CN1187289A - 一种地膜湿铺工艺 - Google Patents
一种地膜湿铺工艺 Download PDFInfo
- Publication number
- CN1187289A CN1187289A CN96109146A CN96109146A CN1187289A CN 1187289 A CN1187289 A CN 1187289A CN 96109146 A CN96109146 A CN 96109146A CN 96109146 A CN96109146 A CN 96109146A CN 1187289 A CN1187289 A CN 1187289A
- Authority
- CN
- China
- Prior art keywords
- film
- technique
- wet
- water
- mulch film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种地膜湿铺工艺。其目的在于提供一种原料易分解,对环境无污染;薄膜与土壤粘连充分,附着性好的地膜湿铺工艺;铺设工艺简单,效率高。本发明的技术解决方案是:(1)将变性淀粉、生物胶、海藻提取物,持水剂及杀虫剂等原料与水混合成浓度为2—8%的浆状物;(2)在田间将上述浆状物喷拉成膜;(3)将该膜进行化学强化;(4)将该膜进行热强化;(5)将经过强化后的膜直接湿铺于地表,待湿膜干燥后形成田间保护膜。
Description
本发明涉及一种地膜湿铺工艺。
目前普遍使用的农用地膜是采用聚乙烯为原料,在田间铺设的工艺,其缺点是:(1)原料不能分解,对环境污染大。(2)薄膜与土壤粘连不充分,附着性差。
本发明的目的在于提供一种可完全分解,对环境无污染;薄膜与土壤粘连充分,附着性好的地膜湿铺工艺。
用于实现本发明目的的技术解决方案,其特点在于:
(1)将变性淀粉、生物胶、海藻提取物,持水剂及杀虫剂等原料与水混合成浓度为2-8%的浆状物;
(2)在田间将上述浆状物喷拉成膜;
(3)将该膜进行化学强化;
(4)将该膜进行热强化;
(5)将经过强化后的膜直接湿铺于地表,待湿膜干燥后形成田间保护膜。
本发明的化点在于:
(1)这种工艺形成的薄膜由于反应物和生成物均为无害物质,在光、气、水和微生物联合作用下可以完全分解失效,对土壤、大气环境及作物生长发育无污染和危害,应用此工艺可替代或部分替代现有以聚乙烯为原料的塑料农用地膜的使用减少因使用塑料农用地膜带来的白色污染;
(2)田间湿铺膜干后能与土壤充分粘连,附着性好,不易被风吹起;
(3)这种湿铺工艺简单易行,效率高。
本工艺的成型原理是:
(1)将变性淀粉、海藻酸钠、淀粉基吸水树脂及生物胶与水混合形成粘稠的浆状物,原料的配比应当是:水92~99%,变性淀粉0.5~5%,海藻酸钠1~7‰,生物胶0.5~9‰,持水剂0.2~3‰,杀虫剂<0.001‰。
所述生物胶为以下原料的一种或几种的组合:瓜尔胶、沙嵩胶、琼脂,所述持水剂为淀粉基吸水树脂、沙蒿胶。
(2)经窄缝喷成薄膜,喷拉成形方法是将装状物加压后通过一宽度可调的窄缝喷入30℃以上的热强化剂溶液中,由于海藻酸离子与钙离子反应在膜中形成网状的海藻酸钙骨架,使薄膜不再能流动而定型强化,形成具有一定温强度的密实薄膜,此时的薄膜可用90℃以上的热水源烫1分钟以上,进一步提高其湿强度而成。
所述强化剂为Ca2(NO3)2或CaCL2。
(3)直接湿铺于田间,待水分干燥后形成一层厚度为几个微米到上百微米近似透明的覆盖物。
干膜的失效期可由原料组份和膜厚度及杀虫剂组分来调节,膜厚度可由改变窄缝喷口的宽度和改变浆状原料的浓度调节,提高强化剂的浓度和温度可提高湿膜的强度并且可缩短反应时间。
下面是本发明的一实施例:
(1)将原料的配比是:水97.33%,变性淀粉2%,海藻酸钠5‰,生物胶1.5‰,持水剂0.2‰,杀虫剂<0.01‰。
(2)经窄缝喷成薄膜,喷拉成形方法是将浆状物加压后通过一宽度可调的窄缝而成膜。
(3)将薄膜直接进入50℃的钙盐水溶液,由于海藻酸离子与钙离子反应在膜中形成网状的海藻酸钙骨架,使薄膜不再能流动而定型强化,形成具有一定湿强度的密实薄膜,此时的薄膜可用90℃以上的热水源烫1分钟以上,进一步提高其湿强度。
所述强化剂为Ca2(NO3)2或CaCL2。
(4)直接湿铺于田间,待水分干燥后形成一层厚度为几个微米到上百微米近似透明的覆盖物。
Claims (11)
1.一种地膜湿铺工艺,其特征在于:
(1)将变性淀粉、生物胶、海藻提取物,持水剂及杀虫剂等原料与水混合成浓度为2-8%的浆状物;
(2)在田间将上述浆状物喷拉成膜;
(3)将该膜进行化学强化;
(4)将该膜进行热强化;
(5)将经过强化后的膜直接湿铺于地表,待湿膜干燥后形成田间保护膜。
2.如权利要求1所述的地膜湿铺工艺,其特征在于:所述原料的配比是:水92~99%,变性淀粉0.5~5%,海藻酸钠1~7‰,生物胶0.5~9‰,持水剂0.2~3‰,杀虫剂<0.001‰。
3.如权利要求1或2所述的地膜湿铺工艺,其特征在于:所述原料的配比是:水97.33%,变性淀粉2%,海藻酸钠5‰,生物胶1.5‰,持水剂0.2‰,杀虫剂<0.01‰。
4.如权利要求1或2所述的地膜湿铺工艺,其特征在于:所述生物胶至少含有以下成份之一:瓜尔胶、沙蒿胶、琼脂。
5.如权利要求3所述的地膜湿铺工艺,其特征在于:所述生物胶至少含有以下成份之一:瓜尔胶、沙蒿胶、琼脂。
6.如权利要求1或2所述的地膜湿铺工艺,其特征在于:所述持水剂为淀粉基吸水树脂、沙蒿胶。
7.如权利要求3所述的地膜湿铺工艺,其特征在于:所述持水剂为淀粉基吸水树脂、沙蒿胶。
8.如权利要求1所述的地膜湿铺工艺,其特征在于:所述热强化是将化学强化后的膜放入90℃以上热水中烫1分钟以上。
9.如权利要求1所述的地膜湿铺工艺,其特征在于:所述湿膜化学强化方法是利用易溶于水的钙盐做强化剂,与海藻酸钠反应在膜中形成网状组织的海藻酸钠骨架,使膜丧失流动性而定型,并增强湿膜强度。
10.如权利要求9所述的地膜湿铺工艺,其特征在于:所述强化剂为Ca2(NO3)2或CaCL2。
11.如权利要求1或2所述的地膜湿铺工艺,其特征在于:喷拉成形方法是将浆状物加压后通过一宽度可调的窄缝喷入30℃以上的热强化剂溶液中定型后直接湿铺于地表。