CN101852572A - Dry-free, environment-friendly, energy-saving and degradable flaying saucer by taking tailings powder as raw material and manufacturing method thereof - Google Patents
Dry-free, environment-friendly, energy-saving and degradable flaying saucer by taking tailings powder as raw material and manufacturing method thereof Download PDFInfo
- Publication number
- CN101852572A CN101852572A CN201010170499A CN201010170499A CN101852572A CN 101852572 A CN101852572 A CN 101852572A CN 201010170499 A CN201010170499 A CN 201010170499A CN 201010170499 A CN201010170499 A CN 201010170499A CN 101852572 A CN101852572 A CN 101852572A
- Authority
- CN
- China
- Prior art keywords
- raw material
- mine tailing
- saucer
- parts
- degradable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to sport goods, in particular to a dry-free, environment-friendly, energy-saving and degradable flaying saucer by taking tailings powder as a raw material and a manufacturing method thereof. The flying saucer is manufactured with the following components in part by weight: 60 to 80 parts of tailings powder, 0.0005 to 0.0015 part of lignocellulose, 5 to 10 parts of cement, 10 to 20 parts of 1 to 5mm quartz sand, 0.0003 to 0.0012 part of photosensitizer and 20 to 30 parts of water. The manufacturing method comprises that the components are mixed in the weight ratio and pressed at the normal temperature to form the flaying saucer. The flying saucer manufactured by the method has the advantages of high strength, high performance index, no change of weight and strength due to moisture absorption during the transportation or storage, cold processing, environment friendliness, energy conservation and degradability.
Description
Technical field
The present invention relates to a kind of sports goods, be raw material with the mine tailing, exempt from oven dry, environmental protection and energy saving degradable clay target and method for making thereof.
Background technology
At present, the clay pigeon that uses in the firing item of sports tournament all is to adopt pitch, resin, rosin based material as binding agent, is equipped with other material and makes.All contain harmful substance in pitch, resin, the rosin, and need hot-formingly in the manufacturing process of clay pigeon, consumed energy is many, complex process, cost height.
In recent years, the clay pigeon that a kind of degradable stone flour modified starch is made has appearred, this clay pigeon is raw material with the stone flour, is binding agent with the modified starch, need heat when making clay pigeon and just can make it play cementation to drying more than 100 ℃, big energy-consuming not only, and owing to heating to process more than 100 ℃, moisture is gasified, and when normal temperature, because the characteristic of starch can get damp again again, absorb moisture, make the standard weights of clay pigeon to change like this, and intensity also can reduce.
Summary of the invention
The purpose of this invention is to provide a kind of is primary raw material with the industrial waste mine tailing, lignocellulosic be binding agent exempt from oven dry, environmental protection and energy saving degradable clay target and method for making thereof, the clay pigeon intensity height that this method is made, performance indications are good, can be because of in transportation or deposit in the process and change weight and intensity because of moisture absorption, process environmental protection and energy saving, degradable under the normal temperature condition.
For achieving the above object, the present invention is achieved through the following technical solutions:
Be raw material with the mine tailing, exempt from oven dry, environmental protection and energy saving degradable clay target, make by weight proportion by following compositions: quartz sand 10-20 part of mine tailing 60-80 part, lignocellulosic 0.0005-0.0015 part, cement 5-10 part, 1-5mm, sensitising agent 0.0003-0.0012 part, water 20-30 part.
Method for making is: mentioned component is mixed compression moulding under the normal temperature by described part by weight.
In the described material composition, mine tailing can be metal tailings powder or stone materials mine tailing.
Described sensitising agent can be ferric stearate, starch base photosensitizer or ferrocene derivatives sensitising agent; Under the irradiation of light, can play the effect that promotes degraded.
Lignocellulosic is the commercially available prod, plays binding agent.
Cement can be portland cement, plays waterproof and solidification.
1-5mm quartz sand play skeleton function.
Compared with prior art, advantage of the present invention is:
1) adopting the industrial waste mine tailing is primary raw material, and cost of manufacture is low, can be because of in transportation or deposit in the process and change weight and intensity because of moisture absorption;
2) be processed under the normal temperature condition, clay pigeon intensity height, performance indications are good, environmental protection and energy saving, degradable.
The specific embodiment
Embodiment 1
Be raw material with the mine tailing, exempt from oven dry, environmental protection and energy saving degradable clay target, make by weight proportion by following compositions: 80 parts of mine tailings, 0.0005 part of lignocellulosic, 8 parts of portland cements, 12 parts of the quartz sands of 1-5mm, 0.0003 part of sensitising agent, 25 parts in water.
Method for making is: mentioned component is mixed compression moulding under the normal temperature by described part by weight.
Embodiment 2
Be raw material with the mine tailing, exempt from oven dry, environmental protection and energy saving degradable clay target, make by weight proportion by following compositions: 60 parts of mine tailings, 0.001 part of lignocellulosic, 5 parts of portland cements, 20 parts of the quartz sands of 1-5mm, 0.0008 part of sensitising agent, 20 parts in water.
Method for making is: mentioned component is mixed compression moulding under the normal temperature by described part by weight.
Embodiment 3
Be raw material with the mine tailing, exempt from oven dry, environmental protection and energy saving degradable clay target, make by weight proportion by following compositions: 65 parts of mine tailings, 0.0015 part of lignocellulosic, 10 parts of portland cements, 16 parts of the quartz sands of 1-5mm, 0.0012 part of sensitising agent, 30 parts in water.
Method for making is: mentioned component is mixed compression moulding under the normal temperature by described part by weight.
In the above-mentioned raw materials composition, mine tailing can be metal tailings powder or stone materials mine tailing.Not containing harmful substance in the mine tailing, be the environmental protection and energy saving material, is the utilization again of dead meal, has solved the stacking problem of discarded mine tailing.
Lignocellulosic is the commercially available prod, plays binding agent, and its adhesive property is good.
Portland cement plays waterproof and solidification; 1-5mm quartz sand play skeleton function, combine the intensity that can strengthen clay pigeon with cement.
Sensitising agent can be ferric stearate, starch base photosensitizer or ferrocene derivatives sensitising agent; Under the irradiation of light, can play the effect that promotes degraded.
The present invention is under nature, and through exposing to the weather, 2-3 can degrade gradually.Clay pigeon of the present invention gets final product ordinary production under normal temperature condition.Produce colored clay pigeon as need, available coloured cement processing, instead of chemical pigment.
Claims (4)
1. be raw material with the mine tailing, exempt from the oven dry, the environmental protection and energy saving degradable clay target, it is characterized in that, make by weight proportion: quartz sand 10-20 part of mine tailing 60-80 part, lignocellulosic 0.0005-0.0015 part, cement 5-10 part, 1-5mm, sensitising agent 0.0003-0.0012 part, water 20-30 part by following compositions.
2. according to claim 1 be raw material with the mine tailing, exempt from the oven dry, the environmental protection and energy saving degradable clay target, it is characterized in that in the described material composition, mine tailing can be metal tailings powder or stone materials mine tailing.
Claim 1 or 2 described be raw material with the mine tailing, exempt from the oven dry, the environmental protection and energy saving degradable clay target, it is characterized in that described sensitising agent can be ferric stearate, starch base photosensitizer or ferrocene derivatives sensitising agent.
Claim 1 or 2 described be raw material with the mine tailing, exempt to dry, the method for making of environmental protection and energy saving degradable clay target, it is characterized in that, described composition is mixed compression moulding under the normal temperature by described part by weight.