CN1191880A - Multifunctional adhesive and its preparation - Google Patents
Multifunctional adhesive and its preparation Download PDFInfo
- Publication number
- CN1191880A CN1191880A CN98100346A CN98100346A CN1191880A CN 1191880 A CN1191880 A CN 1191880A CN 98100346 A CN98100346 A CN 98100346A CN 98100346 A CN98100346 A CN 98100346A CN 1191880 A CN1191880 A CN 1191880A
- Authority
- CN
- China
- Prior art keywords
- pimelinketone
- acetic acid
- multifunctional adhesive
- preparation
- cystose
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention belongs to the preparation of building and decoration material. The adhesive consists of polystyrene, cyclohexanone, polyvinyl acetate emulsion, rosin, ethylene-vinyl acetate copolymer emulsion, heavy calcium carbonate and talcum powder through mixing. It has high adhesion strength and water resistance and low cost, and it is suitable for building decoration.
Description
The present invention relates to a kind of multifunctional adhesive and preparation method thereof, relate to a kind ofly specifically, belong to the preparation of building and ornament materials mixed a kind of multifunctional adhesives and preparation method thereof that makes such as waste and old polystyrene cystose and pimelinketone, poly-acetic acid second dilute emulsions.
At present, waste and old polystyrene cystose, claim porous plastics again, they cause the pollution of environment quite serious, by the railway, on the road limit, river surface, the residential area is seen everywhere, and is both unhygienic, not attractive in appearance again, and the waste product rubbish that these waste and old polystyrene cystoses are a kind of very difficult degradeds is let alone down, and these waste and old polystyrene cystoses will be to the mankind's life and existence formation and generation harm greatly in the course of time.
The object of the present invention is to provide a kind ofly turns waste into wealth, and a kind of multifunctional adhesive of utilization of waste material and the preparation method of this tackiness agent thereof are to solve environmental pollution problems.
The object of the present invention is achieved like this, it mainly by polystyrene cystose, pimelinketone, poly-acetic acid second dilute emulsion, rosin, second rare-acetic acid ethylene copolymer emulsion, water-ground limestone, talcum powder form through mixing, stirring, it is characterized in that: it is the tackiness agent made from following weight percentages:
Polystyrene cystose 0.5-2
Pimelinketone 10-20
Poly-acetic acid second dilute emulsion 5-10
Rosin 1-6
Second is rare-acetic acid ethylene copolymer emulsion 15-35
Water-ground limestone 30-50
Talcum powder 4-10.
Its feature also is: described polystyrene cystose is waste and old polystyrene cystose.
The preparation method of a kind of multifunctional adhesive of the present invention is characterized in that:
1. above-mentioned raw materials by weight percent is purchased and weighs
2. rosin is put in the pimelinketone and dissolves, dissolution time is 48 hours, and is standby,
3. waste and old polystyrene cystose is mixed, stirs with pimelinketone, placed 24 hours, standby,
4. with above-mentioned two kinds of stock solution and poly-acetic acid second dilute emulsion and second rare-container that the acetic acid ethylene copolymer emulsion is together put into agitator mixes, churning time is 10 minutes,
5. in four kinds of solution of above-mentioned blended, successively add water-ground limestone and talcum powder more lentamente,
6. continue to stir, when above-mentioned mixed solution is stirred to white paste dope, stop to stir, churning time is 2 hours, promptly gets a kind of multifunctional adhesive product of the present invention.
Its feature also is: the weight of soaking rosiny pimelinketone solution is 80% of pimelinketone gross weight.
Its feature also is: the pimelinketone of dissolving polystyrene cystose is 20% of a pimelinketone gross weight.
A kind of multifunctional adhesive of the present invention, its bonding viscosity height, water tolerance is strong, and is with low cost, is the ideal material of architectural decoration, and its preparation has been played and has been turned waste into wealth, and utilization of waste material solves environmental pollution problems.
Below in conjunction with embodiment the present invention is described, the scheme of embodiment described here, do not limit the present invention, one of skill in the art can make improvements and change according to spirit of the present invention, described these improvement and variation all should be considered as within the scope of the invention, and scope and spirit of the present invention are limited by claim.
Embodiment:
One, to purchase: waste and old polystyrene cystose, pimelinketone, poly-acetic acid second dilute emulsion, rosin, second is rare-raw materials such as acetic acid ethylene copolymer emulsion, water-ground limestone, talcum powder,
Two, weigh by following weight: (Kg)
Polystyrene cystose 2
Pimelinketone 20
Poly-acetic acid second dilute emulsion 6
Rosin 4
Second is rare-acetic acid ethylene copolymer emulsion 20
Water-ground limestone 40
Talcum powder 8
Three, preparation process
1. 4Kg rosin is put into the pimelinketone container that has 16Kg and dissolved 48 hours, standby,
2. place another container to mix, stir with the 4Kg pimelinketone the waste and old polystyrene cystose of 2Kg again, placed 24 hours, standby,
3. with poly-acetic acid second dilute emulsion of above-mentioned two kinds of stock solution and 6kg and 20Kg second rare-acetic acid ethylene copolymer emulsion-stir, mix with the container of putting into agitator, churning time is 10 minutes.
4. in four kinds of solution of above-mentioned blended, successively add 40Kg water-ground limestone and 8Kg talcum powder more lentamente,
5. continue to stir, when above-mentioned mixed solution is stirred to white paste dope, stop to stir, churning time is 2 hours, promptly gets 100Kg a kind of multifunctional adhesive product of the present invention.
Four, a kind of multifunctional adhesive of the present invention can be used for the caking agent that bonding ceramic tile, timber floor, mosaic, label, plasterboard, glass, PVC plate and decorations are used.
Claims (5)
1, a kind of multifunctional adhesive, it mainly by polystyrene cystose, pimelinketone, poly-acetic acid second dilute emulsion, rosin, second rare-acetic acid ethylene copolymer emulsion, water-ground limestone, talcum powder form through mixing, stirring, it is characterized in that: it is the tackiness agent made from following weight percentages:
Polystyrene cystose 0.5-2
Pimelinketone 10-20
Poly-acetic acid second dilute emulsion 5-10
Rosin 1-6
Second is rare-acetic acid ethylene copolymer emulsion 15-35
Water-ground limestone 30-50
Talcum powder 4-10.
2, according to a kind of multifunctional adhesive of claim 1, its feature also is: described polystyrene cystose is waste and old polystyrene cystose.
3, the preparation method of a kind of multifunctional adhesive of the present invention is characterized in that:
1. above-mentioned raw materials by weight percent is purchased and weighs
2. rosin is put in the pimelinketone and dissolves, dissolution time is 48 hours, and is standby,
3. waste and old polystyrene cystose is mixed, stirs with pimelinketone, placed 24 hours, standby,
4. with above-mentioned two kinds of stock solution and poly-acetic acid second dilute emulsion and second rare-container that the acetic acid ethylene copolymer emulsion is together put into agitator mixes, churning time is 10 minutes,
5. in four kinds of solution of above-mentioned blended, successively add water-ground limestone and talcum powder more lentamente,
6. continue to stir, when above-mentioned mixed solution is stirred to white paste dope, stop to stir, churning time is 2 hours, promptly gets a kind of multifunctional adhesive product of the present invention.
4, according to the multifunctional adhesive of the method for claim 3 preparation, its feature also is: the weight of soaking rosiny pimelinketone solution is 80% of pimelinketone gross weight.
5, according to the multifunctional adhesive of the method for claim 3 preparation, its feature also is: the pimelinketone of dissolving polystyrene cystose is 20% of a pimelinketone gross weight.