CN1174133A - Artificial amber and its production process - Google Patents
Artificial amber and its production process Download PDFInfo
- Publication number
- CN1174133A CN1174133A CN 96111164 CN96111164A CN1174133A CN 1174133 A CN1174133 A CN 1174133A CN 96111164 CN96111164 CN 96111164 CN 96111164 A CN96111164 A CN 96111164A CN 1174133 A CN1174133 A CN 1174133A
- Authority
- CN
- China
- Prior art keywords
- mould
- polyester resin
- unsaturated polyester
- cobalt naphthenate
- cyclohexanone peroxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Unsturated polyester resin as main raw material, cyclohexanone peroxide and cobalt naphthenate as supplementary material, and proper amount of pigment size are compounded into embedding body. Inside mould, proper amount of cpdd resin is first poured as bottom layer, and after treated dry specimen is placed, several times of pouring and demoulding, artificial amber is formed. Artificial amber product thus produced has animated shape and transparent and sparkling appearance exactly like natural amber and is beautiful handicraft with high decorative and practical value. The said method can also used to proted biological specimen for a long period.
Description
The present invention relates to a kind of ambroid and manufacture craft.
Generally organism is made dry preserved specimen or soaks sample, preserve difficulty; Existing is that raw material comes the embedding biological sample with methacrylic acid, its cost of material height, and complex process, the production cycle is long, is generally more than the week, and the production difficulty is big." the ambroid technology " that Chinese patent CN1034562 is proposed adopts unsaturated polyester resin 191 to produce the amber craft product, can not the embedding biological sample.
The present invention is directed to above-mentioned existing problems, its purpose is to provide a kind of employing unsaturated polyester resin to produce ambroid and manufacture craft.
The present invention copys the natural amber pattern, the organism that insect, flowers and plants, fishes and shrimps etc. is had ornamental value and value for preservation is embedded in the transparent high polymer, parison is after skiving, polishing, have form bright characteristics true to nature, life-like, transparent, its shape, look and natural amber are closely similar, be a kind of exquisite handicraft with sight and practicality, but its long preservation biological sample.
The present invention is to be main material with the unsaturated polyester resin, and cyclohexanone peroxide and cobalt naphthenate are batching, and their proportioning is: unsaturated polyester resin: cyclohexanone peroxide: cobalt naphthenate=100: 1-6: 0.1-1.Its manufacture craft is: (1) gathers fresh and alive organism, and according to viewing and admiring needs, it is put in order limb or spreads the wings, oven dry setting under 40-60 ℃ of temperature, fish and mollusk form the dehydration sample after handling with organic solvent; (2) by unsaturated polyester resin: cyclohexanone peroxide: the proportioning of cobalt naphthenate=100: 1-6: 0.1-1 mixes; (3) shape is as required selected corresponding mould for use, and spraying one deck releasing agent in mould is with the mould dry for standby; (4) raw material with above-mentioned allotment pours into the mould bottom, after polyase 13 0-60 under 40-50 ℃ the temperature minute, at ambient temperature, above-mentioned made sample body is put in the mould, divided subsequently for several times to pour into deployed raw material, sample is embedded in wherein, for making the thick glass of 1-3mm, then need add surperficial felt or glass fabric ex hoc genus anne material, after the parison demoulding, carry out the skiving processing and get final product.Unsaturated polyester resin can adopt 195,196,198,189,191, No. 102.
Below in conjunction with embodiment the present invention is described in detail.
Embodiment 1: gather butterfly, beetle, crab, fresh and alive organism such as shrimp, through spreading the wings, whole limb makes it keep mutually vivid as gives birth to attitude, and former state is put into baking oven drying for standby under 40-60 ℃ temperature, adopt 100 parts unsaturated polyester resin, 2 parts cyclohexanone peroxide, 0.1 the cobalt naphthenate of part, an amount of mill base is allocated under 30 ℃ temperature evenly, with die needed as: heart, ornament moulds such as water droplet shape garden shape are ready to, at mould inner wall spraying one deck releasing agent, dry for standby, deployed resin homogenate is poured into mould, putting into baking oven solidified 30-60 minute under 40-50 ℃ of temperature, form bottom, above-mentioned sample need be put into mould by viewing and admiring then, divide to pour into polyester 2 times, sample is embedded in the polyester, after about 24 hours, the demoulding, the skiving polishing gets final product.
Embodiment 2: gather fish and mollusc, putting into organic solution soaked 2-10 hour, taking-up is put into baking oven under 40-60 ℃ temperature or air dry dehydration, it is standby to make exsiccata, adopt 100 parts unsaturated polyester resin, 3 parts cyclohexanone peroxide, 0.2 the cobalt naphthenate of part, an amount of mill base at room temperature is deployed into homogenate, it is poured in the required mould form bottom, then the sample of above-mentioned drying and dehydrating is put into it, divide and pour into the polyester specimen embedding 2 times, carry out the parison demoulding after the curing, adopting abrasive machine or buffing machine to carry out skiving by product design handles, makes amber.
Embodiment 3: gather butterfly through spreading the wings or keeping nature, under 40-60 ℃ temperature dry 2 hours standby, with unsaturated-resin: cyclohexanone peroxide: the ratio of cobalt naphthenate=100: 4: 0.5 is mixed well, it is thick to pour the interior about 1mm of mould into, layer overlay surface felt or glass cloth then, butterfly is put on it, on butterfly, cover layer of surface felt or glass cloth again, pour deployed resin again into, make it cover butterfly, after about 5 hours, resin solidification, along skiving, make the butterfly shape amber of various attitudes along butterfly wings.
Claims (3)
1, a kind of ambroid is characterized in that; It is to be main material with the unsaturated polyester resin, and cyclohexanone peroxide and cobalt naphthenate are batching, and their proportioning is: unsaturated polyester resin: cyclohexanone peroxide: cobalt naphthenate=100: 1-6: 0.1-1.
2, a kind of manufacture craft of ambroid is characterized in that: (1) gathers fresh and alive organism, and according to viewing and admiring needs, it is put in order limb or spreads the wings, oven dry setting under 40-60 ℃ of temperature, fish and mollusk form the dehydration sample after handling with organic solvent; (2) by unsaturated polyester resin: cyclohexanone peroxide: the proportioning of cobalt naphthenate=100: 1-6: 0.1-1 mixes; (3) shape is as required selected corresponding mould for use, and spraying one deck releasing agent in mould is with the mould dry for standby; (4) raw material with above-mentioned allotment pours into the mould bottom, after solidifying 30-60 minute under 40-50 ℃ the temperature, at ambient temperature, above-mentioned made sample body is put in the mould, divided the raw material that pours into allotment for several times subsequently, sample is embedded in wherein, for making the thick amber of 1-3mm, then need add surperficial felt or glass fabric ex hoc genus anne material, after the parison demoulding, carry out the skiving processing and get final product.
3, by the described ambroid of claim 1, it is characterized in that: unsaturated polyester resin can adopt 195,196,198,189,191, No. 102 etc.