CN1194789C - Nanometer order quartz molecule sieve filter element and the exact filtering waterer equipped with the filter element - Google Patents
Nanometer order quartz molecule sieve filter element and the exact filtering waterer equipped with the filter element Download PDFInfo
- Publication number
- CN1194789C CN1194789C CNB021313229A CN02131322A CN1194789C CN 1194789 C CN1194789 C CN 1194789C CN B021313229 A CNB021313229 A CN B021313229A CN 02131322 A CN02131322 A CN 02131322A CN 1194789 C CN1194789 C CN 1194789C
- Authority
- CN
- China
- Prior art keywords
- nanometer
- magnetizer
- filter
- water
- filter element
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a nanometer-grade quartz molecular sieve filter element which comprises a quartz cup body and coating layers of antiseptic nanometer material, wherein the quartz cup body is provided with nanometer-grade micropores; the coating layers are arranged outside the cup body and on the side walls of all micropores on the cup body, wherein material for making the quartz cup body comprises components which are measured by percentages by weight: 4 to 6 shares of nanometer SiO2, 1 to 3 shares of nanometer ZnO2 and 3 to 5 shares of nanometer A2O3, and the coating layers of antiseptic nanometer material comprise components which are measured by percentages by weight: 30 to 50% of nanometer Ag, 20 to 60% of nanometer SiO2 sol and 10 to 40% of nanometer ZrO2. The present invention can remove impurities, suspended substances, bacteria, viruses, follicles, etc. in water. The present invention also relates to a fine filtration waterer with the nanometer-grade quartz molecular sieve filter element, which comprises a water bucket with a lid, a water inlet pipe, a water outlet pipe, a filter core and a filter, wherein the filter element and the filter are arranged in the water bucket, and the filter element is connected with the water outlet pipe; the filter comprises a container on which micropores are densely distributed and absorptive mineralized material which is arranged in the container. The present invention has the advantages of high temperature resistance, corrosion resistance, long service life and low cost.
Description
Technical field
The present invention relates to the water fountain of a kind of filter and this filter of use.
Background technology
At present, water purifier and purifier that invention is both at home and abroad used, its structure comprises bucket, water inlet pipe, outlet pipe and the filter core that is connected with water inlet pipe or outlet pipe substantially.Wherein filter core is generally analog-U shaped pipe of foamed plastics or powdered carbon cast tube etc., and its material all is an organic material, and for example on the market there be common material:
1. polypropylene fiber: the removal of bacterium is better, but owing to be subjected to the secondary pollution of all kinds of impurity, microorganism and colloid in the water, aging mashed core and dead core, the service time of filter core is too short, and because of filter core can not utilize once more, so the cost height;
2. nylon fiber: the price comparison on the market is cheap, the permeable aperture of filter core generally between 10～40 microns, can only filtered water in impurity and suspension more than 10 microns, but can't remove bacterial micro-organism below 10 microns and water-borne glue body;
3. doughnut: the effect of the more preceding two kinds of filter cores of water treatment effect of doughnut filter core will be got well, and generally between 0.05 micron～1 micron, all kinds of impurity in the water, bacterium, microorganism can all be removed in the permeable aperture of doughnut filter core; But meanwhile, also the trace element in the running water has also been removed, because the doughnut filter core is to be raw material with the acetic acid polyamide, this chlorine resistance is relatively poor relatively, aging fast, so the life-span is shorter, in the oxidation reaction of chlorine molecule, produce harmful material and remain in the water, secondary pollution water quality and cost are very high;
4. casting charcoal many pleats fibrous unsaturated polyester plastic foil filter core is U.S.'s product, its product China and U. S. application patent, the user has covered the well-known food of part, beverage, wine already and medicinal water enterprise.It adopts CHBr
3(bromoform) bromination treatment system, its advantage is that manufacturing cost is lower, is to adopt imperceptible many pleats of active carbon filter membrane casting to form.Because China is the cholorination running water, reliability height and the cost of chlorination kill virus and bacterium are low, and be different with U.S. bromination treatment system.The outstanding shortcoming of U.S.'s casting atomic film filter core is aging down fast to the chlorine residue chemical attack in the water quality, secondary pollution and CHBr
3Human body is had the toxic and side effect of destroying the insulin secretion system, and people have drunk this water purification system CHBr
3Residual water, easily cause the insulin secretion imbalance and suffer from diseases such as diabetes, obesity, hypertension and heart disease, particularly catering enterprise adopts the water of bromination water treatment system to produce the CHBr that remains in " Coca-Cola ", " Sprite ", " KFC " food in the water
3Toxic and side effect, and suffer from modern diseases such as diabetes, obesity, hypertension and heart disease, its main cause is exactly the defective of water filtration method; It two is that secondary pollution charcoal end particulate, fiber, malignant bacteria and the contaminating impurity of material aging flow to the drinking-water delivery port, and the user is difficult to find, makes the user lack water purification guarantee and water safety sense.
In sum, the filter core of water dispenser is generally by composite fiber membrane, fiber rolling permeable membrane, doughnut and many pleats of casting mold fibrous carbon membrane cartridge on the present domestic and international market, its material all is fiber, two acetic acid polyamide and three acetic acid polyamide, used material is " acetic acid polyamide " fiber, plastics package, sterilization and sterilization and dechlorination effect are not good, chlorine resistance is poor, and film produces toxin aging the decomposition automatically; Can not regenerate again, be unfavorable for environmental protection; And, chlorine residue and plastics residual poison still being remained in the water purification with the body and the casing of plastic material as water dispenser, bacterium grows in film, forms secondary pollution, is detrimental to health.
Summary of the invention
The objective of the invention is to overcome the defective of above-mentioned prior art, a kind of long service life, low, the free of contamination nanometer order quartz molecule sieve filter core of cost are provided, it not only can thoroughly remove impurity in the water, virus and bacterium, can keep in the water trace element to the human body beneficial again.
Another purpose of the present invention provides a kind of essence filter water fountain that uses nanometer order quartz molecule sieve filter core of the present invention.
Nanometer order quartz molecule sieve filter core of the present invention, comprise having nanometer level microporous quartzy cup and be arranged on the antimicrobial nano material coating that described cup reaches each nanometer level microporous sidewall on the cup outward, the material of wherein making described quartzy cup comprises nanometer SiO by weight
24～6 parts; Nano-ZnO
21～3 part and nanometer Al
2O
33～5 parts.Described antimicrobial nano material coating comprises nanometer Ag 30%～50% by weight percentage; Nanometer SiO
2Colloidal sol 20%～60% and nanometer ZrO
210%～40%.
Nanometer order quartz molecule sieve filter core of the present invention, wherein said each nanometer level microporous aperture changes between 10nm～10000nm, and the porosity is 25%～50%.
Use the essence filter water fountain of nanometer order quartz molecule sieve filter core of the present invention, comprise bucket, water inlet pipe, the outlet pipe with lid and be arranged on bucket interior filter core and filter, wherein said filter core is connected with outlet pipe; Described filter comprises the container and the absorption mineralizing material that places in the described container by the micropore that gathers.
The smart filter of the present invention water fountain, wherein said absorption mineralizing material comprise that by weight 1～2 part of 1～2 part in Himalayas white jade stone, Mount Taishan rutile, 1～2 part of Huashan gold mine lazulite, 1～2 part in Hengshan Mountain serpentine, 1～2 part of Chinese Heng Shan zeolite, 1～2 part in Chinese Song Shan platina ore, Chinese Wutai Mountain dodges 5～10 parts of one or more and 5～10 parts of Chinese Wudang Mountain shenlongjia ginkgo wood active carbons in 1～2 part of 1～2 part of the zinc gold ore, 1～2 part of Chinese Mount Emei medical stone, Chinese Jiuhuashan amethyst stone and Chinese Qinling Mountains Kiwi berry rattan active carbons.
The smart filter of the present invention water fountain wherein also comprises the last magnetizer and the following magnetizer that place bucket inner top and bottom respectively, has at least two through holes respectively on magnetizer and the following magnetizer on this.
The smart filter of the present invention water fountain, wherein said water inlet pipe leads to down below the magnetizer.
The smart filter of the present invention water fountain, wherein said covering is provided with blow-off pipe.
The advantage and the good effect of nanometer order quartz molecule sieve filter core of the present invention are: because it is formed by having nanometer level microporous quartzy cup and being arranged on the antimicrobial nano material coating that cup reaches each nanometer level microporous sidewall on the cup outward, quartzy cup comprises nanometer SiO
2, nano-ZnO
2With nanometer Al
2O
3These nano materials have anticorrosion, antibacterial functions, not aging, not with water and water in material react, nanometer level microporous on the quartzy cup not only can thoroughly be removed impurity and suspensions such as water-borne glue body, asbestos particles, can also filtering bacterium and virus, can keep in the water trace element simultaneously again to the human body beneficial; Antimicrobial nano material coating comprises nanometer Ag, nanometer SiO
2Colloidal sol and nanometer ZrO
2, silver ion that its hydrophily discharged and zirconium ion can kill bacteria, virus, ovarian follicle etc.Wherein nanometer Ag and nanometer ZrO
2Possess antibiotic, anticorrosion, deodorizing, function eliminates the unusual smell; Nanometer order quartz molecule sieve filter core of the present invention is the factor of utilizing in the pure physical method removal water that is detrimental to health, and can not form secondary pollution, so favourable health; And high temperature resistant, corrosion-resistant, mechanical strength is high, is difficult for agingly, the cleaning back is reusable, so long service life, cost is low.
The advantage and the good effect of smart filter water fountain of the present invention are: it comprises filter core and filter, because it has used nanometer order quartz molecule sieve filter core of the present invention, so can thoroughly remove impurity and suspension, bacterium and virus in the water, can keep in the water trace element simultaneously again to the human body beneficial.
Other details of the smart filter of nanometer order quartz molecule sieve filter core of the present invention and nanoscale water fountain and characteristics can just can be cheer and bright by reading the embodiment that hereinafter encyclopaedizes in conjunction with the accompanying drawings.
Description of drawings
Fig. 1 is the structural representation of nanometer order quartz molecule sieve filter core of the present invention;
Fig. 2 is the cutaway view of smart filter water fountain of the present invention.
The specific embodiment
Referring to Fig. 1.Nanometer order quartz molecule sieve filter core of the present invention comprises having nanometer level microporous quartzy cup 21, and each hole sidewall is provided with antimicrobial nano material coating 22 outside quartzy cup 21 and on the cup.Quartzy cup 21 top ends are connected with and are connected connector 23 with water pipe, and connector 23 is made by stainless steel material.Each is nanometer level microporous to be bellmouth, and the aperture changes between 10nm～10000nm, and promptly the minimum-value aperture of each bellmouth is 10nm, and the maximum diameter of hole is 10000nm, and the porosity is 40%, and this porosity all is feasible between 25%～50%.Quartzy cup is by nanometer SiO
25 kilograms, nano-ZnO
23 kilograms and nanometer Al
2O
3Make with nano ceramics technology sintering after 4 kilograms of mixing.The component of antimicrobial nano material coating is by nanometer Ag 4 grams, nanometer SiO
2 Colloidal sol 5 gram and nanometer ZrO
23 grams mix to be formed.Above-mentioned nanometer SiO
2Raw material for quartzy for Chinese Mount Taishan quartz, Chinese Huashan quartz, Chinese Hengshan Mountain quartz, Chinese Heng Shan quartz, Chinese Song Shan quartz, Chinese Wutai Mountain quartz, Chinese delicate eyebrows mountain quartz, Chinese Jiuhuashan is quartzy or other pick up from the quartz of high mountains.
Nanometer order quartz molecule sieve filter core of the present invention can be widely used in the device of liquid filtering, gas purification, solid separation.
Referring to Fig. 2.Smart filter water fountain of the present invention, comprise bucket 2, water inlet pipe 3, outlet pipe 5, be successively set on last magnetizer 6, filter core 1, filter 10 and following magnetizer 8 in the bucket 2 from top to bottom, compressed on the bucket 2 and covered 9, water inlet pipe 3, outlet pipe 5 are arranged on and cover on 9, also are provided with blow-off pipe 4 on the lid 9.Water inlet pipe 3 passes magnetizer 6, filter 10 and following magnetizer 8, stretches into bucket 2 bottoms.Filter core 1 is connected on the outlet pipe 5 by screw thread or other modes.
The magnetic pole of last magnetizer 6 and following magnetizer 8 is opposite, forms magnetic field, has three through holes on each magnetizer respectively, form a plurality of magnetic fields again on each magnetizer like this, the water in the bucket 2 is in activated state under the effect of magnetic field force, bacterium is difficult for growing and breeding, and strengthens mineralising and maintenance again.
Filter core 1 adopts nanometer order quartz molecule sieve filter core of the present invention, bacteria-eliminating efficacy to sporangiocyst, Escherichia coli etc. reaches 100%, and can remove 100% any greater than 0.01 micron impurity particle and carcinogenic volatile organic matter and the epoxide of asbestos fibre filtering, can keep in the water trace element to the human body beneficial.
Smart filter water fountain of the present invention is applicable to source pressure 0.5～2.5kg/cm
2Obtain 0.5～2 liter/minute of the flow of drinking water.Running water is flow at the bottom of 2 barrels in the bucket by water inlet pipe 3, enters filter 10 again, and impurity in the water and suspension are adsorbed mineralizing material 11 absorption, remove peculiar smell, heterochromatic simultaneously; Remove virus in the water, bacterium, microorganism etc. through filter core 1 afterwards, the water in the bucket 2 are magnetized under last magnetizer 6 and 8 effects of play magnetizer, so the water that is flowed out by outlet pipe 5 is by the real pure water of mineralising, magnetization, abundant purification.
When smart filter water fountain of the present invention is worked, the valve (not shown) of blow-off pipe 4 is closed, and after work a period of time, when needing cleaning filter core 1, outlet pipe 5 is closed, open the valve of blow-off pipe 4, pressure water flows into bucket 2 by water inlet pipe 3 and is flowed out by blow-off pipe 4, realizes the cleaning to filter core 1.So smart filter water fountain of the present invention can be dismantled and can clean, and is very easy to use.
Essence of the present invention filter water fountain is as family expenses, pharmacy, food, beverage, wine brewing, hospital, school, food and drink, hotel, aircraft, train, warship, the boat, the general preferred advanced persons that adopt of industry such as factory, petrochemical industry purify waste water treating apparatus.
Claims (10)
1. nanometer order quartz molecule sieve filter core, it is characterized in that it comprises having nanometer level microporous quartzy cup (21) and be arranged on the antimicrobial nano material coating (22) that described cup reaches each nanometer level microporous sidewall on the cup outward, the material of wherein making described quartzy cup comprises by weight
Nanometer SiO
24～6 parts
Nano-ZnO
21～3 part
Nanometer Al
2O
33～5 parts
Described antimicrobial nano material coating comprises by weight percentage
Nanometer Ag 30%～50%
Nanometer SiO
2Colloidal sol 20%～60%
Nanometer ZrO
210%～40%.
2. nanometer order quartz molecule sieve filter core according to claim 1 is characterized in that described each nanometer level microporous aperture changes between 10nm～10000nm, the porosity is 25%～50%.
3. use the essence filter water fountain of claim 1 or 2 described nanometer order quartz molecule sieve filter cores, comprise bucket (2), water inlet pipe (3), outlet pipe (5) and be arranged on bucket (2) interior filter core (1) and filter (10), it is characterized in that described filter core (1) is connected with outlet pipe (5) with lid (9); Described filter (10) comprises by the container (7) of the micropore that gathers and places the interior absorption mineralizing material (11) of described container.
4. smart filter water fountain according to claim 3 is characterized in that described absorption mineralizing material (11) comprises 1～2 part in Himalayas white jade stone by weight, 1～2 part of Mount Taishan rutile, 1～2 part of Huashan gold mine lazulite, 1～2 part in Hengshan Mountain serpentine, 1～2 part of China's Heng Shan zeolite, 1～2 part in China's Song Shan platina ore, 1～2 part of zinc gold ore dodges in Wutai Mountain in China, 1～2 part of China's Mount Emei's medical stone, 5～10 parts of in 1～2 part in China's Jiuhuashan amethyst stone one or more and 5～10 parts of Chinese Wudang Mountain shenlongjia ginkgo wood active carbons and Chinese Qinling Mountains Kiwi berry rattan active carbons.
5. smart filter water fountain according to claim 3 is characterized in that also comprising the last magnetizer (6) and the following magnetizer (8) that place bucket (2) inner top and bottom respectively, has at least two through holes respectively on magnetizer on this (6) and the following magnetizer (8).
6. smart filter water fountain according to claim 4 is characterized in that also comprising the last magnetizer (6) and the following magnetizer (8) that place bucket (2) inner top and bottom respectively, has at least two through holes respectively on magnetizer on this (6) and the following magnetizer (8).
7. smart filter water fountain according to claim 5 is characterized in that described water inlet pipe (3) leads to down below the magnetizer (8).
8. smart filter water fountain according to claim 6 is characterized in that described water inlet pipe (3) leads to down below the magnetizer (8).
9. smart filter water fountain according to claim 4 is characterized in that described lid (9) is provided with blow-off pipe (4).
10. according to claim 7 or 8 described smart filter water fountains, it is characterized in that described lid (9) is provided with blow-off pipe (4).