CN1202183C - Far infrared sanitary interior wall coating material - Google Patents
Far infrared sanitary interior wall coating material Download PDFInfo
- Publication number
- CN1202183C CN1202183C CN 03110945 CN03110945A CN1202183C CN 1202183 C CN1202183 C CN 1202183C CN 03110945 CN03110945 CN 03110945 CN 03110945 A CN03110945 A CN 03110945A CN 1202183 C CN1202183 C CN 1202183C
- Authority
- CN
- China
- Prior art keywords
- interior wall
- wall coating
- coating material
- far infrared
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a far infrared sanitary interior wall coating material with innocuity to a human body and green health care, which solves the problems of poor stability, water washing intolerance and short storage time of the existing interior wall coating material. The present invention mainly uses natural jade powder as an essential component, and is mixed and stirred by adding with matching auxiliary agents, such as acrylic emulsion, water, a dispersing agent, a stabilizer, a defoaming agent, a pH regulator, a slip agent, etc. The present invention realizes the development of a high-grade health care interior wall coating material which can emit far infrared, has the functions of deodorization, antisepsis and metabolism promotion and effects of heat preservation and moisture preservation, and is beneficial to the human body. Thus the present invention is especially suitable for the decoration of interior walls and ceilings in houses, apartments, offices, hospitals, hotels, etc.
Description
Technical field
The present invention belongs to green health interior wall coating in the building coating field.
Background technology
Along with the development of society, the raising of people's living standard; People improve constantly the understanding of own living environment, also more and more higher in requirement to the finishing of inside, house, and existing interior wall coating, as the high-grade porcelain coating of the superpower anti-water of the high light of CN1182762A, CN1097441A multifunctional inner wall coating material and production method thereof, it is sizing material that these coating all adopt polyvinyl alcohol and carboxyphenyl Mierocrystalline cellulose, is that filler is made with raw materials such as lime carbonate, existing common problem, poor stability, not water-fast washing, the shelf lives is short; Do not belong to green material.
Summary of the invention
The object of the invention is, solves above-mentioned existing existing problem, and a kind of good stability is provided, and water-fast washing has green health and to the beautiful health care of the far infrared interior wall coating of the far infrared health care function of human body.
It is as follows that coating of the present invention is formed proportioning:
The material name weight percent
Water 10～20
Dispersion agent 0.1～0.6
Stablizer 0.2～0.6
Frostproofer 0.1～0.5
Postpone siccative 0.2～0.6
Defoamer 0.1～0.3
PH conditioning agent 0.7～1.5
Slip(ping)agent 1.0～2.0
ACRYLIC EMULSION 10～25
400-1000 purpose natural jade powder 50～75.
The mould inhibitor that adds above-mentioned substance gross weight 0.1～0.2% in addition is to increase storage time.
Effect of the present invention:
The beautiful health care of far infrared of the present invention interior wall coating is important component with the natural jade powder, adds ACRYLIC EMULSION, water, color stuffing and auxiliary aid and forms; The present invention has realized that development is a kind of can emission red line far away, and has deodorization, antibiotic and enhance metabolism function and insulation, moisture-keeping efficacy, is the high-class healthy interior wall coating that is of value to human body.Thereby the interior walls and the top ceiling that are specially adapted to dwelling house, apartment, office, hospital, hotel etc. are fitted up.Its coating property index sees Table 1, and coating environmental protection assay sees Table 2, and the emitting far-infrared measurement result of coating sees Table 3;
Table 1 coating property index
Project national standard assay
Do not have lump at condition in container, being uniform state after the stirring does not have the lump uniform liquid
The normal appearance of film of appearance of film is normal
Time of drying (surface drying)/h＜2＜2
Abrasion resistance/time＞1000＞3200
Alkali resistance 24 no abnormal 24 is no abnormal
Low-temperature stability never degenerates
Annotate: national standard is GB/T9756-2001
Table 2 coating environmental protection assay
Interventions Requested national standard assay
Volatile organic compounds (voc) g/L≤200 7
Free formaldehyde g/kg≤0.1 does not detect
Dissoluble lead mg/kg≤90＜8
Soluble cadmium mg/kg≤75＜3
Soluble chromium mg/kg≤60＜5
Soluble mercury mg/kg≤60 do not detect
Annotate: national standard is GB18582-2001
The emitting far-infrared measurement result of table 3 coating
The sample number into spectrum sample temperature (℃) the sample emittance
1# 80.0 0.91
2# 80.0 0.91
3# 80.0 0.90
Illustrate: measured value is normal direction total radiation emittance (using with standard black matrix normal direction total radiation brightness comparative approach and measure, is 2 microns～18 microns with infrared radiometer response wave length scope relatively), and value can be traceable to Radiometric Standard for Low Temperature Blackbodies.
Embodiment
The used dispersion agent of the present invention adopts sodium polymethacrylate, is the DA-140 of Korea S contract polymer Zhu Shi commercial firm.It is the AR-606 of Korea S contract polymer Zhu Shi commercial firm that stablizer adopts hydroxyethyl phenol.It is the E.G of Korea S contract polymer Zhu Shi commercial firm that frostproofer adopts ethylene glycol.Postponing siccative employing alkyl aryl polyether is the solvent of Korea S contract polymer Zhu Shi commercial firm.It is the NDW of Korea S contract polymer Zhu Shi commercial firm that defoamer adopts mineral oil.The PH conditioning agent is the NaOH of concentration 10%; It is the Pangel C-150 of Korea S contract polymer Zhu Shi commercial firm that slip(ping)agent adopts Magnesium Silicate q-agent.
It is the AR-2600 of Korea S contract polymer Zhu Shi commercial firm that ACRYLIC EMULSION adopts the butylacrylic acid ester polymer.
At first, it is standby to pulverize, grind to form 400-1000 purpose jade powder after the natural jade strictness is selected.
Embodiment 1:
As make the coating of 100kg, water intaking 10kg, dispersion agent 0.4kg, stablizer 0.5kg, frostproofer 0.2kg; Postpone siccative 0.2kg; Defoamer 0.2kg, PH conditioning agent 1.5kg, slip(ping)agent 2kg, ACRYLIC EMULSION 10kg, natural jade powder 75kg; Can add mould inhibitor 0.1kg in addition to increase storage time.
Embodiment 2:
As make the coating of 100kg, and water intaking 20kg, dispersion agent 0.6kg, stablizer 0.6kg, frostproofer 0.5kg postpones siccative 0.4kg, defoamer 0.3kg, PH conditioning agent 0.8kg, slip(ping)agent 1.8kg, ACRYLIC EMULSION 25kg, natural jade powder 50kg; Can add mould inhibitor 0.1kg in addition to increase storage time.
Embodiment 3:
As make the coating of 100kg, water intaking 15kg, dispersion agent 0.1kg, stablizer 0.2kg, frostproofer 0.1kg; Postpone siccative 0.6kg; Defoamer 0.1kg, PH conditioning agent 0.7kg, slip(ping)agent 1.0kg, ACRYLIC EMULSION 20kg, natural jade powder 62.2kg; Can add mould inhibitor 0.2kg in addition to increase storage time.
The production of its coating mainly divides two stages:
1, grind scatter stage: special-purpose high speed dispersor is under 400～600 rev/mins of states of low speed, add water, dispersion agent, stablizer, the defoamer that accounts for defoamer total amount 2/3, frostproofer, delay siccative, slip(ping)agent, the natural jade powder that accounts for water inventory 1/2～3/4 successively, after adding, stirring velocity is brought up to 1500～2000 rev/mins, disperses under normal temperature condition 1.5～2 hours.
2, stage of modulating: after grinding dispersion, stirring velocity drops to 300-500 rev/min, add ACRYLIC EMULSION then, account for defoamer total amount 1/3 defoamer, mould inhibitor, PH conditioning agent, account for the water of water inventory 1/2～1/4, add the material back and stir discharging in 20～30 minutes, promptly finish production process.
Claims (2)
1, the beautiful health care of a kind of far infrared interior wall coating is characterized in that, it is as follows that coating of the present invention is formed proportioning:
The material name weight percent
Water 10～20
Dispersion agent 0.1～0.6
Stablizer 0.2～0.6
Frostproofer 0.1～0.5
Postpone siccative 0.2～0.6
Defoamer 0.1～0.3
PH conditioning agent 0.7～1.5
Slip(ping)agent 1.0～2.0
ACRYLIC EMULSION 10～25
400-1000 purpose natural jade powder 50～75.
2, according to the beautiful health care of the said a kind of far infrared of claim 1 interior wall coating, it is characterized in that, add the mould inhibitor of above-mentioned substance gross weight 0.1～0.2%.