CN116696142B - 一种用于制作大型电磁屏蔽指挥帐篷高强度复合屏蔽材料 - Google Patents
一种用于制作大型电磁屏蔽指挥帐篷高强度复合屏蔽材料 Download PDFInfo
- Publication number
- CN116696142B CN116696142B CN202310971105.0A CN202310971105A CN116696142B CN 116696142 B CN116696142 B CN 116696142B CN 202310971105 A CN202310971105 A CN 202310971105A CN 116696142 B CN116696142 B CN 116696142B
- Authority
- CN
- China
- Prior art keywords
- shielding
- film
- layer
- frequency
- strength composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及磁屏蔽技术领域,公开了一种用于制作大型电磁屏蔽指挥帐篷高强度复合屏蔽材料,包括基布层,基布层的外表面均匀涂覆布置分频屏蔽导电涂层结构,分频屏蔽导电涂层结构从外层到内层依次包括导电聚合物喷涂层和金属薄膜层。本发明在基布层外表面快速涂覆分频屏蔽导电涂层结构,由平贴膜和蜂窝膜组成的银薄膜层、导电聚合物喷涂层构成,屏蔽材料的主体位于外部,能够通过导电体的短路作用,破坏了电场的形成,从而截断了电磁波的继续传播,且过程中金属薄膜和涂层接触外界,本身具有较好的热传导性能,涂层上产生的热量快速均匀的分布传递,并和空气热交换,结构的热稳定性强,保证夏季户外高温环境的高强度稳定屏蔽效果。
Description
技术领域
本发明涉及电磁屏蔽技术领域,具体为一种用于制作大型电磁屏蔽指挥帐篷高强度复合屏蔽材料。
背景技术
在野外或者特殊场合,为了保护设备或者人员的安全,电磁屏蔽帐篷成为了必需品。它能够有效地屏蔽周围的电磁波干扰,保护设备正常工作,同时也能够防止敏感信息泄露,这对于军事、安全等领域的通信设备来说尤为重要。《中国新通信》2012年第17期刊载了一种高性能电磁屏蔽帐篷设计方案。结合目前电磁屏蔽帐篷的结构设计,如中国专利公开号:CN213115778U提出了一种低中高频用三合一电磁屏蔽帐篷布,包括编织物主体,所述编织物主体的内侧壁皆均匀设置有第二微波屏蔽织物,编织物主体的外侧壁皆均匀设置有第一微波屏蔽织物,第一微波屏蔽织物的内部等间距设置有上连接带,且第二微波屏蔽织物的内部等间距设置有下连接带,所述第一微波屏蔽织物的外侧壁皆均匀设置有高频屏蔽织物,高频屏蔽织物的外侧壁皆均匀设置有低频吸波织物,且低频吸波织物的外侧壁皆均匀设置有电磁波干扰层。
帐篷布料的电磁屏蔽结构是最为重要的,上述现有技术在实际应用中仍然存在缺陷:在夏季时期,户外温度高。帐篷搭设后,布层在太阳照射的高温环境下,由于层体结构复合多,内置金属网,导致布体吸热能力强,并且在布层内部,导致热量过高不散,内部稳定性不足,影响降低了屏蔽效果。
为此,提出了一种用于制作大型电磁屏蔽指挥帐篷高强度复合屏蔽材料来解决上述的问题。
发明内容
本发明的目的在于提供一种用于制作大型电磁屏蔽指挥帐篷高强度复合屏蔽材料,能够分段屏蔽和高强度稳定使用,以解决上述背景技术中提出的屏蔽稳定性不足问题。
为实现上述目的,本发明提供如下技术方案:一种用于制作大型电磁屏蔽指挥帐篷高强度复合屏蔽材料,包括基布层,所述基布层的外表面均匀涂覆布置分频屏蔽导电涂层结构,分频屏蔽导电涂层结构从外层到内层依次包括导电聚合物喷涂层和金属薄膜层,依次对电磁波进行基础屏蔽和穿透波段的分频屏蔽;
金属薄膜层包括一体化设置的平贴膜和蜂窝膜,所述平贴膜的底面胶接在基布层,让蜂窝膜朝向外界的屏蔽孔口径逐级减小,口径部位的膜壁厚度逐级减小,且所述平贴膜的膜片厚度大于蜂窝膜的膜片厚度,依次对中频电磁波、高频电磁波和低频电磁波进行屏蔽;
导电聚合物喷涂层由导电纳米颗粒、纳米颗粒在聚合物基体层中混合形成涂料层,质量配比为1:1:8,且均匀喷涂于金属薄膜层的外壁面,形成复合导电网络,用于屏蔽电磁波。
作为本发明所述用于制作大型电磁屏蔽指挥帐篷高强度复合屏蔽材料的一种可选方案,其中:所述金属薄膜层设置为银薄膜层。
作为本发明所述用于制作大型电磁屏蔽指挥帐篷高强度复合屏蔽材料的一种可选方案,其中:所述蜂窝膜的屏蔽孔为菱形结构,且每个屏蔽孔相邻连接布置。
作为本发明所述用于制作大型电磁屏蔽指挥帐篷高强度复合屏蔽材料的一种可选方案,其中:所述屏蔽孔从外到里以中心线为界依次包括中频屏蔽膜孔和高频屏蔽膜孔,所述中频屏蔽膜孔最外部的内径为5mm-8cm,所述高频屏蔽膜孔最底部的内径为500μm-800μm。
作为本发明所述用于制作大型电磁屏蔽指挥帐篷高强度复合屏蔽材料的一种可选方案,其中:所述中频屏蔽膜孔侧部的中频屏蔽膜段膜壁厚度为3μm-50μm,所述高频屏蔽膜孔侧部的高频屏蔽膜段膜壁厚度为50μm-4mm。
作为本发明所述用于制作大型电磁屏蔽指挥帐篷高强度复合屏蔽材料的一种可选方案,其中:所述平贴膜的厚度为4mm-6cm。
作为本发明所述用于制作大型电磁屏蔽指挥帐篷高强度复合屏蔽材料的一种可选方案,其中:所述导电纳米颗粒设置为导电氧化锌纳米颗粒。
作为本发明所述用于制作大型电磁屏蔽指挥帐篷高强度复合屏蔽材料的一种可选方案,其中:所述纳米颗粒设置为二氧化硅纳米颗粒。
作为本发明所述用于制作大型电磁屏蔽指挥帐篷高强度复合屏蔽材料的一种可选方案,其中:所述聚合物基体层设置为聚三氟乙烯颗粒层。
作为本发明所述用于制作大型电磁屏蔽指挥帐篷高强度复合屏蔽材料的一种可选方案,其中:所述导电聚合物喷涂层内还添加有陶瓷颗粒,陶瓷颗粒的配比质量少于导电纳米颗粒的配比质量。
与现有技术相比,本发明的有益效果:
1、该用于制作大型电磁屏蔽指挥帐篷高强度复合屏蔽材料,在作为支撑主体的基布层外表面快速涂覆分频屏蔽导电涂层结构,由平贴膜和蜂窝膜组成的银薄膜层、导电聚合物喷涂层构成,屏蔽材料的主体位于外部,能够通过导电体的短路作用,破坏了电场的形成,从而截断了电磁波的继续传播,且过程中金属薄膜和涂层接触外界,本身具有较好的热传导性能,涂层上产生的热量快速均匀的分布传递,并和空气热交换,结构的热稳定性强,保证夏季户外高温环境的高强度稳定屏蔽效果;
2、该用于制作大型电磁屏蔽指挥帐篷高强度复合屏蔽材料,金属薄膜层底部由较薄的平贴膜连接基布层外表面,平贴膜外表面一体化连接的蜂窝膜利用孔径逐渐减小,膜壁厚度也逐渐减小的屏蔽孔依次进行中、高频段电磁波的屏蔽,低频段电磁波主要由较厚的平贴膜进行屏蔽,实现分频屏蔽的效果;
3、该用于制作大型电磁屏蔽指挥帐篷高强度复合屏蔽材料,导电聚合物喷涂层主要由导电氧化锌纳米颗粒、二氧化硅纳米颗粒和聚三氟乙烯颗粒均匀混合形成涂料层,或添加陶瓷颗粒来稳定结构,喷涂于金属薄膜表面,形成基础的电磁屏蔽层,对全频段电磁波进行基础屏蔽。
附图说明
图1为本发明的主视结构示意图。
图2为本发明的局部结构爆炸示意图。
图3为本发明金属薄膜层的局部剖面结构示意图。
图4为本发明金属薄膜层的爆炸结构示意图。
图5为本发明金属薄膜层与导电聚合物喷涂层连接关系的爆炸结构展示示意图。
图中:1、基布层;2、金属薄膜层;201、平贴膜;202、蜂窝膜;2021、中频屏蔽膜段;2022、高频屏蔽膜段;203、屏蔽孔;2031、中频屏蔽膜孔;2032、高频屏蔽膜孔;3、导电聚合物喷涂层。
具体实施方式
下面将结合本发明实施例中的附图,对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
请参阅图1-5所示:
实施例1
一种用于制作大型电磁屏蔽指挥帐篷高强度复合屏蔽材料,包括基布层1,作为帐篷布体的基层,材料为现有技术,提供屏蔽层体的支撑力,基布层1的外表面均匀涂覆布置分频屏蔽导电涂层结构,分频屏蔽导电涂层结构从外层到内层依次包括导电聚合物喷涂层3和金属薄膜层2,依次对电磁波进行基础屏蔽和穿透波段的分频屏蔽;
在作为支撑主体的基布层1外表面快速涂覆分频屏蔽导电涂层结构,屏蔽材料的主体位于外部,能够通过导电体的短路作用,破坏了电场的形成,从而截断了电磁波的继续传播,且过程中金属薄膜和涂层接触外界,本身具有较好的热传导性能,涂层上产生的热量快速均匀的分布传递,并和空气热交换,结构的热稳定性强,保证夏季户外高温环境的屏蔽效果;
金属薄膜层2包括一体化设置的平贴膜201和蜂窝膜202,平贴膜201的底面胶接在基布层1,让蜂窝膜202朝向外界的屏蔽孔203口径逐级减小,口径部位的膜壁厚度逐级减小,且平贴膜201的膜片厚度大于蜂窝膜202的膜片厚度,依次对中频电磁波、高频电磁波和低频电磁波进行屏蔽;
本实施例1中,金属薄膜层2设置为银薄膜层,在大型帐篷表面应用时,能够快速高效的导电,相较铜铝薄膜进行较好的电磁屏蔽。
本实施例1中,蜂窝膜202的屏蔽孔203为菱形结构,且每个屏蔽孔203相邻连接布置,形成蜂窝状结构,蜂窝状的表面积大,菱形结构的屏蔽孔203在太阳照射下会有局部被其它部位遮挡,利用较大的表面和阴影遮挡部位,通过银的高导热效果,能够高效接触外界空气进行热量散发,使用强度高。
需要说明:屏蔽孔203为等边菱形孔。
电磁波是一种横波,具有波长和频率两个基本特性。波长是指电磁波中相邻两个峰或谷之间的距离,通常用λ表示,而频率则是指电磁波的周期性振动次数,通常用f表示。波长和频率之间有如下关系:速度=波长×频率v=λ×f。在低频范围内,电磁波的波长较长,意味着相邻两个峰或谷之间的距离较大。
由此,屏蔽孔203的孔径大小与低中高频率的对应是根据电磁波的波长来确定的。电磁波的波长与频率之间的关系由光速确定,光速约等于3×10^8m/s。其计算公式为:波长λ= 光速c/频率f。
1、低频范围:
频率范围:20Hz-300kHz;
波长范围:10000m-1000m;
需要的孔径大小:3m-60m;
2、中频范围:
频率范围:300kHz-300MHz;
波长范围:1000m-1m;
需要的孔径大小:5mm-8cm;
3、高频范围:
频率范围:300MHz-300GHz;
波长范围:1m-1mm;
需要的孔径大小:500μm-800μm。
本实施例1中,屏蔽孔203从外到里以中心线为界依次包括中频屏蔽膜孔2031和高频屏蔽膜孔2032,中频屏蔽膜孔2031最外部的内径为5mm-8cm,高频屏蔽膜孔2032最底部的内径为500μm-800μm。
在实际应用中,屏蔽孔203可以根据屏蔽波段的需要,进行屏蔽孔203的孔径设计,针对不同波段的电磁波进行屏蔽。
需要说明:低频、中频和高频段的电磁波因为它们对电磁波的穿透和反射行为有所不同,对于金属薄膜层2的厚度要求也是不同的。
1、低频范围:
需要的厚度大小:4mm-6cm;
2、中频范围:
需要的厚度大小:50μm-4mm;
3、高频范围:
需要的厚度大小:3μm-50μm;
进一步地,中频屏蔽膜孔2031侧部的中频屏蔽膜段2021膜壁厚度为3μm-50μm,高频屏蔽膜孔2032侧部的高频屏蔽膜段2022膜壁厚度为50μm-4mm。
即,在中频屏蔽膜孔2031位置,通过孔进行中频屏蔽,孔壁的膜体进行高频屏蔽,则一起进行中高频段电磁波的屏蔽;同理述高频屏蔽膜孔2032位置,相应一起进行中高频段电磁波的屏蔽。
另外,由于孔径设置无法满足低频电磁波屏蔽的需求,并且当低频电磁波传播到小孔时,由于其波长相对较长,会出现折射和衍射现象,这使得低频电磁波能够穿过小孔。
为此,在本实施例1中,平贴膜201的厚度为4mm-6cm,用于屏蔽低频电磁波。
即,金属薄膜层2底部由较厚的平贴膜201连接基布层1外表面,平贴膜201外表面一体化连接的蜂窝膜202利用孔径逐渐减小,膜壁厚度也逐渐减小的屏蔽孔203依次进行中、高频段电磁波的屏蔽,低频段电磁波主要由较厚的平贴膜201进行屏蔽,实现分频屏蔽的效果;
导电聚合物喷涂层3由导电纳米颗粒、纳米颗粒在聚合物基体层中混合形成涂料层,质量配比为1:1:8,且均匀喷涂于金属薄膜层2的外壁面,形成复合导电网络,用于屏蔽电磁波。
本实施例1中,导电纳米颗粒设置为导电氧化锌纳米颗粒。
本实施例1中,纳米颗粒设置为二氧化硅纳米颗粒。
本实施例1中,聚合物基体层设置为聚三氟乙烯颗粒层。
实施例2
在实施例1的基础上,进一步改进导电聚合物喷涂层3的结构性能:
作为本实施例2的进一步改进,导电聚合物喷涂层3内还添加有陶瓷颗粒,陶瓷颗粒的配比质量少于导电纳米颗粒的配比质量。陶瓷颗粒的添加能够增强涂层的硬度和耐磨性,也提高涂层的热稳定性和耐腐蚀性,陶瓷颗粒的添加量在涂层总配比的1-10%范围内,以确保导电涂层具有所需的导电性、机械性能和热稳定性。
即,导电聚合物喷涂层3主要由导电氧化锌纳米颗粒、二氧化硅纳米颗粒和聚三氟乙烯颗粒均匀混合形成涂料层,或添加陶瓷颗粒来稳定结构,喷涂于金属薄膜表面,形成基础的电磁屏蔽层,对全频段电磁波进行基础屏蔽。
需要说明的是,在本文中,诸如第一和第二等之类的关系术语仅仅用来将一个实体或者操作与另一个实体或操作区分开来,而不一定要求或者暗示这些实体或操作之间存在任何这种实际的关系或者顺序。而且,术语“包括”、“包含”或者其任何其他变体意在涵盖非排他性的包含,从而使得包括一系列要素的过程、方法、物品或者设备不仅包括那些要素,而且还包括没有明确列出的其他要素,或者是还包括为这种过程、方法、物品或者设备所固有的要素。
尽管已经示出和描述了本发明的实施例,对于本领域的普通技术人员而言,可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型,本发明的范围由所附权利要求及其等同物限定。
Claims (10)
1.一种用于制作大型电磁屏蔽指挥帐篷高强度复合屏蔽材料,包括基布层(1),其特征在于:所述基布层(1)的外表面均匀涂覆布置分频屏蔽导电涂层结构,分频屏蔽导电涂层结构从外层到内层依次包括导电聚合物喷涂层(3)和金属薄膜层(2),依次对电磁波进行基础屏蔽和穿透波段的分频屏蔽;
金属薄膜层(2)包括一体化设置的平贴膜(201)和蜂窝膜(202),所述平贴膜(201)的底面胶接在基布层(1),让蜂窝膜(202)朝向外界的屏蔽孔(203)口径逐级减小,口径部位的膜壁厚度逐级减小,且所述平贴膜(201)的膜片厚度大于蜂窝膜(202)的膜片厚度,依次对中频电磁波、高频电磁波和低频电磁波进行屏蔽;
导电聚合物喷涂层(3)由导电纳米颗粒、纳米颗粒在聚合物基体层中混合形成涂料层,质量配比为1:1:8,且均匀喷涂于金属薄膜层(2)的外壁面,形成复合导电网络,用于屏蔽电磁波。
2.根据权利要求1所述的一种用于制作大型电磁屏蔽指挥帐篷高强度复合屏蔽材料,其特征在于:所述金属薄膜层(2)设置为银薄膜层。
3.根据权利要求1所述的一种用于制作大型电磁屏蔽指挥帐篷高强度复合屏蔽材料,其特征在于:所述蜂窝膜(202)的屏蔽孔(203)为菱形结构,且每个屏蔽孔(203)相邻连接布置。
4.根据权利要求3所述的一种用于制作大型电磁屏蔽指挥帐篷高强度复合屏蔽材料,其特征在于:所述屏蔽孔(203)从外到里以中心线为界依次包括中频屏蔽膜孔(2031)和高频屏蔽膜孔(2032),所述中频屏蔽膜孔(2031)最外部的内径为5mm-8cm,所述高频屏蔽膜孔(2032)最底部的内径为500μm-800μm。
5.根据权利要求4所述的一种用于制作大型电磁屏蔽指挥帐篷高强度复合屏蔽材料,其特征在于:所述中频屏蔽膜孔(2031)侧部的中频屏蔽膜段(2021)膜壁厚度为3μm-50μm,所述高频屏蔽膜孔(2032)侧部的高频屏蔽膜段(2022)膜壁厚度为50μm-4mm。
6.根据权利要求5所述的一种用于制作大型电磁屏蔽指挥帐篷高强度复合屏蔽材料,其特征在于:所述平贴膜(201)的厚度为4mm-6cm。
7.根据权利要求1所述的一种用于制作大型电磁屏蔽指挥帐篷高强度复合屏蔽材料,其特征在于:所述导电纳米颗粒设置为导电氧化锌纳米颗粒。
8.根据权利要求1所述的一种用于制作大型电磁屏蔽指挥帐篷高强度复合屏蔽材料,其特征在于:所述纳米颗粒设置为二氧化硅纳米颗粒。
9.根据权利要求1所述的一种用于制作大型电磁屏蔽指挥帐篷高强度复合屏蔽材料,其特征在于:所述聚合物基体层设置为聚三氟乙烯颗粒层。
10.根据权利要求1所述的一种用于制作大型电磁屏蔽指挥帐篷高强度复合屏蔽材料,其特征在于:所述导电聚合物喷涂层(3)内还添加有陶瓷颗粒,陶瓷颗粒的配比质量少于导电纳米颗粒的配比质量。