CN1171451A - Method for recovering aluminium foil from waste aluminium foil package and apparatus thereof - Google Patents
Method for recovering aluminium foil from waste aluminium foil package and apparatus thereof Download PDFInfo
- Publication number
- CN1171451A CN1171451A CN96107098A CN96107098A CN1171451A CN 1171451 A CN1171451 A CN 1171451A CN 96107098 A CN96107098 A CN 96107098A CN 96107098 A CN96107098 A CN 96107098A CN 1171451 A CN1171451 A CN 1171451A
- Authority
- CN
- China
- Prior art keywords
- aluminium
- foil
- vapourizing furnace
- aluminium foil
- air
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A method for recovering aluminium foil from waste aluminium foil packages includes such steps as heating waste aluminium foil packages at 500-600 deg. C in gasification furnace full of anoxic atmosphere, that is, the oxygen content is lower than the theoretical oxygen quantity needed by full oxidation of plastic film on foil, to gasify all the paper and plastic film, cooling the residual solid without introduction of external air to gasification furnace, and then separation of aluminium foil from the cooled solid.
Description
The invention relates to a kind of technology, especially refer to the gasification of paper that the aluminium-foil scrap bag is contained and plastic film and the technology of recovery aluminium foil from aluminium-foil scrap bag recovery aluminium foil.
The small packages thirst relieving beverage that the market sells is in fashion day by day, and the packing of small packages beverage is emphasized accessibility more, can abandon conveniently after having drunk.The container of small packages beverage easily causes the pollution of society, in bottle, iron, aluminium pot, vial, paper bag and the Aluminium Foil Package iron, aluminium pot, vial and paper bag be recovered in the technical special problem of all not having, the recovery of Aluminium Foil Package then effect is not good.National governments force to reclaim various containers in the cry of environmental protection, regenerate or subtract uselessly, and Aluminium Foil Package is also in the face of this problem, but the rate of recovery of aluminium-foil scrap bag still can't improve always.The known dealer of having takes off pulp processing with the aluminium-foil scrap bag that reclaims at present, and wherein the paper in the aluminium-foil scrap bag is reproduced into paper pulp, but remaining polyethylene (PE) film and aluminium foil then do not have any utilization plan, then have to drop into incinerator or landfill site, very unfortunate.
Main purpose of the present invention is promptly proposing a kind of method and device that reclaims aluminium foil from the aluminium-foil scrap bag.
Another object of the present invention is proposing a kind of method and device that reclaims an aluminium foil and a combustible gas from the aluminium-foil scrap bag.
A kind of method from aluminium-foil scrap bag recovery aluminium foil of finishing according to content of the present invention comprises the following step:
A) the aluminium-foil scrap bag is placed the inherent anoxic gas of a vapourizing furnace divide and 500-600 ℃ temperature heats, and making that paper and plastic film that this aluminium-foil scrap bag is contained are in fact all gasified, this anoxic gas branch is meant that contained amount of oxygen is lower than the theoretical air requirement of the plastic cement mould complete oxidation that this aluminium-foil scrap is contained;
B) substantially do not import outside air under the situation of this vapourizing furnace, cooling aluminium-foil scrap bag is by the solid phase prod after gasifying; And
C) isolate aluminium foil from this refrigerative solid phase prod.
Conveniently, the step a) formed gas products that gasifies is extracted out and as the fuel with caloric value, an air that is lower than theoretical air requirement is imported into this vapourizing furnace continuously under a base runoff simultaneously from this vapourizing furnace continuously.
Conveniently, the anoxic gas branch of step a) is meant 10% to 70% of this theoretical air requirement.
Conveniently, the temperature of step a) is 300-500 ℃.
Conveniently, this gas products that is drawn out of is recycled and is used as the required fuel of step a) heating in the inventive method.
The present invention also points out a kind of device that reclaims aluminium foil from the aluminium-foil scrap bag that is applicable in addition, comprises:
One vapourizing furnace, it is used for the contained organic substance of aluminium-foil scrap bag that is placed in the stove is carried out gasification reaction under anoxic environment;
One can be to the well heater of this vapourizing furnace heating;
One is connected in the air-intake duct of a side of this vapourizing furnace, and extraneous air promptly enters the inside of this vapourizing furnace through air-intake duct thus;
One charge flow rate controlling organization, it is located at this air-intake duct and controls the air flow quantity that enters this vapourizing furnace via this air-intake duct; And
One windmill of bleeding is used for the furnace gas of this vapourizing furnace is extracted out via a piping system.
Conveniently, this air input controlling organization comprises a under meter; An and flow control valve.
Conveniently, apparatus of the present invention further comprise a water bath and and remove the tar device, this water bath and remove the tar device and be located at this vapourizing furnace and this in regular turn and bleed on this piping system between the windmill wherein, so the furnace gas of this vapourizing furnace top discharge is imported into the water-bath of this water bath and washs, and the washing gas of being discharged by the water-bath top of this water bath is imported into the bottom that this removes the inner filling of tar device filter material.
Fig. 1 is the synoptic diagram of the outer field laminated structure of Aluminium Foil Package.
Fig. 2 is the schematic representation of apparatus that reclaims aluminium foil from the aluminium-foil scrap bag of the present invention.
Fig. 3 is according to being the schema that experimentizes from the method for aluminium-foil scrap bag recovery aluminium foil of the present invention.
The vapourizing furnace heating curve figure of Fig. 4 for experimentizing and obtained according to flow process shown in Figure 3, theoretical air requirement 30%, 500 ℃ of design temperatures.
The analysis of components GC figure of the gas products that Fig. 5 is obtained for experimentizing according to flow process shown in Figure 3.
XRD (X ray diffraction analysis) collection of illustrative plates of the aluminium foil that Fig. 6 is reclaimed for experimentizing according to flow process shown in Figure 3.
The internal layer of Aluminium Foil Package uses paper as wrapping material, and the paper composition accounts for gross weight 73.5%, as for the skin of Aluminium Foil Package, by laminated in regular turn the first layer PE film, second layer PE film, aluminium (AL) paper tinsel, the 3rd layer of PE film, paper and outer PE film is arranged as shown in Figure 1.
In one liter Aluminium Foil Package, contain 5 g plastic cement approximately, (accounting for gross weight 21%), and 1.5 g aluminium foil (accounting for gross weight 5%).Aluminum foil material is just to mount among the PE film for the protection of strengthening product, and its thickness has only 0.007mm.Send the laboratory to analyze Aluminium Foil Package, find that the Aluminium Foil Package composition is carbon and hydrogen and a spot of nitrogen and sulphur except aluminium; Its calorific value can reach 5275Kca1/Kg, no matter from then on can find aluminium-foil scrap bag recovery heat or aluminium is favourable condition.
Because suitable pure of the used aluminium foil of Aluminium Foil Package, and very easily oxidation of fine aluminium, thus recovery technology become very important.Still the aluminium foil that remaining polyethylene coats after the paper of aluminium-foil scrap bag is recovered will be removed the polyethylene of aluminium foil surface, and thermal degradation is the most direct method, but because the activity of aluminium foil, very easily oxidation, therefore gasification may be more feasible method.
Gasification, briefly under the environment of anoxic or a small amount of oxygen, heat up and react, carbon in this process in the organic raw material such as plastic cement combines with oxygen and produces carbon monoxide or carbonic acid gas, and carbon combines the hydrocarbon polymer that produces multiple combination with hydrogen, therefore if gasification process is proper, polyethylene and the gasification of other organism can be produced CO, CO
2, C
2H
4Deng gas, and remaining aluminium foil, so the present invention is promptly at experiment flow and device below promptly having gone up Design Theory, and carries out a series of experiment.
One is applicable to that the device from aluminium-foil scrap bag recovery aluminium foil and combustible gas of the present invention is shown in Fig. 2, and it comprises:
One vapourizing furnace 3, it is used for the contained organic substance of aluminium-foil scrap bag that is placed in the stove is carried out gasification reaction under anoxic environment;
One can be to the well heater 4 of these vapourizing furnace 3 heating;
One is connected in the air-intake duct 2 of a side of this vapourizing furnace 3, and extraneous air promptly enters the inside of this vapourizing furnace 3 through air-intake duct 2 thus;
The furnace gas that one water bath 5, is discharged via a pipeline 90 by these vapourizing furnace 3 tops is imported into the water-bath of this water bath 5 and washs;
One removes tar device 6, is imported into this except that tar device 6 inner bottoms of filling filter material (rice husk) by the washing gas of discharging via pipeline 91 above the water-bath of this water bath 5;
One windmill 8 of bleeding, its gas that will remove tar device 6 tops is extracted out via pipeline 92; And
One under meter 1 with a flow control valve is installed in this air-intake duct 2 to control and to read charge flow rate, and a thief hole 7 is located at this pipeline 92 and is removed tar device 6 between this and bleed between the windmill 8 with this, should be except that tar device 6 expellant gas for sampling analysis.
Optionally, the gas of being extracted out by this windmill 8 of bleeding is collected in the fuel that a furnace gas collector 9 or recirculation are used as this well heater 4 or other heating installation.
In order to find out the proper operation condition of the inventive method, carry out a series of experiment according to flow process shown in Figure 3.The detailed experiments step is as follows:
(1) take out Aluminium Foil Package 150 gram of destarch and not destarch Aluminium Foil Package 150 grams put into vapourizing furnace 3 loam cake locked.
(2) open and to bleed windmill 8 and adjust the flow control valve of under meter 1 and air flow quantity is set at 0% (0 liter/second), 30% (0.0639 liter/second), 60% (0.1278 liter/second) and 90% (0.1917 liter/second) theoretical air, theoretical air is the required amount of oxygen of organic substance of the Aluminium Foil Package in this vapourizing furnace 3 of oxidation.
(3) temperature of setting well heater 4 begins to heat up.
When (4) treating that temperature reaches setting point, carry out gas sampling and inject GC (gas-liquid chromatography) analysis by thief hole 7.
(5) wait to heat up when reaching vertex and beginning planarization, stop heating, resampling also injects GC and analyzes.
When (6) treating that temperature begins to descend, sampling is once again sent among the GC and is analyzed.
(7) taken a sample after, and after windmill 8 is bled in unlatching 80 minutes close the windmill 8 of bleeding, and temperature is slowly descended, and avoid cool ambient air to flow into and cause oxidation.
When (8) treating that vapourizing furnace 3 temperature reach room temperature, the Aluminium Foil Package envelope after opening loam cake and taking out gasification stores.
(9) take out tar by the cleaning channels that removes tar device 6.
(10) treat to put the working conditions of finding out from aluminium-foil scrap bag recovery aluminium foil again in order after all experiments are finished, the aluminium foil of selecting partly to be recovered is XRD (X ray diffraction analysis).
The experimental result of above Aluminium Foil Package gasification, we roughly are divided into three and partly resolve: the parsing of first part:
At first first partly is the parsing by line of heating up, one typically heating curve be shown in Fig. 4.As seen from Figure 4, heating curve is very precipitous, the gasification that Aluminium Foil Package can be very fast after its envrionment temperature reaches gasification condition just, reach the highest temperature, by experiment design temperature and top temperature, the low more then top temperature of design temperature is low more, the high more then top temperature of design temperature is also high more, as long as but the top temperature that can gasify can reach between 580 ℃-600 ℃, when the temperature setting is high more,, will soon fall though top temperature can surmount design temperature, therefore if see originally that to be operable to intensification only need reach about about 300 ℃, the inner calorific value of then reliable aluminium foil burns.The parsing of second part:
Secondly, second partly is the parsing of the GC analytical results of gasifying gas, and a typical gasifying gas composition GC figure is shown in Fig. 5.Can obviously find out by Fig. 5 and to contain 8 kinds of major ingredient in the gasifying gas at least, 8 kinds of compositions such as hydrogen, oxygen, nitrogen, carbon monoxide, methane, carbonic acid gas, ethene and ethane, wherein oxygen, nitrogen, carbonic acid gas are not have calorific value, and remaining composition all has a certain amount of calorific value.The parsing of the 3rd part:
At last the aluminium-foil scrap bag after the gasification is carried out visual inspection, and the selection portion duplicate samples is carried out XRD (X ray diffraction analysis).
Finding in visual inspection, no matter the design temperature of well heater is the several years, is preferable with theoretical air greater than 0 all.Theoretical air is 0, and the paper of aluminium-foil scrap bag becomes the black carbon black and has tar to stick together on aluminium foil; And theoretical air is greater than 0, and the paper of aluminium-foil scrap bag becomes caducous ash, and do not have tar and stick together on aluminium foil.But greater than 0 situation, when design temperature was 200 ℃, it is burned black that the paper that aluminium-foil scrap is wrapped only is, and pats still difficult drop-off with hand at theoretical air.Greater than 0 situation, when design temperature was 700 ℃, the aluminium foil of gasification back aluminium-foil scrap bag presented shrinkage and tarnishes at theoretical air, its be placed into a temperature be 1000 ℃ the High Temperature Furnaces Heating Apparatus heating still the nothing fusion turn out to be aluminum oxide; When design temperature is 200,300 and 500 ℃, the aluminium foil of gasification back aluminium-foil scrap bag still is silvery white gloss, 300 ℃ of Fig. 6 display-setting temperature and theoretical air are the XRD analysis of the aluminium foil of aluminium-foil scrap bag after 30% the gasification, and its composition is essentially fine aluminium (the instrumental error value is in 5%) as can be seen from Figure 6.
The present invention has cooperated above-mentioned specific embodiment to be described, and is familiar with this skill personage and can makes multiple variation based on above description.
Claims (8)
1. the method from aluminium-foil scrap bag recovery aluminium foil is characterized in that, comprises the following step:
A) the aluminium-foil scrap bag is placed the temperature of the inherent oxygen deficient atmospheres of a vapourizing furnace and 500-600 ℃ heat, and making that paper and plastic film that this aluminium-foil scrap bag is contained are in fact all gasified, this oxygen deficient atmospheres is meant that contained amount of oxygen is lower than the theoretical air requirement of the plastic film complete oxidation that this aluminium-foil scrap is contained;
B) substantially do not import outside air under the situation of this vapourizing furnace, solid phase prod after cooling aluminium-foil scrap bag is gasified; And
C) isolate aluminium foil from this refrigerative solid phase prod.
2. by the described method that reclaims aluminium foil from the aluminium-foil scrap bag of claim 1, it is characterized in that, wherein the step a) formed gas products that gasifies is extracted out from this vapourizing furnace continuously, and an air that is lower than theoretical air requirement is imported into this vapourizing furnace continuously under a base runoff simultaneously.
3. by the described method of claim 1, it is characterized in that wherein the oxygen deficient atmospheres of step a) is meant 10% to 70% of this theoretical air requirement from aluminium-foil scrap bag recovery aluminium foil.
4. by the described method of claim 1, it is characterized in that wherein the temperature of step a) is 300-500 ℃ from aluminium-foil scrap bag recovery aluminium foil.
5. by the described method of claim 2, it is characterized in that wherein this gas products that is drawn out of is recycled and is used as the required fuel of step a) heating from aluminium-foil scrap bag recovery aluminium foil.
6. one kind is applicable to the device that reclaims aluminium foil from the aluminium-foil scrap bag, it is characterized in that, comprises:
One vapourizing furnace, it is used for the contained organic substance of aluminium-foil scrap bag that is placed in the stove is carried out gasification reaction under anoxic environment;
One can be to the well heater of this vapourizing furnace heating;
One is connected in the air-intake duct of a side of this vapourizing furnace, and extraneous air promptly enters the inside of this vapourizing furnace through air-intake duct thus;
One charge flow rate controlling organization, it is located at this air-intake duct and controls the air flow quantity that enters this vapourizing furnace via this air-intake duct; And
One windmill of bleeding is used for the furnace gas of this vapourizing furnace is extracted out via a piping system.
7. by the described device of claim 6, it is characterized in that wherein this charge flow rate controlling organization comprises a under meter from aluminium-foil scrap bag recovery aluminium foil; An and flow control valve.
8. by the described device that reclaims aluminium foil from the aluminium-foil scrap bag of claim 6, it is characterized in that, it further comprises a water bath and and removes the tar device, this water bath and remove the tar device and be located in regular turn on this vapourizing furnace and this are bled this piping system between the windmill wherein, so the furnace gas of this vapourizing furnace top discharge is imported into the water-bath of this water bath and washs, and the washing gas of being discharged by the water-bath top of this water bath is imported into the bottom that this removes the inner filling of tar device filter material.