CN1173149C - Cold method worked degradable environment proteotion novel type stone dust and modified starch mixed color clay pigeon target - Google Patents
Cold method worked degradable environment proteotion novel type stone dust and modified starch mixed color clay pigeon target Download PDFInfo
- Publication number
- CN1173149C CN1173149C CNB031111297A CN03111129A CN1173149C CN 1173149 C CN1173149 C CN 1173149C CN B031111297 A CNB031111297 A CN B031111297A CN 03111129 A CN03111129 A CN 03111129A CN 1173149 C CN1173149 C CN 1173149C
- Authority
- CN
- China
- Prior art keywords
- starch
- parts
- modified starch
- stone flour
- degradable environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention provides a degradable environmental protection novel stone powder modified starch mixed color flying disk target manufactured by a cold method, which relates to the technical field of sports equipment manufacture and particularly relates to a manufacturing material of flying disk shooting targets in flying disk shooting sports and a manufacturing process of the flying disk shooting targets. The present invention is made from raw materials with the following parts by weight: 90 parts of stone powder, 8 to 9 parts of starch, 1 to 1.5 parts of accelerating agents, 5 to 6 parts of orange fluorescent powder, 1 to 1.5 parts of stabilizing agents, 37 to 38 liters of water through starch modification, mixing, stirring and molding. Because starch is degradable, the environment is not polluted by substances formed after the flying disk shooting target is broken by shooting. Because the composite orange fluorescent powder is added in the total material, the internal color and the external color of the disk target are consistent, and the visual effect is greatly improved. The present invention is processed by a cold method, and compared with the traditional heating extrusion methods, the cold method has the advantages of simple process, little energy consumption, low cost, etc.
Description
Technical field
The present invention relates to the manufacturing technology field of sports equipment, particularly the clay-pigeon shooting target in the clay-pigeon shooting campaign manufactures material and manufacture technology.
Background technology
At present, widely used clay-pigeon shooting target in the clay-pigeon shooting campaign, be to be that main Binder Materials or small part are done Binder Materials with natural resin with pitch, be equipped with other attached material again, through heating and melting, the processing method of molding compacting is manufactured and is formed, during pitch need be used, high temperature coal tar pitch and asphalt, with throwing target strength and the fragility of being hit and indeformable at normal temperatures that guarantees the flying saucer rake, because pitch contains aromatic hydrocarbons, itrogenous organic substance, harmful substances such as oxygen-bearing organic matter, so can cause certain harm to health, and this kind clay-pigeon shooting target is after the gunslinging fragmentation, a large amount of asphalt stocks hang down, remain in the earth, because the pitch degradation time is long, the soil property of earth is caused serious harm, severe contamination environment.Also have a bit, the color of general clay pigeon international popular is orange colour, salmon pink, because pitch target and natural resin target all adopt the mode surface colour outside of spraying color, material internal is not mixed into colour component, after the fragmentation of pitch target, fragment is black, and natural resin target fragment is white in color, and is bad to athletic visual effect.And adopt the processing method of heating and pushing, and the technology more complicated, the energy consumption height is manufactured the cost height.
Summary of the invention
The objective of the invention is the problem that exists at prior art, and provide a kind of technology simple, manufacture that cost is low, energy consumption is little, good visual effect manufacture material and manufacture technology thereof with what starch was made Binder Materials with cold process processing degradable environment-friendly novel stone flour modified starch mixed colors clay pigeon.
Technology contents of the present invention is described below:
Cold process processing degradable environment-friendly novel stone flour modified starch mixed colors clay pigeon is manufactured material, mainly be to make: 90 parts of stone flours, starch 8-9 part, accelerator 1-1.5 part, orange fluorescent material 5-6 part, stabilizing agent 1-1.5 part, water 37-38 liter (every part in kilogram, amount of water) by the raw material of following weight portion.
Described stone flour comprise silica, lime stone, calcite, dolomite, marble,
Wherein a kind of or its two or more composition of granite, magnesite, zircon, high-al clay, feldspar, wollastonite, syenite, diopside, talcum, zeolite, sepiolite, illite, or nontoxic, whiteness is at the solid waste powder more than 40%, all kinds of mineral tailings powder, industrial residue, all kinds of soil and surflaes, wherein, 27 parts of 200 purpose stone flours, 63 parts of 400 purpose stone flours.
Described starch be meant each kind of starch all can, use after modified oxidized.
Described accelerator selects for use CMC to manufacture.
Described stabilizing agent is meant calcium hydroxide or calcium sulfate.
Cold process processing degradable environment-friendly novel stone flour modified starch mixed colors clay pigeon manufacture technology step is as follows:
1) with above-mentioned various constituents in the weighing of above-mentioned weight portion ratio, standby;
2), be half pasty state with the starch conversion oxidation;
3) starch of handling well is added water with stone flour and mix, stirred 2-3 minute;
4) under the moving situation of not stall, add orange fluorescence powder, stirred 2-3 minute;
5) add stabilizing agent, do not stop to stir 3-5 minute;
6) add accelerator then, ceaselessly stirred 1-2 minute,
7) at last above-mentioned compound is joined in the flying saucer rake make-up machine cold moudling.
It is emphasized that: this process bulk temperature is controlled at 15-45 ℃, and the reinforced time in per step will be controlled in 30 seconds evenly reinforced slowly.
Outstanding beneficial effect of the present invention is as adhesive with starch, alternative traditional is that main Binder Materials or small part are done Binder Materials with natural resin with pitch, since starch degradable, thus clay-pigeon shooting target material environmentally safe after the gunslinging fragmentation, owing to use compound tangerine
The yellow fluorescent material of ↑ 2M is added in the overall material, makes the inside and outside color uniformity of dish target, has improved visual effect greatly, and this is that the flying saucer rake of other type does not possess.Because the present invention adopts cold process processing, compares with traditional pressing method of heating, have that technology is simple, power consumption less, low cost and other advantages, the present invention can replace pitch dish target fully, will produce very big economic benefit and social benefit.
Following table is price, processing method comparison and the occupation rate of market of various clay-pigeon shooting targets.
The specific embodiment
Embodiment 1:
1) take by weighing agstone 90Kg, wherein, 200 purpose stone flour 27Kg, 400 purpose stone flour 63Kg, 38 liters in starch 8Kg, accelerator 1Kg, orange fluorescent material 6Kg, stabilizing agent 1Kg, water, standby;
2), be half pasty state with the starch conversion oxidation;
3) starch of handling well is added water with agstone and mix, stirred 2-3 minute;
4) under the moving situation of not stall, add orange fluorescence powder, stirred 2-3 minute;
5) add stabilizing agent calcium hydroxide, do not stop to stir 3-5 minute;
6) add accelerator CMC then, ceaselessly stirred 1-2 minute;
7) at last above-mentioned compound is joined in the flying saucer rake make-up machine cold moudling.
It is emphasized that: this process bulk temperature is controlled at 15-45 ℃, and the reinforced time in per step will be controlled in 30 seconds evenly reinforced slowly.
↑r1A
Embodiment 2:
1) take by weighing calcite in powder 90Kg, wherein, 200 purpose stone flour 27Kg, 400 purpose stone flour 63Kg, 37.5 liters in starch 8.5Kg, accelerator 1.3Kg, orange fluorescent material 5.5Kg, stabilizing agent 1.3Kg, water, standby;
2), be half pasty state with the starch conversion oxidation;
3) starch of handling well is added water with calcite in powder and mix, stirred 2-3 minute;
4) under the moving situation of not stall, add orange fluorescence powder, stirred 2-3 minute;
5) add the stabilizing agent gypsum, do not stop to stir 3-5 minute;
6) add accelerator CMC then, ceaselessly stirred 1-2 minute;
7) at last above-mentioned compound is joined in the flying saucer rake make-up machine cold moudling.
It is emphasized that: this process bulk temperature is controlled at 15-45 ℃, and the reinforced time in per step will be controlled in 30 seconds evenly reinforced slowly.
Embodiment 3:
1) take by weighing nontoxic, whiteness at the solid waste powder 90Kg more than 40%, wherein, 200 purpose 27Kg, 400 purpose 63Kg, 38 liters in starch 9Kg, accelerator 1.5Kg, orange fluorescent material 6Kg, stabilizing agent 1.3Kg, water, standby;
2), be half pasty state with the starch conversion oxidation;
3) starch of handling well is added water with above-mentioned stone flour and mix, stirred 2-3 minute;
4) under the moving situation of not stall, add orange fluorescence powder, stirred 2-3 minute;
5) add stabilizing agent lime, do not stop to stir 3-5 minute;
6) add accelerator CMC then, ceaselessly stirred 1-2 minute;
7) at last above-mentioned compound is joined in the flying saucer rake make-up machine cold moudling.
It is emphasized that: this process bulk temperature is controlled at 15-45 ℃, and the reinforced time in per step will be controlled in 30 seconds evenly reinforced slowly.
Claims (6)
1. cold process processing degradable environment-friendly novel stone flour modified starch mixed colors clay pigeon is manufactured material, it is characterized in that it mainly being that raw material by following weight portion is made: 90 parts of stone flours, starch 8-9 part, accelerator 1-1.5 part, orange fluorescent material 5-6 part, stabilizing agent 1-1.5 part, every part are in kilogram, and amount of water is: water 37-38 liter.
2. cold process processing degradable environment-friendly novel stone flour modified starch mixed colors clay pigeon according to claim 1 is manufactured material, it is characterized in that: described stone flour comprises silica, lime stone, calcite, dolomite, marble, granite, magnesite, zircon, high-al clay, feldspar, wollastonite, syenite, diopside, talcum, zeolite, sepiolite, wherein a kind of or its two or more composition of illite, or it is nontoxic, whiteness is at the solid waste powder more than 40%, all kinds of mineral tailings powder, industrial residue, all kinds of soil and surflaes, wherein, 27 parts of 200 purpose stone flours, 63 parts of 400 purpose stone flours.
3. cold process according to claim 1 processing degradable environment-friendly novel stone flour modified starch mixed colors clay pigeon is manufactured material, it is characterized in that: described starch be meant each kind of starch all can, through the use of modified oxidized back.
4. cold process processing degradable environment-friendly novel stone flour modified starch mixed colors clay pigeon according to claim 1 is manufactured material, and it is characterized in that: described accelerator selects for use CMC to manufacture.
5. cold process processing degradable environment-friendly novel stone flour modified starch mixed colors clay pigeon according to claim 1 is manufactured material, and it is characterized in that: described stabilizing agent is meant calcium hydroxide or calcium sulfate.
6. the manufacture technology of cold process processing degradable environment-friendly novel stone flour modified starch mixed colors clay pigeon according to claim 1 is characterized in that the manufacture technology step is as follows:
1) above-mentioned various constituent is in the weighing of above-mentioned weight portion ratio, and is standby;
2), be half pasty state with the starch conversion oxidation;
3) starch of handling well is added water with stone flour and mix, stirred 2-3 minute;
4) under the moving situation of not stall, add orange fluorescence powder, stirred 2-3 minute;
5) add stabilizing agent, do not stop to stir 3-5 minute;
6) add accelerator then, ceaselessly stirred 1-2 minute;
7) at last above-mentioned compound is joined in the flying saucer rake make-up machine cold moudling;
It is emphasized that: this process bulk temperature is controlled at 15-45 ℃, and the reinforced time in per step will be controlled in 30 seconds evenly reinforced slowly.