CN1197719C - Sand blasting technology for generating colour decorative pattern on surface of stainless steel - Google Patents
Sand blasting technology for generating colour decorative pattern on surface of stainless steel Download PDFInfo
- Publication number
- CN1197719C CN1197719C CN 02134576 CN02134576A CN1197719C CN 1197719 C CN1197719 C CN 1197719C CN 02134576 CN02134576 CN 02134576 CN 02134576 A CN02134576 A CN 02134576A CN 1197719 C CN1197719 C CN 1197719C
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- sandblast
- floral designs
- color
- sand blasting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a sand blasting method for generating color decorative patterns on the surface of stainless steel. In the method, an image mould is attached to a natural-color (silver) or color stainless steel plate of which the thickness is from 0.6 to 3mm to form sand blasting patterns on the surface of the stainless steel through sand blasting, and a transparent protective film is arranged on the surface of the patterns. The manufacturing and forming method has the advantages of simplicity and convenience, and decorative surfaces which have color stainless steel sand blasting patterns and are made in the method have the advantages of magnificence and multiple colors. The present invention not only keeps the advantages of original color stainless steel decorative materials, but also has the advantage of multiple pattern change; moreover, because of intensive contrast between a 8K mirror surface formed on the surface of stainless steel and a sand blasting surface, the present invention also has the advantage of stronger decorative effect and is suitable for various industries needing decoration of household appliances, kitchen devices, decoration, industrial art, etc.
Description
Technical field
The present invention relates to a kind of formation method of ornament materials, the ostentatious formation method of especially a kind of colored stainless steel sandblast floral designs.
Background technology
At present, adopt stainless steel more and more general as ornament materials.Yet, employed stainless steel decorating material board is generally silvery white on the market now, dull coloring, and a kind of stainless steel materials of colour is arranged, though its color is various, splendid, its floral designs just form by serigraphy and chemical attack, it is comparatively dull that its decorative effect seems, can't embody the decorative beauty of modern architecture, not reach best decorative effect, it is cumbersome that secondly changing patterns will be made the silk screen version in addition.
Summary of the invention
In view of the above problems, the object of the present invention is to provide a kind of ostentatious formation method of colored stainless steel sandblast floral designs simple to operate.
The present invention adopts such technical scheme to solve the problems referred to above:
The ostentatious formation method of colored stainless steel sandblast floral designs has two kinds of methods, and the step of first method is as follows: step (1) is placed on the CrO that contains variable concentrations to thickness at the mirror face stainless steel plate of 0.6～3mm
3And H
2SO
4Solution in, painted by chemical oxidation, on stainless steel surfaces, form different colors; Step (2) is by the different thick image moulds of design producing 0.1～3mm; Step (3) places the image mould to be close to fixingly on the mirror surface color corrosion resistant plate that is formed by step (1), put into sand-blasting machine then, carries out blasting treatment, forms floral designs thus; Step (4) is removed the lip-deep image mould of corrosion resistant plate, and cleaning, drying corrosion resistant plate has then just formed the combination with decorative surfaces with argenteous sandblast face and colored stainless steel sandblast floral designs of colored two kinds of sharp contrasts of minute surface.The stainless steel surfaces of color sand blasting floral designs.The step of another kind method is as follows: step (1) is by the different thick image moulds of design producing 0.1～3mm; Step (2) places the image mould thickness on the corrosion resistant plate surface of 0.6～3mm and be close to fixing, put into sand-blasting machine then, carry out blasting treatment, form the stainless steel materials of wounded in the battle line pattern with silvery white sandblast face and the contrast of silvery white stainless steel materials minute surface; Step (3) is put into stainless steel materials and is contained CrO
3And H
2SO
4Solution in to carry out chemical oxidation painted, form the colored stainless steel sandblast floral designs of the sheet material minute surface of sandblast face with different color and different color; Step (4) is removed the lip-deep image mould of the corrosion resistant plate of color sand blasting floral designs, and cleaning, drying forms colored stainless steel sandblast floral designs combination with decorative surfaces then.
The invention has the beneficial effects as follows: this preparation method is simple and convenient, and splendid, the rich color of making thus of colored stainless steel sandblast floral designs combination with decorative surfaces, it has not only kept the advantage of original color stainless steel ornament materials, and floral designs change various, can be by customer requirements change pattern indiscriminately ad. as one wishes, convenient and easy, and the sharp contrast of its surface formation 8K minute surface and sandblast face, make it to have stronger decorative effect.
The specific embodiment
The ostentatious formation method of colored stainless steel sandblast floral designs has two kinds of methods, and the step of first kind of formation method is as follows: step (1) is the argenteous corrosion resistant plate of 8K minute surface to be placed on contain CrO
3And H
2SO
4Solution in, form layer oxide film by chemical reaction, this oxide-film forms different colors by the interference of light effect on the surface of stainless steel materials; Step (2) be by computer carving cutting machine cutting PVC, timber, etc. protective material, by different thick erect image or the negative-appearing image image moulds of design producing 0.1～3mm, this image mould is the erect image mould of diging up the negative-appearing image mould of pattern part or remove the pattern periphery in protective material in protective material; Step (3) be the image mould place be close on the colored stainless steel plate surface that forms by step (1) fixing, put into sand-blasting machine then, the blasting pressure of sand-blasting machine is controlled in the scope that does not make the stainless steel distortion, stainless steel surfaces to band image mould carries out blasting treatment, if adopt the negative-appearing image mould, then sand grains is sprayed in the middle of the mould on the visible colored stainless steel minute surface and forms the floral designs that are made of sandblast face; If adopt the erect image mould, then sand grains is sprayed on the stainless steel mirror of mould pattern periphery, forms by peripheral sandblast face and colored stainless steel floral designs minute surface and contrasts formed floral designs; Step (4) is that the lip-deep image mould of the colored stainless steel plate of wounded in the battle line pattern is removed; cleaning, drying corrosion resistant plate then; form colored stainless steel sandblast floral designs combination with decorative surfaces; can cover the diaphragm that one deck has strong adhesion in its surface at last; be not damaged with protection colored stainless steel sandblast floral designs surface; can finish processing and handle, generate finished product.
The step of another kind of formation method is as follows: step (1) be by computer carving cutting machine cutting PVC, timber, etc. protective material, by different thick erect image or the negative-appearing image image moulds of design producing 0.1～3mm, this image mould is the erect image mould of diging up the negative-appearing image mould of pattern part or remove the pattern periphery in protective material in protective material; Step (2) is to place the image mould on the silvery white corrosion resistant plate surface of 8K minute surface and be close to fixing, put into sand-blasting machine then, the blasting pressure of sand-blasting machine is controlled in the scope that does not make the stainless steel distortion, stainless steel surfaces to band image mould carries out blasting treatment, if adopt the negative-appearing image mould, then sand grains is sprayed on the visible silvery white stainless steel mirror in the middle of the mould and forms the floral designs that are made of sandblast face, is argenteous stainless steel mirror around the pattern; If adopt the erect image mould, then sand grains is sprayed on the stainless steel mirror of mould periphery, forms by peripheral sandblast face and silvery white stainless steel floral designs minute surface and contrasts formed floral designs; Step (3) is the sheet material that is generated through step (2) to be put into contain CrO
3And H
2SO
4Solution in to carry out chemical oxidation painted, because the two kinds of surface appearances of minute surface surperficial and without sandblast through sandblast are different, its chemistry is put and is answered the speed difference, formed oxide thickness difference, such oxide-film that generates are subjected to the interference of light effect and have just formed the two colored stainless steel sandblast floral designs with the different sandblast face of color and sheet material minute surface; Step (4) is that the sheet material of handling through above-mentioned steps is removed the image mould; cleaning, drying; form colored stainless steel sandblast floral designs combination with decorative surfaces; can cover the diaphragm that one deck has strong adhesion in its surface at last; to guarantee that colored stainless steel sandblast floral designs surface is not damaged; can finish processing and handle, generate finished product.
Claims (6)
1, the ostentatious formation method of a kind of colored stainless steel sandblast floral designs, its step is as follows:
(1) thickness is placed at the mirror face stainless steel plate of 0.6～3mm contains CrO
3And H
2SO
4Solution in, painted by chemical oxidation, on stainless steel surfaces, form different colors;
(2) by the different thick image moulds of design producing 0.1～3mm;
(3) the image mould place be close on the mirror surface color corrosion resistant plate that forms by step (1) fixing, put into sand-blasting machine then, carry out blasting treatment, formation has argenteous sandblast face and two kinds of floral designs combination with decorative surfaces that sharp contrast is arranged of colour mirrorlike surface thus;
(4) the lip-deep image mould of the corrosion resistant plate of color sand blasting floral designs is removed, then cleaning, drying.
2, the ostentatious formation method of a kind of colored stainless steel sandblast floral designs, its step is as follows:
(1) by the different thick image mould of design producing 0.1～3mm;
(2) place the image mould thickness on the corrosion resistant plate surface of 0.6～3mm and be close to fixing, put into sand-blasting machine then, carry out blasting treatment, form the stainless steel materials of wounded in the battle line pattern with silvery white sandblast face and the contrast of silvery white stainless steel materials minute surface;
(3) above-mentioned stainless steel materials is put into the CrO that contains variable concentrations
3And H
2SO
4Solution in to carry out chemical oxidation painted, form the stainless steel surfaces of the color sand blasting floral designs of sandblast face with different color and different color sheet material minute surface;
(4) the lip-deep image mould of the corrosion resistant plate of color sand blasting floral designs is removed, then cleaning, drying.
3, according to claim 1 or the ostentatious formation method of 2 described colored stainless steel sandblast floral designs, it is characterized in that afterwards, at colored stainless steel sandblast floral designs surface coverage layer protecting film in step (4).
4,, it is characterized in that described image mould is to adopt the engraving cutting machine to make according to claim 1 or the ostentatious formation method of 2 described colored stainless steel sandblast floral designs.
5, according to claim 1 or the ostentatious formation method of 2 described colored stainless steel sandblast floral designs, the making material that it is characterized in that described image mould is PVC, timber, iron plate or other protective material.
6, according to claim 1 or the ostentatious formation method of 2 described colored stainless steel sandblast floral designs, it is characterized in that described visual mould is erect image or negative-appearing image.