CN109226994A - A kind of hard-face overlaying welding flux-cored wire - Google Patents
A kind of hard-face overlaying welding flux-cored wire Download PDFInfo
- Publication number
- CN109226994A CN109226994A CN201811289579.2A CN201811289579A CN109226994A CN 109226994 A CN109226994 A CN 109226994A CN 201811289579 A CN201811289579 A CN 201811289579A CN 109226994 A CN109226994 A CN 109226994A
- Authority
- CN
- China
- Prior art keywords
- welding
- hard
- cored wire
- wire
- flux
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of hard-face overlaying welding flux-cored wire, belongs to surface reconditioning field of engineering technology.Flux-cored wire composition range by mass percentage are as follows: C:1.0%-2.0%, Si:0.4%-1.5%, Mn:0.4%-1.5%, Cr:4.5%-9.5%, Nb:2.0%-5.5%, Mo:2.0%-5.5%, W:2.0%-4.0%, V:0.5%-2.0%, remaining is Fe.The advantage is that welding wire has welding technological properties excellent, appearance of weld is excellent, and the de- slag of welding wire is excellent, overlay cladding pore-free, 5 layers of flawless of built-up welding, the mechanical equipment excellent wear-resisting property of Bead weld repair.
Description
Technical field
The invention belongs to surface reconditioning field of engineering technology, in particular to a kind of hard-face overlaying welding flux-cored wire.
Background technique
It is especially the mechanical equipment used under high temperature high corrosion atmosphere in the presence of a harsh environment, it is desirable that abrading section has higher
Service life, in this case it is required that abrading section high temperature hardness with higher and preferable toughness, working face are not present
The defects of loose, crackle, do not occur peeling chip off-falling in use.For the service life for improving equipment under adverse circumstances, hair
A kind of submerged-arc overlaying welding flux-cored wire of high alloy, surfacing hardness HRC56-62 is illustrated.
The alloy system that the high rigidity submerged-arc overlaying welding flux-cored wire of country surfacing hardness HRC56-62 uses at present has
Cr13NiMoV, CrMoV and CrMoWV etc., the overlay cladding hardness with higher of the above alloy series solder wire and preferable toughness, but
Wearability under the adverse circumstances of high temperature high corrosion is general, and the service life of equipment of Bead weld repair is relatively low.
For the service life for improving prosthetic appliance, a kind of submerged arc overlay welding welding wire that alloy system is CrNbMoWV, heap have been invented
Layer selects high phosphorus content, and phosphorus content 1.0-2.0% adds a variety of strong carbide shapes for the crack resistance for improving overlay cladding
At element nb, Mo, W, V, a variety of carbide are formed, carbide dispersion is precipitated, and forms the tiny tissue of crystal grain, is conducive to improve heap
The cracking resistance of layer.Since overlay cladding contains a large amount of carbide, carbide has very high microhardness, thus built-up welding
Layer has very excellent wear-resisting property.
Summary of the invention
The purpose of the present invention is to provide a kind of hard-face overlaying welding flux-cored wires, solve submerged arc overlay welding welding wire wear-resisting property
The problem of difference.Improve the service life of Bead weld repair part.
It solves the basic ideas of technical problem: adding high level carbon and a variety of alloying elements in welding wire, improve overlay cladding
Hardness, to improve the wear-resisting property of overlay cladding.The alloy for adding a variety of carbides, the disperse in deposited metal
It is precipitated, refines crystal grain, improve the cracking resistance of overlay cladding.
A kind of hard-face overlaying welding flux-cored wire, by mass percentage composition range are as follows: C:1.0%-2.0%, Si:0.4%-
1.5%, Mn:0.4%-1.5%, Cr:4.5%-9.5%, Nb:2.0%-5.5%, Mo:2.0%-5.5%, W:2.0%-
4.0%, V:0.5%-2.0%, remaining is Fe.
Submerged-arc overlaying welding flux-cored wire is provided using the present invention, is welded in following weld procedure specification: welding current 300-
500A, weldingvoltage 28-32V, surfacing hardness HRC56-62.
The key problem in technology that the present invention solves the problems, such as is to select a variety of carbide former Nb, Mo, W, V, forms a variety of carbon
Compound, carbide dispersion are precipitated, and form the tiny tissue of crystal grain, are conducive to the cracking resistance for improving overlay cladding.Due to overlay cladding
Containing a large amount of carbide, carbide has very high microhardness, thus overlay cladding has very excellent wear-resisting property.
It is an advantage of the current invention that welding wire has welding technological properties excellent, appearance of weld is excellent, and the de- slag of welding wire is excellent,
Overlay cladding pore-free, 5 layers of flawless of built-up welding, the mechanical equipment excellent wear-resisting property of Bead weld repair.Welding wire provided by the invention can
For bearing the Bead weld repair of the mechanical equipment of certain impact load.
Specific embodiment
Embodiment 1
A kind of hard-face overlaying welding flux-cored wire, by mass percentage composition range are as follows: C:1.1%, Si:0.45%, Mn:
0.65%, Cr:4.9%, Nb:2.9%, Mo:2.8%, W:2.7%, V:0.6%, remaining is Fe.The above welding wire, use are following
Specification welding: welding current 380A, weldingvoltage 30V.Overlay cladding flawless, surfacing hardness HRC57, overlay cladding have excellent
Good wear-resisting property.
Embodiment 2
A kind of hard-face overlaying welding flux-cored wire, by mass percentage composition range are as follows: C:1.6%, Si:0.75%, Mn:
1.45%, Cr:8.9%, Nb:3.9%, Mo:3.5%, W:3.4%, V:0.9%, remaining is Fe.The above welding wire, use are following
Specification welding: welding current 380A, weldingvoltage 30V.Overlay cladding flawless, surfacing hardness HRC61, overlay cladding have excellent
Good wear-resisting property.
Embodiment 3
A kind of hard-face overlaying welding flux-cored wire, by mass percentage composition range are as follows: C:1.5%, Si:0.45%, Mn:
0.65%, Cr:5.9%, Nb:1.9%, Mo:1.8%, W:0.7%, V:0.2%, remaining is Fe.The above welding wire, use are following
Specification welding: welding current 380A, weldingvoltage 30V.Welding wire welding overlay cladding is cracked, surfacing hardness HRC57, heap
Layer wear-resisting property is poor, will appear peeling phenomenon in the equipment use process of Bead weld repair.
Claims (2)
1. a kind of hard-face overlaying welding flux-cored wire, which is characterized in that composition range by mass percentage are as follows: C:1.0%-2.0%,
Si:0.4%-1.5%, Mn:0.4%-1.5%, Cr:4.5%-9.5%, Nb:2.0%-5.5%, Mo:2.0%-5.5%, W:
2.0%-4.0%, V:0.5%-2.0%, remaining is Fe.
2. welding wire according to claim 1, which is characterized in that the weld procedure specification of the welding wire are as follows: welding current
300-500A, weldingvoltage 28-32V, surfacing hardness HRC56-62.