CN1204323C - Mixed material suitable for making heat ground surface - Google Patents
Mixed material suitable for making heat ground surface Download PDFInfo
- Publication number
- CN1204323C CN1204323C CN 03133858 CN03133858A CN1204323C CN 1204323 C CN1204323 C CN 1204323C CN 03133858 CN03133858 CN 03133858 CN 03133858 A CN03133858 A CN 03133858A CN 1204323 C CN1204323 C CN 1204323C
- Authority
- CN
- China
- Prior art keywords
- mixed material
- kilograms
- activated carbon
- cellulose
- lime
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a mixed material for preparing a geothermal surface, which is characterized in that the mixed material is prepared from yellow soil, lime, cinder, waterproof powder, cellulose, activated carbon and water through proportionally mixing. The mixed material has heat storage and thermal insulating properties; when used as a geothermal material, the mixed material has faster heating, slower cooling and better heat supply effect than the existing cement mortar materials.
Description
Affiliated technical field
The present invention relates to a kind of mixed material of doing the ground hot side, belong to New Building Materials.
Background technology
Be used widely as the heating of house mode with underground heat in recent years, the underground heat heating method is: heating line is layered on the ground, does face floor tile or floor again with cement mortar above the pipeline.Because cement mortar density is big, make the ground hot material and conduct heat slowly, be not incubated, dry and cracked easily, influence heating effect.
Summary of the invention
The objective of the invention is: a kind of novel mixed material of doing the ground hot side is provided, its good heat-transfer, insulation can improve heating effect.
Technical scheme of the present invention is: a kind of mixed material of doing the ground hot side, and it is characterized in that: this mixed material is made up of following composition, and wherein each composition weight proportion scope is:
Loess 95-130, lime 30-50, ashes 15-35, waterproof powder 2-8, cellulose 1-5
Activated carbon 2-7, water 25-60
Prescription preferred weight ratio range of the present invention is:
Loess 100-110, lime 35-45, ashes 20-30, waterproof powder 4-8, cellulose 3-4
Activated carbon 2-4, water 30-40
Prescription optimum weight proportioning of the present invention is:
Loess 100, lime 35, ashes 20, waterproof powder 4, cellulose 3,
Activated carbon 2, water 30
The production method that above-mentioned each component is made mixed material of the present invention by proportioning is:
Yellow mud and lime are soaked in water, add ashes, waterproof powder, cellulose, activated carbon, stir and spare all, make the mixture finished product, the production temperature remains on 10 ℃ to the natural temperature in summer.
This product is bonding shape, is contained in to seal in the packaging bag to preserve 3-5 month, and sealing is in order to keep the humidity of mixture.Tiling is covered on the ground heat pipe during use, and thick about 35 centimetres, through two times press polish, air dry was finished about 48 hours.
Yellow mud is a Main Ingredients and Appearance in present technique, and its cohesive is good, and soft property is good after the moulding, it is a natural materials, do not need processing,, add cellulose and can prevent crackle so cost is low, ashes can reduce the density of mixed material, improve gas permeability, improve hardness, lime has the sterilizing effect, activated carbon can make air filtration, also has waterproof powder in the mixed material.Every technical performance through this product of evidence has satisfied the requirement of making the ground hot material.With the mixed material of present technique with make 2 square metres of plates that thickness is identical respectively of cement mortar, under equal condition such as environment temperature, heating power, be heated to 20 ℃, reinforced cement-mortar board has been used 15 minutes, and adopt the plate of present technique only to use 6 minutes heat time heating time, when naturally cooling to 13 ℃, reinforced cement-mortar board has been used 20～30 minutes, and the plate of present technique has been used 4～6 minutes, evidence uses the mixed material of present technique than using the fast of cement mortar material heat, and cold is slow, the heat-storage heat-preserving performance is arranged, can improve heating effect, present technique also has the low advantage of cost.
Embodiment 1
Take by weighing 100 kilograms of raw material loess, 35 kilograms of limes, 20 kilograms in ashes, 4 kilograms of waterproof powder, 3 kilograms of celluloses, 2 kilograms of activated carbon, 30 kilograms in water, this raw material is current material, yellow mud and lime were soaked in water about 30 minutes, fully soak saturating, add ashes, waterproof powder, cellulose, activated carbon, stir and spare all, make the mixture finished product, the production temperature is 15 ℃-25 ℃.
Embodiment 2
Take by weighing 95 kilograms of raw material loess, 50 kilograms of limes, 35 kilograms in ashes, 8 kilograms of waterproof powder, 5 kilograms of celluloses, 7 kilograms of activated carbon, 40 kilograms in water, yellow mud and lime were soaked in water about 30 minutes, add ashes, waterproof powder, cellulose, activated carbon, stir all even, make the mixture finished product, the production temperature is 20 ℃-28 ℃.
Embodiment 3
Take by weighing 130 kilograms of raw material loess, 30 kilograms of limes, 15 kilograms in ashes, 2 kilograms of waterproof powder, 1 kilogram of cellulose, 2 kilograms of activated carbon, 25 kilograms in water, yellow mud and lime are soaked in water, add ashes, waterproof powder, cellulose, activated carbon, stir all even, make the mixture finished product, the production temperature is 10 ℃.
Claims (3)
1, a kind of mixed material of doing the ground hot side, it is characterized in that: this mixed material is made up of following composition, and wherein each composition weight proportion scope is:
Loess 95-130, lime 30-50, ashes 15-35, waterproof powder 2-8, cellulose 1-5, activated carbon 2-7, water 25-60.
2, a kind of mixed material of doing the ground hot side according to claim 1, it is characterized in that: wherein the weight proportion scope of each composition is:
Loess 100-110, lime 35-45, ashes 20-30, waterproof powder 4-8, cellulose 3-4, activated carbon 2-4, water 30-40.
3, a kind of mixed material of doing the ground hot side according to claim 1, it is characterized in that: wherein the weight proportion scope of each composition is:
Loess 100, lime 35, ashes 20, waterproof powder 4, cellulose 3, activated carbon 2, water 30.