CN1186846A - Aluminium rolling oil composition with annealing cleanness - Google Patents
Aluminium rolling oil composition with annealing cleanness Download PDFInfo
- Publication number
- CN1186846A CN1186846A CN96114016A CN96114016A CN1186846A CN 1186846 A CN1186846 A CN 1186846A CN 96114016 A CN96114016 A CN 96114016A CN 96114016 A CN96114016 A CN 96114016A CN 1186846 A CN1186846 A CN 1186846A
- Authority
- CN
- China
- Prior art keywords
- component
- composition
- rolling oil
- oil
- accounts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The aluminium rolling oil composite contains intersoluble C8-C18 emtrol and fatty ester, and has good annealing clearness and abrasion resistance. The said composite of the present invention contains also proper amount of antioxidant, antistatic agent, antibubbling agent and narrow-fraction alpha-polyolefine synthetic oil or refined mineral oil, and all this makes it has excellent antioxidant property and safety.
Description
The invention provides a kind of aluminium rolling oil composition with fine annealing detergency.Said composition mainly comprises Fatty Alcohol(C12-C14 and C12-C18) and fatty acid ester, and being specially adapted to close-cut fraction polyalphaolefin synthetic oil is base oil, and has good resistance to abrasion, antioxygen and characteristics such as safe in utilization.
Known Fatty Alcohol(C12-C14 and C12-C18) and fatty acid ester have certain abrasion resistance and annealing cleanness, therefore can be added to them in some base oil by a certain percentage and add the compound of other performance, be deployed into multiple aluminium rolling oil, can be used for aluminium foil, the aluminium sheet of rolling different mass and thickness.
Japanese Patent JP0165194 relates to the aluminum foil rolling oil compositions of a kind of only fatty alcohol, fatty acid ester and base oil.Said composition is characterised in that 40 ℃ of kinematic viscosity of base oil are 1.0～4.5mm
2/ S, Fatty Alcohol(C12-C14 and C12-C18) general formula are R
1OH (R
1For having the alkyl of 8～11 carbon atoms) the fatty acid ester general formula is R
2COOR
3(R
2For having the alkyl of 5～10 carbon atoms, R
3For having the alkyl of 1～4 carbon atom), the total content of Fatty Alcohol(C12-C14 and C12-C18) and fatty acid ester is 1～8m%.Said composition only relates to annealing cleanness and does not relate to resistance to abrasion, antioxygen and security.
Do not see that as yet disclosed is the aluminium rolling oil composition patent of base oil with the polyalphaolefin synthetic oil both at home and abroad.
The purpose of this invention is to provide a kind of aluminium rolling oil composition with fine annealing detergency and resistance to abrasion.
The composition that the present invention proposes mainly comprises Fatty Alcohol(C12-C14 and C12-C18) component (A) and fatty acid ester component (B).The general formula of component (A) is:
R
0R in the OH formula
0For having the alkyl of 8～18 carbon atoms.
Component (B) can be dissolved each other with component (A), and the general formula of component (B) is: R
1COOR
2R in the formula
1Representative has the alkyl of 6～22 carbon atoms, R
2Representative has the alkyl of 1-6 carbon atom.For example: component (A) can be C
8H
17OH, C
12H
25OH, C
13H
37OH; Component (B) can be C
7H
15COOCH
3, C
11H
23COOCH
3, C
16H
33COOC
4H
9
The annealing cleanness of aluminium rolling oil is meant under annealing temperature, oil product will be rapidly from aluminium sheet or aluminium foil surface volatilization, do not stay any vestige, be that product surface does not have spot, this just requires base oil must have suitable viscosity, narrower boiling range scope, and when the structure of compound and base oil adapt, just compatibility preferably can be arranged, also could guarantee the annealing cleanness of oil product.In addition, base oil has higher flash-point, is the essential condition that guarantees the aluminium rolling safety in production.For the base oil in the present composition, it is characterized in that the boiling range scope less than 70 ℃, 40 ℃ of kinematic viscosity are 1.0～4.0mm
2/ S.Fatty Alcohol(C12-C14 and C12-C18) (A) can be preferably the R in its general formula
0Be the alkyl with 8～16 carbon atoms, fatty acid ester (B) can be preferably the R in its general formula
1Be alkyl with 8～18 carbon atoms, R
2It is compound with 1～4 carbon atom alkyl.
Composition stable in properties proposed by the invention, and have good annealing cleanness and resistance to abrasion.Total add-on of Fatty Alcohol(C12-C14 and C12-C18) (A) and fatty acid ester (B) is 1～10m% of aluminium rolling oil composition, and surplus is a base oil.Wherein the consumption of component (B) can be 10～90m% of component (A) and component (B) total mass.Rolling oil composition for rolling aluminium foil is preferably 50～90m%; Rolling oil composition for Rolling Aluminium Plate is preferably 10～50m%.When component (B) mass percent exceeds this scope, can influence the annealing cleanness and the resistance to abrasion of aluminium rolling oil.Usually the oil film strength of aluminium rolling oil is 2352 to 294.0N, and annealing cleanness is 2～4 grades, and the composition oil film strength that the present invention proposes is 274.4～343.0N, and annealing cleanness is 1～2 grade.
Further aim of the present invention is when guaranteeing good annealing cleanness and resistance to abrasion, improves the antioxidant property and the safety in utilization of oil product.
Aluminium rolling oil recycles at a certain temperature for a long time, and with processing aluminium material surface be in tight the contact with aluminium powder, under the katalysis of aluminium, the oxidation meeting of hydro carbons is quickened greatly, generate some acids and other carbonyl compound, acid number is raise, and annealing cleanness degenerates, the quality of influence of rolled product.Add an amount of oxidation inhibitor as can be seen by table-1 and can make oil product have good oxidation-resistance, guarantee the annealing cleanness of product.
Table 1
Annotate: test conditions is 110 ℃, add 1% aluminium bits.
| Oil sample | Virgin state | After the 48h oxidation | ||||
| Acid number mgKOH/g | 40 ℃ of mm of viscosity 2/s | Annealing cleanness | Acid number mgKOH/g | 40 ℃ of mm of viscosity 2/s | Annealing cleanness | |
| Base oil base oil+an amount of oxidation inhibitor | 0.01?????? | 2.23 | 1 grade 1 grade | ??0.56 ??0.01 | ??2.35 ??2.26 | 4～5 grades 1～2 grade |
In the composition proposed by the invention, the consumption of various additives component sees Table 2:
Table 2
| Component | Optional value m% | Optimum value m% |
| (A) fatty acid ester of Fatty Alcohol(C12-C14 and C12-C18)+(B) | ????1～10 | ????3～8 |
| Oxidation inhibitor | 0.1～0.5 | ?0.1～0.3??? |
| Static inhibitor | 0.0001～0.005 | ?0.0001～0.001?? |
| Kilfoam | 0.0001～0.005 | ?0.0001～0.001??? |
| Base oil | Surplus | Surplus |
Above-mentioned each component is mixed under 25～50 ℃ and stirred 3 hours, can obtain the aluminium rolling oil of different purposes, modulation is convenient, all can implement in common laboratory.
The ratio of various additives is by boxlike annealing test method in the present composition, and test such as load carrying capacity of lubricant assay method (four ball methods) is determined, the actual applying working condition that ROLLING OIL has been simulated in these tests preferably.Wherein boxlike annealing test method is: the standard aluminum box (adopts fine aluminium to make, aluminium box size Φ 75mm * h12～18mm, have three apertures on the lid, hole width between centers lid limit 2mm, the three hole lines of centres are mutually hexagonal angle) after NaOH solution (mass ratio 1: 15), the erosion of salpeter solution (volume ratio 1: 5) chemistry are washed, wash twice with dehydrated alcohol, dry back is checked and is had or not blackening.If do not have, then pipette the 0.15ml oil sample to the aluminium box with microsyringe, build lid, put into retort furnace, constant temperature 1h under 345 ± 5 ℃ of conditions closes electricity then, when furnace temperature is reduced to room temperature, takes out the grading of aluminium box.Ranking method is: 1 grade for there not being stain; 2 grades is atomic stain; 3 grades is slight stain; 4 grades are flavescence, peripheral deepening; 5 grades are obfuscation; 6 grades for shading and black slag being arranged.
The following stated embodiment describes the present invention in detail, and in these embodiments, unless otherwise indicated, all umbers and per-cent are all by mass.
Embodiment 1
20g is had the Fatty Alcohol(C12-C14 and C12-C18) of 8 carbon atoms and 30g, and to have general formula be C
7H
15COOCH
3Fatty acid ester mix, under 40 ℃, stir, the products obtained therefrom physicochemical data is: density (20 ℃) 0.8011mg/cm
3Hydroxyl value 158mgKOH/g saponification value 123mgKOH/g
Embodiment 2
It is C that 5 parts of Fatty Alcohol(C12-C14 and C12-C18) with 12 carbon atoms and 20 parts are had general formula
11H
23COOCH
3Fatty acid ester mix, under 45 ℃, stir, the products obtained therefrom physicochemical data is: density (20 ℃) 0.8098mg/cm
3Hydroxyl value 151mgKOH/g saponification value 126mgKOH/g
Embodiment 3
The Fatty Alcohol(C12-C14 and C12-C18) and the 30g that 20g are had 12 carbon atoms have general formula C
16H
33COOC
4H
9Fatty acid ester mix to be incorporated under 45 ℃ and stir, products obtained therefrom, physicochemical data is: density (20 ℃) 0.8359mg/cm
3Hydroxyl value 187mgKOH/g saponification value 97mgKOH/g
Embodiment 4
40g is had the Fatty Alcohol(C12-C14 and C12-C18) of 18 carbon atoms and 20g, and to have general formula be C
18H
33COOC
4H
9Fatty acid ester mix, under 50 ℃, stir, the products obtained therefrom physicochemical data is:
Density (20 ℃) 0.8438mg/cm
3Hydroxyl value 242mgKOH/g saponification value 31mgKOH/g
Embodiment 5
6 parts of Fatty Alcohol(C12-C14 and C12-C18) with 12 carbon atoms and 4 parts had general formula C
11H
23COOCH
3Fatty acid ester mix to be incorporated under 40 ℃ and stir, the products obtained therefrom outward appearance is a transparent liquid, the physico-chemical analysis data are:
Density (20 ℃) 0.8180mg/cm
3Hydroxyl value 209mgKOH/g saponification value 33mgKOH/g
Embodiment 6
8 parts of Fatty Alcohol(C12-C14 and C12-C18) with 12 carbon atoms and 2 parts had general formula C
7H
15COOCH
3Fatty acid ester mix, under 40 ℃, stir, products obtained therefrom is a transparent liquid, the physico-chemical analysis data are:
Density (20 ℃) 0.8067mg/cm
3Hydroxyl value 224mgKOH/g saponification value 26mgKOH/g
Embodiment 7
The composition of embodiment 1 to embodiment 6 gained is joined respectively in the polyalphaolefin synthetic oil of different fraction scopes, and add 0.2m% oxidation inhibitor 3 μ g/g kilfoams and 3 μ g/g static inhibitor, can modulate the aluminium rolling oil of different purposes.The results are shown in Table 3 with boxlike annealing test method evaluation annealing cleanness:
Table 3
| Numbering | Base oil fraction ℃ | 40 ℃ of viscosity mm 2/s | Composition | Dosage m% | Annealing cleanness | Oil film strength N | Purposes |
| 1# oil | 200～239 | ??1.62 | Example 1 product | ??3 | 1 grade | 303.8 | Rolling aluminum foil |
| 2# oil | 205～235 | ??1.70 | Example 2 products | ??5 | 1 grade | 294.0 | Rolling aluminum foil |
| 3# oil | 205～235 | ??1.70 | Example 3 products | ??5 | 2 grades | 294.0 | Rolling aluminum foil |
| 4# oil | 235～270 | ??2.37 | Example 4 products | ??6 | 2 grades | 313.6 | Roll aluminium sheet |
| 5# oil | 235～265 | ??2.28 | Example 5 products | ??5 | 1 grade | 303.8 | Roll aluminium sheet |
| 6# oil | 235～265 | ??2.28 | Example 6 products | ??8 | 1 grade | 333.2 | Roll aluminium sheet |
Data results proves: add aluminium rolling oil composition provided by the present invention, can make aluminium rolling oil have good annealing cleanness, resistance to abrasion.
Claims (9)
1, a kind of aluminium rolling oil composition comprises base oil, it is characterized in that mainly containing in the said composition Fatty Alcohol(C12-C14 and C12-C18) (A) and fatty acid ester (B), and component (A) general formula is: R
0OH (R
0For containing the alkyl of 8～18 carbon atoms), component (B) can be dissolved each other with component (A), and the general formula of component (B) is: R
1COOR
2(R in the formula
1Representative has the alkyl of 6～22 carbon atoms, R
2Representative has the alkyl of 1～6 carbon atom).
2,, it is characterized in that base oil be the boiling range scope less than 70 ℃, flash-point (remaining silent) is 1.0～4.0mm greater than 80 ℃, 40 ℃ kinematic viscosity according to the described aluminium rolling oil composition of claim 1
2Close-cut fraction polyalphaolefin synthetic oil or the refined mineral oil of/s.
3, according to the described aluminium rolling oil composition of claim 1, it is characterized in that: R in component (A) general formula
0For having the alkyl of 8～16 carbon atoms, the R in component (B) general formula
1For having the alkyl of 8～18 carbon atoms, R
2For having the alkyl of 1～4 carbon atom.
4, according to the described aluminium rolling oil composition of claim 1, it is characterized in that: total consumption of Fatty Alcohol(C12-C14 and C12-C18) (A) and fatty acid ester (B) is 1-10m%, and surplus is a base oil.
5, according to the described aluminium rolling oil composition of claim 4, when it is characterized in that being used for rolling aluminium foil, the mass percent that component (B) accounts for component (A) and component (B) total mass is 50～90m%; When being used for Rolling Aluminium Plate, the mass percent that component (B) accounts for component (A) and component (B) total mass is 10～50m%.
6,, it is characterized in that also containing in the said composition oxidation inhibitor, static inhibitor, kilfoam according to the described aluminium rolling oil composition of claim 1.
7, according to the described aluminium rolling oil composition of claim 6, it is characterized in that Fatty Alcohol(C12-C14 and C12-C18) in the said composition (A) and fatty acid ester (B) account for 1～10m%, oxidation inhibitor accounts for 0.1～0.5m%, static inhibitor accounts for 0.0001～0.005m%, kilfoam accounts for 0.0001～0.005m%, and surplus is a base oil.
8, according to the described aluminium rolling oil composition of claim 6, it is characterized in that Fatty Alcohol(C12-C14 and C12-C18) in the said composition (A) and fatty acid ester (B) account for 3～8m%, oxidation inhibitor accounts for 0.1～0.3m%, and static inhibitor accounts for 0.0001～0.001m%, kilfoam accounts for 0.0001～0.001m%, and surplus is a base oil.
9,, it is characterized in that each component was fully stirred 3 hours down at 25～50 ℃ according to claim 6,7 or 8 described aluminium rolling oil compositions.