CN116574548A - Amide type organic friction improver, preparation method and application thereof - Google Patents
Amide type organic friction improver, preparation method and application thereof Download PDFInfo
- Publication number
- CN116574548A CN116574548A CN202310517551.4A CN202310517551A CN116574548A CN 116574548 A CN116574548 A CN 116574548A CN 202310517551 A CN202310517551 A CN 202310517551A CN 116574548 A CN116574548 A CN 116574548A
- Authority
- CN
- China
- Prior art keywords
- friction
- friction modifier
- organic friction
- base oil
- type organic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides an amide type organic friction modifier, a preparation method and application thereof, wherein the structural formula is as follows:the organic friction modifier is an amide compound, diacetone acrylamide and oleylamine are used as reaction substrates, and the reaction is carried out for 24 hours at the temperature of 80 ℃ and the vacuum degree of 0.095MPa, so that the product is obtained. The nitrogen atoms and oxygen atoms in the molecular structure of the organic friction modifier have lone pair electrons, and can form an ordered molecular adsorption film on the surface of metalThe friction of the surface of the metal friction pair is reduced, and the friction-reducing agent has excellent friction-reducing performance in base oil.
Description
Technical Field
The invention relates to the technical field of lubricating oil additives, in particular to an amide type organic friction modifier, a preparation method and application thereof.
Background
At present, the combustion conversion efficiency of automobile fuel is about 38%, and 33% of energy converted into mechanical power is lost due to friction; in order to reduce fuel consumption and emissions, improving fuel economy, in addition to an effective way of improving combustion efficiency of an engine, reducing the friction coefficient of lubricating oil is considered as an effective way of improving fuel economy. Zinc dialkyldithiophosphates (ZDDP) have been used for over seventy years in engine oil formulations, but ZDDP results in exhaust emissions containing P, S and the like, and also reduces the life of the automobile exhaust catalyst. With the continuous upgrading and development of emission regulations of various countries in the world, the requirements of increasingly strict energy conservation and emission reduction and fuel economy improvement of the automobile industry are met, and engine lubricating oil and additives are developing towards the trend of low sulfur, phosphorus and low ash; the amount of ZDDP used will then decrease gradually while still ensuring that the engine oil has stable lubricating properties, and therefore low sulfur phosphorous, ash-free organic friction modifiers (Organic Friction Modifier) have been widely studied and used. The organic friction modifier is a substance which can form a physical or chemical adsorption film on the friction surface so as to reduce the friction coefficient, improve the lubricating property and enhance the film forming capability; the friction modifier can improve the mixing and boundary lubrication of the engine and reduce friction loss, thereby achieving the purpose of energy saving.
Therefore, the development of efficient ashless organic friction modifiers that gradually reduce or replace the use of ZDDP would have significant application prospects.
Disclosure of Invention
The invention aims to provide an amide type organic friction modifier, a preparation method and application thereof, wherein the friction modifier has excellent antifriction performance in poly alpha-olefin base oil, and simultaneously has good synergistic effect when being used together with Zinc Dialkyl Dithiophosphate (ZDDP), so that the usage amount of the ZDDP in the base oil can be reduced, and a lower friction coefficient can be obtained.
The amide type organic friction modifier prepared by the invention has the advantages of simple preparation process, low preparation cost, high yield and excellent antifriction performance.
The invention is realized by the following technical scheme:
an amide-type organic friction modifier having the structure shown below:
(1)DAAMOA
a method of preparing an amide-type organic friction modifier as described above, comprising: diacetone acrylamide and oleylamine are used as reaction substrates, and react for 24 hours at the temperature of 80 ℃ and the vacuum degree of 0.095MPa to obtain the product.
Specifically, the preparation method of the organic friction modifier comprises the following steps:
diacetone acrylamide and oleylamine with the molar ratio of 1:1 are taken as reaction substrates to react for 24 hours at the temperature of 80 ℃ and the vacuum degree of 0.095MPa, so as to obtain the target product.
The invention also provides application of the amide type organic friction modifier, which is used in the poly alpha-olefin base oil, and the using amount of the organic friction modifier in the base oil is 0.5-2 wt% based on the mass of the base oil. For example, the organic friction modifier may be used in the base oil in an amount of 0.5wt%, 0.6wt%, 0.7wt%, 0.8wt%, 0.9wt%, 1wt%, 1.1wt%, 1.2wt%, 1.3wt%, 1.4wt%, 1.5wt%, 1.6wt%, 1.7wt%, 1.8wt%, 1.9wt% or 2wt% based on the mass of the base oil.
Further, the organic friction modifier and ZDDP are added to the base oil simultaneously, the ZDDP being added in an amount of 0.5% to 2.0% by weight of the base oil. For example, the ZDDP is added to the base oil in an amount of 0.5 wt.%, 0.6 wt.%, 0.7 wt.%, 0.8 wt.%, 0.9 wt.%, 1 wt.%, 1.1 wt.%, 1.2 wt.%, 1.3 wt.%, 1.4 wt.%, 1.5 wt.%, 1.6 wt.%, 1.7 wt.%, 1.8 wt.%, 1.9 wt.%, or 2 wt.%, based on the mass of the base oil.
The invention has the technical characteristics and beneficial effects that:
the amide type organic friction modifier, the preparation method and the application thereof have the advantages that the preparation flow of the organic friction modifier is simple, the preparation cost is low, the yield is high, and the organic friction modifier can be dissolved in poly alpha-olefin base oil; the nitrogen atoms and the oxygen atoms in the molecular structure of the organic friction modifier are provided with lone pair electrons, electrons can be provided for electron-deficient orbits of metals, the organic friction modifier has a strong adsorption effect on the metals, further an ordered molecular adsorption film is formed on the surfaces of the metals, friction on the surfaces of friction pairs of the metals is reduced, and the organic friction modifier has good antifriction performance; when used together with ZDDP, the composition has good synergistic effect, can reduce the use amount of ZDDP in base oil, and can obtain lower friction coefficient.
Drawings
FIG. 1 is a synthetic route diagram of example 1 of the present invention.
FIG. 2 is an infrared spectrum of the friction modifier prepared in example 1 of the present invention.
FIG. 3 is a mass spectrum of the friction modifier prepared in example 1 of the present invention.
FIG. 4 is a graph showing the comparison of friction coefficients at different temperatures for the friction modifier prepared in example 1 of the present invention.
FIG. 5 is a graph showing the comparison of friction coefficients of the friction modifier prepared in example 1 of the present invention at various addition amounts.
FIG. 6 is a graph of friction coefficient comparisons for friction modifiers prepared in example 1 of the present invention used with ZDDP.
Detailed Description
The invention is further illustrated and described below in connection with specific examples.
Example 1
3.38g (0.02 mol) of diacetone acrylamide and 5.35g (0.02 mol) of oleylamine are weighed into a 25ml single-neck flask, and reacted for 24 hours at the temperature of 80 ℃ and the vacuum degree of 0.095MPa to obtain 8.29g (yield 99.1 wt%) of a target product, namely DAAMOA, wherein the reaction process is shown in figure 1.
And (3) infrared spectrum analysis:
the infrared spectrum of DAAMOA containing target product obtained in the above example 1 is shown in FIG. 2, 3500-3400cm in the infrared spectrum of DAAMOA -1 The characteristic absorption peak of the N-H bond of (2) disappears, which indicates that the N-H bond in the oleylamine reacts; 1710cm in DAAMOA infrared spectrogram of product -1 The ketone c=o stretching vibration absorption peak at this point disappeared while appearing at 1662cm -1 C=n bond stretching vibration absorption peak of (c=n), indicating ketone-c=o in diacetone acrylamide and-NH in oleylamine molecule 2 The reaction occurs, producing a-c=n bond. Further, it was demonstrated that the ketoamine condensation reaction occurred between oleylamine and diacetone acrylamide.
Mass spectrometry:
the mass spectrum of the product DAAMOA is shown in figure 3, and a peak is obvious at a mass-to-charge ratio of 419.4005, and the product is obtained by carrying out ketoamine condensation reaction on diacetone acrylamide and oleylamine and removing a molecule of water. As can be seen by combining an infrared spectrogram and a mass spectrogram analysis, diacetone acrylamide and oleylamine undergo a ketoamine condensation reaction to generate a product DAAMOA.
Friction performance test:
the test instrument is a TE-77 long-range reciprocating friction test machine, and the upper friction pair isThe cylindrical pins, the lower friction pair is a 38mm multiplied by 58mm multiplied by 3.9mm plate, the materials are GCr15 steel, and the contact mode is line contact.
The product DAAMOA obtained in example 1 was dissolved in poly-alpha-olefin base oil (PAO 6, exxonMobil) in an amount of 1wt% (based on the mass of the base oil) with stirring, and the reciprocating friction test was performed at 25 ℃, 80 ℃, 135 ℃ respectively under the following test conditions: load 100N, stroke 10mm, frequency 10Hz, time 3600s.
TABLE 1 average coefficient of friction for products of example 1 subjected to reciprocating friction tests at different temperatures
As can be seen from the data presented in table 1 and the friction coefficient curves presented in fig. 4, the friction coefficient of the sample added with the DAAMOA product of example 1 at different temperatures is reduced by 11.3% to 27.5% compared with the base oil PAO 6.
Further examining the tribological properties of the product of example 1, DAAMOA, added in amounts of 0.5 wt.%, 1 wt.% and 2 wt.% respectively, based on the mass of the base oil PAO6, the test conditions were: the load is 100N, the stroke is 10mm, the frequency is 10Hz, the temperature is 80 ℃, and the time is 3600s.
TABLE 2 average coefficient of friction for the products of example 1 tested for reciprocating friction at various addition levels
As can be seen by combining the data presented in Table 2 and the friction coefficient curves presented in FIG. 5, the friction coefficient of the samples added with different amounts of DAAMOA product of example 1 was reduced by 21.1% to 27.5% compared with the base oil PAO 6.
Tribological property evaluations were performed on the product of example 1, DAAMOA, and ZDDP. The samples were oil samples obtained by adding 1wt% DAAMOA, 1wt% ZDDP, 0.5wt% DAAMOA+0.5wt% ZDDP to base oil PAO6 (the following mass percentages are based on the mass of PAO6, respectively). The test conditions were: the load is 100N, the stroke is 10mm, the frequency is 10Hz, the temperature is 135 ℃, and the time is 3600s.
TABLE 3 average coefficient of friction for the products of example 1 and ZDDP used alone and after compounding
As can be seen from the data and friction coefficient curves presented in table 3 and fig. 6, the friction coefficient of the product of example 1, DAAMOA, after being compounded with ZDDP, is significantly lower than that of the product obtained by adding DAAMOA and ZDDP alone, and the reduction is more than 20.5%, which indicates that the product and ZDDP have a synergistic effect.
The invention has the beneficial effects that:
the amide type organic friction modifier, the preparation method and the application thereof have the advantages that the preparation flow of the organic friction modifier is simple, the preparation cost is low, the yield is high, and the organic friction modifier can be dissolved in base oil PAO 6; the organic friction modifier has lone pair electrons on nitrogen atoms and oxygen atoms in a molecular structure, can provide electrons for electron-deficient orbits of metals, has strong adsorption effect on the metals, further forms an ordered molecular adsorption film on the surfaces of the metals, reduces friction on the surfaces of friction pairs of the metals, and has good antifriction performance; the organic friction modifier has good synergistic effect when used together with ZDDP, can reduce the use amount of ZDDP in base oil, and obtains lower friction coefficient.
The foregoing description of the preferred embodiments of the invention is not intended to be limiting, but rather is intended to cover all modifications, equivalents, alternatives, and improvements that fall within the spirit and scope of the invention.
Claims (6)
1. An amide-type organic friction modifier characterized in that the organic friction modifier has a structural formula of formula (1):
2. a method of preparing the amide type organic friction modifier of claim 1, comprising: diacetone acrylamide and oleylamine are used as reaction substrates, and react for 24 hours at the temperature of 80 ℃ and the vacuum degree of 0.095MPa to obtain the product.
3. The method for preparing an amide type organic friction modifier according to claim 2, wherein the molar ratio of diacetone acrylamide to oleylamine is 1:1.
4. Use of an amide type organic friction modifier according to claim 1, wherein the organic friction modifier is added to a base oil in an amount of 0.5 to 2.0wt% of the base oil based on the mass of the base oil.
5. The use of an amide type organic friction modifier according to claim 4 wherein the base oil is a polyalphaolefin.
6. The use of an amide type organic friction modifier according to claim 4 wherein the organic friction modifier and zinc dialkyldithiophosphate are added simultaneously to the base oil in an amount of 0.5wt% to 2.0wt% of the base oil.