CN1170653A - Novel high toughness shock and wear resistant surface welding electrode - Google Patents
Novel high toughness shock and wear resistant surface welding electrode Download PDFInfo
- Publication number
- CN1170653A CN1170653A CN 97104063 CN97104063A CN1170653A CN 1170653 A CN1170653 A CN 1170653A CN 97104063 CN97104063 CN 97104063 CN 97104063 A CN97104063 A CN 97104063A CN 1170653 A CN1170653 A CN 1170653A
- Authority
- CN
- China
- Prior art keywords
- welding
- wear
- surface welding
- welding electrode
- surfacing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention aims solving the problem of surface welding electrode in available technology, which results in surface welded metal layer with poor toughness, shock and wear resistance. The said surface welding electrode has coating including marble-fluotrite-graphite sludge system as well as duriron, ferromanganese, metal chromium, high-carbon ferrochromium, ferro-molybdenum, ferrovanadium and other components. It is used mainly for surface welding the wear surface of carbon-steel and cast iron workpieces operating under mobile load condition.
Description
The present invention relates to a kind of anti abrasive surfacing welding.
Usually, welding rod built-up welding on the surface easy to wear of steel construction that anti abrasive surfacing welding often uses as a class, this class surfacing welding generally is by carbon, chromium, molybdenum, vanadium, manganese, alloying elements such as tungsten are strengthened, deposited metal has higher hardness (HRC is greater than 40 usually), certain wearability is also arranged, yet, the poor toughness of this class surfacing welding, crack resistance and anti impact wear-proof lead to ability, so just limited this extensive use of class surfacing welding on engineering, because in some workplace, excavator for example, the scraper bowl of loading machine, the flank of tooth, through the work under the moving load condition of being everlasting, the heap metal of the welding rod of built-up welding only has high rigidity and general wearability can not meet the demands on the workpiece of working under this condition, the deposited metal of this class welding rod also should have certain toughness having under the preceding dike of certain degree of hardness, and has higher crack resistance and impact wear resistance.
For example, international monopoly WO86/04284 discloses a kind of surfacing welding of high rigidity, and this welding rod is the surfacing welding by the ferrite base of alloying elements such as graphite, chromium, molybdenum, vanadium reinforcement, and this electrode coating composition and heavy degree thereof are:
Marble 18-25 fluorite 11-18 graphite 2.5-3 ferrochrome 12.5-15
Molybdenum-iron 25-30 vanadium iron 8-10 ferrotianium 5-6 ferrosilicon 4.2-5
Ferromanganese 0.7-1.2 mica 0.5-1.5 cellulose 0.5-1.5 soda 0.4-0.6
The hardness of the deposited metal of this welding rod quite high (HRC is greater than 59-61) has certain " red hardness " and wearability, still, according to the alloying element analysis of the reinforcement of this welding rod, the poor toughness of its deposited metal, crack resistance and anti impact wear-proof are poor.Simultaneously, according to slag system ingredient's analysis of this welding rod, the welding arc stablility of this welding rod and welding procedure are also bad.
In order to overcome above-mentioned deficiency of the prior art, the objective of the invention is to propose the surfacing welding that a kind of novel high-tenacity and shock-resistance weares and teares.
The paint ingredient of the surfacing welding electrode of novel high-toughness and wear-resistant of the present invention and percentage by weight thereof contain for:
Marble 10-15 fluorite 1-5 graphite 5-15 brium carbonate 3-20
Potash 1-5 iron powder 12-18 ferrophosphorus 1-3 ferrosilicon 4-8
Ferromanganese 2-6 crome metal 8-1 2 high carbon ferro-chrome 10-15 molybdenum-iron 1-3
Vanadium iron 1-3 aluminium powder 1-5 cellulose 1-3
The core wire of this welding rod is the H08A steel, and electrode size is φ 4.0mm, and coating back welding rod external diameter is φ 6.2mm, and utilizing modulus is 3.0 potassium-sodium water glass, and welding rod sintering temperature and time are 300 ℃ * 2 hours.
This welding rod utilizes the built-up welding of dc source reversed polarity, built-up welding one deck on steel plate, and postwelding deposited metal layer hardness HRC30-35, deposited metal layer sclerosis after mechanical shock, hardness can reach HRC50-55.This deposited metal toughness height has high crack resistance and anti impact wear-proof ability.
The impact wear resistance of welding rod obtains by following test:
Matrix of samples is No. 45 rod iron material of φ 11.28mm * 40mm, the end of this bar is the deposited metal that is processed into the welding rod of the present invention of the high 3-5mm of being after the built-up welding, the built-up welding standard is I=140A, speed of welding is the V=180mm/ branch, the anti impact wear-proof test is carried out in the above-mentioned end of this sample carry out on MLD dynamic load abrasive test machine, result of the test is as shown in table 1.
The anti impact wear-proof test of table 1 deposited metal
| The test reactor welding rod | Wear rate V (Grams Per Minute) |
| Surfacing welding of the present invention | ????0.44 |
| D202 (surfacing welding that contains carbon, chromium, molybdenum alloy) | ????1.0 |
Experimental condition: ballistic work 2.0J, 15 minutes impact wear time
V=Δ w/t (Grams Per Minute), Δ w impact wear amount
From the result of the test of table 1 as can be seen, the anti impact wear-proof ability of surfacing welding of the present invention is higher than general surfacing welding significantly.
What the present invention proposed is that a kind of austenite is the surfacing welding that matrix passes through graphite, chromium, molybdenum, vanadium reinforcement, in order to make this welding rod have high tenacity, high cracking resistance and anti impact wear-proof ability, a kind of new alloying system and corresponding percentage content thereof have been adopted.
At first, surfacing welding of the present invention is compared with the surfacing welding of above-mentioned international monopoly, improved the degree of graphite and chromium significantly, promptly adopted graphite 5-15%, crome metal 8-12, high carbon ferro-chrome 10-15, surfacing welding of the present invention in this degree scope again with an amount of metallic element molybdenum, vanadium matches and has just formed austenitic matrix and disperse in austenite crystal or the carbide of crystal boundary, simultaneously, the alloying element molybdenum, the all right crystal grain thinning of vanadium, thereby make deposited metal under the certain degree of hardness condition, have high tenacity, high crack resistance and anti impact wear-proof ability, these are that the surfacing welding by matrix with the ferrite of above-mentioned international monopoly is inaccessible.
In addition, the ferrophosphorus that adds less than 3% in electrode coating also is favourable, and P elements forms eutectic structure in built-up welding belongs to, and hinders grain growth, and impels partly carbide of crystal boundary dissolving, can improve the shock peening effect of deposited metal.Yet, when ferrophosphorus content greater than 3% the time, the crack resistance of deposited metal degenerates.
When content of graphite greater than 15%, the hardness of deposited metal improves, but crack resistance is poor, weld fumes is big, and weld edge produces black pollution, when high carbon ferro-chrome and crome metal respectively greater than 12% and 15% the time, deposited metal toughness is lower, crack resistance and anti impact wear-proof ability are also found molybdenum-iron and vanadium iron all greater than 3% o'clock, the toughness of deposited metal, crack resistance and anti impact wear-proof ability.When content of graphite less than 5% the time, the carbide content deficiency of deposited metal, ferrite content increases, simultaneously, the protective value of gas is poor, the stability and the welding fabrication of welding arc degenerate.
Surfacing welding of the present invention adopts marble-fluorite-graphite slag system, although the slag system of this and above-mentioned international monopoly is similar, the degree of the proportioning of these compositions has significant difference, and the present invention has adopted the proportioning of the best of a kind of mentioned component.Welding rod of the present invention adopts marble 10-15%, fluorite 1-5% and graphite 5-15%, is combined with arc stabilizer brium carbonate, aluminium powder etc. simultaneously, can significantly improve the stability of electric arc, improves the bead-welding technology performance of welding rod.Test shows that when the content of marble and fluorite surpassed the scope of 10-15 and 1-5% respectively, welding slag was topped bad, and the removability of slag is bad, and spatter increases, and appearance of weld is poor.
In sum, the eutectic structure that the metallographic structure of the deposited metal of welding rod of the present invention produces based on austenite and crystal boundary, have enough dispersing carbide in the austenite matrix, the carbide of dissolving is separated out in the austenite matrix, case hardness increases, and has high tenacity, high cracking resistance and impact-resistant abrasion-proof performance simultaneously.
The metallographic structure (* 400) of Fig. 1 welding rod deposited metal of the present invention
Fig. 1 is the metallographic structure figure (* 400) of welding rod deposited metal of the present invention, and as seen from Figure 1, the matrix of deposited metal is the dendroid austenite, crystal boundary continuous distributed eutectic structure and carbide. After impacting, carbide precipitate in the austenite crystal.
Welding rod of the present invention is compared with the welding rod of international monopoly WO86/04282, deposited metal is not only higher hardness after mechanical shock, have simultaneously high tenacity and high cracking resistance and impact-resistant abrasion-proof performance, therefore, the built-up welding of easy-wearing surface on the workpiece such as the mild steel that is suitable for working under the moving load condition, potassium steel and cast iron, for example built-up welding on the scraper bowl of excavator, loading machine, the flank of tooth.
Embodiment 1
A kind of surfacing welding of the present invention, the composition of this electrode coating and weight percent content thereof are:
Marble 10 fluorites 5 graphite 6 brium carbonates 15 potash 3.5
Iron powder 18 ferrophosphorus 1.5 ferrosilicon 5 ferromanganese 5 crome metals 10
High carbon ferro-chrome 12 molybdenum-irons 2 vanadium iron 2 aluminium powders 3 celluloses 2
Welding rod is the H08A steel, electrode size φ 4.0mm, and the welding rod external diameter φ 6.2mm after the coating, utilizing modulus is 3.0 potassium-sodium water glass, welding rod sintering temperature and time are 300 ℃ * 2 hours.
This surfacing welding utilizes the built-up welding of dc source reversed polarity, built-up welding one deck on the ZGMn13 steel plate, and surfacing hardness HRC32 after the built-up welding, hardness rises to HRC53 after mechanical shock, the overlay cladding flawless.Utilize aforesaid method to carry out the anti impact wear-proof test of the deposited metal of this welding rod, the wear rate V of this welding rod of result of the test is 0.40 Grams Per Minute, shows that this welding rod has high impact wear resistance.
Embodiment 2
The paint ingredient of institute's employing surfacing welding and weight percent content thereof are with embodiment 1, and all the other conditions are also identical with embodiment 1, and difference only is the built-up welding on grey cast-iron of this welding rod, and built-up welding one deck does not split.The wear rate V of this surfacing welding is 0.5 Grams Per Minute, shows that also this has high anti impact wear-proof ability.
Claims (2)
1. a wear-resistant surfacing welding is characterized in that, the paint ingredient of the surfacing welding of high-tenacity and wear-resistance and weight percent content are:
Marble 10-15 fluorite 1～5 graphite 5-15 brium carbonate 3-20
Potash 1-5 iron powder 12-18 ferrophosphorus 1-3 ferrosilicon 4-8
Ferromanganese 2-6 crome metal 8-12 high carbon ferro-chrome 10-15 molybdenum-iron 1-3
Vanadium iron 1-3 aluminium powder 1-5 cellulose 1-3
2. surfacing welding according to claim 1 is characterized in that, the deposited metal superficial layer hardness of this welding rod is HRC30-35, and the superficial layer hardness after mechanical shock is HRC50-55.