CN1174068C - Waterproof building glue - Google Patents
Waterproof building glue Download PDFInfo
- Publication number
- CN1174068C CN1174068C CNB021434972A CN02143497A CN1174068C CN 1174068 C CN1174068 C CN 1174068C CN B021434972 A CNB021434972 A CN B021434972A CN 02143497 A CN02143497 A CN 02143497A CN 1174068 C CN1174068 C CN 1174068C
- Authority
- CN
- China
- Prior art keywords
- glue
- waterproof
- cement
- liter
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to waterproof building glue. After acrylic emulsion is diluted with water by the waterproof building glue, cement is mixed for preparing rigid glue solution; the rigid glue solution is compounded with flexible glue solution prepared from styrene acrylate emulsion to form rigid and flexible waterproof glue. The waterproof building glue of the present invention has the advantages of low price, simple preparation and processing technology, good weatherability, strong waterproof performance, strong adhesive performance, etc.
Description
Technical field
The present invention relates to chemical material field, particularly relate to a kind of building marine glue.
Background technology
Waterproofing work is occupied important status in construction work, the quality of waterproof effect is directly connected to the quality and the work-ing life of engineering.At present, known waterproof paint or coiled material have a variety of, and wherein high, middle-grade product has SBS modifying asphalt, polyurethane, Ethylene Propylene Terpolymer, neoprene latex etc., and low grade products has reclaimed rubber and asbestos emulsified bitumen coating etc., but all exist such or such defective, as:
1) positively charged ion neoprene latex
This series products needs " three cloth four are coated with " in construction process, construction process is loaded down with trivial details, wastes time and energy;
2) waterproof paint
This type of waterproof paint price comparison is cheap, but its product type is single, is divided into flexibility or rigidity coating: rigidity water-proofing material poor toughness wherein, and when fracture took place cement basic layer, water-proof material also can rupture, and causes a layer top seepage; And the poor rigidity of flexible waterproof material is afraid of to prick, press, pound, and therefore needing to increase rigidity water-proofing material in construction process makes protective layer, has increased construction costs;
3) SBS modified asphalt waterproof coiled material
The defective of this series products maximum is all quite loaded down with trivial details with its production technique and construction technology, the processing requirement height, as working-yard moisture greater than 9%, just can't construct, make WATER REPELLENT before, also to carry out early stage and handle basic unit (screed-coat), to increase sticking power, bonding force, coiled material also will heat with fire, roastingization, poor stability, and also this waterproof roll costs an arm and a leg, the construction costs height.
Summary of the invention
The objective of the invention is to overcome the defective of above-mentioned prior art, provide that a kind of preparation is simple, construction technology is easy, cost is low, and ageing-resistant, waterproof, building marine glue that cohesiveness is good.
The objective of the invention is to be achieved through the following technical solutions:
A kind of building marine glue, this waterproof glue be by following two portions composition in use respectively coating form:
The A component:
ACRYLIC EMULSION 1
Cement 1-2
Water 0.5-2
The B component:
Benzene emulsion 1
Water 0.2-0.5
The said ratio relation is in volume parts.
Building marine glue of the present invention at first with the ACRYLIC EMULSION dilute with water, mixes cement again, after fully stirring.
Waterproof glue of the present invention in use, will be through three layers of brushing, the first layer is made rarer concentration brushing with the A set of dispense earlier, be convenient in the pore that glue penetrates into cement sand bed, the second layer is selected the component than heavy-gravity B for use, makes it form waterproof membrane, selects the component than heavy-gravity A for use for the 3rd layer, increased both waterproof of coat-thickness and intensity, ageing-resistant again.
Waterproof glue of the present invention also can be used with flexible web, when using to overcome flexible web and sand-cement slurry, and the crannied defective of sand-cement slurry.
Building marine glue of the present invention has the following advantages:
1) raw material of this waterproof glue is easy to get, and cheap, and compound method is simple;
2) constructional method is easy, as long as after stirring, brushing evenly just can reach the waterproof purpose;
3) this waterproof glue has certain water-solublely, and it is not afraid of humidity, as long as no open fire can be constructed, processing requirement is low;
4) film forming speed is fast, under the normal temperature state, gets final product film forming in 20 minutes;
5) good weatherability general high temperature resistantly reaches 80 ℃, and low temperature resistant reaching-20 ℃ the high temperature trickling can not take place, the cold cracking phenomenon after the construction;
6) can under normal temperature condition, construct, improve workman's work situation greatly, reduce labor intensity;
7) raw materials used all pollution-free, nontoxicity is not fired, transportation safety, convenience;
8) cohesive strength height, for chap, crack, the sand-cement slurry of weathering or dusting, after brushing, can gain in strength, reach and do not ftracture, do not fall slag, waterproof.
In order more to show the premium properties of this waterproof glue, enclose the examining report of this product, this report is made by material of construction product quality supervision and inspection station, Ningxia Hui Autonomous Region, is numbered (peaceful building materials inspection) word Z2002-489, and detected result is as follows:
Assay
| Interventions Requested | Unit | Measured result | |
| Folding strength | a | MPa | 3.0(5d) |
| b | 2.9(5d) | ||
| Ultimate compression strength | a | MPa | 19.9(5d) |
| b | 15.6(5d) | ||
| Adhesive tensile resistance intensity | a | MPa | 0.44(5d) |
| b | 0.42(5d) | ||
| Waterproof test | Carton inwall brush coating adds 16 centimetres in water, leaves standstill 24 hours, does not seep water | ||
| Freezing and thawing test | The cement briquette surface brush coating that adds gum forming, with-20 ℃, 2h+20 ℃, 2h, 15 freeze-thaw cycle, do not have ftracture, come off, unusual phenomenon such as foaming | ||
Annotate: above-mentioned a, b represent two samples respectively.
Embodiment
Embodiment 1:
Get 1 liter of 1 liter of ACRYLIC EMULSION, cement and be mixed with glue 1 with 1.5 premium on currency,
Get 1 liter of 1 liter of ACRYLIC EMULSION, cement and be mixed with glue 2 with 1 premium on currency,
Get 1 liter of benzene emulsion and be mixed with flexible glue with 0.2 premium on currency;
The above-mentioned glue for preparing 1 brushing in basic unit, is coated flexible glue above, and outermost layer evenly is coated with glue 2 and brushes.
Embodiment 2:
Get 1 liter of 1 liter of ACRYLIC EMULSION, cement and be mixed with glue 1 with 1.5 premium on currency,
Get 1 liter of 1 liter of ACRYLIC EMULSION, cement and be mixed with glue 2 with 1 premium on currency,
Get 1 liter of benzene emulsion and be mixed with flexible glue with 0.2 premium on currency;
The above-mentioned glue for preparing 1 brushing in basic unit, is coated glue 2 above, and outermost layer evenly is coated with and brushes flexible glue liquid.
Embodiment 3:
Get 2 liters of 1 liter of ACRYLIC EMULSION, cement and be mixed with glue 1 with 2 premium on currency,
Get 1 liter of 1 liter of ACRYLIC EMULSION, cement and be mixed with glue 2 with 1 premium on currency,
Get 1 liter of benzene emulsion and be mixed with flexible glue with 0.5 premium on currency;
The above-mentioned glue for preparing 1 brushing in basic unit, is coated flexible glue above, and outermost layer evenly is coated with glue 2 and brushes.
Embodiment 4:
Get 1 liter of 1 liter of ACRYLIC EMULSION, cement and be mixed with glue 1 with 2 premium on currency,
Flexible web is spread to basic unit, then with the above-mentioned glue for preparing 1 brushing.
Claims (1)
1. building marine glue, it is characterized in that this waterproof glue be by following two portions composition in use respectively coating form:
The A component:
ACRYLIC EMULSION 1
Cement 1-2
Water 0.5-2
The B component:
Benzene emulsion 1
Water 0.2-0.5
The said ratio relation is in volume parts.