CN116462939A - 树脂模制品和包括其的雷达模块 - Google Patents
树脂模制品和包括其的雷达模块 Download PDFInfo
- Publication number
- CN116462939A CN116462939A CN202211674375.7A CN202211674375A CN116462939A CN 116462939 A CN116462939 A CN 116462939A CN 202211674375 A CN202211674375 A CN 202211674375A CN 116462939 A CN116462939 A CN 116462939A
- Authority
- CN
- China
- Prior art keywords
- molded article
- resin molded
- weight
- article according
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种具有优异的抗冲击性和耐候性以及低介电损耗的树脂模制品和一种包括该树脂模制品的雷达模块,其中该树脂模制品具有在77GHz的频率范围内的3.7F/m或更小的介电常数和0.023或更小的介电损耗、具有根据ASTM D3763的400kg·m/s2或更大的高速冲击强度,并且具有在77~79GHz的频率范围内的‑0.8dB或更大的电磁波透射系数。
Description
相关申请的交叉引用
本申请要求于2022年1月18日在韩国知识产权局提交的韩国专利申请第10-2022-0007004号的权益,其公开内容通过引用整体并入本文作为参考。
技术领域
本发明涉及一种具有优异的抗冲击性和耐候性和低介电损耗的树脂模制品和包括该树脂模制品的雷达模块。
背景技术
作为诸如汽车的车辆的进步的一部分,对具有各种设计和功能的部件的需求迅速增加。特别是,随着车辆事故的问题日益增多,利用诸如车辆雷达的发送/接收控制装置来提高驾驶员在驾驶车辆时的安全性的技术变得越来越重要。
此类发送/接收控制装置技术的示例包括ACC技术或CDM技术,该ACC技术检测前方车辆并根据前方车辆的速度控制车辆的速度,并且该CDM技术在预测到前方车辆与主车辆之间的碰撞时操作具有对驾驶员的警报的自动制动器。
另一方面,通过在车辆上搭载有雷达模块,并通过经由从该雷达模块辐射的激光束的发送/接收来收集前方车辆的移动信息和周围环境的变化信息,从而实现发送/接收控制装置技术。
通常,雷达模块包括用于发送/接收激光束的天线、诸如毫米波射频集成电路(radio frequency integrated circuit,RFIC)等的内部电子组件,和用于保护这些组件的雷达天线罩。此外,用于保护雷达模块的盖设置在雷达天线罩的前面。
用于遮盖诸如雷达天线罩的雷达模块的前面和所述盖的透射盖需要具有足够的刚度来保护内部组件(诸如雷达内部的天线)不受外部环境影响,使得内部组件正常操作,并且需要最小化在从天线辐射的雷达束的透射期间的透射损耗。
因此,与作为增强填料的玻璃纤维(glass fiber,GF)混合的PBT类主要材料通常用作雷达模块诸如雷达天线罩和盖,但是随着玻璃纤维含量的增加,所需材料的机械性能增加,而其脆性劣化,使得难以确保由于外部冲击引起的刚性,并且还存在影响雷达传输性能的介电性能劣化的问题。另外,当将橡胶类添加剂与PBT类主要材料混合以改善韧性时,可以改善抗冲击性,但是耐候性降低,并且存在的问题在于,根据橡胶类添加剂的分散性,介电性能存在偏差。
因此,需要开发抗冲击性、耐候性优异、低介电损耗优异的诸如雷达天线罩、盖等雷达模块材料。
[相关技术文献]
[专利文献]
(专利文献1)KR 10-2021-0054605A。
发明内容
本发明的一个方面提供了一种树脂模塑制品,其可以有效地用作具有优异的抗冲击性、耐候性和介电性能的雷达模块材料。
本发明的另一方面提供一种包括树脂模制品的雷达模块。
根据本发明的一个方面,提供一种树脂模制品,具有在77GHz的频率范围内的3.7F/m或更小的介电常数和0.023或更小的介电损耗,根据ASTM D3763的400kg·m/s2或更大的高速冲击强度,和在77~79GHz的频率范围内的-0.8dB或更大的电磁波透射系数。
根据本发明的另一方面,提供一种包括该树脂模制品的雷达模块。
(1)本发明提供一种树脂模制品,具有在77GHz的频率范围内的3.7F/m或更小的介电常数和0.023或更小的介电损耗,具有根据ASTM D3763测定的400kg·m/s2或更大的高速冲击强度,并具有在77GHz~79GHz的频率范围内的-0.8dB或更大的电磁波透射系数。
(2)在上述(1)中,本发明提供一种树脂模制品,根据ASTM D3763,其高速冲击吸收能为3.5kg·m2/s2或更大。
(3)在上述(1)或(2)中,本发明提供一种树脂模制品,具有在77GHz的频率范围内的2.5~3.5F/m的介电常数,0.005~0.020的介电损耗。
(4)在上述(1)~(3)中的任一项中,本发明提供一种树脂模制品,其具有根据ASTMD3763的400kg·m/s2或更大的高速冲击强度和3.8kg·m2/s2或更大的高速冲击吸收能量。
(5)在上述(1)~(4)中的任一项中,本发明提供一种树脂模制品,其在77GHz~79GHz的频率范围内的电磁波透射系数为-0.5dB或更大。
(6)在上述(1)~(5)中的任一项中,本发明提供一种树脂模制品,其色差(△E)为3.0或更小,并且该色差表示1,250kJ/m2紫外线(340nm)照射后的色度与照射前的色度相比的变化:△E=照射后的色度-照射前的色度。
(7)在上述(1)~(6)中的任一项中,本发明提供一种树脂模制品,其包括聚酯类树脂组合物、无机填料和橡胶型冲击改性剂,该聚酯类树脂组合物具有包括聚对苯二甲酸丁二醇酯(PBT)和聚碳酸酯(PC)的基料树脂。
(8)在上述(7)中,本发明提供一种树脂模制品,其中基料树脂包括65~95重量%的聚对苯二甲酸丁二醇酯(PBT)和5~35重量%的聚碳酸酯(PC)。
(9)在上述(7)中,本发明提供一种树脂模制品,其基于100重量份的基料树脂包括5~30重量份的无机填料。
(10)在上述(7)中,本发明提供一种树脂模制品,其基于100重量份的基料树脂包括5~15重量份的橡胶型冲击改性剂。
(11)在上述(7)中,本发明提供一种树脂模制品,其中该无机填料为玻璃纤维。
(12)在上述(7)中,本发明提供一种树脂模塑制品,其中橡胶型冲击改性剂选自线性低密度聚乙烯和乙烯丙烯酸丁酯共聚物中的一者或多者。
(13)在上述(7)中,本发明提供一种树脂模制品,其包括100重量份的包括聚对苯二甲酸丁二醇酯(PBT)和聚碳酸酯(PC)的基料树脂、10~20重量份的无机填料和7~10重量份的橡胶型冲击改性剂,其中基料树脂包括70~90重量%的聚对苯二甲酸丁二醇酯(PBT)和10~30重量%的聚碳酸酯(PC)。
(14)在上述(1)~(13)中的任一项中,本发明提供一种为电磁波吸收材料的树脂模制品。
(15)在(1)~(13)中的任一项中,本发明提供作为雷达模块用材料的树脂模制品。
(16)本发明提供一种雷达模块,其包括上述(1)~(15)中的任一项的树脂模制品。
(17)在上述(15)中,本发明提供了一种雷达装置,其中雷达模块包括选自车辆雷达天线罩(radome)和车辆雷达盖(RADAR cover)中的任意一种或多种。
有益效果
根据本发明的树脂模制品的介电损耗、表面冲击强度、电磁波透射系数和颜色变化同时满足特定条件,因此具有耐候性、抗冲击性和介电性能优异的效果。
根据本发明的雷达模块包括树脂模制品,因此具有耐候性、抗冲击性和介电性能同时优异的效果。
具体实施方式
在下文中,将更详细地描述本发明以允许更清楚地理解本发明。
应当理解,在本发明的说明书中使用的词语或术语不应当被解释为限于具有在常用字典中定义的含义。还应当理解,基于发明人可以适当地定义词语或术语的含义以最佳地解释本发明的原理,词语或术语应当被解释为具有与它们在相关技术的上下文和本发明的技术思想中的含义一致的含义。
[术语的定义]
在本说明书中,术语“介电常数(permittivity)(F/m)”是指当电势差施加到某一材料的两端时,相反极性的电荷在所施加的表面上累积的程度。例如,当将特定材料插入两个导体之间,然后将电压施加到导体上时,如果在施加(+)电压的材料表面上感应出(-)电荷,并且在没有电流流动的情况下在施加(-)电压的材料表面上感应出(+)电荷,则由材料中感应出的电荷量形成的每单位长度(m)的电容(Farad)的大小被称为介电常数(F/m)。
在本说明书中,所谓“介质损耗(dielectric loss)”是指对电介质施加电场时,若电位移相对于电场产生相位延迟,则在材料中一部分电能变化为热,被称为介质损耗,以损耗角正切(loss tangent)表示。
在本说明书中,术语“包括”和“具有”及其派生词,无论它们是否被具体公开,都不是要排除任何附加的部件、步骤或过程的存在。为了避免任何不确定性,除非另有说明,否则通过使用术语“包括”要求保护的所有材料和方法可以包括任何另外的添加剂、补充剂或化合物。相反,术语“基本上由…组成”在除了对操作性不重要的那些之外排除了来自任何随后描述的范围内的任何其他组分、步骤或程序。术语“由…组成”排除了没有具体说明或列出的任何组分、步骤或程序。
[测定方法和条件]
在本说明书中,在制备尺寸为100mm×100mm、厚度为2T的样品之后,使用矢量网络分析仪(Vector Network Analyzer)(MS46322A,ANRITSU公司)和分裂柱介电谐振器(SplitPost Dielectric Resonator)(QWED公司),通过开式谐振腔(OPEN RESONATOR)分析法测量“介电常数和介电损耗”,并在77GHz的频率下测量。
在本说明书中,高速冲击强度和高速冲击吸收能是根据ASTM D3763标准,通过制备尺寸为100mm×100mm和厚度为2T的样品,使用Dynatup(CEAST9350,INSTRONCorporation),在室温(23±2℃)和50%的相对湿度下,冲击速度设定为3.3m/s,数据采集时间范围设定为30ms来测量的。
在本说明书中,利用自由空间方法(其使用介质聚光透镜)来测量“电磁波透射系数(electromagnetic wave transmission coefficient)”,并且以在77GHz的频率范围中设置的测量频率和在样品的中心点周围设置的测量位置来执行测量,并且电磁波透射系数由在该频率范围中的电磁波透射系数S21的最大绝对值表示。
在本说明书中,“色差(chrominance)(△E)”是使用加速老化试验机(Weather-O-Meter(Ci5000),ATLAS公司)测量的,并且在制备60mm×150mm(宽度×高度)的样品之后,在样品的镜面和腐蚀样品上照射约50kJ/m2/天的紫外线(340nm),总共1250kJ/m2(约25天),这在以下条件下进行:黑色PNL温度:70±2℃(亮)和38±2℃(暗),循环条件:40分钟(50±5%RH)的照射、20分钟(表面喷涂)的照射、60分钟(50±5% RH)的照射和60分钟(95±5% RH/背面喷涂)的非照射,辐照度:0.75±0.02W/m2(340nm),以及过滤器组合:RIGHT LIGHT(内过滤器)和QUARTZ(外过滤器)。然后,计算照射后的色度(chromaticity)相对于照射前的色度的变化(照射后的色度-照射前的色度),并表示为色差(△E)。
树脂模制品
本发明提供一种抗冲击性、耐候性、介电性能优异的树脂模制品,其可以容易地用作雷达模块,特别是车辆用雷达模块材料。
根据本发明的实施例的树脂模制品可以具有在77GHz的频率范围内的3.7F/m或更小的介电常数和0.023或更小的介电损耗,可以具有根据ASTM D3763的400kg·m/s2或更大的高速冲击强度,并且可以具有在77~79GHz的频率范围内-0.8dB或更大的电磁波透射系数。
另外,所述树脂模制品的色差(△E)可以为2.0或更小,其中该色差可以表示与照射前的色度相比,用1,250kJ/m2的紫外线(340nm)照射后的色度的变化(照射后的色度-照射前的色度)。
根据本发明的实施例,树脂模制品同时满足上述介电常数、介电损耗、高速冲击强度、电磁波透射系数和颜色变化,从而具有抗冲击性、耐候性和介电性能均以平衡方式而优异的效果。
具体而言,该树脂模制品在77GHz的频率范围内的介电常数为3.7F/m或更小且介电损耗为0.023或更小,更具体而言,在77GHz的频率范围内的介电常数为2.5F/m~3.5F/m且介电损耗为0.005~0.020,进一步具体而言,在77GHz的频率范围内的介电常数为3.0F/m~3.2F/m且介电损耗为0.005~0.015。
此外,根据ASTM D3763,树脂模制品可具有400kg·m/s2或更大的高速冲击强度,并且根据ASTM D3763,树脂模制品可具有3.5kg·m2/s2或更大的高速冲击吸收能、3.8kg·m2/s2或更大的高速冲击吸收能、或4.0kg·m2/s2或更大的高速冲击吸收能。
作为另一个示例,根据ASTM D3763,树脂模制品可以具有400kg·m/s2或更大的高速冲击强度,并且可以具有3.8kg·m2/s2或更大的高速冲击吸收能。
另外,该树脂模制品在77GHz~79GHz的频率范围内的电磁波透射系数可以为-0.8dB或更大,具体地为-0.8dB~0dB,具体地为-0.5dB或更大,或者为-0.5dB~0dB。在这种情况下,树脂模制品的抗冲击性、耐候性和介电性能以平衡的方式而优异,并且其雷达透射性能也可以同时是优异的。
另外,树脂模制品的色差(△E)可以为3.0或更小,具体地为2.0或更小或1.0或更小,其中色差表示与照射前的色度相比,用1,250kJ/m2的紫外线(340nm)照射后的色度的变化(照射后的色度-照射前的色度)。
另外,根据本发明的实施例,树脂模制品可以是电磁波吸收材料,作为另一示例,树脂模制品可以是用于雷达模块的材料。
同时,树脂模制品可以包括聚酯型树脂组合物,其具有包括聚对苯二甲酸丁二醇酯(polybutylene terephthalate,PBT)和聚碳酸酯(polycarbonate,PC)的基料树脂、无机填料和橡胶型冲击改性剂,作为另一个示例,树脂模制品可以是聚酯型树脂组合物的注塑制品。
此外,由于树脂模制品包括聚酯型树脂组合物,所以树脂模制品可以满足上述介电常数、介电损耗、高速冲击强度、电磁波透射系数和颜色变化,因此可以具有优异的抗冲击性、耐候性和介电性能。
下文,将详细描述聚酯型树脂组合物的各组分。
基料树脂
基料树脂包括聚对苯二甲酸丁二醇酯(PBT)和聚碳酸酯(PC),具体地,可以通过混合聚对苯二甲酸丁二醇酯(PBT)和聚碳酸酯(PC)获得。
另外,基料树脂可以包括65~95重量%的聚对苯二甲酸丁二醇酯(PBT)和5~35重量%的聚碳酸酯(PC),并且具体地,基料树脂可以包括70~90重量%的聚对苯二甲酸丁二醇酯(PBT)和10~30重量%的聚碳酸酯(PC)。
聚对苯二甲酸丁二醇酯(PBT)
聚对苯二甲酸丁二醇酯(PBT)具有由下式1表示的重复单元,并且是熔融温度为215℃~235℃的聚酯型树脂。
[式1]
在上述式1中,n是50~200的整数。
当考虑到包括聚对苯二甲酸丁二醇酯(PBT)的聚酯型树脂的加工性能和机械物理性能的平衡改进时,聚对苯二甲酸丁二醇酯可以具有根据ASTM D2857测量的0.6~1.8dl/g的特性粘度(IV,η),并且具体地,聚对苯二甲酸丁二醇酯可以具有0.7~1.3dl/g或0.9~1.3dl/g的特性粘度。
聚碳酸酯(PC)
聚碳酸酯可以通过使芳香族二羟基化合物与选自光气或碳酸酯前体的化合物反应来制备,具体地,可以通过使芳香族二羟基化合物与光气反应或使用芳香族二羟基化合物与碳酸酯前体诸如碳酸二苯酯、碳酸二芳基酯、碳酸亚乙酯等的酯交换反应来制备。
芳香族二羟基化合物的示例包括:双(4-羟基苯基)甲烷、1,1-双(4-羟基苯基)乙烷、2,2-双(4-羟基苯酚)丙烷(双酚A)、2,2-双(4-羟基苯基)丁烷、1,1-双(4-羟基苯基)环戊烷、1,1-双(4-羟基苯基)环己烷、双(4-羟基苯基)醚、双(4-对羟基苯基)硫醚(bis(4-sihydroxyphenyl)sulfide)、甚至烷基或卤素取代的芳香族二羟基化合物等,具体地可以使用2,2-双(4-羟基苯酚)丙烷(双酚A)。
另外,聚碳酸酯可以是均聚物,或者两种或更多种芳族羟基化合物的共聚物。
此外,聚碳酸酯的重均分子量可以为30,000~80,000g/mol,或40,000~70,000g/mol,在这种情况下,包括聚碳酸酯的树脂模制品的耐化学性和抗冲击性还可以是优异的。
作为另一个示例,聚碳酸酯的熔融指数可以是2~20g/10min,或在300℃和1.2kg负荷下的熔融指数为2~12g/10min,或熔融指数为2~12g/10min。
无机填料
无机填料用于防止树脂模制品的弯曲变形和补充抗冲击性,具体地,可以是玻璃纤维。
此外,玻璃纤维可具有1~50μm,或3~30μm的平均直径,以及100μm~3mm、300μm~1mm,或500μm~1mm的平均长度。
作为另一个示例,玻璃纤维可以是短切原丝(chopped strand)产品,并且玻璃纤维可以具有圆形、矩形、椭圆形、哑铃形或菱形形状的横截面,并且可以具有7~20μm或7~15μm的平均直径,和2~6mm或3~6mm的平均长度。
另外,基于100重量份的基料树脂,可以以5~30重量份或10~20重量份的量包括无机填料,并且如果量小于该范围的下限,则机械强度可能劣化,并且如果量大于该范围的上限,则介电损耗可能增加。
橡胶型冲击改性剂
在本发明的一个实施例中,橡胶型冲击改性剂用于补充包括橡胶型冲击改性剂的树脂模制品的耐候性,其可以选自线性低密度聚乙烯(linear low-densitypolyethylene,LLDPE)和乙烯丙烯酸丁酯共聚物中的一者或多者。
此外,基于100重量份的基料树脂,橡胶型冲击改性剂可以5~15重量份或7~10重量份的量包括在内,如果量小于该范围的下限,则抗冲击性可能显著降低,而如果量大于该范围的上限,则模制品的外观特性可能劣化。
作为另一个示例,树脂模制品包括100重量份的包括聚对苯二甲酸丁二醇酯(PBT)和聚碳酸酯(PC)的基料树脂、5~30重量份的无机填料和5~15重量份的橡胶型冲击改性剂,其中基料树脂可以包括65~95重量%的聚对苯二甲酸丁二醇酯(PBT)和5~35重量%的聚碳酸酯(PC)。
同时,根据本发明的实施例,聚酯型树脂组合物还可包括典型的添加剂,只要其不影响其所需的性能即可,并且添加剂可以是例如抗氧化剂、热稳定剂、光稳定剂、紫外线吸收添加剂、消光剂、增塑剂、脱模剂、抗静电剂、阻燃剂、防滴剂、辐射稳定剂,或其组合。此外,当包括添加剂时,基于100重量份的聚酯型树脂组合物,可以以5重量份或更少、或0.001~5重量份的量包括添加剂。
雷达模块
根据本发明的另一方面,提供了一种包括该树脂模制品的雷达模块。
在上文中,雷达模块可以包括选自车辆雷达天线罩和车辆雷达盖中的一者或多者。
本发明的雷达模块包括上述树脂模制品,因此具有优异的抗冲击性、耐候性和介电性能。
实施例
下文参考示例对本发明进行详细说明。然而,根据本发明的示例可以被修改为其他各种形式,并且本发明的范围不应被解释为限于下文描述的示例。提供本发明的示例以向本领域技术人员更充分地描述本发明。
下文中,实施例和比较例中使用的化合物包括在上述对应的材料中,是市售的一般材料,其典型的具体特征如下。
(1)聚对苯二甲酸丁二醇酯(PBT):1100-211M(CHANG CHUN Group)
(2)聚碳酸酯(PC):PC1300-15(LG CHEM)
(3)无机填料:玻璃纤维(T-187H/MW12,NIPPON ELECTRONIC)
(4)橡胶型冲击改性剂:乙烯丙烯酸丁酯共聚物(ELVALOY AC3427,DuPont)
实施例1
使用超级混合器均匀混合包括80重量%的PBT和20重量%的PC的基料树脂,和基于100重量份的基料树脂的15重量份的无机填料和7.5重量份的橡胶型冲击改性剂来制备树脂组合物,使用双螺杆挤出机在250℃熔融揉合树脂组合物,以通过挤出加工制备粒料。将该粒料在100℃干燥5小时或更久,然后使用LS 170-ton注塑机在250℃的注射温度和100℃的模具温度下注塑,以制造树脂模制品。
实施例2
除了在实施例1中使用10重量份橡胶型冲击改性剂外,以与实施例1相同的方式制备树脂模制品。
比较例1
使用(LG CHEM)材料作为比较例1的材料。
比较例2
使用超级混合器均匀混合包括70重量%PBT和30重量%SAN的基料树脂,和基于100重量份的基料树脂的20重量份的无机填料来制备树脂组合物,使用双螺杆挤出机在250℃熔融揉合树脂组合物,通过挤出加工制备粒料。将该粒料在100℃干燥5小时或更久,然后使用LS 170-ton注塑机在250℃的注射温度和100℃的模具温度下注塑,以制造树脂模制品。
实验例1
对实施例1和实施例2的树脂模制品以及比较例1和比较例2的材料的抗冲击性、介电性能、耐候性和雷达透射性能进行比较分析,结果示于下表1中。
(1)抗冲击性
抗冲击性通过ASTM D3763的落面冲击强度(falling surface impactstrength)、高速冲击强度和冲击吸收能来确认。
对于落面冲击强度,制备五个尺寸各为100mm×100mm和厚度为2.25T的样品,然后将五个粒径各为25mm和重量各为500g的球分别以距样品30cm的高度处投落在五个样品上,以视觉确认是否存在表面裂纹。当所有样品的表面上都存在裂纹时,将其评价为X,当一些样品的表面上存在裂纹时,将其评价为△,当所有样品的表面上都不存在裂纹时,将其评价为○。
高速冲击强度和冲击吸收能是根据ASTM D3763标准,通过制备尺寸为100mm×100mm和厚度为2T的样品,使用Dynatup(CEAST9350,INSTRON Corporation),在室温(23±2℃)和50%的相对湿度下,冲击速度设定为3.3m/s,数据采集时间范围设定为30ms来测量的。
(2)介电性能
介电性能通过介电常数和介电损耗(tan损耗)来确认,介电常数和介电损耗是在制作了尺寸100mm×100mm、厚度2T的样品后,使用矢量网络分析仪(MS46322A,ANRITSU公司),通过开式谐振腔(OPEN RESONATOR)分析法测定,在频率77GHz下测定。
(3)耐候性
使用加速老化试验机(Weather-O-Meter(Ci5000),ATLAS公司),制备60mm×150mm(宽度×高度)的样品,在样品的镜面和腐蚀样品上照射约50kJ/m2/天的紫外线(340nm),总共1250kJ/m2(约25天),这在以下条件下进行:黑色PNL温度:70±2℃(亮)和38±2℃(暗),循环条件:40分钟(50±5% RH)的照射、20分钟(表面喷涂)的照射、60分钟(50±5% RH)的照射和60分钟(95±5% RH/背面喷涂)的非照射,辐照度:0.75±0.02W/m2(340nm),以及过滤器组合:RIGHT LIGHT(内过滤器)和QUARTZ(外过滤器)。然后,用色差(△E)和G/S等级展示结果,色差(△E)表示照射后的色度与照射前的色度相比的变化(照射后的色度-照射前的色度)。根据结果,色差(ΔE)为3.0或更小、G/S等级为4级或更大时的耐候性优异。
这里,G/S等级表示灰度级,其中从白色到全黑的渐变亮度被分类为10个等级,其以10%被逐步地分类,0表示全白,并且10表示全黑。
(4)雷达透射(LADAR transmission)性能
雷达透射性能通过在77GHz和77GHz到79GHz的频率范围内的电磁波透射系数来确认,电磁波透射系数利用自由空间方法(其使用介质聚光透镜)来测量,并且测量是在77GHz和77GHz到79GHz的频率范围内设定的测量频率和在样品的中心点周围设定的测量位置下进行的,并且由在该频率范围内的电磁波透射系数S21的最大绝对值来表示。
[表1]
如上表1所示,实施例1和实施例2的树脂模制品满足本发明给出的介电损耗、表面冲击强度和电磁波透射系数以及色差的特定值,并且与对比例1和对比例2的树脂模制品相比具有显着优异的耐候性、抗冲击性和介电性能。
同时,在比较例1的情况下,所有样品在落面冲击性能试验中都有裂纹,因此不能确认它的其他性能。
Claims (17)
1.一种树脂模制品,具有:
在77GHz的频率范围内的3.7F/m或更小的介电常数和0.023或更小的介电损耗;
根据ASTM D3763的400kg·m/s2或更大的高速冲击强度;和
在77GHz~79GHz的频率范围内的-0.8dB或更大的电磁波透射系数。
2.根据权利要求1所述的树脂模制品,其中所述树脂模制品具有根据ASTM D3763的3.5kg·m2/s2或更大的高速冲击吸收能。
3.根据权利要求1所述的树脂模制品,其中所述树脂模制品具有在77GHz的频率范围内的2.5F/m~3.5F/m的介电常数和0.005~0.020的介电损耗。
4.根据权利要求1所述的树脂模制品,其中所述树脂模制品具有根据ASTM D3763的400kg·m/s2或更大的高速冲击强度和3.8kg·m2/s2或更大的高速冲击吸收能。
5.根据权利要求1所述的树脂模制品,其中所述树脂模制品具有在77GHz~79GHz的频率范围内的-0.5dB或更大的电磁波透射系数。
6.根据权利要求1所述的树脂模制品,其中所述树脂模制品的色差(△E)为3.0或更小,并且其中所述色差表示与照射前的色度相比在用1,250kJ/m2的紫外线(340nm)照射后的色度变化:
△E=照射后的色度-照射前的色度。
7.根据权利要求1的所述树脂模制品,包括聚酯型树脂组合物,所述聚酯型树脂组合物包括:
基料树脂,其包括聚对苯二甲酸丁二醇酯(PBT)和聚碳酸酯(PC);
无机填料;和
橡胶型冲击改性剂。
8.根据权利要求7所述的树脂模制品,其中所述基料树脂包括65~95重量%的聚对苯二甲酸丁二醇酯(PBT)和5~35重量%的聚碳酸酯(PC)。
9.根据权利要求7所述的树脂模制品,其中基于100重量份的所述基料树脂,包括5~30重量份含量的所述无机填料。
10.根据权利要求7所述的树脂模制品,其中基于100重量份的所述基料树脂,包括5~15重量份含量的所述橡胶型冲击改性剂。
11.根据权利要求7所述的树脂模制品,其中所述无机填料为玻璃纤维。
12.根据权利要求7所述的树脂模制品,其中所述橡胶型冲击改性剂选自线型低密度聚乙烯和乙烯丙烯酸丁酯共聚物中的一者或多者。
13.根据权利要求7所述的树脂模制品,包括:
100重量份的包括聚对苯二甲酸丁二醇酯(PBT)和聚碳酸酯(PC)的基料树脂;
10~20重量份的所述无机填料;和
7~10重量份的橡胶型冲击改性剂,其中所述基料树脂包括70~90重量%的聚对苯二甲酸丁二醇酯(PBT)和10~30重量%的聚碳酸酯(PC)。
14.根据权利要求1所述的树脂模制品,其中所述树脂模制品是电磁波吸收材料。
15.根据权利要求1所述的树脂模制品,其中所述树脂模制品是用于雷达模块的材料。
16.一种雷达模块,包括根据权利要求1所述的树脂模制品。
17.根据权利要求16所述的雷达模块,其中所述雷达模块包括选自车辆雷达天线罩和车辆雷达盖中的一者或多者。