CN1174264A - 阻燃喷胶棉及其生产工艺 - Google Patents

阻燃喷胶棉及其生产工艺 Download PDF

Info

Publication number
CN1174264A
CN1174264A CN 96117063 CN96117063A CN1174264A CN 1174264 A CN1174264 A CN 1174264A CN 96117063 CN96117063 CN 96117063 CN 96117063 A CN96117063 A CN 96117063A CN 1174264 A CN1174264 A CN 1174264A
Authority
CN
China
Prior art keywords
fireproof
spun
bonded fabric
retardant
fire retardant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 96117063
Other languages
English (en)
Inventor
黄松钦
黄光华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 96117063 priority Critical patent/CN1174264A/zh
Publication of CN1174264A publication Critical patent/CN1174264A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种阻燃喷胶棉及其生产工艺,它是在已经开棉、梳棉、成型的纤维棉片采用喷洒或浸入法使其表面包覆一层由丙烯酸乳液和由磷氮系化合物阻燃剂或和卤系化合物阻燃剂与增溶剂、水等组成阻燃粘合胶,本发明制作的阻燃喷胶棉除具有一般喷胶棉优点外,还具有遇火不燃烧,防火性能佳,可广泛用于工业、生活各领域。

Description

阻燃喷胶棉及其生产工艺
本发明属于纤维制品---阻燃喷胶棉及其生产工艺。
现有市售的喷胶棉轻便、耐用,是一种使用面比较广的纤维制品,然而由于它不防火,易燃等缺点极大的限制了它的用途。
本发明目的在于克服现有技术之缺点而提供一种阻燃喷胶棉及其生产工艺。
阻燃喷胶棉是在已经开棉机、梳棉机、成型机加工处理成的膨松、压叠成型的涤纶纤维棉片用浸入或喷洒方法让其表面包复一层由丙烯酸乳液与磷氮系化合物阻燃剂和或卤系化合物阻燃剂、增溶剂、水等原料配制成的阻燃粘合胶。喷胶棉生产工艺流程是:
材料选用,纤维棉片加工,阻燃粘合胶配制,涂复,烘干定型,成品。
现将具体生产工艺描述如下:
一、材料选用
1、纤维材料选用:本发明选用聚脂类纤维,如涤纶纤维,其熔点为240-260℃,丹尼数为30-150。
2、粘合剂:本发明选用丙烯酸乳液如IR-407树脂乳液做粘合剂,它用于纺织物上有着良好的回弹性和耐干湿洗性。
3、阻燃剂:本发明选用的阻燃剂有磷氮系化合物阻燃剂或是卤系化合物阻燃剂或是磷氮系化合物阻燃剂和卤系阻燃剂混合物。上述的磷氮系化合物阻燃剂可以是磷酸氢二铵、磷酸二氢铵、OO=乙基-N,N-双(2-羟基二基)氨甲基磷酸酯,2撑双[三( 2-氯三基)溴化磷]。上述的卤系阻燃剂可以是磷酸三(2、3-二氯丙基)酯,磷酸三(2-溴-3-氯丙基)酯,缩水甘油二溴甲苯基醚。
4、增溶剂:本发明选用增溶剂是尿素,氯化铵。
5、消泡剂:本发明选用含硅消泡剂。
6、PH值调节剂:本发明选用醋酸和醋酸钠做PH值调节剂。
三、纤维棉片加工:将涤纶纤维依次放入开棉机、给棉机、梳棉机、成型机加工成膨松、厚薄均匀的纤维棉片待用。
四、阻燃粘合胶配制:
1、配制:
按一定配比称取的粘合剂、阻燃剂、水以及增溶剂、消泡剂、PH值调节剂备好待用。
2、混合搅拌:
先将阻燃剂与增溶剂倒入搅拌斧中,加水搅拌均匀成阻燃剂混合物。
3、阻燃粘合剂制作:
将粘合剂倒入另一个搅拌斧中,并将上述已充分搅匀的阻燃剂溶液慢慢加入粘合剂中,边加边搅拌,加入消泡剂消泡,同时用PH值调节剂调节溶液PH值呈中性,即配制成阻燃粘合胶。
五、涂复:
将上述已配制好的阻燃粘合胶用喷胶机均匀地喷洒或用浸入法在上述已排叠成一定厚度的棉片两个面上,达到将纤维棉片与空气隔离之目的。
六、烘干:
将已经均匀喷洒或浸有阻燃粘合胶的棉片送入烘干机内烘干,分次进行烘平。烘干温度控制在80°-150℃,每次烘干时间5-10分钟,即制成本发明成品阻燃喷胶棉。
与现有技术相比,本发明的阻燃喷胶棉除具有一般喷胶棉所具有的松、柔软、不发霉、耐洗等特点外,还具有阻燃防火或只熔不燃功能,大大拓展了原有喷胶棉用途,可广泛地用于工业、生活各个领域。
附图是本发明生产工艺流程图。
下面通过实施例详细描述本发明。
实施例1是旅行睡袋、风衣等100g/m2的薄形阻燃喷胶棉,制作。
以磷酸二氢铵250kg,尿素3kg,氯化铵3kg,加水1200kg,混合搅拌均匀后,滴加入200kg的PrinalIR-407树脂乳液中,边加边搅拌混合,加入含硅消泡剂消泡,以工业纯醋酸和醋酸钠(少量)调节溶液PH值呈中性,即制成阻燃胶。以熔点254℃丹尼数为30的用上述通常喷胶棉生产工艺生产好100g/m2薄形涤纶纤维棉片,将棉片一个面用喷洒法(喷胶压力控制在1kg)先使棉片纤维表面包复一层阻燃粘合胶液薄膜后,送进烘干机,进行第一道烘干,烘干温度约100℃,时间5分钟,第一道烘干后,再在棉片的另一面喷洒阻燃胶后,进行第二道烘干,烘干温度120℃,时间5分钟后,再进行第三道烘干,烘干温度150℃,时间5分钟,彻底烘干并热定型后即可截剪包装。
实施例2,生产250g/m2以上的阻燃喷胶棉棉絮,座垫等工艺。
涤纶纤维丹尼数为90,熔点254℃,按上述常规生产工艺制作好250g/m2棉片,喷胶压力控制在3kg左右,三次烘干温度为150℃、170℃、200℃,其余工艺同实施例1。

Claims (7)

1、一种阻燃喷胶棉及其生产工艺之阻燃喷胶棉,其特征在于聚酯纤维棉片表面包复一层由磷氮系化合物阻燃剂和或卤系化合物阻燃剂与丙烯酸乳液、水、增溶剂组成的阻燃粘合胶。
2、根据权利要求1所述的阻燃喷胶棉,其特征在于阻燃粘合胶配制方法是先将磷氮系化合阻燃剂或和卤系化合物阻燃剂与增溶剂、水均匀成阻燃剂混合物,再将阻燃剂混合物边搅拌边加入丙烯酸乳液中,加适量消泡剂消除泡沫,并用PH值调节剂调节溶液呈中性即可。
3、根据权利要求1所述的阻燃喷胶棉,其特征在于上述的磷氮化合物阻燃剂为磷酸氢二铵、磷酸二氢铵、OO=乙基-N,N-双(2-羟基二基)氨甲基磷酸酯,2撑双[三(2-氯三基)溴化磷]。
4、根据权利要求1所述的阻燃喷胶棉,其特征在于上述磷酸三(2、3-二氯丙基)酯,磷酸(2-溴-3-氯丙基)酯,缩水甘油二溴甲苯基醚。
5、根据权利要求1所述的阻燃喷胶棉,其特征在于上述的丙烯酸乳液是Prinal IR-407树酯乳液。
6、根据权利要求1所述的阻燃喷胶棉,其特征在于上述的增溶剂是尿素、氯化铵。
7、一种阻燃喷胶棉及其生产工艺之生产工艺,其特征在于其工艺流程包括材料选用,纤维棉片加工,阻燃粘合胶配制,涂复,烘干定型,成品。
CN 96117063 1996-08-16 1996-08-16 阻燃喷胶棉及其生产工艺 Pending CN1174264A (zh)