CN116925568A - 一种分散翠蓝染料组合物和染料制品 - Google Patents
一种分散翠蓝染料组合物和染料制品 Download PDFInfo
- Publication number
- CN116925568A CN116925568A CN202310783558.0A CN202310783558A CN116925568A CN 116925568 A CN116925568 A CN 116925568A CN 202310783558 A CN202310783558 A CN 202310783558A CN 116925568 A CN116925568 A CN 116925568A
- Authority
- CN
- China
- Prior art keywords
- component
- turquoise blue
- blue dye
- dye composition
- formula
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种分散翠蓝染料组合物和染料制品，所述分散翠蓝染料组合物包括组分A、组分B、组分C和组分D，其中组分A为式(I)所示化合物中的至少一种，组分B为式(II)所示的化合物中的至少一种，组分C为式(III)所示化合物中的至少一种，组分D为式(IV)所示化合物中的至少一种。本发明的分散翠蓝染料组合物和染料制品应用于疏水性纤维材料染色时，具有优良的分散性、渗透性和染色坚牢度，可减少筒子纱染色内外层色差，适用于色织和针织后加工整理工艺。
Description
技术领域
本发明涉及一种分散翠蓝染料组合物和染料制品，尤其涉及一种适合印染疏水性纤维材料的分散翠蓝染料组合物和染料制品。
背景技术
分散染料复配增效是获取高性能染料新品种的有效途径，分散翠蓝S-GL色泽艳丽，主要用于浸染和印花，在市场上一直比较受欢迎，但该染料发色强度不高、提升率较低，印染时较难获得深浓色，尽管CN102732061A、CN107383936A等专利提供了一种分散翠蓝染料，但仍需进一步提升其性能来满足不断变化的客户要求，如适应中高端涤氨面料的印染。
发明内容
本发明目的是提供一种分散翠蓝染料组合物和染料制品，应用于疏水性纤维材料染色时，具有优良的分散性、渗透性和染色坚牢度，可减少筒子纱染色内外层色差，适用于色织和针织后加工整理工艺。
本发明采用的技术方案是：
一种分散翠蓝染料组合物，包括组分A、组分B、组分C和组分D，其中组分A为式(I)所示化合物中的至少一种，组分B为式(II)所示的化合物中的至少一种，组分C为式(III)所示化合物中的至少一种，组分D为式(IV)所示化合物中的至少一种，所述分散翠蓝染料组合物中，组分A的质量百分含量为20～75％，组分B的质量百分含量为15～75％，组分C的质量百分含量为1～20％，组分D的质量百分含量为1～15％；
式(I)中：
R1为H、C1～C4的烷基、C1～C4的烷氧基或CF3；
R2、R3各自独立为C1～C8的烷基、-(CH2)m-OK1、-(CH2)n-Ph；其中Ph为苯基，K1选自C1～C4的烷基，m、n各自独立为2或3；
式(III)中：
R4、R5各自独立为C1～C4烷基或苄基；
式(IV)中：
R6、R7各自独立为C1～C18烷基。
本发明中，所述的C1～C4烷基可以是甲基、乙基、直链或支链的丙基、直链或支链的丁基。所述的C1～C4烷氧基可以是甲氧基、乙氧基、直链或支链的丙氧基、直链或支链的丁氧基。所述的C1～C18烷基可以是甲基、乙基、直链或支链的丙基、直链或支链的丁基、直链或支链的己基、直链或支链的辛基、直链或支链的十二烷基、直链或支链的十八烷基等。
作为优选，所述组分A选自下列之一或其中两种以上任意比例的混合物：
作为优选，所述组分C选自下列之一或其中两种以上任意比例的混合物：
作为优选，所述组分D选自下列之一或其中两种以上任意比例的混合物：
作为优选，所述分散翠蓝染料组合物中，组分A的质量百分含量为20～75％，组分B的质量百分含量为为20～75％，组分C的质量百分含量为1～15％，组分D的质量百分含量为1～10％。
作为进一步的优选，所述的分散翠蓝染料组合物，包含组分A、组分B、组分C和组分D，其中：
组分A选自式(I-1)、(I-2)中的至少一种；
组分B为式(II)；
组分C选自式(III-1)、(III-2)中的至少一种；
组分D选自式(IV-1)、(IV-2)及(IV-6)中的至少一种；
其中组分A的质量百分含量为20～75％，组分B的质量百分含量为15～75％，组分C的质量百分含量为1～20％，组分D的质量百分含量为1～15％。
作为特别优选，所述的分散翠蓝染料组合物，由组分A、组分B、组分C和组分D组成，所述组分A的质量百分含量为20～75％，组分B的质量百分含量为15～75％，组分C的质量百分含量为1～20％，组分D的质量百分含量为1～15％。
需要强调的是，本发明所述的分散翠蓝染料化合物，在吡啶酮羟基邻位偶合的染料通常以醌腙体形式存在，亦即通式(IV)染料实质具有下式(IVa)所示的醌腙体结构，考虑到本领域技术人员的书写习惯，在发明内容和实施例部分仍采用了偶氮体的书写形式，这并不影响本发明的实质：
R6、R7与上述式(IV)化合物中的定义相同。
需要说明的是，由于染料行业的特殊性，所述的组分A、B、C和D很难也没有必要制成纯品，通常在其合成中会产生少量的副产物，无需单独分离，可一并用于染料的复配，其量优选控制在10％以内(基于染料组分重，不计助剂)。
本发明所述的分散翠蓝染料组合物，还允许加入质量百分含量不超过5％的调色组分，如C.I.分散黄54、C.I.分散黄64、C.I.分散黄119、C.I.分散黄143、C.I.分散黄182、C.I.分散橙25、C.I.分散橙61、C.I.分散红73、C.I.分散红80、C.I.分散红145、C.I.分散红158等。
上述方案中，C.I.指的是染料索引号(COLOR INDEX)，是英国染色家协会(SDC)和美国纺织化学家和染色家协会(AATCC)合编出版的国际染料颜料品种汇编。所述的“染料部分”指的是染料滤饼(原染料)，不包括任何后整理助剂，但允许含有合成中带来的少量杂质，该杂质不影响染料的使用性能，所述的染料质量百分含量或质量份皆以染料滤饼折干量计算。
本发明所述的分散翠蓝染料组合物，作为商品出售或应用于纺织材料印染时，通常还需要加入助剂进行后处理。因此，本发明还提供了一种可作为商品出售或直接应用于纺织材料印染的分散翠蓝染料制品，由所述的分散翠蓝染料组合物和助剂组成，助剂和分散翠蓝染料组合物的重量之比为0.2～5:1。所述的助剂为分散染料复配时常用的分散剂、扩散剂及其它表面活性剂等，优选自下列之一或其中两种以上的混合物：木质素磺酸盐(如木质素磺酸钠(木质素85A、木质素83A))、烷基萘磺酸甲醛缩合物(如甲基萘磺酸甲醛缩合物(分散剂MF))、萘磺酸甲醛缩合物(扩散剂NNO)、苄基萘磺酸甲醛缩合物(扩散剂CNF)、硫酸钠等。
本发明所述的分散翠蓝染料制品的制备方法如下：将前述的染料单体化合物(原染料)按配比混合后，在助剂、水的存在下用砂磨机或研磨机等粉碎机进行微粒子化；另外也可将染料单体化合物分别在助剂、水的存在下用砂磨机或研磨机等粉碎机进行微粒子化处理后按比例进行混合。本发明所述的分散翠蓝染料制品，用砂磨机或研磨机研磨后为液状，喷雾干燥后可为粉状、颗粒状，这是本领域技术人员公知的制备方法。
本发明所使用的式(I)～(IV)所示的染料化合物可方便地按本领域技术人员熟知的方式合成，也可采用市售商品，利用本发明染料组合物制成的染料制品，可按行业内惯用方式对疏水性纤维材料(如聚酯及其混纺交织物)进行染色，如采用普通浸染法或高温高压染色法进行染色，也可用于筒子纱染色和直接印花。其中，普通浸染法如将疏水性纤维材料进行预处理，放入染缸中进行浸染，染毕，冷水清洗至中性，绞干，再进行还原清洗，烘干；筒子纱染色如将原纱松筒-倒角-装笼-进入染缸-前处理-水洗-加入纱线染色(1℃/1min)升温至70℃匀染10min—(1℃/1min)升温至100℃匀染10min—(1℃/min)升温至130℃保温45-60min—高温排水—洗水—还原清洗—脱水—烘干；直接印花如将织物进行染前处理，烘干，定形，在印花机上印分散染料色浆，再进行蒸化，利用汽蒸方式使织物上的染料固色，最后水洗，拉幅定型。
与现有技术相比，本发明的有益效果在于：本发明提供的分散翠蓝染料组合物和染料制品，应用于聚酯及其混纺织物的染色，特别是涤氨混纺织物的染色，具有提升性好、对氨纶沾污性小、耐水洗牢度、耐升华牢度性能优异等特点，也特别适用于筒子纱染色。
具体实施方式
下面结合具体实施例对本发明进行进一步描述，但本发明的保护范围并不仅限于此：
实施例1：
将40克式(I-1)所示的染料，40克式(II)所示的染料，15克式(III-1)所示的染料，5克式(IV-1)所示的染料，255克的分散剂MF，加2000克水混拼后，研磨分散并干燥，即得成品，该成品能提供聚酯及其混纺织物翠蓝色色调。
实施例2：
将45克式(I-1)所示的染料，45克式(II)所示的染料，5克式(III-2)所示的染料，5克式(IV-2)所示的染料，280克的扩散剂CNF，加2000克水混拼后，研磨分散并干燥，即得成品，该成品能提供聚酯及其混纺织物翠蓝色色调。
实施例3～23
按照实施例1-2所述的方法，不同的是采用表1中组分A、组分B、组分C、组分D所示的染料及重量，加入助剂200克(分散剂MF为50克，木质素磺酸钠为150克)，加水2000克拼混后制成浆液，研磨分散并干燥，制得成品，该染料能提供给聚酯及其混纺织物各项牢度性能优良的翠蓝色色调。
表1
实施例24：
将45克前述式(I-1)所示的染料，30克式(II)所示的染料，10克式(III-1)所示的染料，10克式(IV-1)所示的染料，5克C.I.分散黄54，250克的分散剂MF，加2500克水混拼后，研磨分散并干燥，即得成品，该成品能提供聚酯及其混纺织物翠蓝色色调。
对比例1：
将CN107383936A中实施例1作为对比例1。
对比例2：
将CN102558908A中实施例1作为对比例2。
对比例3：
将CN106752086A中实施例7作为对比例3。
对比例4：
将CN103613953A中实施例1作为对比例4。
染色实施例：
分别称取2克实施例1～24制得的分散染料、对比例1～4的染料，采用常规高温高压染色法处理涤/氨交织物，处理过程中，控制染色深度(o.w.f)4.0％，浴比1∶25，调染浴pH值4～5，室温入染，以1℃/min升温至130℃，保温60min，按常法还原净洗、水洗、干燥，冷却到70℃取出。观察样布色光，采用国际标准ISO 105-X12、AATCC 61-2A、ISO 105-P01分别测试其耐摩擦、耐水洗、耐升华色牢度，结果见表2：
表2
/>
由上表可知：本发明制备的分散翠蓝染料组合物，用于涤纶/氨纶织物的印染，其耐摩擦、耐水洗沾色牢度明显优于对比例1～4，能够满足高牢度要求面料的印染；而且实施例1～24采用上述高温高压法筒子纱染色涤纶时，层差与色渍也明显优于对比例1～4。
Claims (10)
1.一种分散翠蓝染料组合物，其特征在于：所述分散翠蓝染料组合物包括组分A、组分B、组分C和组分D，其中组分A为式(I)所示化合物中的至少一种，组分B为式(II)所示的化合物中的至少一种，组分C为式(III)所示化合物中的至少一种，组分D为式(IV)所示化合物中的至少一种，所述分散翠蓝染料组合物中，组分A的质量百分含量为20～75％，组分B的质量百分含量为15～75％，组分C的质量百分含量为1～20％，组分D的质量百分含量为1～15％；
式(I)中：
R1为H、C1～C4的烷基、C1～C4的烷氧基或CF3；
R2、R3各自独立为C1～C8的烷基、-(CH2)m-OK1、-(CH2)n-Ph；其中Ph为苯基，K1选自C1～C4的烷基，m、n各自独立为2或3；
式(III)中：
R4、R5各自独立为C1～C4烷基或苄基；
式(IV)中：
R6、R7各自独立为C1～C18烷基。
2.如权利要求1所述的分散翠蓝染料组合物，其特征在于：所述组分A选自下列之一或其中两种以上任意比例的混合物：
3.如权利要求1所述的分散翠蓝染料组合物，其特征在于：所述组分C选自下列之一或其中两种以上任意比例的混合物：
4.如权利要求1所述的分散翠蓝染料组合物，其特征在于：所述组分D选自下列之一或其中两种以上任意比例的混合物：
5.如权利要求1所述的分散翠蓝染料组合物，其特征在于：所述分散翠蓝染料组合物中，组分A的质量百分含量为20～75％，组分B的质量百分含量为为20～75％，组分C的质量百分含量为1～15％，组分D的质量百分含量为1～10％。
6.如权利要求1或5所述的分散翠蓝染料组合物，其特征在于：所述的分散翠蓝染料组合物，包含组分A、组分B、组分C和组分D，其中：
组分A选自式(I-1)、(I-2)中的至少一种；
组分B为式(II)；
组分C选自式(III-1)、(III-2)中的至少一种；
组分D选自式(IV-1)、(IV-2)及(IV-6)中的至少一种；
7.如权利要求6所述的分散翠蓝染料组合物，其特征在于：所述的分散翠蓝染料组合物，由组分A、组分B、组分C和组分D组成。
8.如权利要求1所述的分散翠蓝染料组合物，其特征在于：式(IV)所示的化合物具有下式(IVa)所示的醌腙体结构，
其中R6、R7与上述式(IV)化合物中的定义相同。
9.一种分散翠蓝染料制品，其特征在于：所述分散翠蓝染料制品由所述的分散翠蓝染料组合物和助剂组成，助剂和分散翠蓝染料组合物的重量之比为0.2～5:1。
10.如权利要求9所述的分散翠蓝染料制品，其特征在于：所述的助剂选自下列之一或其中两种以上的混合物：木质素磺酸盐、烷基萘磺酸甲醛缩合物、萘磺酸甲醛缩合物、苄基萘磺酸甲醛缩合物、硫酸钠。