CN1181142C - Porcelain-like paint and its prepn - Google Patents
Porcelain-like paint and its prepn Download PDFInfo
- Publication number
- CN1181142C CN1181142C CNB021325537A CN02132553A CN1181142C CN 1181142 C CN1181142 C CN 1181142C CN B021325537 A CNB021325537 A CN B021325537A CN 02132553 A CN02132553 A CN 02132553A CN 1181142 C CN1181142 C CN 1181142C
- Authority
- CN
- China
- Prior art keywords
- water
- porcelain
- auxiliary agent
- whiteruss
- viscotrol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to building material, particularly to porcelain-like paint and a preparing method thereof. The porcelain-like paint is prepared from 20 to 30 wt% of sierozem powder, 14 to 20 wt% of talcum powder, 14 to 20 wt% of ground limestone, 0.25 to 0.4 wt% of methyl cellulose or hydroxypropyl cellulose, 0.01 to 0.03 wt% of polyacrylamide, 30 to 45 wt% of water and proper quantities of auxiliary agent. The porcelain-like paint has the characteristics of high covering rate, strong adhesive force, no discoloration or facing, no cracking, no skinning, high-low temperature resistance, high water resistance, scrubbing resistance, easy construction and no deterieration, and the preparing method is easy to popularize.
Description
Technical field: the present invention relates to a kind of material of construction, promptly a kind of porcelain-imitated coating and preparation method.
Technical background: in prior art, porcelain-imitated coating is of a great variety, disclose a kind of name as Chinese invention patent ublic specification of application CN1127773A and be called " " Zhugang " paint for wall surface ", its prescription mainly is made up of starch, carboxymethyl cellulose, silicon sol, urea-formaldehyde resin, water-ground limestone, talcum powder, ultramarine and water; Its weight percent is starch 3-10, carboxymethyl cellulose 0.1-3, silicon sol 1-20, urea-formaldehyde resin 0.5-15, water-ground limestone 20-40, talcum powder 1-20, ultramarine 0.05-0.5, water 40-50.Its shortcoming is to contain the formaldehyde composition, and is harmful.The product luminance brightness is low simultaneously, poor water resistance.
Summary of the invention: the objective of the invention is provides a kind of safety, environmental protection, improved porcelain-imitated coating of performance and preparation method at above-mentioned deficiency.
Technical solution of the present invention is: porcelain-imitated coating is prepared from by following raw materials by weight percent: grey calcium powder 20-30%, talcum powder 14-20%, water-ground limestone 14-20%, methylcellulose gum or hydroxypropylcellulose 0.25-0.4%, polyacrylamide 0.01-0.03%, water 30-45%, auxiliary agent are an amount of.
Described auxiliary agent is Viscotrol C 0.025-0.075% and whiteruss 0.025-0.075%.
Described auxiliary agent can also be Viscotrol C 0.02-0.06%, whiteruss 0.02-0.06% and 638 wetting agent 0.01-0.03%.
Above-mentioned described auxiliary agent also contains an amount of borax, alum, salt.
The water-ground limestone good film-forming property improves coating hardness; Methylcellulose gum or hydroxypropylcellulose are used to improve the cementing properties of coating; Polyacrylamide suspension, viscosity are good, are used to improve the water tolerance of coating; Viscotrol C and whiteruss are used to improve the light of coating; 638 wetting agents (market is on sale) humidity is good, and hot weather construction is convenient; Borax, alum, salt are properties-correcting agent, improve contracting property, the toughness of coating, do not come off.
The preparation method: 1, methylcellulose gum is joined in 100 ℃ of hot water, on the bubble 20-30 minute, stir, pour into then in the cold water, constantly stir, to the dissolving back is stand-by fully;
2, polyacrylamide, 638 wetting agents are dissolved in (about 80 degree) in the warm water, stand-by after treating to dissolve fully;
3, the 1st glue that obtains of step is injected in the stirred pot, injects tap water then, during water filling with adjuvant used, pour in the stirred pot after filtering, stirred 10 minutes;
4, add the 2nd step solution again, stirred 15 minutes;
5, add ash charge calcium powder, talcum powder, heavy calcium carbonate at last successively, be stirred to no particle.
6, go out jar, it is even to regrind with water mill, and pack draws finished product.
Advantage of the present invention is: 1, fineness, hiding rare are good.2, viscosity, hardness are good, attached Gai Liqiang.3, nonpoisonous and tasteless, resistance to acids and bases is strong.4, do not fade behind the blade coating, do not fade, do not split, non-scale.5, easily construct, never degenerate, high-low temperature resistant.6, smooth smooth, good brightness, good hand touch behind the blade coating.7, strong, the scrubbing resistance of water tolerance.8, cost is low, and cold method for making is easily promoted.
Below in conjunction with embodiment the present invention is described in further detail:
Embodiment:
Embodiment 1
Porcelain-imitated coating is prepared from by following raw materials by weight percent: grey calcium powder 25%, talcum powder 20%, water-ground limestone 20%, methylcellulose gum or hydroxypropylcellulose 0.3%, polyacrylamide 0.02%, water 34.68%.
Embodiment 2
Porcelain-imitated coating is prepared from by following raw materials by weight percent: grey calcium powder 28%, talcum powder 18%, water-ground limestone 18%, methylcellulose gum or hydroxypropylcellulose 0.4%, polyacrylamide 0.01%, water 35.51%, Viscotrol C 0.04%, whiteruss 0.04%.
Embodiment 3
Porcelain-imitated coating is prepared from by following raw materials by weight percent: grey calcium powder 20%, talcum powder 22%, water-ground limestone 20%, methylcellulose gum or hydroxypropylcellulose 0.3%, polyacrylamide 0.02%, water 37.58%, Viscotrol C 0.04%, whiteruss 0.04%, 638 wetting agent 0.02%.
Embodiment 4
Porcelain-imitated coating is prepared from by following raw materials by weight percent: grey calcium powder 25%, talcum powder 18%, water-ground limestone 18%, methylcellulose gum or hydroxypropylcellulose 0.3%, polyacrylamide 0.02%, water 38.58%, Viscotrol C 0.04%, whiteruss 0.04%, 638 wetting agents 0.02%, borax, alum, salt are an amount of.
Embodiment 5
The porcelain-imitated coating preparation method: to prepare 1.4 tons of coating is example
1, methylcellulose gum 4.15kg is joined in 25kg, the 100 ℃ of hot water bubble and went up 20-30 minute, pour dissolving in the 225kg cold water then into, it is stand-by to treat to be dissolved into fully liquid back, needs to stir.
2, polyacrylamide 0.25kg, 638 wetting agent 0.25kg being put into 10kg warm water (about 80 degree) treats to dissolve fully back stand-by.
3, the 1st step glue is injected in the stirred pot, injects the about 275kg of tap water then, during water filling with used Viscotrol C 0.5kg, whiteruss 0.5kg, an amount of borax, alum, salt, the filter bag of packing into filter once pour in the stirred pot, stirring 10 minutes.
4, add the 2nd step solution again, stirred 15 minutes.
5, add successively ash charge calcium powder 350kg, talcum powder 250kg, heavy calcium carbonate 250kg, be stirred to no particle.
6, go out jar, draw finished product with regrind even, pack of water mill.
Claims (5)
1, a kind of porcelain-imitated coating is characterized in that it is prepared from by following raw materials by weight percent: basic Mierocrystalline cellulose 0.25-0.4%, polyacrylamide 0.01-0.03% in grey calcium powder 20-30%, talcum powder 14-20%, water-ground limestone 14-20%, methylcellulose gum or the hydroxyl, water 30-45%, auxiliary agent are an amount of.
2,, it is characterized in that described auxiliary agent is Viscotrol C 0.025-0.075% and whiteruss 0.025-0.075% according to the described porcelain-imitated coating of claim 1.
3,, it is characterized in that described auxiliary agent is Viscotrol C 0.02-0.06%, whiteruss 0.02-0.06% and 638 wetting agent 0.01-0.03% according to the described porcelain-imitated coating of claim 1.
4,, it is characterized in that described auxiliary agent also contains an amount of borax, alum and salt according to claim 2 or 3 described porcelain-imitated coatings.
5, a kind of method for preparing the described porcelain-imitated coating of claim 3 is characterized in that being finished by following steps:
(1) methylcellulose gum is joined in 100 ℃ of hot water, on the bubble 20-30 minute, stir, pour into then in the cold water, constantly stir, to the dissolving back is stand-by fully;
(2) polyacrylamide, 638 wetting agents are put into 80 ℃ of warm water, stand-by after treating to dissolve fully;
(3) glue that (1) step was obtained injects in the stirred pot, injects tap water then, with pouring in the stirred pot after used Viscotrol C and the whiteruss filtration, stirs 10 minutes during water filling;
(4) add (2) step solution again, stirred 15 minutes;
(5) add ash charge calcium powder, talcum powder and heavy calcium carbonate at last successively, be stirred to no particle;
(6) go out jar, it is even to regrind with water mill, and pack draws finished product.