CN116606579A - 一种地坪防火涂料 - Google Patents
一种地坪防火涂料 Download PDFInfo
- Publication number
- CN116606579A CN116606579A CN202310314192.2A CN202310314192A CN116606579A CN 116606579 A CN116606579 A CN 116606579A CN 202310314192 A CN202310314192 A CN 202310314192A CN 116606579 A CN116606579 A CN 116606579A
- Authority
- CN
- China
- Prior art keywords
- component
- parts
- water
- floor
- fire retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种地坪防火涂料，由甲组分和乙组分均匀混合组成，甲组分由下述第一组分和第二组分均匀混合而成，其中，第一组分按质量份构成：水性环氧固化剂25‑35份、水22‑26份、分散剂0.6‑1份、第一消泡剂0.2‑0.4份、流平剂0.4‑0.6份、钛白粉12‑15份和蜡粉1份。本发明的地坪防火涂料，在施工完成后其硬度，不易被压坏，不易产生形变和留下痕迹，并且本地坪防火涂料在材料上使用了水性改性丙烯酸树脂等，使得该地坪防火涂料不仅没有任何的异味，而且还具有良好的抗拉抗裂性能，使用起来更加可靠，通过添加三氧化二锑和纳米二氧化铝分别作为阻燃剂和吸附剂，使得该地坪涂料干燥后，具有防火和吸附性能，可以进行防火和对空气中的有害气体等进行吸附。
Description
技术领域
本发明涉及地坪涂料技术领域，具体为一种地坪防火涂料。
背景技术
凡是用水作溶剂或者作分散介质的涂料，都可称为水性涂料。依据涂料中粘合剂类别,水性涂料被分为两大类：天然物质或矿物质(如硅酸钾)的天然水性涂料和人工合成树脂(如丙烯酸树脂)的石油化工水性涂料。此处仅对人工合成树脂类的水性涂料进行阐述。水性涂料包括水溶性涂料、水稀释性涂料、水分散性涂料(乳胶涂料)3种。水溶性涂料是以水溶性树脂为成膜物，以聚乙烯醇及其各种改性物为代表，除此之外还有水溶醇酸树脂、水溶环氧树脂及无机高分子水性树脂等。地坪涂料就是采用环氧树脂原料为主剂，添加颜料，溶剂，助剂固化剂经过调配而成的地面装饰材料，研究生产而成的环氧油性地坪漆等都成为地坪涂料，地坪涂料对于保护地面，起到防尘，耐磨，清洁，防潮的效果，所以被现代工业地面，商业地面，车库地面等广泛使用和推广；
目前地坪行业中大多是以环氧地坪涂料为主流，环氧地坪涂料在耐候，防腐，硬度上较聚氨酯体系的地坪涂料偏劣势，同时普通聚氨酯有存在异味大的缺陷，并且现有的地坪涂料防火性能一般，而且还不具有吸附功能，且抗拉抗裂性能较差，容易出现开裂的情况，因此我们提出一种地坪防火涂料，用于解决上述问题。
发明内容
(一)解决的技术问题
针对现有技术的不足，本发明提供了一种地坪防火涂料，解决了现有目前地坪行业只要是环氧为主流，环氧在耐候，防腐，硬度上较聚氨酯体系偏劣势，同时普通聚氨酯又存在异味大等问题。
(二)技术方案
为实现以上目的，本发明通过以下技术方案予以实现：一种地坪防火涂料，由甲组分和乙组分均匀混合组成，甲组分由下述第一组分和第二组分均匀混合而成，其中，第一组分按质量份构成：水性环氧固化剂25-35份、水22-26份、分散剂0.6-1份、第一消泡剂0.2-0.4份、流平剂0.4-0.6份、钛白粉12-15份和蜡粉1份；
第二组分按质量份构成：第二消泡剂0.2-0.4份、二丙二醇丁醚5份、三氧化二锑20-30份和吸附剂15-25份；
乙组分为水性高分子环氧乳液100份；
所述水性高分子环氧乳液为水性改性丙烯酸树脂乳液。
优选的，所述甲乙组分按质量份比为4：3。
优选的，所述第一组分各原料均加入高速分散机中高速分散混合，分散混合时间为30min，且分散细度为30μm以下。
优选的，所述第一组分混合完成后将第二组分依次加入高速分散机中与第一组分进行均匀分散混合，混合时间为5-10分钟。
优选的，所述水为去离子水，且所述水分为三次依次加入混合溶液中。
优选的，所述吸附剂为纳米二氧化铝。
优选的，所述水性改性丙烯酸树脂乳液为通过三异硬酯酰基钛酸异丙酯对甲基丙烯酸甲酯进行改性制得。
优选的，包括以下施工工艺：将甲组分和乙组分按比例称重加在一起充分搅拌3-5min后，加入8-10％水和颜料继续均匀搅拌并静置5min，涂布量0.15-0.2KG/m2。
(三)有益效果
本发明提供了一种地坪防火涂料。具备以下有益效果：
本发明的地坪防火涂料，在施工完成后其硬度，不易被压坏，不易产生形变和留下痕迹，并且本地坪防火涂料在材料上使用了水性聚酯氨等，使得该地坪防火涂料没有任何的异味，不会对周围的空气环境造成影响，使用起来更加可靠，并且添加了三氧化二锑作为阻燃剂使得其具有一定的防火性能，通过添加的纳米二氧化铝作为吸附剂，可以在该地坪涂料干燥后，内部的纳米二氧化铝可以作为吸附剂使用，可以对空气中的有害气体等进行吸附，通过三异硬酯酰基钛酸异丙酯对甲基丙烯酸甲酯进行改性制得的异丙基三油酸酰氧基钛酸酯改性丙烯酸树脂具有良好的耐磨性、附着力以及柔韧性，制备成涂料时，无需外加抗划伤助剂，其具有良好的抗划伤性能。
具体实施方式
下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例：
本发明实施例提供一种地坪防火涂料，由甲组分和乙组分均匀混合组成，甲组分由下述第一组分和第二组分均匀混合而成，其中，第一组分按质量份构成：水性环氧固化剂25-35份、水22-26份、分散剂0.6-1份、第一消泡剂0.2-0.4份、流平剂0.4-0.6份、钛白粉12-15份和蜡粉1份；
第二组分按质量份构成：第二消泡剂0.2-0.4份、二丙二醇丁醚5份、三氧化二锑20-30份和吸附剂15-25份；
乙组分为水性高分子环氧乳液100份；
水性高分子环氧乳液为水性改性丙烯酸树脂乳液。
甲乙组分按质量份比为4：3。
第一组分各原料均加入高速分散机中高速分散混合，分散混合时间为30min，且分散细度为30μm以下，在高速分散机的作用下可以预先制得甲组分中的第一组分，以便后续使用。
第一组分混合完成后将第二组分依次加入高速分散机中与第一组分进行均匀分散混合，混合时间为5-10分钟，将第一组分和第二组分充分分散混合即可制得相应的甲组分，从而便于与乙组分进行分散混合，然后制得该地坪防火涂料。
水为去离子水，且水分为三次依次加入混合溶液中，将去离子水分为三份，第一份去离子水在制取甲组分中的第一组分时使用，制得第一组分，第二份去离子水在将第一组分与第二组分进行分散混合时使用，从而制得完整的甲组分，第三份去离子水则是在将甲组分与乙组分进行混合时使用，从而可以制得完整的地坪防火涂料。
吸附剂为纳米二氧化铝，在地坪涂料干燥后纳米三氧化二铝中的水分流失，从而使得其孔漏出，使其具有一定的吸附性能，从而可以对空气中的部分气体进行吸附，并且采用纳米二氧化铝作为原料还可以使得该地坪防火涂料具有绝缘性，并且可以调整流动性能。
所述水性改性丙烯酸树脂乳液为通过三异硬酯酰基钛酸异丙酯对甲基丙烯酸甲酯进行改性制得，通过三异硬酯酰基钛酸异丙酯对甲基丙烯酸甲酯进行改性制得的异丙基三油酸酰氧基钛酸酯改性丙烯酸树脂具有良好的耐磨性、附着力以及柔韧性，制备成涂料时，无需外加抗划伤助剂，其具有良好的抗划伤性能。
施工工艺：将甲组分和乙组分按比例称重加在一起充分搅拌3-5min后，加入8-10％水和颜料继续均匀搅拌并静置5min，涂布量0.15-0.2KG/m2。
与现有的环氧面漆相比较，其硬度，不易被压坏，不易产生形变和留下痕迹，并且现有的环氧面漆普遍使用普通聚氨酯制成，在使用时会产生较大的异味，影响周围空气环境，本地坪防火涂料在材料上使用了水性聚酯氨等，使得该地坪防火涂料没有任何的异味，不会对周围的空气环境造成影响，使用起来更加可靠，并且添加三氧化二锑作为阻燃剂使得其具有一定的防火性能，通过添加的纳米二氧化铝作为吸附剂，可以在该地坪涂料干燥后，内部的纳米二氧化铝可以作为吸附剂使用，可以对空气中的有害气体等进行吸附，通过三异硬酯酰基钛酸异丙酯对甲基丙烯酸甲酯进行改性制得的异丙基三油酸酰氧基钛酸酯改性丙烯酸树脂具有良好的耐磨性、附着力以及柔韧性，制备成涂料时，无需外加抗划伤助剂，其具有良好的抗划伤性能。
需要说明的是，在本文中，诸如第一和第二等之类的关系术语仅仅用来将一个实体或者操作与另一个实体或操作区分开来，而不一定要求或者暗示这些实体或操作之间存在任何这种实际的关系或者顺序。而且，术语“包括”、“包含”或者其任何其他变体意在涵盖非排他性的包含，从而使得包括一系列要素的过程、方法、物品或者设备不仅包括那些要素，而且还包括没有明确列出的其他要素，或者是还包括为这种过程、方法、物品或者设备所固有的要素。在没有更多限制的情况下，由语句“包括一个引用结构”限定的要素，并不排除在包括所述要素的过程、方法、物品或者设备中还存在另外的相同要素。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (8)
1.一种地坪防火涂料，其特征在于：由甲组分和乙组分均匀混合组成，甲组分由下述第一组分和第二组分均匀混合而成，其中，第一组分按质量份构成：水性环氧固化剂25-35份、水22-26份、分散剂0.6-1份、第一消泡剂0.2-0.4份、流平剂0.4-0.6份、钛白粉12-15份和蜡粉1份；
第二组分按质量份构成：第二消泡剂0.2-0.4份、二丙二醇丁醚5份、三氧化二锑20-30份和吸附剂15-25份；
乙组分为水性高分子环氧乳液100份；
所述水性高分子环氧乳液为水性改性丙烯酸树脂乳液。
2.根据权利要求1所述的一种地坪防火涂料，其特征在于：所述甲乙组分按质量份比为4：3。
3.根据权利要求1所述的一种地坪防火涂料，其特征在于：所述第一组分各原料均加入高速分散机中高速分散混合，分散混合时间为30min，且分散细度为30μm以下。
4.根据权利要求1所述的一种地坪防火涂料，其特征在于：所述第一组分混合完成后将第二组分依次加入高速分散机中与第一组分进行均匀分散混合，混合时间为5-10分钟。
5.根据权利要求1所述的一种地坪防火涂料，其特征在于：所述水为去离子水，且所述水分为三次依次加入混合溶液中。
6.根据权利要求1所述的一种地坪防火涂料，其特征在于：所述吸附剂为纳米二氧化铝。
7.根据权利要求1所述的一种地坪防火涂料，其特征在于：所述水性改性丙烯酸树脂乳液为通过三异硬酯酰基钛酸异丙酯对甲基丙烯酸甲酯进行改性制得。
8.根据权利要求1所述的一种地坪防火涂料，其特征在于：包括以下施工工艺：将甲组分和乙组分按比例称重加在一起充分搅拌3-5min后，加入8-10％水和颜料继续均匀搅拌并静置5min，涂布量0.15-0.2KG/m2。