantages and beneficial effect: this formed coke is complete smoke-less, intensity height not only, water tolerance, thermostability and reactive behavior are better, and because the gasification coke breeze is the byproduct behind all coal seed gasifications such as low-rank coal, low grade coal, cheap, the source is wide; Commercial lime and gypsum price as activator are also more cheap, are easy to obtain, and therefore, this product price is cheap.The formed coke of making simultaneously, maintenance at ambient temperature need not be dried or additional other maintenance of equipment, can save a large amount of energy and fund, is fine industrial raw material and domestic fuel.
Describe concrete enforcement of the present invention and technological process below in detail:
1) coal is gasified in the 500-1000 ℃ of scope coke breeze (semicoke) that the back produces, maximum particle size is general＜and 30 millimeters, put into feed bin;
2) with industrial gypsum (SO3 content＞30%), maximum particle size after the coarse crushing＜20 millimeter;
3) with commercial lime (effective CaO content＞60%), add water and clear up, make its complete slaking;
4) measure respectively from the gasification coke breeze of feed bin and the gypsum after the coarse crushing, add to the pulverizer mix grinding in proportion, make its maximum particle size＜0.4 millimeter;
5) material after the pulverizing is delivered to kneading machine;
6) water and the lime after the slaking with 8-20% adds kneading machine; When the intensity of formed coke has particular requirement, can add the silicate cement of 0-10% according to different requirement of strength;
7) mixed pinching 10-30 minute;
8) use the shaper extrusion forming, forming pressure is 80-200Mpa;
9) cover with plastics film or other simple and easy water conservation measure maintenance 3-10 days at ambient temperature.
Embodiment 1:
The prescription of formed coke is: the gasification coke breeze is 70% (its ash content of coal is 31%), and commercial lime is 15%, and industrial gypsum is 15%, and pulverizing its maximum particle size of back is 0.2 millimeter; Add 15% mixed the pinching 20 minutes of water, extrusion forming, its forming pressure is 120Mpa.One week of moisture-keeping maintaining, seasoning 3 days.The finished product formed coke is experimentized, if it is as follows:
Formed coke seasoning ultimate compression strength 8.21Mpa
Formed coke water saturation ultimate compression strength 6.9Mpa
Thermostability index S T+6 72%
CO reduction ratio 58% in the time of 900 ℃
Embodiment 2:
The prescription of formed coke is: the gasification coke breeze is 85% (its ash content of coal is 39%), and commercial lime is 5%, and industrial gypsum is 10%, and pulverizing its maximum particle size of back is 0.15 millimeter; Add 18% mixed the pinching 25 minutes of water, extrusion forming, its forming pressure is 100Mpa.Moisture-keeping maintaining 5 days, seasoning 5 days.The finished product formed coke is experimentized, if it is as follows:
Formed coke seasoning ultimate compression strength 10.21Mpa
Formed coke water saturation ultimate compression strength 8.9Mpa
Thermostability indication ST+6 78%
CO reduction ratio 54% in the time of 900 ℃
Embodiment 3:
The prescription of formed coke is: the gasification coke breeze is 80% (its ash content of coal is 42%), and commercial lime is 5%, and industrial gypsum is 15%, and pulverizing its maximum particle size of back is 0.25 millimeter; Add 13% mixed the pinching 30 minutes of water, extrusion forming, its forming pressure is 150Mpa.Moisture-keeping maintaining 10 days, seasoning 1 day.The finished product formed coke is experimentized, if it is as follows:
Formed coke seasoning ultimate compression strength 13.21Mpa
Formed coke water saturation ultimate compression strength 9.6Mpa
Thermostability indication ST+6 82%
CO reduction ratio 41% in the time of 900 ℃
Claims (3)
1, a kind of inorganics of the coke breeze that gasifies activates the bonding formed coke, it is characterized in that it mainly divides coke breeze by gas and formed as the industrial gypsum and the commercial lime of inorganics activator, and its weight percent is: coke breeze 60-90% gasifies
Industrial gypsum 3-20%
Commercial lime 3-20%
2, the inorganics according to the described a kind of coke breeze that gasifies of claim 1 activates the bonding formed coke, it is characterized in that above-mentioned formed coke also contains the silicate cement of 0-10% (weight percent).
3, a kind of production processing method of formed coke according to claim 1 is characterized in that: make its maximum particle size less than 0.4 millimeter behind will gasify according to the above ratio coke breeze and the industrial gypsum mix grinding; With the complete slaking of a certain proportion of commercial lime; The material after pulverizing and the lime of slaking are put to kneading machine, and the material after maybe will pulverizing and the lime of slaking and a certain amount of silicate cement are put to kneading machine, add that water 8-20% is mixed to be pinched 10-30 minute; Use the shaper extrusion forming, forming pressure is 80-200Mpa; Under room temperature and wet condition, carry out maintenance.